Elektroda busa nikel termodifikasi NiCo2O4 (NiCo2O4/Busa Nikel) dengan morfologi hollow spheres telah berhasil dipreparasi menggunakan metode hidrotermal. Karakterisasi material menggunakan Scanning Electron Microscopy Energy Dispersive X-Ray (SEM-EDX) dan Transmission Electron Microscopy (TEM) menunjukkan bahwa struktur lubang dari NiCo2O4 berhasil terbentuk dari hasil penghilangan template SiO2 nanospheres yang terlah disintesis sebelumnya. NiCo2O4 yang terdeposisi pada busa nikel dikarakterisasi menggunakan Scanning Electron Microscopy Energy Dispersive X-Ray (SEM-EDX) dan X-Ray Photoelectron Spectroscopy (XPS). Kinerja elektroda NiCo2O4/ busa nikel untuk penentuan kadar glukosa dalam larutan Natrium Hidroksida (NaOH) dievaluasi dengan teknik siklik voltammetry. Struktur lubang NiCo2O4 dapat meningkatkan luas permukaan elektrokatif dan mempercepat transfer elektron sehingga sensor dapat menunjukkan linearitas arus oksidasi yang tinggi (R2=0,9895) pada rentang konsentrasi 0,25 – 2,0 μM dengan nilai perkiraan batas deteksi (LOD) sebesar 0,13 μM dan sensitivitas 22,57 mAμM-1 serta nilai relative standard deviation (RSD) sebesar 1,86% setelah tujuh kali pengukuran. Hasil tersebut menunjukkan kinerja material yang sangat baik dan potensi yang menjanjikan untuk pengembangan sensor glukosa selanjutnya

---

Modified nickel foam electrodes NiCo2O4 (NiCo2O4 / Ni Foam) with hollow spherical morphology were successfully prepared using the hydrothermal method. Material characterization using Scanning Electron Microscopy Energy Dispersive X-Ray (SEM-EDX) and Transmission Electron Microscopy (TEM) which shows the hole structure of NiCo2O4 developed from the results of removing the template on SiO2 nanospheres that has been previously synthesized. NiCo2O4 deposited on the surface of nickel foam was characterized using Scanning Electron Microscopy Energy Dispersive X-Ray (SEM-EDX) and X-Ray Photoelectron Spectroscopy (XPS). The performance of NiCo2O4/ Nickel foam electrodes for glucose levels in Sodium Hydroxide (NaOH) solutions was evaluated by cyclic voltammetry techniques. The NiCo2O4 hole structure can increase electrocative surface area and increase electron transfer so that the sensor can show high linearity of oxidation currents (R2 = 0,9895) in the concentration range of 0,25 – 2,0 μM with estimated limit of detection (LOD) value of 0,13 μM and sensitivity of 22.57 mAμM-1 and the relative standard deviation value (RSD) of 1,86% after seven measurements. These results show excellent material performance and promising potential for further sensor development.