Evaluasi Performa Organik Coating pada Struktur Baja Karbon A 36 di Lingkungan Konsentrat Tembaga dengan Teknik Electrochemical Impedance Spectroscopy = Evaluation of Organic Coating Performance on Carbon Steel A 36 in Copper Concentrate Environment Using Electrochemical Impedance Spectroscopy

Ahmad Fauzi; Ahmad Zakiyuddin, supervisor; Reza Miftahul Ulum, examiner; Alfian Ferdiansyah Madsuha, examiner; Dwi Marta Nurjaya, examiner (Fakultas Teknik Universitas Indonesia, 2021)

 Abstrak

Pabrik pengeringan konsentrat tembaga memiliki peranan penting sebagai tahap akhir dalam proses penambangan tembaga. Keberlangsungan operasi pabrik sangat dipengaruhi oleh kondisi bangunan dan fasilitas yang berbahan dasar baja. Persentase tembaga yang ada dalam konsentrat berkisar antara 20-40 %, Kalkopirit memiliki jumlah tembaga yang besar pada akhir ekstraksi. Pengaruh kehadiran kalkopirit dapat meningkatkan laju korosi pada baja melalui pasangan galvanik. pemilihan sistem coating untuk mellindungi baja menjadi penting dimana ketahanan material coating dipengaruhi oleh kekuatan terhadap cacat pada lapisan. Pada penelitian ini lima sistem organik coating yang diaplikasikan pada baja karbon A 36 dievaluasi kekuatannya terhadap korosi akibat kehadiran konsentrat tembaga dengan metode Electrochemical Impedance Spectroscopy (EIS), uji sembur garam dan uji tarik. Hasil pengujian menunjukkan bahwa sistem coating C2, C3, C4 dan C5 mempertahankan sifat penghalang yang baik selama proses perendaman, nilai impedansi |Z| pada frekuensi rendah lebih dari 108 Ω.cm2 setelah 30 hari. Coating modifikasi epoksi (C1) memiliki impedansi terendah dengan resistansi di bawah 106 Ω.cm2 memberikan perlindungan korosi yang buruk

The copper concentrate dewatering plant has an important role as a step end in the copper mining process. The continuity of plant operation is very influenced by the condition of buildings and facilities made of steel. Percentage of copper present in the copper concentrate is in the range of 20 to 40 %. Thus, Chalcopyrite is preferable to get large amount of copper at the end of the extraction. The presence of chalcopyrite increases the corrosion rate of carbon steel through a galvanic couple. Probably the most important step in coating selection is to evaluate the conditions under which the coating must perform. In this study, five organic coating systems were applied to A-36 steel and evaluated evaluated for their strength against galvanic corrosion in the presence of copper concentrate by electrochemistry impedance spectroscopy (EIS) measurement, salt spray test and pull off test. The test results showed that C2, C3, C4 and C5 coating systems maintained good barrier property during the immersion process, the impedance value |Z| at a low frequency are more than 108 Ω.cm2 after 30 days in immersion exposure. Epoxy modified coating (C1) had the lowest impedance with resistance under 106 Ω.cm2 providing poor corrosion protection.

 File Digital: 1

Shelf
 T-Ahmad Fauzi .pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2021
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xiv, 72 pages : illustration + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T-pdf 15-22-83043310 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20515886
Cover