"Penelitian ini membahas tentang pembuatan gemuk bio lithium komplek menggunakan pelumas hasil epoksidasi minyak sawit. Diharapkan dengan penggunaan minyak sawit dan complexing agent akan didapatkan komposisi dan produk gemuk bio lithium yang memiliki sifat biodegradable dan memiliki ketahanan terhadap suhu lebih tinggi dari 206ºC. Complexing agent yang ditambahkan adalah asam asetat. Komposisi complexing agent divariasikan 0, 2, 3 dan 5 persen. Additive extreme pressure dan anti wear juga ditambahkan dan divariasikan 0 ; 0,5 ; 1 dan 2 persen. Produk yang didapatkan diuji karakteristik dropping point, penetration dan four ball test. Hasil dari penelitian didapatkan dropping point lebih dari 206ºC akibat pengaruh penggunaan complexing agent. Didapatkan pula produk gemuk bio lithium yang memiliki kualitas lebih baik dibandingkan gemuk komersil.

---

In this research the bio grease lithium complex had been made used lubricant from epoxidation crude palm oil. The grease that had been made are expected to have biodegrability and have stability at high temperature more than 206ºC. The complexing agent which be add in to mixture acetic acid. Different amount of complexing agent 0; 2; 3 and 5 persen. Anti wear and extreme pressure additive is added and variated also to 0 ; 0,5 ; 1 and 2 persen. Dropping point test, penetration test and four ball test is provide to the product. The result of this research dropping point test increased from 206ºC, in fluenced by complexing agent. A bio lithium grease which has a better quality than commersial grease is obtained."

"Gemuk lithium kompleks azelat dibuat dengan menambahkan pengompleks asam azelat dan lithium serta sabun lithium konvensional dengan asam 12-hidroksistearat dan lithium pada base oil. Pada penelitian ini bahan penyusun gemuk yaitu base oil dari minyak sawit yang di epoksidasi, lithium hidroksida, asam 12-hidroksistearat dan asam azelat yang dikomposisikan untuk mendapatkan gemuk sesuai standard internasional.Berdasarkan penelitian yang pernah dilakukan didapatkan hasil gemuk lithium kompleks terbaik dengan komposisi asam azelat sebesar 2,5% dari bobot keseluruhan gemuk yang dibuat. Dalam penelitian ini gemuk lithium kompleks azelat dibuat dengan memvariasikan asam azelat sebesar 0%, 1%, 2,5%, 3% dan 4%. Hasil yang didapatkan pada penelitian ini adalah gemuk lithium kompleks azelat dengan nilai dropping point di atas 220_C dengan nilai NLGI 2 dan 3.

---

Lithium azelaic complex grease is made by adding azelaic acid as complexing agent and lithium as well as conventional lithium soap with 12-hidroxystearic acid and lithium on the base oil. In this study the raw material of grease that is base oil from epoxidized palm oil, lithium hydroxide, 12-hidroxyistearic acid and azelaic acid are composed to get grease that fulfill international standards.

Based on the conducted study lithium complex grease obtained best results with azelaic acid composition of 2.5% of total grease weight are made. In this study, lithium complex grease is made by varying azelaic acid 0%, 1%, 2.5%, 3% and 4%. Results obtained in this study is a lithium azelaic complex grease with dropping points values above 220_C with the NLGI 2 and 3."

