"Pada umumnya modifier stronsium ditambahkan pada paduan Al-Si hipoeutektik dengan kadar Si < 12 %. Penambahan modifier stronsium pada paduan Al-Si hipoeutektik terbukti efektif meningkatkan sifat-sifat mekanis paduan. Sedangkan penambahan modifier stronsium pada paduan aluminium hipereutektik belum banyak dilakukan. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan modifier stronsium terhadap sifat mekanis paduan Al-Si hipereutektik (Si>12,7%). Sifat mekanis yang ingin diketahui setelah penambahan modifier stronsium adalah kekerasan, kekuatan tarik dan keausan. Dalam penelitian ini digunakan material AC8A dengan standar kadar Si sebesar 11-13%. Ditambahkan kristal silikon murni ke dalam material AC8A untuk mendapatkan kondisi hipereutektik (Si>12.7%). Perbedaan penambahan kadar stronsium dalam paduan AC8A hipereutektik merupakan variabel dalam penelitian ini, sedangkan kondisi-kondisi proses lainnya dibuat sama. Stronsium yang ditambahkan adalah sebesar 0% wt, 0.126% wt, 0.208% wt, 0.284% wt dan 0.299% wt.Hasil penelitian menunjukkan bahwa dengan penambahan modifier stronsium pada paduan AC8A hipereutektik akan mengubah bentuk silicon eutektik dari acircular menjadi fibrous dan fasa intermetalik yang terbentuk menjadi lebih tersebar. Selain itu silikon primer akan ditekan pertumbuhannya sehingga berukuran lebih kecil dan lebih tersebar merata. Hasil pengujian kekerasan dan keausan menunjukkan adanya kekerasan dan ketahanan aus yang cenderung meningkat dengan peningkatan kadar stronsium yang ditambahkan. Kekerasan cenderung meningkat secara berturut-turut dari 41 HRB menjadi 44 HRB, 45 HRB, 43 HRB dan 48 HRB. Ketahanan aus meningkat dengan laju aus yang cenderung semakin menurun secara berturut-turut dari 3.27 x 10^-5 mm3/mm menjadi 2.01 x 10^-5 mm3/mm, 1.82 x 10^-5 mm3/mm, 2.27 x 10^-5 mm3/mm, dan 1.28 x 10^-5 mm3/mm. Kekuatan tarik yang didapatkan berturut-turut dari 173 Mpa menjadi 187 Mpa, 168 Mpa, 172 Mpa dan 185 Mpa. Nilai elongasi cenderung mengalami penurunan yaitu dari 0.125 menjadi 0.123, 0.118, 0.124 dan 0.114.

---

In general, stronsium modifier is added to hypoeutectic Al-Si alloys with Si content < 12%. Addition of stronsium modifier in hypoeutectic Al-Si alloys effectivelly improve mechanical properties of alloys. Whereas, addition of stronsium modifier in hypereutectic Al-Si alloys is done rarely. This research has purpose to know effect of stronsium modifier addition on mechanical properties of hypereutectic Al-Si alloys. The mechanical properties that will be observed in this research are hardness, tensile strength and wear resistant. This research use AC8A material with 11-13% standard of Si content. Silicon crystal is added to AC8A material for obtaining hypereutectic condition (Si >12.7%). The difference of amount stronsium addition is as variable on this research. The other condition casting process, such as : strontium modifier addition temperature, cast temperature, solidification time and casting time are the same. The amount of strontium modifier which added is 0,126% wt, 0.208% wt, 0.284% wt and 0.299% wt.

The result of research show that with addition of strontium modifier to hypereutectic AC8A alloy will change eutectic silicon morphology from acircular to fibrous and intermetallic phase that be formed become more uniformly dispersed. Another, the growth of primary silicon will be suppressed until finer in size and more uniformly dispersed. The results both of hardness and wear testing show presence of disposed increasing in hardness and wear resistant with rising of Sr content that be added. The hardness disposed increase, in succession, from 41 HRB to 44 HRB, 45 HRB, 43 HRB and 48 HRB. Wear resistant disposed increase with disposed decreasing of wear rate, in succession, from 3.27 x 10-5 mm3/mm to 2.01 x 10^-5 mm3/mm, 1.82 x 10^-5 mm3/mm, 2.27 x 10^-5 mm3/mm, and 1.28 x 10^-5 mm3/mm. Tensile strength that be obtained, in succession, from 173 Mpa to 187 Mpa, 168 Mpa, 172 Mpa and 185 Mpa. The value of elongation disposed decrease from 0.125 to 0.123, 0.118, 0.124 and 0.114."

