Synthesis of tio2 nanotube in ti-10ta-10nb thin film by anodization

Deni Ferdian, Yudha Pratesa (Faculty of Engineering, Universitas Indonesia, 2012)

 Abstrak

The purpose of this research was to study the synthesis of TiO2 nanotubes on Ti-10Ta-10Nb thin film and the effect of applied potential on the tube size, length and morphology. The Ti-10Ta-10Nb thin film was deposited by dc magnetron sputtering on the CP Ti substrate. The anodization of this Ti-10Ta-10Nb thin film was performed in the solution containing 1M H3PO4 + 1.5wt.% HF at the potential readings of 4, 6, 8 and 10 V for 10 minutes. The results showed that there was a slight increase in the tube diameter from approximately 25 nm at 4 V to 50 nm at 8 V. The length of nanotube varied from 700-900 nm. Interestingly, at the potential of 10 V, the nanotube diameters were damaged with slight decreases in nanotube lengths (500 nm).

 Metadata

Jenis Koleksi : Artikel Jurnal
No. Panggil : UI-IJTECH 3:2 (2012)
Entri utama-Nama orang :
Subjek :
Penerbitan : Depok: Faculty of Engineering, Universitas Indonesia, 2012
Sumber Pengatalogan : LibUI eng rda
ISSN : 20869614
Majalah/Jurnal : International Journal of Technology
Volume : Vol. 3, No. 2, July 2012: Hal. 140-144
Tipe Konten : text
Tipe Media : unmediated
Tipe Carrier : volume
Akses Elektronik : https://doi.org/10.14716/ijtech.v3i2.96
Institusi Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 4 R. Koleksi Jurnal
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
UI-IJTECH 3:2 (2012) 08-23-59121857 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 9999920535802
Cover