Preparasi komposit busa nikel termodifikasi graphene dan MnO2 sebagai superkapasitor = Preparation of graphene and MNO2 modified nickel foam composites as supercapacitors

Salsabila Dinitasari; Ivandini Tribidasari Anggraningrum, supervisor; Rahmat Wibowo, supervisor; Yoki Yulizar, examiner; Dita Arifa Nurani, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)

 Abstrak

Pada penelitian ini preparasi komposit busa nikel termodifikasi mangan oksida dan graphene dan uji performanya sebagai elektroda untuk superkapasitor telah berhasil dilakukan. Karakterisasi menggunakan SEM-EDX menunjukkan morfologi berupa bercak putih dan terbentuknya lapisan berupa lembaran yang menyelimuti kerangka busa nikel menunjukkan keberadaan mangan oksida dan graphene. Sedangkan karakterisasi dengan Spektroskopi Raman menunjukkan adanya peak yang mengindikasikan D band dan G band  dengan rasio ID/IG yang dapat menentukan keberadaan material elektroaktif graphene. Uji elektrokimia menggunakan teknik Cyclic Voltammetry (CV) menunjukkan nilai kapasitansi spesifik tertinggi pada Busa nikel/MnO2/Graphene yaitu sebesar 1117,32 F/g pada scanrate optimum 5 mV.s-1. Uji elektrokimia menggunakan teknik Galvanostatic Charge-discharge (GCD) menunjukkan performa terbaik adalah pada Busa nikel/MnO2/Graphene pada arus yang diberikan sebesar 2 mA, dengan nilai kapasitansi spesifik mencapai 977,77 F/g, densitas energi sebesar 27,5 Wh/kg dan densitas daya sebesar 4500 W/kg. Uji elektrokimia menggunakan teknik Electrochemical Impedance Spectroscopy (EIS) menghasilkan Nyquist plot. Nilai Rct  diperoleh untuk masing-masing elektroda busa nikel/MnO2, busa nikel/graphene, dan busa nikel/MnO2/graphene adalah sebesar 415 Ω; 580,58 Ω; dan 1460 Ω.

In this research, the preparation of nickel foam composites modified with manganese oxide and graphene and its performance test as electrodes for supercapacitor has been successfully carried out. Characterization using SEM-EDX showed morphology in the form of white spots and the formation of a layer in the form of a sheet covering the nickel foam framework indicating the presence of manganese oxide and graphene. Meanwhile, the characterization using Raman spectroscopy showed that there was a peak indicating the D band and G band with the ID/IG ratio which could determine the presence of graphene electroactive material. The electrochemical test using the Cyclic Voltammetry (CV) technique showed the highest specific capacitance value for MnO2/graphene/Ni foam, which was 1117.32 F/g at an optimum scan rate of 5 mV.s-1. The electrochemical test using the Galvanostatic Charge-discharge (GCD) technique shows that the best performance is on MnO2/graphene/Ni foam at a given current of 2 mA, with a specific capacitance value of 977.77 F/g, an energy density of 27.5 Wh/kg and a power density of 4500 W/kg. Electrochemical tests using the Electrochemical Impedance Spectroscopy (EIS) technique produced a Nyquist plot. The Rct value obtained for each electrode of MnO2/Ni foam , graphene/Ni foam, and MnO2/graphene/Ni foam is 415 Ω; 580.58 Ω; and 1460 Ω.

 File Digital: 1

Shelf
 S-Pdf-Salsabila Dinitasari.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xviii, 53 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-pdf 14-22-90732597 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20508521
Cover