"Pada penelitian ini, telah dibuat gemuk bio campuran Li-Ca 12HSA Asetat Kompleks menggunakan base oil minyak sawit terepoksidasi dengan thickening agent Lithium 12HSA Asetat Kompleks dan Kalsium 12HSA Asetat Kompleks. Komposisi thickening agent divariasikan untuk mendapatkan gemuk dengan tingkat konsistensi NLGI 2 (multipurpose), sifat tahan terhadap suhu dan yang tinggi air serta sifat anti aus yang baik. Gemuk bio campuran ini dibuat 2 jenis yaitu perbandingan antara lithium asetat/lithium stearat maupun kalsium asetat/kalsium stearat sebesar 3:1 (Gemuk Bio Campuran A) dan 5:1 (Gemuk Bio Campuran B). Gemuk bio campuran ini dibuat melalui reaksi saponifikasi 2 tahap yaitu pada suhu 125°C dan 200°C. Gemuk bio campuran ini dilakukan pengujian meliputi uji sifat fisika-kimia dan uji performa gemuk. Gemuk bio campuran Li-Ca 12HSA Asetat Kompleks yang diperoleh memiliki dropping point 339°C (@NLGI 2), jumlah keausan sebesar 0.4 mg pada persentase kalsium 12HSA Asetat Kompleks 35% atau persentase lithium 12HSA Asetat Kompleks 65% sedangkan nilai water wash out masih berada antara gemuk bio tunggal Lithium 12HSA Asetat Kompleks dan gemuk bio tunggal Kalsium 12HSA Asetat Kompleks.

---

In this research, making a mixture of bio grease Li-Ca 12HSA Acetate complex using epoxidized palm oil base oil with a thickening agent Lithium 12HSA Acetate Complex and Calcium 12HSA Acetate Complex. Thickening agent composition was varied to get grease with the consistency of NLGI 2 (multipurpose), high temperature , resistant water high and a good anti-wear. Bio grease mixture was made 2 types of comparisons between the lithium acetate / lithium stearate or calcium acetate / calcium stearate of 3:1 (Bio Grease Mixture A) and 5:1 (Bio Grease Mixture B). Bio Grease Mixture reaction was prepared by saponification two stages, at a temperature of 125°C and 200°C. This mixture of bio grease do testing properties of physical-chemical and performance. Bio grease Li-Ca mixture have dropping point 339°C (@ NLGI 2), antiwear 0.4 mg of the percentage calcium 12HSA Acetate Complex 35% or the percentage of lithium 12HSA Acetate Complex 65% while the value of wash out water between bio grease Lithium 12HSA Acetate Complex and bio grease Calcium 12HSA Acetate Complex."

"Sebagian besar gemuk yang dijual di pasaran menggunakan bahan base oil minyak mineral dan thickening agent sabun lithium. Aplikasi gemuk dijumpai pada sistem pelumasan yang sederhana seperti pelumasan ball bearing pada as roda dan lain-lain. base oil EFAMEGLI dan mineral oil. Gemuk yang dibuat ini diharapkan mempunyai sifat biodegradability dibandingkan dengan gemuk dengan bahan base oil minyak mineral, dikarenakan gemuk bio menggunakan base oil minyak nabati. Bahan thickening yang digunakan adalah sabun kalsium dan litium, dimana gemuk kalsium diperuntukkan pada gemuk foodgrade sedangkan gemuk litium untuk gemuk tahan panas. Pembuatan gemuk bio dan semi bio dibuat dengan autoclave (reaktor tertutup), dengan temperatur pemasakan 160-200_C. Kemudian dilakukan pendinginan dan homogenisasi. Adapun uji karakteristik yang dilakukan diantaranya penetration, dropping point dan four ball test. Dari hasil pengamatan secara visual warna yang dihasilkan putih dan bentuknya halus (homogen). Dari hasil uji pada gemuk semi bio dengan komposisi sabun litium 15% menunjukkan bahwa dengan pengaruh komposisi EFAMEGLI dapat menaikan dropping point dan memperbaiki anti keausannya. Sedangkan untuk penetrasi dengan NLGI # 2 dan 3 terdapat pada komposisi EFAMEGLI 20-40%.

