"Carbon monoxide (CO) poisoning is the most common of all poisoning in industriestoday and is responsible for over half of the poisoning fatalities reported each year inThe United State. However, in Indonesia is not data or report according to Carbonmonoxide poisoning eventhough its founded in some area incidently. But, ifIndonesia become industrial country, we may make prediction which this problemswill get improve and become greater than today. There are some report todayaccording to deadness related to carbon monoxide poisoning. For example, personsare dead in garage in which ingine of car is on and some people dead in building thatis fire. The people dead is as a result of carbon monoxide poisoning.Carbon monoxide poisoning occur too much caused by some reasons. Thepossibilities of carbon monoxide poisoning are ambiquitous. It has colorless andodorless. Therefore, gives no warning of its presence under any circumstance. lnaddition, almost all of industrial toxins have characteristic odor, taste or appearanceor produce some sort of irritation that warns the potensial victim, a factor not presentin carbon monoxide poisoning. Another reason that makes this form of poisoningparticularly insidous is that the early sympthoms can resemble other diseases. Butthe same with other diseases like nausea, headache and dizziness ect. So that thepersons who has carbon monoxide poisoning found by wrong diagnosis and hasfatal impact. Beside this that also has been senses CO poisoning can cause muscleweakness so that the victim will not be able to get out from poison resources areaeventhough they know hazardous matter coming up to them."

"Gas karbonmonoksida merupakan salah satu gas yang berbahaya bagi kesehatan apabila dihirup dalam jumlah tertentu. Oleh karena itu, perlu dilakukan suatu upaya untuk mengurangi konsentrasi gas tersebut di alam yaitu dengan menggunakan metode adsorpsi. Dalam penelitian ini, zeolit alam Malang dan Lampung diuji kapasitas adsorpsi gas CO-nya dalam proses adsorpsi dari 0 psia sampai 178 psia dengan interval 25 psi dengan variasi ukuran dan suhu adsorpsi. Kedua jenis zeolit tersebut dibandingkan kapasitas adsorpsi, baik setelah maupun sebelum mengalami pengaktifan. Proses pengaktifan menggunakan metode dealuminasi, pertukaran ion dan kalsinasi. Dari hasil penelitian diketahui bahwa adsorben dengan kapasitas adsorpsi terbesar yaitu zeolit alam Lampung dengan ukuran 37-50 mikron dan suhu adsorpsi 25°C dengan kapasitas adsorpsi sebesar 0,5866 mmol/g pada tekanan 175 psia. Hasil ini juga ditunjang dengan karakterisasi adsorben menggunakan metode BET dan XRF untuk mengetahui luas permukaan, ukuran pori dan kandungan Si/Al pada tiap adsorben. Dengan demikian telah didapatkan spesifikasi zeolit dengan kapasitas adsorpsi terbesar terhadap gas CO dari kedua zeolit alam yang digunakan pada percobaan ini.

---

Carbon monoxide is one of a toxic gas which harmful for health if being sniffed in current volume. Thus, it is need to be treated to decrease the concentration of those gas in our environment using adsorption method. In this research, Malang and Lampung natural zeolite are being tested its adsorption capacity of CO in pressure condition 0 to 178 psia with 25 psi interval and using variation of adsorbent size and adsorption temperature. Both of those zeolites are being compared its adsorption capacity, before and after the activation process. Activation processes are de-alumination, ion exchange, and calcinations.

The result of this research is Lampung natural zeolite which has 37-50 mikron in size that being operated in 25°C is an adsorbent which has the highest adsorption capacity of CO, 0,5866 mmol/g at 175 psia. This result is supported with characterization of each adsorbent using BET and XRF method to know its surface area, porous size, and ratio of Si/Al. So, it can be found the best specification of an adsorbent which has the highest adsorption capacity of CO between two of natural zeolite in this research."

"Kasus kebakaran sebagai penghasil gas karbon monoksida (CO) yang tinggi masih menjadi salah satu permasalahan yang harus diselesaikan, mengingat seringnya terjadi peristiwa kebakaran. Jika terjadi kebakaran, potensi kematian akibat keracunan gas CO akan semakin meningkat. Oleh karena itu, diperlukan suatu usaha untuk mengurangi kadar CO, salah satunya adalah dengan metode adsorpsi gas CO menggunakan metode volumetrik dengan temperatur konstan (temperetur 25°C) pada tekanan 0 psia -315 psia dengan interval 50 psi. Sehingga dapat dilakukan perhitungan adsorpsi isotermal Gibbs menggunakan Zeolit Alam Lampung teraktivasi yang dimodifikasi oleh TiO2 melalui metode sol-gel. Variasi kandungan TiO2 yang dilakukan adalah 10, 15, 20, 25 dan 30 (wt%). Dari hasil penelitian diketahui bahwa pelapisan TiO2 terhadap Zeolit Alam Lampung dapat meningkatkan kapasitas adsorpsi. Dari variasi kandungan TiO2 yang telah dilakukan didapatkan komposisi optimum TiO2 sebesar 20 % dan didapatkan kapasitas adsorpsi paling besar yaitu nmax= 0,54361 mmol/gram dengan kandungan TiO2 3,58 (wt%) dan luas permukaan 96,25 m2/gram.

