Hasil Pencarian  ::  Simpan CSV :: Kembali

"ABSTRAKShape Memory Polyurethane (SMPU) telah disintesis dari penambahan polyethylene glycol (PEG-6000) sebagai segmen lunak dan 4,4'-Methylenebis (Cyclohexyl isocyanate) (HMDI) sebagai segmen keras serta 1,1,1-Trimethylol propane (TMP) sebagai chain extender. SMPU lalu ditambahkan nanopartikel Fe3O4 berukuran 20-50 nm untuk meningkatkan sifat kemagnetan. Untuk mengkonfimasi bentuk ikatan antarmuka komposit SMPU digunakan FTIR (Fourier Transform Infrared Spectroscopy). FE-SEM digunakan untuk mengetahui interface dari filler dan matriks SMPU. Konfirmasi nilai kemagnetan menggunakan VSM (vibrating sampel magnetometer) dan pengujian tarik menggunakan microtensile menunjukkan bahwa penambahan Fe3O4 dengan persentase 11 wt% menghasilkan nilai kemagnetan dan sifat mekanik tertinggi.

---

ABSTRACTShape Memory Polyurethane (SMPU) has been synthesized by reacting polyethylene glycol (PEG-6000) as softsegment, 4,4'-Methylenebis (Cyclohexyl isocyanate) (HMDI) as hardsegment and 1,1,1-Trimethylol propane (TMP) as chain extender. SMPU was added by Fe3O4 as filler to provide magnetical property. Magnetite which had confirmed by Scanning Elctron Magnetic (SEM) have size 20-50 nm. Functional group was investigated by FTIR (Fourier Transform Infrared Spectroscopy). The magnetic behavior of the nanocomposites was observed by vibrating sample margnetometer (VSM). FE-SEM is used to acknowledge interface between filler and Shape Memory Polyurethane (SMPU) matrix. Mechanical properties tested by microtensile testing showed adding 11% Fe3O4 obtaining magnetic and nanocomposites SMPU resulted in improved materials with higher magnetical and mechanical properties."

"ABSTRAKPolyurethane dengan bahan dasar Polyethyelene Glycol (PEG mw: 6000) sebagai soft segment, 4,4’-methyelenebis(cyclohexyl isocyanate) (HMDI) sebagai hard segment dan 1,1,1-trimethylol propane (TMP) sebagai chain extender digunakan untuk membuat material dengan shape memory berbasis polimer. Bahan komposit yang digunakan adalah partikel nan magnetit Fe3O4 berukuran 20-50nm. Variasi komposisi HMDI digunakan sebagai variabel dengan pengujian yang dilakukan adalah FTIR (Fourier Transform Infrared Spectroscopy) dan NMR (Nuclear Magnetic Resonance) untuk menginvestigasi rantai polimer yang terbentuk dan menghitung perbandingan hard segment dan soft segment di dalam material, UTM (Universal Testing Machine) dan Aktuasi Fisik untuk menganalisa kekuatan mekanis dap uji recovery fisik dan Uji STA (Simultanoeus Thermal Analysis) untuk menganalisa pengaruh kristalinitas terhadap sifat mekanik. Dari penelitian ini diketahui bahwa, penambahan komposisi HMDI yang lebih banyak akan meningkatkan sifat mekanik nanokomposit SMPU, namun kadar HMDI yang berlebihan justru akan menurunkan sifat mekanisnya. Dari hasil observasi juga didapatkan bahwa penambahan HMDI akan memicu terjadinya separasi fasa yang akan memeberikan efek shape memory pada sampel. Komposisi terbaik yang didapatkan adalah sampel dengan perbandingan 1 mol PEG, 7 mol HMDI, 2 mol TMP dan 1 mol partikel dan Fe3O4 dengan Rf dan Rr yang baik yaitu 100% dengan kekuatan tarik yang masih cukup baik yaitu 4,1 MPa.

---

ABSTRACTIn this study, polyurethane was synthesized with Polyethylene Glyocol (PEG mw: 6000) as soft segment, 4,4'-Methylenebis (Cyclohexyl Isocyanate) (HMDI) as hard segment and 1,1,1-Trimethylol Propane (TMP was a chain extender will be used to make a shape memory material polymer based. 20-50nm nanoparticles of magnetite (Fe3O4) bas Led as Filler material. Variations in composition of HMDI used as a variable with some characterization perforrmed using FTIR (Fourier Transform Infrared Spectroscopy) to investigate the formation of polymer chains and to examine the percentation of hard segment and soft segment content, UTM (Universal Testing Machine) and Physical Actuation to analyze tensile strength and physical recovery. STA (Simultanoeus Thermal Analysis) to analyze effect of crystallization on mechanical properties. In this research it was shown that the incrase of addition of HMDI will increase mechanical properties, but the exceed of HMDI composition made the mechnical properties decrease. Besides, increasing HMDI composition will trigger phase separation that leads to shape memory effect. The best composisiton obtained was sample with ratio of 1 mol of PEG, 7 moles of HMDI, 2 moles of TMP and 1 mol Fe3O4 nanoparticle with Rf and Rr are excellent which are 100% for both of them and tensile strength obtained is pretty good which is 4,1 MPa"

"Provides a comprehensive foundation on the nature of personality theory, as well as its contributions to science. This book encompasses a biographical sketch of each theorist, related research, and applications to real life. It also presents sections on topics such as ego identity, gender studies, mindfulness and self-actualization."

"This book covers the mechanism, salient features, and important aspects of various subtractive, additive, forming and hybrid techniques to manufacture near net-shaped products. The latest research in this area as well as possible future research are also highlighted."

"Paduan "Shape memory" adalah paduan yang mempunyai sifat untuk dapat ?teringat" kembali terhadap bentuknya semula apabila dipanaskan. Sifat ingat bentuk ini dihasilkan sebagai akibat terjadinya suatu transformasi fasa induk dan fasa martensit yang reversible. Agar diperoleh sifat ingat bentuk ("shape memory"), maka paduan Cu dengan struktur a dan B harus dilarutkan kembali menjadi fasa tunggal B dengan proses perlakuan pelarutan ("So1ution treatment") hingga mencapai temperatur 750 - 900°C Proses perlakuan pelarutan ini biasanya menyebabkan proses pertumbuhan butir. Pengaruh ukuran besar butir terhadap sifat korosi pa- duan Cu-Zn-A1 diteliti dengan menggunakan ?accelerated test" dan pengukuran elektrokimia. Hasil pengamatan menunjukkan bahwa,paduan dengan fasa B maupun fasa martensit ,keduanya menunjukkan peningkatan laju desengsifikasi ("dezincification") dengan meningkatnya temperatur perlakuan pelarutan. Hasil analisa elemen dengan EDAX mendukung mekanisme desengsifikasi berdasarkan pelarutan anodik dari kuningan diikuti dengan redeposisi Cu dari larutan."

"The SMST Conferences focus on real-world issues and applications of shape memory materials. This volume includes more than 75 edited technical papers and is an excellent reference on the latest technical advances, industrial applications, and current state-of-the-art in shape memory and superelastic technologies."