Pengaruh Durasi Penyinaran (Lightcure) Terhadap Kekerasan dan Depth Of Cure Resin Komposit Bulk-Fill = Influence of Different Exposure Time (Lightcure) on Microhardness and Depth Of Cure of Bulk-Fill Composite Resin

Alamsyah Putra; Bambang Irawan, supervisor; Decky Joesiana Indrani, supervisor; Ellyza Herda, examiner; Yosi Kusuma Eriwati, examiner (Fakultas Kedokteran Gigi Universitas Indonesia, 2022)

 Abstrak

Latar belakang : Resin komposit bulkfill merupakan resin terbaru yang dapat direstorasi dengan kedalaman 4-5 mm dalam sekali penyinaran. Polimerisasi dipengaruhi oleh durasi penyinaran dan besaran irradiansi lightcuring untuk mendapatkan kekerasan permukaan dan depth of cure yang optimal. Tujuan: Penelitian ini bertujuan untuk mengetahui perbedaan nilai kekerasan resin komposit dan depth of cure resin komposit Tetric® N- Ceram bulk-fill yang disinari lightcure dengan durasi 5 detik, 10 detik dan 15 detik. Metode Penelitian: Dalam penelitian ini digunakan 24 spesimen resin komposit Tetric® N-Ceram bulk-fill berbentuk silinder dengan ukuran diameter 6 mm dan tebal 4 mm. Selembar mylar strip diletakkan diatas permukaan resin komposit sebelum dilakukan proses curing. Polimerisasi dilakukan menggunakan Light Curing Unit (LED DBA iLed) selama 5 detik, 10 detik dan 15 detik dengan irradiansi 1100 mW/cm2. Setelah polimerisasi, spesimen direndam dalam akuades pada suhu 37oC selama 24 jam. Spesimen dibagi menjadi tiga kelompok (n=8) yaitu; kelompok resin komposit dengan penyinaran 5 detik, penyinaran 10 detik dan penyinaran 15 detik. Spesimen diuji menggunakan HMV-G Series Micro Vickers Hardness Tester (Shimadzu, Jepang) dengan beban 100 gram selama 10 detik untuk mendapatkan nilai kekerasan. Data dianalisis dengan uji statistik Kruskall Wallis dan Post-Hoc Mann Whitney. Hasil Penelitian: Hasil uji statistik menunjukkan kenaikan bermakna nilai kekerasan permukaan dan depth of cure pada resin komposit Tetric® N-Ceram bulk-fill. Nilai kekerasan dan depth of cure tertinggi terlihat pada resin komposit Tetric® N-Ceram bulk-fill pada kelompok penyinaran 15 detik, yaitu sebesar 41,61 ± 1,25 KHN dan 72,71 ± 1,88. Kesimpulan: Disimpulkan bahwa semakin bertambah durasi penyinaran lightcure yang disinari, semakin bertambah nilai kekerasan permukaan dan depth of cure resin komposit Tetric® N-Ceram bulk-fill.

Background : Bulkfill composite resin is the newest resin that can be restored to a depth of 4-5 mm in one step. Polymerization is determined by the irradiation time and the amount of light curing irradiance to obtain optimal microhardness and depth of cure. Objective: The aim of this study was to determine the difference in the value of the microhardness of the composite resin and the depth of cure of the Tetric® N-Ceram bulk- fill composite resin irradiated by lightcure with a duration of 5 seconds, 10 seconds and 15 seconds. Method: Twenty four specimens of Tetric® N-Ceram bulk-fill Composite Resin were used in this study. All materials were prepared into disk-shaped specimens of 6 mm in diameter and 4 mm in thickness. A piece of mylar strip was placed on the top of the specimens just before the polymerization.. Polymerization was carried out using a Light Curing Unit (LED DBA iLed) for 5 seconds, 10 seconds and 15 seconds with an irradiance of 1100 mW/cm2. After polymerization, specimens were immersed in 37 aquadest solution for 24 hours. Specimens were divided into three groups (n=8) that is; composite resin group with 5 seconds of irradiation, 10 seconds of irradiation and 15 seconds of irradiation. Specimens were tested with HMV-G Series Micro Vickers Hardness Tester (Shimadzu, Jepang) with 100 gram indentation in 10 seconds. Data were analyzed using Kruskall Wallis and Post-Hoc Mann Whitney to assess the significant differences among groups Result: The results of statistical tests showed a significant increase in the value of microharhardness and depth of cure on Tetric® N-Ceram bulk- fill composite resin. The highest microhardness and depth of cure values were seen in the Tetric® N-Ceram bulk-fill composite resin in the 15 second irradiation group, namely 41.61 ± 1.25 KHN and 72.71 ± 1.88. Conclusion: It was concluded that the longer the duration of irradiation of the irradiated lightcure, the higher the microhardness value and depth of cure of the Tetric® N-Ceram bulk-fill composite resin.

 File Digital: 1

Shelf
 S-Alamsyah Putra.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Jakarta: Fakultas Kedokteran Gigi Universitas Indonesia, 2022
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource (rdcarrier)
Deskripsi Fisik : xii, 37 pages : illustration + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-pdf 14-23-07696326 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20524397
Cover