Relative Cooling Power of La0.7Ca0.3Mn1–xCuxO3 (0.0 ? x ? 0.03)

Seong Cho Yu (Faculty of Engineering, Universitas Indonesia, 2016)

 Abstrak

Manganite perovskite has a wide variety of potential applications as an advanced material, for example, in magnetic random access memory, spintronics, magnetoelectric, magnetic field sensors and cooling technology, based on magnetism and magnetic materials. In work on cooling technology, magnetic materials show a magnetocaloric effect. Manganite perovskite has some fundamental properties, such as Curie temperature, magnetic entropy change, temperature span and relative cooling power. Current works report detailed properties of manganite perovskite in La0.7Ca0.3MnO3 doped with Cu, which show magnetocaloric effects. The samples were synthesized by a conventional solid state reaction. A small amount of doping Cu 1%~3% at a Mn site maintains the First-Order Magnetic Transition (FOMT) without leading into the Second-Order Magnetic Transition (SOMT). Maximum magnetic entropy change increased as the Cu-doped decreased. Introducing a small percentage of Cu-doped on La0.7Ca0.3Mn1-xCuxO3 also implies decreasing the Curie temperature, TC. For all samples under external application in a field of 10 kOe, these resulted in a slightly wider temperature span and the Relative Cooling Power (RCP) of about 39 J/kg to 47 J/kg as the Cu-doped decreased. The small amount of Cu-doping on La0.7Ca0.3MnO3 keeps the rate of relative cooling power in a wider temperature range. It may be beneficial for cooling technology based on magnetism and magnetic materials.

 Metadata

Jenis Koleksi : Artikel Jurnal
No. Panggil : UI-IJTECH 7:3 (2016)
Entri utama-Nama orang :
Subjek :
Penerbitan : Depok: Faculty of Engineering, Universitas Indonesia, 2016
Sumber Pengatalogan : LibUI eng rda
ISSN : 20869614
Majalah/Jurnal : International Journal of Technology
Volume : Vol. 7, No. 3, April 2016: Hal. 417-423
Tipe Konten : text
Tipe Media : unmediated
Tipe Carrier : volume
Akses Elektronik : https://doi.org/10.14716/ijtech.v7i3.2959
Institusi Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 4 R. Koleksi Jurnal
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
UI-IJTECH 7:3 (2016) 08-23-57327038 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 9999920521679
Cover