---

Most of grease that sold in the market is using base oil made form mineral oil and thickening agent from lithium soap, Grease application, it is use don simple lubrication system such as ball bearing on axle Wheel and etc. In this experiment the grease had been made from mixing base oil from EFAMEGLI and mineral oil. The thickening material that had been used are calcium soap and lithium soap. The grease that had been made are expected to have a better biodegrability and stability compared to grease with mineral oil as base oil. This could be happened because of usage of vegetable oil as base oil, which has an edible and biodegradeble char_cter compared to mineral oil. Bio and semi bio grease production wih autoclave (close reactor) with heater temperatur at 160-200 OC. After that cooling and homogenisation. The test characteristic such as penetration, dropping point dan four ball test. By using vegetable oil and mineral oil in biogrease production we could know that the grease are made with autoclave (close reactor) which has a whiter color and more refined (homogen). The test result shown that to obtain biogrease 15 % lithium with a base oil from EFAMEGLI and mineral oil with a better penetration, dropping point and anti wornout stability compared to grease with base oil from mineral oil need much more composition of vegetable oil (EFAMEGLI) 20-40% to have NLGI number 2-3."

"Pada penelitian ini dibuat gemuk bio yang ramah lingkungan menggunakan bahan dasar minyak biji kapuk randu yang memiliki kadar asam trigliserida sebanyak 25-28% yang dapat berpontensi menjadi gemuk. Pengental yang digunakan adalah sabun litium 12-hidroksistearat dan litium kompleks dengan asam azelat sebagai agen pengompleks. Berat gemuk yang dihasilkan sebanyak 200 gram dengan rasio perbandingan jumlah campuran komposisi minyak dasar dan pengental sabun yaitu 85%:15%, 88%:12%, 89%:11%, 90%:10%, 93%:7% dan 95%:5%. Gemuk yang dihasilkan telah dilakukan pengujian, yaitu uji penetrasi, uji dropping point dan uji four ball. Gemuk terbaik yang dihasilkan dengan sabun litium 12-hidroksistearat pada komposisi 90%:10% sedangkan gemuk terbaik yang dihasilkan dengan sabun litium kompleks pada komposisi 89%:11%. Berdasarkan uji Penetrasi dan uji four-ball gemuk yang dihasilkan adalah gemuk NLGI (National Lubricating Grease Institute) 2, namun nilai dropping point didapatkan sebesar 158 ? dan 130 ?.

---

This research studied bio-grease production based on cottonseed oil which has a triglyceride acid content of 25-28% that has the potential to become grease. The Thickener is lithium 12-hydroxystearic soap and lithium complex soap with azelaic acid added as a complexing agent. The weight of the grease produced was 200 grams with the ratio of the total mixture composition of base oil and thickening agent are 85%:15%, 88%:12%, 89%:11%90%:10%, 93%:7% and 95%:5%. The resulting grease will be tested, namely penetration test, dropping point test, and four-ball test. The best grease with lithium 12-hydroxy stearate soap is grease at 90%:10%of composition ratio and the best grease lithium complex soap at 89%:11%. Based on the penetration and four-ball tests, the bio grease is NLGI (National Lubricating Grease Institute) 2, but the dropping point values were 158 ? and 130 ?."

"ABSTRAKPada riset ini dilakukan studi pembuatan gemuk bio ramah lingkungan, melalui proses saponifikasi-pelarutan-kristalisasi-homogensasi. Minyak-dasar yang digunakan adalah olein sawit yang dimodifikasi, untuk meningkatkan ketahanan oksidasinya. Sebagai pengental adalah sabun logam-12-hidroksistearat. Dari studi ini diketahui bahwa preparasi minyak-dasar, yaitu modifikasi olein sawit menjadi pelumas bio yang memiliki gugus-gugus polar (epoksida -COC, hidroksida -OH, ester -COOC-), sangat penting dalam proses pembuatan gemuk bio. Gugus-gugus tersebut menjadikan gemuk bio memiliki performa pelumasan yang melampaui performa gemuk mineral. Gemuk bio dengan konsistensi NLGI2 (tingkat kekerasan gemuk multiguna) dapat diperoleh pada komposisi sabun 10-15 % dengan dropping point 200 oC untuk gemuk litium dan 110 oC untuk gemuk kalsium. Penggunaan pengomplek Ca-asetat menghasilkan gemuk kalsium kompleks dengan dropping point 300oC pada komposisi sabun total 15% dan rasio mol Ca-asetat/Ca-12-hidroksistearat 5:1. Gemuk bio yang diperoleh dihomogenisasi melalui metode pengadukan (2-pengaduk-turbin yang berputar berlawanan arah).

