Telah dilakukan sintesis dan karakterisasi dielektrik amorf terhadap bahan berbasis barium titanat dengan penambahan unsur Pb. Dalam penelitian ini cuplikan Ba(1_,¢Pb,Ti0, diperoleh melalui metalurgi serbuk dengan bahan dasar BaCO3, PbCO,, dan TiO2 yang merupakan grade reagen dari E-Merck dengan perbandingan stoikidmetri nominal masing-masing 0,1 : 0,9 : 1. Analisis tennal menunjukkan bahwa bahan memiliki titik leleh pada 1350°C dimana temperatur tersebut lebih rendah dari BaTiO, Fasa gelas diperoleh melaiui pemanasan bahan hingga meleleh pada temperatur 1350°C diikuti oleh pendinginan oepat dalam medium nitrogen cair hingga membentuk cairan super dingin_ Difraktogram sinar-X dengan cacah step dan panjang gelombang. A (Cu Ka.)=1,5405 A yang diperoleh pada temperatur kamar, menunjukkan hilangnya seluruh puncak Bragg dan terjadi penggeiembungan cacah latar pada bahan. Kurva distribusi radial hasil pengamatan tanpa melakukan reduksi data diperoieh dengan menggunakan paket program kristallografi GSAS, secara kualitatif menunjukkan keminpan dengan fungsi distribusi radial yang ditunjukkan oleh zat cair sederhana. Pengukuran terhadap besaran konstanta dielelctrik relatif menunjukkan kenaikan yang tinggi pada 12O°C hingga 360°C dan temperatur curie dicapai pada 140°C dimana nilai konstanta dielektdk relatifnya adalah 4,13x10°.' Jangkauan temperatur yang Iebar dengan konstanta dieiektrik tinggi yang diperoleh menunjukkan bahwa sampel cocnk untuk temperatur tinggi dan berfluktuasi pada daerah jangkauan tersebut.

---

Barium titanate based with amorphous dielectric materials with Pb as a substituent atom have been synthesized and characterized. ln this study, Ba(,_,,Pb,,TiO3 were synthesized by using powder metallurgy trom BaCO3, PbCO3 and Ti02, which were reagents from E-Merck with nominal stoichiometric ratio of 0.1 : 0.9 : 1 respectively. Themwal analysis showed that the sample melting point is of 1350°C which is lower than that of BaTiO3. The glassy states was obtained by heating at the melting point temperature of 1350°C followed by quenching in liquid nitrogen media rapidly when the supercooled conditions achieved. The X-ray diffractograms were obtained with step scan and 2. (Cu Ka) =1,5405 A at room temperature showed the Bragg peaks dissapeared completely and the fluctuation of background prohle was occurred. The observed radial distribution function without data reduction were obtained by using of GSAS crystallographic software package which qualitatively showed that the function resembles the radial distribution function belongs to simple fluids. The relative dielectric constant that was measured from room temperature showed that there is a signiticant increasing value starting at 120°C up to 36O°C and the Curie temperature was occurred at 140°C while the value of corresponding relative dielectric constant is of 4,13x105. Broad range of temperature in which high dielectric constant was obtained indicates that the sample is suitables for high and tluctuating temperature in the range.