Karakterisasi lapisan tipis titanium dioksida dari prekursor titanium tetraisopropoksida dan pengujian aktivitasaya sebagai fotokatalis

Rachmat Triandi Tjahjanto; Jarnuzi Gunlazuardi, supervisor; Agus Nurhadi, examiner; Wahyudi Priyono Suwarso, examiner; Widayanti Wibowo, examiner; Sihombing, Riwandi, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2001)

 Abstrak

Telah dilakukan immobilisasi TiO2 dalam bentuk lapisan tipis pada permukaan kaca preparat. Teknik pelapisan menggunakan teknik proses sol-gel (PSG) dari prekursor titanium tetraisopropoksida yang dilarutkan dalam isopropanol pada konsentrasi 0,05 M dan 0,1 M. Lapisan tipis yang diperoleh dikarakterisasi dengan instrumen spektrofotometer UV-Vis, difraksi sinar-x, foto SEM, serta dilakukan uji aktivitas mendegradasi fenol sebagai model limbah organik dan uji adsorbsi.
Hasil XRD menunjukkan bahwa kristal yang diperoleh anatase dan tidak terdeteksi adanya rutil. Dari difraktogram tersebut juga dapat diperkirakan ukuran kristal yang dihasilkan adalah sekitar 19 - 39 nm. Foto SEM menunjukkan permukaan yang cukup berpori, namun uji adsobsi menunjukkan peningkatan luas permukaan hanya 20%. Dari hasil uji aktivitas dapat diprediksi bahwa katalis dengan tebal 6,33 µm, dan kandungan TiO2 1,04 mg/cm2 akan memiliki aktivitas optimum.

The Characterization of Thin Layer Titanium Dioxide from Titanium Tetraisopropoxide Precursor and the Examination of Its Activity as Photo CatalystImmobilization of TiO2 as thin layer on microscope slide glasses has been done. The slide was coated by sol-gel technique with titanium tetraisopropoxide as precursor diluted in isopropanol at the concentration of 0.05 M and 0.1 M. The thin films produced were characterized with W-Vis spectrophotometer, X-ray diffraction analyzer (XRD), SEM, and the activity as photo catalyst was examined by degrading phenol as an organic pollutant model, and also done adsorption examination.
The XRD results show that the crystal produced were in the anatase form and there are no rutile form detected. The results were also provide that the expectation size of the crystal was about 19 -- 37 nm. SEM results show moderate porosity of the thin layer surface but the adsorption examinations provide that the effective surface width increased in only 20 percent. From the result of activity examinations was been able to predict that thin layer catalyst at the thick of 6.33 µm, and TiO2 loading of 1.04 mg/cm2 has maximum activity.

 File Digital: 1

Shelf
 T 9464a.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T9464
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2001
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : viii, 37 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T9464 15-17-347343891 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 72739
Cover