---

ABSTRACTThis research studies the manufacturing of eco-friendly biogrease via saponification-dilution?recrystallization-homogenization process. The base oil for the biogrease is prepared by modification of palm olein via esterification-epoxidation-addition process to improve its oxidation stability. The thickening agent for the biogrease is metal-12-hydroxystearate soap. From this study it was found that the preparation of base oil through modification of palm olein into biolubricant containing polar groups (-COC, -OH, -COOC-) is important step in the manufacturing process of biogrease. The biogrease NLGI2 (consistency level of multipurpose grease)) can be obtained when soap composition is 10-15 % with dropping point of 200 oC for lithium biogrease and 110 oC calcium biogrease. The use of acetic acid as complexing agent for the calcium grease can significantly improve its dropping point to 300oC at ratio mol Ca-asetat/Ca-12-hydroxystearate 5:1 with total thickening agent 15%. The biogrease is homogenized by mixing method (2-turbin rotated in the opposite direction)."

"ABSTRAKPada riset ini dilakukan studi pembuatan gemuk bio ramah lingkungan, melalui proses saponifikasi-pelarutan-kristalisasi-homogensasi. Minyak-dasar yang digunakan adalah olein sawit yang dimodifikasi, untuk meningkatkan ketahanan oksidasinya. Sebagai pengental adalah sabun logam-12-hidroksistearat. Dari studi ini diketahui bahwa preparasi minyak-dasar, yaitu modifikasi olein sawit menjadi pelumas bio yang memiliki gugus-gugus polar (epoksida -COC, hidroksida -OH, ester -COOC-), sangat penting dalam proses pembuatan gemuk bio. Gugus-gugus tersebut menjadikan gemuk bio memiliki performa pelumasan yang melampaui performa gemuk mineral. Gemuk bio dengan konsistensi NLGI2 (tingkat kekerasan gemuk multiguna) dapat diperoleh pada komposisi sabun 10-15 % dengan dropping point 200 oC untuk gemuk litium dan 110 oC untuk gemuk kalsium. Penggunaan pengomplek Ca-asetat menghasilkan gemuk kalsium kompleks dengan dropping point 300oC pada komposisi sabun total 15% dan rasio mol Ca-asetat/Ca-12-hidroksistearat 5:1. Gemuk bio yang diperoleh dihomogenisasi melalui metode pengadukan (2-pengaduk-turbin yang berputar berlawanan arah).

---

ABSTRACT

This research studies the manufacturing of eco-friendly biogrease via saponification-dilution?recrystallization-homogenization process. The base oil for the biogrease is prepared by modification of palm olein via esterification-epoxidation-addition process to improve its oxidation stability. The thickening agent for the biogrease is metal-12-hydroxystearate soap. From this study it was found that the preparation of base oil through modification of palm olein into biolubricant containing polar groups (-COC, -OH, -COOC-) is important step in the manufacturing process of biogrease. The biogrease NLGI2 (consistency level of multipurpose grease)) can be obtained when soap composition is 10-15 % with dropping point of 200 oC for lithium biogrease and 110 oC calcium biogrease. The use of acetic acid as complexing agent for the calcium grease can significantly improve its dropping point to 300oC at ratio mol Ca-asetat/Ca-12-hydroxystearate 5:1 with total thickening agent 15%. The biogrease is homogenized by mixing method (2-turbin rotated in the opposite direction)."

