Sintesis Ni-phen/MC sebagai Katalis Reaksi Karboksilasi Fenilasetilena dengan CO2 = Synthesis of Ni-phen/MC as Catalyst for carboxylation Reaction of phenylacetylene with CO2

Riri Andriyanti; Iman Abdullah, supervisor; Dita Arifa Nurani, supervisor; Agustino Zulys, examiner; Muhammad Ridwan, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019)

 Abstrak

Carbon dioxide is a renewable C1 resource for synthesis chemicals. CO2 in carboxylation reactions requires catalysts Ni complex for CO2 activation. However, the use of Ni complex homogeneous catalysts in the reaction is still less efficient due to the difficult in separating the product and catalyst. Therefore, it is necessary to heterogenize the Ni complex in solid supporting such as mesoporous carbon. In this research, a carboxylation reaction with CO2 was tested using a Ni catalyst that was functionalized with phenanthroline (phen) ligand impregnated on the solid support of mesoporous carbon. Soft template method has been successfully used in mesoporous carbon synthesis with phloroglucinol and formaldehyde prekursors as a carbon source, Pluronic F127 as a structural directing agent, and HCl as an acid catalyst. Modification of the catalyst was carried out by impregnation of Ni from Ni(NO3)2.6H2O which was then functionalized with phenanthroline (phen) ligands into mesoporous carbon to form Ni-phen/MC catalysts. Mesoporous carbon material (MC) and Ni-phen/MC are characterized by FT-IR, XRD, SEM-EDX, and SAA. The results of SAA characterization showed that the pore diameter of MC was 6.7174 nm and Ni-phen/MC was 5.08 nm which indicate that the material was mesoporous. Ni-phen/MC material was then used as a heterogeneous catalyst in the carboxylation reaction of phenylacetylene with CO2. The reaction were carried out in several variations of conditions, temperature variations (25oC, 50oC and 75oC), time variations (4 hours, 8 hours and 16 hours), variations in catalyst types (MC, Ni-phen and Ni-phen/MC). Based on the results of the reaction, the optimum conditions was obtained at 25oC for 8 hour of reaction time using Ni-phen/MC catalyst. The main product of the carboxylation reaction is identified by the HPLC instrument, while the remaining catalyst that has been used in the reaction was identified using the FT-IR instrument.

Carbon dioxide is a renewable C1 resource for synthesis chemicals. CO2 in carboxylation reactions requires catalysts Ni complex for CO2 activation. However, the use of Ni complex homogeneous catalysts in the reaction is still less efficient due to the difficult in separating the product and catalyst. Therefore, it is necessary to heterogenize the Ni complex in solid supporting such as mesoporous carbon. In this research, a carboxylation reaction with CO2 was tested using a Ni catalyst that was functionalized with phenanthroline (phen) ligand impregnated on the solid support of mesoporous carbon. Soft template method has been successfully used in mesoporous carbon synthesis with phloroglucinol and formaldehyde prekursors as a carbon source, Pluronic F127 as a structural directing agent, and HCl as an acid catalyst. Modification of the catalyst was carried out by impregnation of Ni from Ni(NO3)2.6H2O which was then functionalized with phenanthroline (phen) ligands into mesoporous carbon to form Ni-phen/MC catalysts. Mesoporous carbon material (MC) and Ni-phen/MC are characterized by FT-IR, XRD, SEM-EDX, and SAA. The results of SAA characterization showed that the pore diameter of MC was 6.7174 nm and Ni-phen/MC was 5.08 nm which indicate that the material was mesoporous. Ni-phen/MC material was then used as a heterogeneous catalyst in the carboxylation reaction of phenylacetylene with CO2. The reaction were carried out in several variations of conditions, temperature variations (25oC, 50oC and 75oC), time variations (4 hours, 8 hours and 16 hours), variations in catalyst types (MC, Ni-phen and Ni-phen/MC). Based on the results of the reaction, the optimum conditions was obtained at 25oC for 8 hour of reaction time using Ni-phen/MC catalyst. The main product of the carboxylation reaction is identified by the HPLC instrument, while the remaining catalyst that has been used in the reaction was identified using the FT-IR instrument.

 File Digital: 1

Shelf
 S-Riri Andriyanti.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xviii, 91 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-pdf 14-22-17959606 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20501614
Cover