Sintesis nano komposit hidroksiapatit/β-Trikalsium fosfat/alginat tersubtitusi magnesium secara ex-situ = Synthesis of hydroxyapatite/β-Tricalcium phosphate/alginate substituted magnesium nanocomposites ex-situ

Muhammad Rafi Tauchid Nugroho; Nurlely, supervisor; Ariadne Lakshmidevi Juwono, examiner; Djonaedi Saleh, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021)

 Abstrak

Hidroksiapatit adalah material yang banyak digunakan untuk aplikasi implan tulang, karena mempunyai komposisi kimia yang sama dengan tulang manusia. Biphasic Calcium Phosphate (BCP) adalah campuran dari non-resorbable Hidroksiapatit (HA) dan resorbable β-Tricalcium Phosphate (β-TCP). Doping ion magnesium ke dalam HA/β-TCP akan membawa perbaikan pada reaksi biologis. Pada penelitian ini sintesis Mg-HA diiradisi dengan gelombang mikro menggunakan daya 720 watt selama 10 menit, dengan variasi substitusi Mg(OH)2 0.1M, 0.2M, dan 0.3M. Serbuk Mg-HA yang terbentuk disinter pada suhu 1300˚ C selama 3 jam untuk membentuk fasa biphasik Mg-HA/β-tricalcium phosphate kemudia dikarakterisasi dengan XRD. Sintesis nano-komposit Mg-HA/Alginat dilakukan dengan mencampurkan serbuk hasil sintering dengan alginat dan CaCl2 sebagai agen taut silang (cross linker agent). Larutan campuran diaduk menggunakan magnetic stirrer selama 3 jam kemudian dibiarkan selama 24 jam agar pencampuran sempurna. Metode karakterisasi komposit Mg-HA/β-TCP/Alginat menggunakan FTIR dan SEM-EDX. Hasil XRD menunjukan subtitusi Mg mereduksi ukuran kristal, parameter kisi dan indeks kristalinitas. Perlakuan thermal hingga suhu 1300 ˚ C pada HA membentuk dua fasa yaitu HA dan β-TCP. SEM-EDX menunjukan bahwa partikel yang terdapat pada komposit Mg-HA/β-TCP/Alginat berukuran tidak sama mempengaruhi grain growth.

Hydroxyapatite is a material that is widely used for bone implant applications because it has the same chemical composition as human bone. Biphasic Tricalcium Phosphate (BCP) is a mixture of non-resorbable hydroxyapatite (HA) and resorbable β-Tricalcium Phosphate (β-TCP). Doping of magnesium ion into HA/β-TCP will bring about improvement in biological reactions. In this study, the synthesis of Mg-HA was irradiated with microwaves using 720 watts of power for 10 minutes, with variations of 0.1M, 0.2M, and 0.3M Mg (OH)2 substitution. The Mg-HA powder formed was sintered at 1300˚C for 3 hours to form a biphasic phase of Mg-HA/β-tricalcium phosphate which was then characterized by XRD. The synthesis of Mg-HA/Alginate nano-composites was carried out by mixing the sintered powder with alginate and CaCl2 as a cross-linker agent. The mixed solution was stirred using a magnetic stirrer for 3 hours then left for 24 hours for complete mixing. The characterization method for Mg-HA / β-TCP / Alginate composites used FTIR and SEM-EDX. XRD results showed that Mg substitution reduced crystal size, lattice parameters, and crystallinity index. Thermal treatment up to a temperature of 1300 ˚ C on HA forms two phases, namely HA and β-TCP. SEM-EDX showed that the particles contained in the Mg-HA/β-TCP/Alginate composite had different sizes affecting grain growth.

 File Digital: 1

Shelf
 S-Muhammad Rafi Tauchid Nugroho.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xi, 45 pages : illustration + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-pdf 14-22-45718790 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20515022
Cover