Sintesis dan Karakterisasi Material Mangan Ferit (MnFe2O4 dan MnFe2O4/NGP) untuk Aplikasi Fotokatalis dan Sonokatalis dalam Mendegradasi Methylene Blue = Synthesis and Characterization of Manganese Ferrite (MnFe2O4 and MnFe2O4 / NGP) Materials for Photocatalyst and Sonocatalyst Applications in Degradation of Methylene Blue

Lendi Larici; Rosari Saleh, supervisor; Lusitra Munisa, examiner; Djoko Triyono, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)

 Abstrak

Nanokomposit MnFe2O4/NGP dengan variasi 5, 10, dan 15 wt.% digunakan untuk
sebagai katalis untuk mendegradasi methylene blue pada proses fotokatalitk dan
sonokatalitik. MnFe2O4 dan MnFe2O4/NGP 5, 10, 15 wt.% disintesis dengan
menggunakan metode hydrothermal. Impuritas dan fase lain tidak ditemukan pada
pengukuran x-ray diffraction (XRD) dan x-ray fluorescence (XRF). Keberadaan
NGP terkonfirmasi dari pengukuran XRD, thermogravimetric analysis (TGA),
spektroskopi Raman, dan x-ray photoelectron spectroscopy (XPS). Penambahan
luas sampel spesifik seiring bertambahnya NGP dikonfirmasi melalui pengukuran
Brunauer-Emmet Teller (BET). Morfologi dari MnFe2O4 yang menyerupai persegi
dan cenderung berkumpul didapat dari pengukuran transmission electron
microscopy (TEM). Katalis memiliki kemampuan degradasi yang lebih baik pada
proses photocatalytic dengan cahaya tampak dibanding cahaya UV. Kondisi sistem
terbaik dari katalis untuk mendegradasi methylene blue adalah pada dosis katalis
0.2 g/L, konsentrasi H2O2 8 mL, dan pH 13. Penambahan NGP pada MnFe2O4
terbukti meningkatkan kemampuan degradasi methylene blue. Katalis juga terbukti
memiliki stabilitas yang tinggi setelah digunakan sebanyak lima kali. Spesies aktif
dari katalis pada proses fotokatalitik dan sonokatalitik adalah hidroksil radikal.

MnFe2O4/NGP nanocomposites with variations of 5, 10, and 15 wt.% were used as
catalysts to degrade methylene blue in the photocatalytic and sonocatalytic
processes. MnFe2O4 and MnFe2O4/NGP 5, 10, 15 wt.% were synthesized using the
hydrothermal method. Impurities and other phases were not found in x-ray
diffraction (XRD) and x-ray fluorescence (XRF) measurements. The presence of
NGP was confirmed by XRD measurements, thermogravimetric analysis (TGA),
Raman spectroscopy, and x-ray photoelectron spectroscopy (XPS). The increase in
specific sample area as NGP increases was confirmed by Brunauer-Emmet Teller
(BET) measurements. The morphology of MnFe2O4 which resembles a square and
tends to congregate was obtained from transmission electron microscopy (TEM)
measurements. The catalyst has better degradation ability in photocatalytic
processes with visible light than UV light. The best system conditions for the
catalyst to degrade methylene blue were at a catalyst dose of 0.2 g / L, 8 mL H2O2
concentration, and a pH of 13. The addition of NGP to MnFe2O4 was proven to
increase the degradation ability of methylene blue. The catalyst has also been shown
to have high stability after being used five times. The active species of catalyst in
photocatalytic and sonocatalytic processes are hydroxyl radicals

 File Digital: 1

Shelf
 S-Lendi Larici.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource (rdacarries)
Deskripsi Fisik : xiii, 42 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-Pdf 14-22-71153097 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20514141
Cover