Pengaruh Penambahan Unsur Kromium terhadap Sifat Magnetik Lapisan Ni90Co5Fe5-xCrx (x=0,1,2,3,4) yang Disintesis dengan Metode Elektrodeposisi = Effects of Cr Composition on Magnetic Properties of Ni90Co5Fe5-xCrx (x=0,1,2,3,4) Films Synthesized by Electrodeposition Method

Yemima Gratia Florenza Glekomisen; Budhy Kurniawan, supervisor; Setia Budi, supervisor; Vivi Fauzia, examiner; Arief Sudarmaji, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)

 Abstrak

Lapisan paduan NiCoFeCr telah berhasil disintesis menggunakan metode elektrodeposisi dengan penambahan zat aditif Na-sakarin dalam pengaruh arus deposisi sebesar-25mA selama lima menit pada suhu ruang. Pengaruh komposisi Kromium (Cr) sebesar 0 hingga 39,78at% Cr terhadap struktur, morfologi, dan sifat magnetik lapisan paduan NiCoFeCr telah diteliti. Berdasarkan hasil X-Ray Diffractometer (XRD), peningkatan komposisi Cr tidak mengubah struktur kristal FCC dan space group Fm-3m. Hasil karakterisasi Scanning Electron Microscopy (SEM) menunjukkan terbentuknya microvoids dan microcracks yang diindikasikan oleh evolusi gelembung gas hidrogen ketika komposisi Cr bertambah. Lapisan paduan NiCoFeCr (0 hingga 39,78at% Cr) menunjukkan sifat feromagnetik berdasarkan hasil Vibrating Sample Magnetometer (VSM). Lapisan paduan NiCoFeCr (0 hingga 39,78at% Cr) mengalami penurunan saturasi magnetisasi (Ms) sebesar 159,85 emu/g hingga 4,20 emu/g dan mengalami peningkatan koersivitas (Hc) sebesar 51,84 Oe hingga 257,73 Oe. Peningkatan komposisi Cr menyebabkan saturasi magnetisasi (Ms) menurun dan koersivitas (Hc) meningkat.

 


NiCoFeCr film alloys were synthesized using the electrodeposition method by adding Na-saccharin additives under the deposition current of -25mA for five minutes at room temperature. The effect of chromium (Cr) addition with composition 0 to 39.78at%  on the structure, morphology, and magnetic properties were investigated. From the X-Ray Diffractometer (XRD) results, the increase in Cr composition does not change the FCC crystal structure and Fm-3m space group. The result of the Scanning Electron Microscopy (SEM) observation reveals a formation of microvoids and microcracks indicated by the evolution of hydrogen gas bubbles when the Cr composition is increased. The NiCoFeCr (0 to 39.78at% Cr) film alloys exhibit ferromagnetic properties based on the results of the Vibrating Sample Magnetometer (VSM). The saturation magnetization (Ms) and coercivity (Hc) of NiCoFeCr (0 to 39.78at% Cr) varied between 159.85 emu/g to 4.20 emu/g and 51.84 Oe to 257.73 Oe, respectively. The decrease in saturation magnetization (Ms) and the increase in coercivity (Hc) values are due to an increase in Cr composition.

 File Digital: 1

Shelf
 S-Yemima Gratia Florenza Glekomisen.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xii, 48 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-Pdf 14-21-735722250 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20508586
Cover