"Karena sifatnya yang menarik seperti ketahanan aus yang tinggi, koefisien ekspansi termal yang rendah, ketahanan korosi yang baik serta kemampuan cor yang baik, paduan aluminium - silikon hipereutektik telah menjadi suatu kandidat material untuk aplikasi - aplikasi yang membutuhkan sifat mekanis yang baik seperti piston.Walaupun demikian, paduan ini memiliki kekurangan yaitu paduan akan semakin bertambah brittle seiring dengan bertambahnya kandungan silicon dikarenakan oleh adanya silikon primer yang kasar. Terdapat berbagai cara untuk meminimalkan ukuran dari fasa silikon salah satunya adalah modifikasi dengan penambahan modifier.Pada penelitian ini, material AC8A didesain pada kondisi hipereutektik. Modifier fosfor ditambahkan dengan komposisi 0,0025 wt%, 0,0027 wt %, 0,0038 wt %, 0,0046 wt % dan 0,0061 wt % P. Untuk mengetahui sifat mekanis material, dilakukan pengujian kekuatan tarik, kekerasan serta keausan. Pengujian struktur mikro, SEM dan EDAX dilakukan untuk mengetahu perubahan struktur mikro serta fasa - fasa yang terbentuk dalam paduan.Hasil penelitian menunjukkan bahwa penambahan fosfor pada material AC8A hipereutektik akan mengubah morfologi dan ukuran silikon primer dari yang berbentuk poligonal dan kasar menjadi berbentuk blocky dan halus. Silikon eutektik juga mengalami perubahan karena pertumbuhannya yang berasal dari ujung silikon primer dan dipengaruhi oleh morfologi dan ukuran silikon prime. Silikon eutektik berubah dari jarum - jarum halus yang panjang menjadi batangan pendek dan seperti titik dengan panjang rata - rata yang lebih pendek.Hasil pengujian kekerasan menunjukkan, dengan bertambahnya kadar fosfor (0,0025 wt%, 0,0027 wt %, 0,0038 wt %, 0,0046 wt % dan 0,0061 wt %), kekerasan akan meningkat dari 38 HRB menjadi 39 HRB,40 HRB, 41 HRB dan 42 HRB. Peningkatan juga terjadi pada nilai ketahanan aus material. Sedangkan nilai kekuatan tarik tidak menunjukkan kecenderungan tertentu dikarenakan terdapatnya porositas pada sampel.

---

Because of the interesting properties such as high wear resistance, low thermal expansion coefficient, high resistance to corrosion and castability, hypereutectic Al-Si alloys have become a candidate material for potential applications including piston. Nevertheless, it has a disadvantage which is it becomes more brittle as the ratio of silicon is added because of the presence of coarse primary silicon. There are a lot of ways to minimize silicon phases, one of them is modification using modifier.

In this research, aluminium alloy desaigned as AC8A was desaigned in hypereutectic condition. Phosphorus modifier was added to the melt with composition 0,0025 wt%, 0,0027 wt %, 0,0038 wt %, 0,0046 wt % dan 0,0061 wt % P. Tensile strength, hardness and wear were tested in order to know mechanical properties of material. Microstructure testing, SEM and EDAX were conducted to observe microstructure changing and phases formed in alloy.

Results of this research show that phosphorus addition in hypereutectic AC8A alloy changes the morphology and size of primary silicon from coarse polygonal to fine blocky structure. Eutectic silicon is also changed because it grows from the tip of angles on the primary silicon and is influenced by the morphology and size of primary silicon. The eutectic silicon changes from long fine needle-like shape to short bars and dots with less average length.

Hardness testing shows that by increasing phosphorus addition (0 wt %, 0,003 wt%, 0,004 wt% , 0,005 wt% dan 0,006 wt%) to the melt, hardness of the material increases from 38 HRB to 39 HRB, 40 HRB, 41 HRB, and 42 HRB. Furthermore, the value of wear resistance also increases. Nevertheless, tensile strength doesn't show any tendency because of porosity."

