Studi Pengaruh Expansi Tube pada Tube Bundle Heat Exchanger Terhadap Crack, Korosi Dinding Dalam dan Luar Baja Karbon ASTM A179 = Study of the Effect of Tube Expansion on Tube Bundle Heat Exchanger Against Crack, Corrosion of Inner and Outer Walls of ASTM A179 Carbon Steel

Eko Kusumo; Ahmad Zakiyuddin, supervisor; Deni Ferdian, examiner; Alfian Ferdiansyah Madsuha, examiner (Fakultas Teknik Universitas Indonesia, 2023)

 Abstrak

Heat Exchanger sering mengalami kegagalan yang disebabkan karena kurang tepat sambungan antara tube budle dan Tube Sheet. Terjadi karena berlebih nya nilai expansion yang terjadi pada tube bundle. Selama proses fabrikasi yang sering terjadi adalah berlebihnya nilai dari expnasi tube bundle. Tujuan dari penelitian ini untuk mengetahu kegagalan yang sering terjadi akibat korosi dan crack pada dinding pipa pada tube bundle heat exchanger. Analisa dilakukan pada tube dengan membandingkan nilai expansion rate sebesar 0%, 10%, 13%, 16% dan kemudian di observasi pada dinding tube badian luar dan dalam. Hasil dari penelitian dilakukan Analisa dengan Visual dan dimensi, Hardness, Polarisasi, Metallography. Strukture mikro material setelah di expansi nerubah bentuk menjadi lebih memanjang yang mempengaruhi nilai kekerasan, semakin tinggi nilai kekerasan maka laju korosi nya semakin meningkat. Microstructure of the material after expansion changes shape to be more elongated which affects the hardness value, the higher the hardness value, the corrosion rate increases.

Heat Exchanger often fails due to improper joint tube to tube sheet joint expansion. Among them is the excessive expansion rate on the tube. Based on common during the fabrication process, it can be found several cases related to excess tube expansion compared to international standards. The aim of this study was to analyst the failure of corrosion and tube wall cracks in the tube bundle heat exchanger. The analysis was carried out on the tube by comparing the expansion rate values of 0%, 10%, 13%, 16% and then observing the condition of the inner and outer walls of the tube. The experimental result were characterized using Visual Dimensional, Hardness test, Polarization, Metallography.

 File Digital: 1

Shelf
 T-Eko Kusumo.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2023
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xiii, 61 pages : illustration + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T-pdf 15-23-51124593 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 9999920524549
Cover