Pengaruh temperatur sintering dan komposisi bahan baku terhadap sifat karateristik material Cordereite (2MgO.2Al2O3.5SiO2)

Mukhammad Amin; Ellyza Herda, supervisor; Ronnie Rusli, examiner; A. Harsono, examiner; Agus Purwanto, examiner; Aziz Khan Jahja, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2000)

 Abstrak

Pengaruh Temperatur Sintering dan Komposisi Bahan Baku Terhadap Sifat Karateristik Material Cordereite (2MgO.2Al2O3.5SiO2) Pasca Sarjana, 2000 Cordierite [2MgO.2A12O3.5SiO21 adalah merupakan material yang tahan temperatur tinggi sampai dengan 1365 ° C, disamping itu material tersebut memiliki termal ekspansi yang rendah yaitu ג= 2 x 10'° s/d ג = 3 x 10-° dan kekuatan mekanik yang tinggi. Penelitian dan pengembangan keramik cordierite telah dilakukan melalui beberapa tahapan penelitian, diawali dengan penelitian tentang pembuatan serbuk cordierite dari berbagai macam bahan baku alam seperti Kaolin (AI2 03 2SiO 2H2O), Kuarsa (Si02), Talk (3MgO4SiO2H2O) Sian Bauxit (AI203) . Setelah dilakukan pencampuran dari bahan baku tersebut, kemudian dilakukan penganalisaan dengan DTA untuk mengetahui suhu sintering. Selanjutnya campuran tersebut dicetak dan dibakar (sintering) pada berbagai suhu. Karakterisasi yang dilakukan adalah analisa fasa dengan XRD, pengukuran sifat-sifat fisis (densitas, porositas dan water absorbsion), termal ekspansi, kekerasan Vickers serta pengukuran kekuatan patah (bending strength). Dari hasil karakterisasi beberapa sampel ternyata sampel 3 dengan komposisi Kaolin 41.99 %,Talk 36.96 %, Alumina 21.05 % dengan suhu sintering 1350 ° C mempunyai sifat fisis yang paling balk yaitu bending strength 423,255 Kg/cm2, porositas 0.5257 %,densitas 3.7049 g/cm water absorbsion 7.4145%, serta kekuatan vickers 788,46 Kgf/mm2. Dad hasil karakterisasi tersebut maka komposisi dari sampel 3 dapat dipergunakan dan memenuhi syarat untuk aplikasi sebagai refraktori, Kiln Furniture, selubung termokopel,dan sebagai bahan untuk komponen alat penyaring gas pada mobil (Exhaust gas filter/catalys gas carrier).

Cordierite [2MgO.2A1203.5SiO2] are promising refractory materials for high temperature ceramic application up to 1365 ° C. beside that these materials have a low thermal ג= 2 x 10'° s/d ג = 3 x 10-° and high mechanical strength. Research and development of cordierite ceramics have been done in some stages of researches, first is the preparation of cordierite powders with variation of nature raw materials like Kaulin (AI2 03 2SiO 2H2O), Kuarsa (Si 02), Talk (3MgO4 SiO2 H2O) and Bauxit (AIZ 03 ). After mixing of raw materials, the mixed powders were analyzed by using of DTA, then those powders were formed and fired (sintered) at various temperatures. The characterization consist phase analysis with XRD, measurement of physical properties (density, porosity, water absorpsion), thermal expansion, vickers hardness and bending strength. The physical and mechanical characterization indicated that, the sample with the composition of 41,99 % Kaolin, 36,96 % Talk, 21,05 % Alumina and sintering temperature of 1350 °C have the best physical and mechanical properties. The porosity,density,water absorbsion, bending strength, and vickers hardness are 0,5357 %,3.7049 glcm 3, 7.4145 %, 423,255 Kg/cm2, 788.46 Kgf/mm2 respectively. It is concluded that the sample have fulfiled enough to aplicable as refractories, Kiln Furniture, thermocouple tube and otomotif component (exhaust gas filter/catalys gas carrier).

 File Digital: 1

Shelf
 T544-Pengaruh temperatur-TOC.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi: UI - Tesis (Membership)
No. Panggil : T-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2000
Program Studi :
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xiii, 50 pages : illustration ; 28 cm + appendix
Catatan Bibliografi : pages 48-50
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T-Pdf 15-19-225371382 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 70663
Cover