Pada penelitian ini, nanopartikel ZnO, MnCo2O4, dan nanokomposit ZnO/MnCo2O4 berhasil disintesis dengan metode green synthesis menggunakan ekstrak daun Sigar Jalak (Flueggea virosa) dalam sistem dua fasa antara n-heksana dan air. Ekstrak daun Sigar Jalak fraksi n-heksana mengandung metabolit sekunder, seperti alkaloid, saponin, dan terpenoid yang sebelumnya telah dikarakterisasi dengan FTIR dan Spektrofotometer UV-Vis. Alkaloid berperan sebagai sumber basa lemah dan saponin sebagai capping agent/ agen penstabil dalam proses sintesis. Berdasarkan hasil karakterisasi dengan spektrofotometer UV-Vis DRS didapatkan nilai energi band gap dari nanopartikel ZnO, MnCo2O4, dan nanokomposit ZnO/MnCo2O4 masing-masing sebesar 3,15 eV, 1,99 eV, dan 2,3 eV. Nanokomposit ZnO/MnCo2O4 hasil sintesis, diuji aktivitas fotokatalitiknya terhadap zat warna malasit hijau dibawah sinar tampak selama 120 menit dan dibandingkan aktivitasnya tersebut dengan nanopartikel ZnO dan nanopartikel MnCo2O4. Hasil menunjukkan bahwa nanokomposit ZnO/MnCo2O4 memiliki aktivitas fotokatalitik yang lebih baik daripada nanopartikel ZnO dan nanopartikel MnCo2O4. Persen degradasi yang diperoleh dari nanopartikel ZnO, MnCo2O4, dan nanokomposit ZnO/MnCo2O4 masing-masing sebesar 91,85%, 77,54%, dan 50,49%. Kinetika reaksi fotodegradasi nanokomposit ZnO/MnCo2O4 terhadap malasit hijau mengikuti pseudo orde satu.

---

In this research, ZnO, MnCo2O4 nanoparticles, and ZnO/MnCo2O4 nanocomposites were successfully synthesized by green synthesis method using Common Bushweed (Flueggea virosa) leaf extract in two-phase system (n-hexane and water). The n-hexane fraction of Common Bushweed leaf extract contains secondary metabolites, such as alkaloids, saponins, and terpenoids which has previously been characterized by FTIR and UV-Vis Spectrophotometer. Alkaloids act as a source of weak bases and saponins as capping agents/stabilizing agents in the synthesis process. Based on the results of the characterization using the UV-Vis DRS spectrophotometer, the band gap energy values of ZnO, MnCo2O4 nanoparticles, and ZnO/MnCo2O4 nanocomposites were 3.15 eV, 1.99 eV, and 2.3 eV. The synthesized ZnO/MnCo2O4 nanocomposites, tested its photocatalytic activity against green malachite dye under visible light for 120 minutes and compared its activity with ZnO nanoparticles and MnCo2O4 nanoparticles. The results showed that ZnO/MnCo2O4 nanocomposites had better photocatalytic activity than ZnO nanoparticles and MnCo2O4 nanoparticles. The percentage of degradation obtained from ZnO, MnCo2O4 nanoparticles, and ZnO/MnCo2O4 nanocomposites were 91.85%, 77.54%, and 50.49%, The kinetics of the photodegradation reaction of ZnO/MnCo2O4 nanocomposites against green malachite is pseudo-first order.