Optimasi rapat arus proses Plasma Electrolytic Oxidation untuk meningkatan ketahanan korosi dan aus Zircalloy-4 = Current density optimization of Eletrolytic Oxidation Plasma process for improving corrosion and wear resistance of the Zircalloy-4

Fajar Al Afghani; Anawati, supervisor; Ariadne Lakshmidevi Juwono, examiner; Nurlely, examiner; Bambang Soegijono, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021)

 Abstrak

Plasma electrolytic oxidation (PEO) digunakan untuk meningkatkan ketahanan korosi dan aus material kelongsong Pressurrized water reactor yaitu zircalloy-4 (Zr-4). Rapat arus merupakan salah satu parameter yang mempengaruhi sifat-sifat pelapisan PEO. Ada 3 rapat arus berbeda yang digunakan untuk proses PEO Zr-4 yaitu 30, 50 dan 70 mA/cm2 pada penelitian ini. Pengaruh rapat arus terhadap karakterisasi lapisan permukaan dan tampang lintang PEO, komposisi element dan fasa, evaluasi korosi dan ketahanan aus diamati. Hasil percobaan menunjukkan bahwa rapat arus 70 mA/cm2 memiliki ketahanan korosi terbaik dengan nilai Rcoating= 20 x106 Ω/cm2 karena memiliki komposisi element Si 27,74% sebagai pasif film. Namun rapat arus 70 mA/cm2 memiliki ketahanan aus yang paling baik yaitu laju keausan= 8,86 x 10-6 mm3/mm karena memiliki persentase pori terendah dibanding rapat arus lainnya yaitu 4,5%. Mempertimbangkan ketahanan aus yang lebih diperlukan dalam pengembangan pelapisan Zr-4, sehingga rapat arus 70 mA/cm2 adalah yang paling optimal dalam meningkatkan karakteristik Zr-4 dalam penelitian ini.

Plasma Electrolytic Oxidation (PEO) is used to improve the corrosion and wear resistance of PWR cladding material, namely zircaloy-4. Current density is one of the parameters that affect the properties of the PEO coating. There are 3 different current densities used for the PEO Zr-4 process, namely 30, 50 and 70 mA/cm2 in this study. The effect of current density on the surface layer characterization and cross section of PEO, element and phase composition, evaluation of corrosion and wear resistance were observed. The experimental results show that the current density of 30 mA/cm2 has the best corrosion resistance Rcoating= 20 x106 Ω/cm2 because it has an elemental composition of 27.74% Si as a pasif film. However, the current density of 70 mA/cm2 has the best wear resistance because its surface porosity 4.5% is lowest than others. Considering that more wear resistance is needed in the development of Zr-4 coating, so that the current density of 70 mA is the most optimal in improving the characteristics of Zr-4 in this study.

 File Digital: 1

Shelf
 T-Fajar Al Afghani.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xi, 43 pages : illustrations + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T-pdf 15-22-92759196 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20527719
Cover