"Piston pada motor adalah komponen dari mesin pembakaran dalam yang berfungsi sebagai penekan udara masuk dan penerima hentakan pembakaran pada ruang bakar cylinder liner. Material penyusun piston tersebut adalah aluminium AC8H yang sifatnya ringan, kuat, dan tahan aus. Dalam proses pengecoran paduan aluminium, penambahan modifier dan perlakuan panas merupakan proses yang dapat mempengaruhi sifat mekanis coran paduan. Sifat mekanis yang dimaksud adalah kekerasan, kekuatan tarik, keuletan serta keausan.Penelitian ini bertujuan untuk mengetahui kemungkinan penggantian proses perlakuan panas T6 (artificial ageing) yang merupakan standar dari proses pembuatan piston dengan proses penambahan modifier dan kemungkinan mempersingkat proses perlakuan T6 (artificial ageing) dengan proses T4 (natural ageing). Penelitian dilakukan dengan melebur ingot AC8H yang kemudian ditambahkan modifier stronsium dalam ladle. Jumlah kandungan stronsium yang dihasilkan setelah proses penambahan modifier adalah sebesar 0,00072% Sr, 0,0068% Sr, 0,0133% Sr dan 0,031% Sr. Hal yang sama dilakukan dengan menambahkan modifier phospor, dimana kandungan phospor yang dihasilkan menjadi 0,0036% P,0,0038% P, 0,0041% P dan 0,0046% P. Pada perlakuan panas setelah proses pengecoran, hasil ascast dilakukan proses T6 (artificial ageing) dan T4 (natural ageing) dengan pengamatan 0 jam, 24 jam, 48 jam , 72 jam, 96 jam dan 120 jam. Masing masing sampel hasil percobaan diatas dilakukan pengujian karakterisasi struktur mikro dan sifat mekanis.Hasil pengujian menunjukkan bahwa penambahan 0,031 % Sr dan Proses perlakuan panas T4 (natural ageing) 96 jam dan 120 jam setelah quenching memiliki sifat mekanis yang telah masuk range standar kualifikasi komponen piston. Dalam implementasi hasil ini masih harus dilanjutkan dengan uji coba melalui proses engine dyno test.

---

Piston is motor components of the engine which works as a press incoming air and recipient burning fuel in the cylinder liner space. Material of aluminum piston is AC8H that are lightweight, strong, and wear resist. In the process of casting aluminum alloy, adding modifiers and heat treatment is a process that can affect the mechanical properties as cast alloy. Mechanical properties of the object is referred to hardness, tensile strength, elongation and wear resistance.This research aims to find out the possibility of replacing the T6 heat treatment process (artificial ageing), as standard process of making a piston with the addition of modifiers and possibility to shorten the treatment T6 (artificial ageing) with the T4 (natural ageing). Research conducted by melt ingot AC8H then added Strontium in ladle. Strontium added that the amount until contain 0.00072% Sr, 0.0068% Sr, 0.0133% Sr, and 0.031% Sr. The same is done by adding Phospor until contain 0,0036% P, 0.0038% P, 0.0041% P and 0.0046% P. In the heat treatment process sample after casting will be process with T6 and T4 observation 0 hour, 24 hours, 48 hours, 72 hours, 96 hours and 120 hours. Each sample of an experiment conducted over the microstructure characterization and mechanical properties test.The test results indicate that the addition of 0.031% Sr. and heat treatment process T4 (natural ageing) 96 hours and 120 hours after quench as mechanical properties have already entered the qualifying standard range of part-piston. Implementation of the experiment must be continued to engine dyno test process before mass production."

"Penelitian ini betujuan untuk mengetahui pengaruh temperatur cetakan dan temperatur tuang terhadap hasil pengecoran piston pada material aluminium AC8A menggunakan metode gravity die casting dengan program simulasi Z-Cast. Penelitian ini menggunakan simulasi pengecoran. Simulasi ini menggunakan software Z-Cast Pro 3.0 dan desain pada penelitian ini menggunakan software Solid Works 2021 untuk menghasilkan gambar 3D. Penelitian ini menggunakan produk piston dengan variasi variabel temperatur cetakan dan temperatur tuang. Variasi variabel temperatur cetakan yang digunakan adalah 250°C, 300°C, dan 350°C. Variabel yang digunakan untuk variasi temperatur tuang adalah 660°C, 700°C, dan 750°C. Shrinkage karena adanya proses pembekuan atau solidifikasi yang tidak merata pada produk, disebabkan oleh penyusutan volume logam cair pada proses pembekuan serta tidak mendapatkan pasokan logam cair dari riser. Pada penelitian tidak menggunakan riser dengan keadaan optimal pada temperatur cetakan 250°C dan temperatur tuang 660°C, penggunaan riser berukuran 40 mm didapatkan hasil temperature cetakan 350°C dan temperatur tuang 750°C , ukuran riser 50 mm dengan keadaan optimal pada temperatur cetakan 250°C dan temperatur tuang 660°C. Upaya untuk mengurangi cacat dengan membesarkan ukuran riser, dengan ukuran riser 50 mm akan menghasilkan produk coran denga temperatur cetakan dan temperatur tuang yang rendah. Shrinkage pada riser 50 mm lebih sedikit dibandingkan ukuran 40 mm dan tidak menggunakan riser.

