Pengaruh Basisitas Biner Pada Proses Selektif Reduksi Bijih Nikel Laterit Jenis Limonit = Effect of Binary Basicity on Selective Reduction Process of Limonitic Nickel Laterite Ore

Khulud Saekhan; Bambang Suharno, supervisor; Deni Ferdian, examiner (Fakultas Teknik Universitas Indonesia, 2020)

 Abstrak

Perkembangan metode selektif reduksi dilakukan untuk mengolah bijih nikel laterit untuk menghasilkan kadar nikel yang tinggi tanpa menggunakan energi yang besar. Batubara bituminous umum digunakan pada proses selektif reduksi karena kandungan fixed carbon yang tinggi untuk meningkatkan derajat metalisasi nikel dan besi. Penambahan CaO pada basisitas biner dapat membentuk senyawa silikat seperti akermanite. Penelitian ini akan mempelajari proses selektif reduksi bijih nikel laterit menggunakan reduktor batubara bituminous dengan aditif Na2SO4 dan CaO pada basisitas biner. Penelitian ini menggunakan bijih nikel limonit dengan kandungan 1,38% Ni dan 38,2% Fe dengan penambahan aditif natrium sulfat 10% berat (Na2SO4), variasi soikiometri 0,1-0,5 dan variasi penambahan CaO pada basisitas biner 0,1-1,0. Penelitian ini bahwa hasil optimum pada stoikiometri 0,1 dan basisitas 0,1 yaitu 6,142% Ni dengan recovery 89,94%. Grade nikel menurun dengan bertambahnya jumlah CaO pada basisitas biner.

Selective reduction methods are being developed to process nickel laterite ore to produce nickel with high content with small amount of energy. Bituminous coal is commonly used in selective reduction process because of its high fixed carbon content to increase degree of metallization of nickel and iron. CaO addition on binary basicity can form silicate compound like akermanite. This research was carried out to study selective reduction process nickel laterite ore using bituminous coal with additives Na2SO4 and calcium oxide on binary basicity. This research used limonite ore with 1.38% Ni and 38.2% Fe content. The reduction was conducted at 1150°C for 60 minutes with 10 wt.% additive sodium sulphate (Na2SO4) and 0.71% S bituminous coal with stoichiometric variations of 0.1-0.5 and CaO based on binary basicity variations of 0.1-1.0. This research shows that the reduction process with stoichiometry 0.1 and basicity 0.1 produced the most optimal grade and nickel recovery, 6.142% Ni and 89.94%. The recovery of nickel decline as the ratio of CaO in binary basicity increases.

 File Digital: 1

Shelf
 S-Khulud Saekhan.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2020
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xiv, 49 pages : illustration ; 28 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-pdf 14-22-62308512 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20506032
Cover