---

Case of fire has a high content of gas carbon monoxide production which has to be solved because of the high frequency of this incident. If it happens, the potential death caused by CO poisoning will increase. Therefore, an effort is needed to reduce CO concentration. One of them is CO gas adsorption method using a volumetric method with a constant temperature (25°C) at pressure 0 psia -315 psia at intervals of 50 psi. It can be calculated by Gibbs adsorption isotherm using activated Lampung Natural Zeolites modified by TiO2 via sol-gel methods. Variations of TiO2 content is done with 10, 15, 20, 25 and 30 (wt%). From the result of this research shows that TiO2 coating on Natural Zeolites Lampung can increase adsorption capacity. TiO2 content of the variations that have been carried out the optimum composition of TiO2 obtained by 20% and the greatest adsorption capacity is nmax = 0.54361 mmol / g with a TiO2 content of 3.58 (wt%) and the surface area 96.25 m2/gram."

"Penggunaan plastik terus meningkat, menghasilkan peningkatan limbah plastik. Pada 2015, limbah dari industri pengemasan menghasilkan 141 juta ton. Pada tahun yang sama, produksi berjumlah hingga 381 juta ton, naik 3,6% dari 2014, dari 367 juta ton. Maka itu, diusulkan agar plastik sachet, yang terbuat dari polypropylene (PP), digunakan sebagai sumber karbon alternative untuk sintesis carbon nanotube (CNT). Sebelum melanjutkan dengan sintesis carbon nanotubes (CNT) menggunakan plastic sachet, sangat penting untuk menghilangkan warna dari limbah PP. Penghilangan warna dilakukan dengan merendam plastik sachet di dalam reagen hidrogen peroksida (H2O2). Sintesis CNT dengan sintesis nyala dicoba. Sintesis memanfaatkan SS 316 sebagai substrat katalis, setelah mengalami perlakuan panas oksidatif, selama 30 menit pada suhu 800oC, sebagai metode pra-perlakuan katalis. Hasil karakterisasi dari XRD, SEM-EDS dan TEM, menggambarkan bahwa PP yang tidak berwarna tidak dapat disintesis menjadi CNT, menunjukkan pertumbuhan CNT yang tidak lengkap dengan diameter 38,89 nm. Ini memiliki hasil rendah 4,206% dibandingkan dengan hasil CNT disintesis dari serpih biru dan SR, yang masing-masing mencapai nilai 8,966% dan 11,167%.The study on the suitability of plastic sachet, mainly made of polypropylene (PP), as an alternative source of carbon for the synthesis of carbon nanotubes will be greatly emphasised. Before proceeding with the synthesis of carbon nanotubes (CNT) using plastic sachet, it is imperative to remove the colours that are embedded on them. The removal of colour is done by submerging plastic sachets into hydrogen peroxide (H2O2). H2O2 is readily available and an economically favourable chemical oxidant. CNT production by flame synthesis was attempted. The synthesis makes use of SS 316 as the catalyst substrate, after having undergone oxidative heat treatment, for 30 minutes under 800oC, as the catalyst pre-treatment method. The characterization results of the CNT via XRD, SEM-EDS and TEM, implied that decoloured PP (clear PP) is incapable of being synthesised to CNT. This was further supported with the depiction of incomplete growth of CNT with an average diameter of 38.89nm through its resulting TEM imaging. It produces a low yield of 4.206% in comparison with CNT synthesised from blue and SR flakes, that reaches a value of 8.966% and 11.167% respectively."

"ABSTRACTGas CO merupakan salah satu gas yang berbahaya. Gas ini bisa menyebabkan kematian apabila dihirup dengan kadar yang sangat tinggi. Sudah banyak kejadian atau kecelakaan fatal yang disebabkan oleh gas ini. Gas CO tidak berwarna, tidak berbau namun sangat beracun. Jika tidak berhati-hati, bisa berbahaya bagi kelangsungan hidup makhluk hidup, utamanya manusia. Sintesis nanopartikel NdFeO3 atau senyawa-senyawa dari logam tanah jarang (rare-earth orthoferrites) merupakan salah satu upaya untuk meningkatkan sensitivitas pada sensor gas. Dalam penelitian ini disintesis empat macam sampel NdFeO3 yang disintesis melalui sintesis presipitasi dansol-gel citrate serta digunakan dua bahan baku, yakni bahan baku impor dan lokal. Karakterisasi sintesis menggunakan XRD, TEM, FT-IR dan TGA. Hasil XRD menunjukkan jika sampel NdFeO3 memiliki struktur orthorombic dan partikel berukuran 21,3 ; 15,56; 37,55 dan 46,53 nanometer, FT-IR menunjukkan adanya fase pembentukan NdFeO3 pada peak 400 cm-1-750 cm-1, TEM menunjukkan morfologi partikel serta ukuran partikel berukuran nanometer. dan TGA menunjukkan karakterisasi thermal serta perubahan massa partikel NdFeO3 dan hasil pengujian sensor menunjukkan jika respon sensor terhadap gas CO memiliki hasil yang variatif.