"Gemuk kalsium kompleks berpotensi digunakan dalam aplikasi food grade H-1. Agen pengompleks yang paling umum digunakan adalah asam asetat sedangkan asam azelat banyak digunakan sebagai agen pengompleks dalam gemuk litium kompleks, di mana kedua asam pengompleks rantai pendek ini memberikan gemuk dengan peforma yang sangat baik bila digunakan secara terpisah. Dalam penelitian ini, gemuk bio kalsium kompleks disintesis dengan menggunakan minyak goreng kelapa sawit sebagai minyak dasar, asam 12 – hidroksistearat sebagai asam lemak, bersama dengan kombinasi asam asetat dan asam azelat sebagai agen pengompleks. Gemuk dibuat dengan cara saponifikasi, diikuti dengan pendinginan dan homogenisasi. Komposisi campuran asam asetat dan asam azelat divariasikan untuk menunjukkan pengaruh interaksi antara kedua agen pengompleks ini yang ditentukan dengan melakukan uji peforma gemuk. Gemuk bio kalsium kompleks yang dihasilkan dari kombinasi ca-asetat dan ca-azelat memiliki NLGI 2 dengan sifat anti-aus dan mulur yang sangat baik dibandingkan hanya menggunakan satu agen pengompleks, dengan komposisi rasio persen berat terbaik dari asam asetat/asam azelat berada pada 80:20. Namun, dropping point yang dicapai masih lebih rendah dibanding ketika gemuk bio kalsium kompleks dibuat hanya dengan menggunakan asam asetat.

---

Calcium complex grease has the potential to be used in H–1 food-grade application. The most common complexing agent used is acetic acid while azelaic acid is widely used as a complexing agent in lithium complex grease where these two short-chain complexing acids provide the final grease with great performance when used individually. In this study, calcium complex grease was synthesized by using palm oil as base oil, 12 – hydroxystearic acid as fatty acid, along with combination of acetic and azelaic acids as the complexing agents. Grease was manufactured by saponification, followed by cooling and homogenization. The weight percent composition of acetic acid and azelaic acid was varied to indicate the effect of the interaction between these two complexing agents which was determined by grease performance characteristic tests. The combination of ca-acetate and ca-azelaic as complexing salts in grease formulation had NLGI grade 2 consistency with excellent anti-wear properties and grease tackiness compared to calcium complex bio grease contains only single complexing agent, with the best weight percent ratio composition of acetic acid/azelaic acid was at 80:20. However, the dropping point achieved was still lower than when acetic acid was used alone in the formulation of calcium complex bio grease."

"ABSTRAKGemuk bio kalsium sulfonat kompleks yang dibuat menggunakan minyak sawit terepoksidasi sebagai base oil dan sabun kalsium sulfonat kompleks sebagai thickening agent yang terdiri dari kalsium sulfonat, kalsium karbonat, kalsium hidroksi stearat, dan kalsium asetat sebagai pengompleks dengan memvariasikan komposisi thickening agent. Gemuk tersebut dibuat dengan tahapan saponifikasi di reaktor batch tertutup, dilanjutkan dengan pendinginan dan homogenisasi. Pengaruh sabun kalsium sulfonat kompleks terhadap kualitas gemuk dapat terlihat pada uji karakteristik seperti penetrasi, dropping point, serta four ball test untuk mengetahui performa dari gemuk. Gemuk terbaik dihasilkan dengan komposisi thickening agent 56,01% yang terdiri dari kalsium sulfonat sebagai sabun utama serta kalsium karbonat, kalsium hidroksi stearat, dan kalsium asetat (Ca-karstetat) sebagai pengompleksnya dengan tingkat konsistensi NLGI 2 dan memiliki nilaidropping point 301 0C. Pada four ball test gemuk bio kalsium sulfonat kompleks ini menghasilkan nilai keausan yang sangat kecil hingga 0,01mg.

---

ABSTRACTBio calcium sulfonate complex grease produced from epoxise of palm oil use thickening agent calcium sulfonate complex, which is a mixture of calcium sulfonate, calcium carbonate, calcium hidroxy stearat, calcium acetat with a variety of thickening agent. Grease is made using stages saponification in the closed batch reactor, continue with cooling and homogenization. Effect of calcium sulfonate complex soap grease quality can be seen on the test characteristics such as penetration, dropping point, and the four ball test to determine the performanceof the grease. The best grease produced by the composition of 56,03% thickening agent which composed from calcium sulfonate as the main soap and calcium carbonate, calcium hydroxy stearate, and calcium acetate (Ca-Carstetate) as complexing with the level of consistency NLGI 2 and has a dropping point value 301 0C. In the four ball test bio calcium sulfonate complex grease it produces a very small value of the wear of up to 0.01 mg."

