Bio-oil hasil pirolisis lambat bonggol jagung memiliki kandungan senyawa oksigenat yang banyak. Senyawa oksigenat paling banyak dalam bio-oil adalah asam asetat. Dari hasil uji C-NMR kandungan senyawa oksigenat dan alifatik dalam bio-oil masing-masing sebesar 53,8% dan 46,2%. Senyawa alifatik pada bio-oil memiliki sedikit percabangan dengan tingkat percabangan yang pendek. Kandungan senyawa oksigenat yang banyak terdapat dalam bio-oil menurunkan nilai kalor bio-oil, menyebabkan korosif, serta tidak stabil sehingga perlu dilakukan proses hidrodeoksigenasi untuk mengurangi kandungan senyawa oksigenat dalam bio-oil. Pada penelitian ini, bio-oil dihasilkan melalui proses pirolisis lambat bonggol jagung. Reaksi hidrodeoksigenasi dilakukan dalam reaktor tangki berpengaduk dengan katalis NiCu/ZrO2 pada temperatur 200oC dan tekanan 14 bar. Pengaruh komposisi pelarut heksadekana terhadap komposisi biofuel dilakukan pada 65%, 75%, 82,5%, dan 90%. Dari hasil XRF dan EDX kandungan nikel dan tembaga pada katalis masing-masing sebesar 1,96% dan 1,47%. Katalis NiCu/ZrO2 dengan struktur monosiklik yang bersifat amfoter ini mampu mengurangi kandungan senyawa oksigenat sampai tersisa 17% dan meningkatkan senyawa alkana hingga 83% pada komposisi pelarut heksadekana 90%. Hasil penelitian menunjukkan bahwa peningkatan komposisi pelarut berdampak pada penurunan kandungan senyawa oksigenat. Pada persentase pelarut yang tinggi diperkirakan pelarut yang berada pada kondisi superkritis memiliki diffusivitas yang tinggi yang dapat mengurangi hambatan perpindahan massa reaktan dalam reaksi. Komposisi pelarut pada 90% menghasilkan produk terbaik dengan kandungan furan sebesar 0% dan kandungan aldehid serta fennol yang paling sedikit diantara variasi komposisi pelarut yang ada.

---

Bio-oil from the slow pyrolysis of corn cobs contains a lot of oxygenate compounds. The most abundant oxygenate compound in bio-oil is acetic acid. From the results of the C-NMR test, the oxygenate and aliphatic compounds in bio-oil were 53.8% and 46.2%, respectively. The aliphatic compounds in bio-oil have little branching with a short level of branching. The oxygenate compounds in bio-oil reduces the heating value of bio-oil, causes corrosiveness, and is unstable. Therefore bio-oil need to be upgrade through hydrodeoxygenation process to reduce the content of oxygenate compounds in bio-oil. In this study, bio-oil was produced through a slow pyrolysis process of corn cobs. The hydrodeoxygenation reaction was carried out in a stirred tank reactor with a NiCu/ZrO2 catalyst at 200oC and 14 bar. Hexadecane composition will be varied at 65%, 75%, 82.5%, and 90%. From the XRF and EDX results nickel and copper content in the catalyst was 1.96% and 1.47%, respectively. The NiCu/ZrO2 catalyst with an amphoter monocyclic structure is able to reduce the oxygenate compounds to 17% and increase alkanes to 83% at 90% hexadecane solvent composition. The results showed that increase in the solvent composition caused the decrease in the amount of oxygenate compounds. At a high percentage of solvent, it is estimated that the solvent in supercritical conditions has a high diffusivity which can reduce the mass transfer resistance of the reactants in the reaction. The solvent composition at 90% produced the best product with 0% furan content and the least aldehyde and phenol content among the various solvent compositions.