---

ABSTRACTCarbon monoxide is a one of dangerous gases. It can cause a death if it is inhaled in a high concentration. There are so many moments or fatality accident caused by this gas. Carbon monoxide is colorless, has no smell but it is very-very toxic. If we are not aware, life of organism, especially human being is under danger. Therefore,  detector devices of carbon monoxide is urgently needed, in order to prevent the toxic influences of carbon monoxide gas around us.nanoparticle synthesis from rare-earth orthoferrite is a one of attempts to improve the sensivity of a gas sensor. In this research where nanoparticle NdFeO3 is synthesized with precipitation and sol-gel citrate method and use two kind of raw materials, Sigma Aldrich and PSTA-BATAN. XRD result showed that NdFeO3 nanoparticles is an orthorombic structure and showed that the size of the particle is in 21,3; 15,56; 37,55 and 46,55 nanometer, FT-IR showed theres a forming phase of NdFeO3 at 400 cm-1-750 cm-1, TEM showed the particless morphology and TGA showed the thermal characteristics. The result of CO gas sensor test, showed that response to the analit gas is variative."

"Penelitian ini dilakukan untuk pengurangan kadar CO dan penjernihan asap kebakaran dengan pemanfaatan karbon aktif dari tempurung kelapa termodifikasi TiO2. Pada hasil uji XRF kandungan TiO2 didalam karbon aktif termodifikasi TiO2 sebesar 20,54 % wt. Pada hasil uji BET, luas permukaan terjadi peningkatan dari 760,30 m2/g menjadi 782,54 m2/g dari karbon aktif dan karbon aktif termodifikasi TiO2. Untuk uji kinerja, karbon aktif termodifikasi TiO2 ukuran 200 mesh dengan massa 3 gram memiliki kapasitas adsorpsi CO paling tinggi (12,59 %) dan nilai t10 untuk penjernihan asap paling baik yaitu dengan waktu 20 menit, 27 menit, 28 menit.

---

This research was conducted for the reduction of CO levels and purification by use of fire smoke from coconut shell activated carbon modified TiO2. In the XRF test results in the TiO2 content of activated carbon modified TiO2 of 20,54 % wt. The test results showed the BET surface area increased from 760,30 m2/g to 782,54 m2/g of activated carbon and activated carbon modified TiO2. To test performance, activated carbon modified TiO2 with a size 200 mesh and 3 gram have the highest CO adsorption capacity (12,59 %) and t10 values for the purification of smoke that is best with a time of 20 minutes, 27 minutes, 28 minutes."

"Carbon nanotubes (CNT) merupakan material yang banyak menjadi obyek penelitian di bidang teknologi nano karena kegunaannya yang sangat aplikatif. Salah satu kegunaan CNT adalah sebagai media yang potensial untuk penyimpanan hidrogen. Penelitian ini mensintesis CNT menggunakan katalis Fe-Co-Mo/MgO dengan sumber karbon LPG dan melihat pengaruh komposisi katalis dan temperatur terhadap yield, diameter, morfologi, luas permukaan, volume pori serta cacat struktur yang sesuai untuk digunakan sebagai adsorben pada penyimpanan gas hidrogen. Hasilnya diperoleh CNT jenis MWNT dengan pengaruh komposisi optimum ditunjukkan oleh komposisi 40-40-20 (%wt) dengan hasil CNT sebesar 0,45 gram dan yield 2,25 (g CNT/g katalis) serta diameter sekitar 27-54 nm. Temperatur yang menghasilkan yield tertinggi adalah T= 850-950 0C dengan yield sebesar 2,75 (g CNT/g katalis) dan adanya peningkatan temperatur dapat meningkatkan diameter luar CNT, menurunkan luas permukaan dan volume pori serta menurunkan cacat struktur CNT.

---

Carbon Nanotubes (CNT) is a material which has been widely used as an object of many researches in nano technology field because its applicative uses. One of CNT's uses is as a potential media for hydrogen storage. In this research, CNT is produced using Fe-Co-Mo/MgO catalyst and LPG as carbon source. The aim of this research is to see the effect of catalyst composition and synthesis temperature on yield, diameter, morphology, surface area, pore volume and structure defects which are suitable to be used as an adsorbent for hydrogen storage.

The result showed that the CNT product was MWNT structure and the optimum catalyst composition was represented by 40-40-20 (%wt) composition with the CNT product was 1,45 gram, carbon yield was 2,25 (g of CNT/g of catalyst) with the diameter about 27-54 nm. The synthesis temperature that produces the highest yield was at T= 850-950 0C with the carbon yield 2,75 (g of CNT/g of catalyst). The effect of improving synthesis temperature can increase the outer diameter of the CNT, decrease surface area, and pore volume as well as decrease the CNT structure defects."