"Ko-pirolisis polipropilena dan minyak kelapa sawit memberikan cara pemanfaatan limbah plastik polipropilena. Penelitian ini akan meneliti reaksi ko-pirolisis di dalam reaktor tangki berpengaduk menggunakan katalis ceramic foam ZrO2/Al2O3-TiO2 untuk mengakomodasi ukuran molekul reaktan yang besar. Tujuan penelitian ini adalah untuk mendapatkan pengaruh laju pemanasan dan komposisi rasio umpan plastik polipropilena dari 0, 25, 50, 75, dan 100 % berat umpan terhadap hasil produk ko-pirolisis dan komposisi bio-oil. Produk dari ko-pirolisis akan dianalisis menggunakan metode Karl- Fischer, FTIR, GC-MS, C-NMR, dan DEPT 135 untuk menentukan kemungkinan jalur reaksi, komposisi senyawa, dan ikatan kimia yang ada di dalam bio-oil dan wax. Terdapat pengaruh laju pemanasan dan rasio umpan polipropilena terhadap jumlah produk dan senyawa kimia di dalam bio-oil. Penggunaan katalis ceramic foam ZrO2/Al2O3-TiO2 mampu meningkatkan kualitas dan yield produk akhir. Sistem pirolisis katalitik laju pemanasan tinggi tidak menunjukkan efek sinergis antara PP dan CPO dalam yield dan komponen non-oksigenat karena fraksi non-oksigenat yang rendah di bio-oil dan yield bio-oil yang rendah. Sistem pirolisis termal menunjukkan efek sinergis yang lebih tinggi antara PP dan CPO terhadap yield bio-oil yang lebih tinggi. Sistem pirolisis katalitik laju pemanasan rendah menunjukkan efek sinergis tertinggi antara PP dan CPO dalam hal jumlah fraksi non-oksigenat dan yield dari bio-oil. Analisis C-NMR dan DEPT-135 dari bio-oil menunjukkan bahwa sistem katalitik dan termal dengan laju pemanasan tinggi memiliki jumlah karbon yang terikat pada oksigen lebih tinggi dibandingkan dengan sistem katalitik laju pemanasan rendah yang menunjukkan efisiensi deoksigenasi yang lebih tinggi.

---

Co-pyrolysis of polypropylene and crude palm oil gives the benefit of utilizing plastic waste of polypropylene. In the present research, co-pyrolysis reaction in a stirred tank reactor will be investigated using ZrO2/Al2O3-TiO2 ceramic foam catalyst to accommodate the large molecular size of reactants. The objectives are to obtain effects of heating rate and feed composition of polypropylene plastic from 0, 25, 50, 75, and 100 wt.% of total feed weight on yields of co-pyrolysis products and composition of bio-oil. The products were analyzed using Karl-Fischer, FTIR, GC-MS, C-NMR, and DEPT 135 to determine the possible reaction pathway, compound compositions, and chemical bonds in the bio-oil and wax. There is an effect of heating rate and feed composition on the yield and chemical compound of the product. The use of ZrO2/Al2O3-TiO2 ceramic foam catalyst improve the quality and yield of the final product. Catalytic high heating rate pyrolysis showed no synergetic effects between PP and CPO on bio-oil yield and non- oxygenates components due to low non-oxygenates fractions in bio-oil and low bio-oil yield. Thermal pyrolysis showed synergetic effects between PP and CPO on bio-oil yield. Catalytic low heating rate pyrolysis showed high synergetic effects between PP and CPO in terms of the quantity of non-oxygenates fractions in bio-oil and the bio-oil yield. C- NMR and DEPT-135 of bio-oil suggested that catalytic and thermal high heating rate system contained higher amount of carbon bound to oxygen compared to the catalytic low heating rate system which indicated higher deoxygenation efficiency."