---

This research aims to determine the effect of mold temperature and pouring temperature on the results of piston casting on AC8A aluminum material using the gravity die casting method with Z-Cast simulation program. This research uses casting simulation. This simulation uses Z-Cast Pro 3.0 software and the design in this research uses Solid Works 2021 software to produce 3D images. This research uses piston product using variable variations in mold temperature and pouring temperature. The variable of mold temperature variations used are 250°C, 300°C, and 350°C. The variables used to vary the pouring temperature are 660°C, 700°C, and 750°C. Shrinkage is due to the uneven solidification process in the product, due to the shrinkage of the liquid metal volume during the solidification process and not getting a supply of liquid metal from the riser. In the research without using a riser with optimal conditions at a mold temperature of 250°C and a pouring temperature of 660°C, using a 40 mm riser resulted in a mold temperature of 350°C and a pouring temperature of 750°C, a riser size of 50 mm with optimal conditions at the mold temperature 250°C and pouring temperature 660°C. Efforts to reduce defects by increasing the riser size, with a riser size of 50 mm will produce cast products with low mold temperatures and casting temperatures. Shrinkage on a 50 mm riser is less than the 40 mm size and does not use a riser."

"Paduan aluminium ADC 12 merupakan paduan yang banyak digunakan dalam industri otomotif yang dewasa ini industri tersebut berkembang dengan pesat. Paduan harus memiliki sifat mekanis seperti yang diinginkan. Sifat mekanis tuangan diantaranya adalah sifat kekerasan, dipengaruhi oleh struktur mikro. Sedangkan struktur mikro dipengaruhi kecepatan pembekuan dari tuangan. Pada penelitian ini dilakukan pengujian kecepatan pembekuan pada benda uji yang memiliki variasi ketebalan 15, 35, 55 dan 80 mm dan pengaruh penggunaan cil dan riser (penambah) untuk mempenga uhi kecepatan pembekuan. Dari hasil pengujian kekerasan memperlihatkan, bahwa pada ketebalan 15 mm yang menggunakan cil memiliki kecepatan pembekuan yang tinggi dan struktur mikro yang halus dengan nilai kekerasan terbesar (14 HN). Sedangkan penggunaan penambah (riser) sebagai kompensasi untuk mencegah cacat akibat penyusutan pada ketebalan 35 mm, menyebabkan kecepatan pembe kuannya lambat dan bentuk struktur mikro yang kasar dengan nilai kekerasan terendah (68 BHN)."

"Masalah yang sering timbul setelah material dicelup pada proses laku panas pengerasan pengendapan (precipitation hardening) adalah terjadinya distorsi dan perubahan sifat mekanis. Faktor yang menyebabkan timbulnya distorsi dan perubahan sifat mekanis tersebut antara lain adaiah adanya perubahan tegangan dalam dan perubahan struktur mikro. Perubahan tegangan dalam dan perubahan struktur mikro yang tejadi pada paduan Al 2024, dipengaruhi antara lain oleh, jenis dan kondisi media celup. Untuk mengetahui pangaruh jenis dan koridisi media celup tersebut maka dilakukan penelitian mengenai pengaruh temperatur dan konsentrasi media celup UCON® Quenchant A terhadap distorsi dan perubahan sifat mekanis paduan Al 2024. Pada penelitian ini didapatkan hasil bahwa paduan Al 2024 yang dicelup dalam UCON® Quenchant A dengan temperatur 38 °C dan konsentrasi 36 % mengalami distorsi minimum dan memiliki sifat mekanis yang sesuai dengan batas yang distandarkan."

