Perilaku Balok Prategang Pratarik Menggunakan Beton Bubuk Reaktif = Behavior of Prestress Pretension Beams Using Reactive Powder Concrete

Ignatius Harry Sumartono; Heru Purnomo, supervisor; Bastian Okto Bangkit Sentosa, examiner; Nuraziz Handika, examiner; Jessica Sjah, examiner (Fakultas Teknik Universitas Indonesia, 2023)

 Abstrak

Perilaku balok prategang pratarik yang terbuat dari beton bubuk reaktif dengan kekuatan tekan di atas 120 MPa yang termasuk dalam klasifikasi beton dengan kinerja ultra tinggi diselidiki untuk mempelajari sifat fisik dan mekanik beton dan kinerja balok prategang terhadap uji beban statis. Sifat mekanik material RPC diselidiki berupa nilai kuat tekan beton, kuat tarik beton, nilai modulus elastisitas beton dan kualitas beton yang diuji dengan alat UPV dibandingkan dengan beton kuat tekan tinggi dengan kuat tekan 70 MPa. Perawatan beton saat umur awal menggunakan uap panas suhu tinggi memastikan perkembangan kekuatan tekan beton. Pengujian eksperimental dilakukan terhadap 4 buah balok pratarik yang didesain untuk digunakan sebagai balok jembatan jalan raya yaitu balok #1 (30/50-HSC-NF-S); balok #2 (30/50-RPC-F-S); balok #3 (17/50-RPC-NF-S); balok #4 (17/50-RPC-NF-S). Mekanikal properties beton RPC menunjukan nilai yang lebih unggul dibanding dengan dengan beton HSC. Dari hasil uji statis hanya balok #3 (balok RPC yang tidak menggunakan serat baja dalam adukan) yang menunjukan nilai tahanan lentur dibawah nilai teoritis akibat terjadi kehancuran getas yang terjadi pada balok. Serat baja efektif mempertahankan keutuhan balok sehingga memaksimalkan tahanan lentur, mencegah kehancuran getas yang eksplosif, dan mencegah fragmentasi beton saat beban puncak.


The behavior of prestress pretension beams made of Reactive Powder Concrete (RPC) concrete with compressive strength above 120 MPa included in the Ultra High Performance Concrete (UHPC) classification was investigated to study the mechanical properties of concrete and the performance of prestressed beams against static load tests. The mechanical properties of RPC materials include concrete compressive strength, concrete tensile strength, concrete elastic modulus values ​​and concrete density compared to 70 MPa High Strength Concrete (HSC) concrete. Curing concrete at an early age using high temperature hot steam (steam curing) ensures the development of the compressive strength of concrete. Experimental tests were carried out on 4 pretension beams designed to be used as highway bridge beams, namely beam #1 (30/50-HSC-NF-S); beam #2 (30/50-RPC-F-S); beam #3 (17/50-RPC-NF-S); beam #4 (17/50-RPC-NF-S). The mechanical properties of RPC concrete show superior values ​​compared to HSC concrete. From the results of the static test, only beam #3 (RPC beam which does not use steel fiber in mixing) which shows a value of flexural resistance below the theoretical value due to brittle destruction that occurs in the beam. Steel fiber effectively maintains beam integrity thereby maximizing bending resistance, preventing explosive brittle destruction, and preventing concrete fragmentation during peak loads

 File Digital: 1

Shelf
 T-Ignatius Harry Sumartono.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2023
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xv, 90 pages ; illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T-pdf 15-24-76156230 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 9999920526251
Cover