"Kondukfor ACSR (Aluminium Conducfor Steel Reinforced) konvensional yang digunakan saat ini dapat dioperasikan secara kontiniu pada suhu 90°C dan mempunyai kapasitas hantar arus (KHA) yang relatif rendah. Untuk meningkafkan KHA, kondukfor mesti dioperasikan pada suhu yang lebih tinggi dan oleh karena itu mesti terbuat dari paduan aluminium tahan panas ( Thermo-Resistant ). Penggunaa konduktor paduan aluminium tahan panas ini yang disebut dengan TAL (Thermo Resistant Aluminium Alloy) dipandang cukup bagus karena dapat memberikan peningkatan KHA, terutama untuk daerah tropis dimana suhu lingkungan (ambient temperature) pada umumnya relatif tinggi. Kondukfor TAL ini dapat dioperasikan secara kontiniu pada suhu 150 °C atau lebih tinggi dengan KHA sekitar 1,5-1,6 kali konduktor ACSR.Penelitian tehadap sifaf mekanis dan struktur mikro konduktor TAL bertujuan untuk mergetahui sifaf-sifaf mekanis dari konduktor TAL dan perbandingannya dengan konduktor aluminium konvensional serta mempelajari bagaimana hubugan sifat mekanis dergan struktur mikronya. Penelitian lakukan terhadap kawat TAL dengan diameter 3,20 mm. Ada dua jenis kawat TAL yang digunakan, yaitu : TAL+, kawat TAL yang dalam proses pembuatannya ditambahkan RE (rare earth metal) atau logam tanah jarang dan TAL-, tanpa penambahan RE. Sebagai pembanding digunakan kawat AAC (All Aluminium Conductor) dengan diameter yang sama.Sifat mekanis yang diuji adalah kuat tarik, elongasi, kekerasan, sifaf tahan panas dan sifat 'creep'. Pengujian kuat tarik dan elongasi dengan Mesin Uji Tarik Shimadzu AG8-1000B dengan mengukur gaya (BF, breaking force) dan elongasi pada saat putus. Kekerasan diukur dengan Vickers hardness testet. Pengujian sifat tahan panas dilakukan dergan mergukur kuat tarik sampel yang dipanaskan pada suhu 230 °C selama 1 sampai 5 jam dan pemanasan selama satu jam pada suhu 90 sampai 275°C. Kemudian dibandingkan dengan kuat tarik sampel sebelum dipanasksan. Pengujian creep dengan Mesin Uji Creep SSI Satec inc. dergan metoda creep-rupfure, diamati perpanjangan (creep-strain) dan waktu putus (tR1 time to rupture). Untuk mamperoleh struktur kawat TAL dilakukan pengamatan dengan mikroskop optik, Scaning Electron Microscope (SEM) dan Transmision Electron Miosroscape (TEM).Dari pergujian didapatkan bahwa kuat tarik rata-rata kawaf TAL adalah 18,28 kg/mm2, lebih kuat dari kawat AAC (16,99 kg/mm2). Kuat tarik rata-rata kawat TAL+ adalah 19,35 kg/mm2, sedangkan TAL- 17,20 kg/mm2. Elongasi rata-rata kawaf TAL 2,69%, sedangkan AAC 2,44%. Elongasi TAL+ adalah 2,85% dan TAL- 253%. Hasil pergujian sifat tahan panas (TR) menunjukan bahwa kawat TAL mempunyai sifaf tahan panas lebih tinggi dibangding kawaf AAC. Pemanasan selama satu jam pada suhu 230o c menyebabkan kuat tarik; kawat TAL+ turun menjadi 18,11 kg/mm2 (TR 93,60%), TAL- menjadi 16,41 kg/mm2 (TR=95,44%) dan ACC turun menjadi 14,36 kg/mm2 (TR=84,55%). Hasil pengujian creep diperoleh kecenderungan kawat TAL mempunyai waktu putus (tr, time to rupture) lebih panjang disbanding ACC. Kawat TAL- mempunyai waktu putus lebih panjang dari TAL+. Pada struktur mikro konduktor TAL+ dan TAL- terdapat presipitat ZrAl3 pada matriks aluminium. Peningkatan sifat tahan panas dan sifat creep ini disebabkan pembentukan presipitat ZrAl3 akibat adanya penambahan Zr. ZrAl3 ini dapat berfungsi sebagai pemaku (pinning) daerah batas butir dan sebagai penghalang gerakan dislokasi. Pada pengamatan dengan TEM dihasilkan pola difraksi electron yang dapat digunakan untuk menentukan jenis presipitat yang terdapat pada matriks aluminium."