"ABSTRAKEceng gondok atau dikenal sebagai gulma perairan merupakan serat alamyang berpotensi sebagai bahan dasar komposit. Sifat mekanik yang tinggi danketersediaan yang melimpah dapat menjadi serat dalam komposit. Pada penelitianini eceng gondok diberi perlakuan permukaan dengan silane coupling agent agarmerekat pada resin epoksi. Eceng gondok kering ditekan dingin dan tekan panasdengan variasi suhu. Eceng gondok tekan panas suhu 1100C menaikan kekuatantarik (28,36 N/mm2). Perlakuan permukaan dengan perendaman silane couplingagent 5, 10, dan 15 menit meningkatkan sudut kontak dengan resin epoksi.Komposit eceng gondok tekan panas dengan perendaman 15 menit memilikikekuatan bending yang tertinggi (20.524 N/mm2). Pada patahan komposit, hasilobservasi SEM menunjukan pengaruh penambahan silane coupling agent yangsangat signifikan.

---

ABSTRACTWater hyacinth is an aquatic weed which has potential of natural fibre as raw

material composite. High mechanical properties and availability are the reason

water hyacinth can be natural fibre in composite. In this experiment, surface of

water hyacinth treated by silane coupling agent for adhere with epoxy resin. Dry

water hyacinth has cold pressed and hot pressed with temperature variation. Water

hyacinth which has hot pressed with temperature 1100C increased the tensile

strength (28,36 N/mm2). Surface treatment by using silane coupling agent

immersion 5, 10, and 15 minutes increases the contact angle with epoxy resin.

Composite which use water hyacinth by immersion 15 minutes had the highest

bending strength (20.524 N/mm2). On the fracture of composites, SEM

observations showed the influence of the addition of silane coupling agent was

very significant."

"Eceng gondok berpotensi menjadi bahan penguat pada material komposit karena mengandung selulosa yang tinggi. Namun, penambahan serat alam pada matriks polimer dapat menurunkan sifat mekanik komposit yang dipengaruhi oleh interaksi antarmuka yang lemah sehingga diperlukan perlakuan permukaan. Eceng gondok akan diberi perlakuan terlebih dahulu dengan tekan panas lalu diberi perlakuan alkali, silane, dan kombinasi alkali-silane. Kemudian, variasi eceng gondok dicampurkan dengan poliester untuk membuat komposit dengan metode hand lay-up. Untuk pengamatan kualitas ikatan serat dan matriks diamati melalui Scanning Electron Microscopy (SEM) dan FTIR. Hasil penelitian menunjukkan bahwa serat dengan perlakuan permukaan memiliki keterbasahan dan sifat mekanik yang lebih baik dibandingkan serat tanpa perlakuan. Dengan perlakuan permukaan, sudut kontak yang terbentuk menjadi lebih kecil yaitu dari 55,9⁰ menjadi 40,9⁰; 29,8⁰; dan 23⁰ sehingga keterbasahan serat terhadap matriks menjadi lebih baik. Selain itu, kekuatan bending tanpa perlakuan permukaan meningkat dari 21,99 MPa menjadi: 36,86 MPa dengan perlakuan alkali; 43,10 MPa perlakuan silane; dan 52,78 MPa dengan kombinasi alkali-silane.

---

Water hyacinth has good potential to be a reinforcement in composite materals because of they contain a high cellulose. However, the addition of natural fibers in the polymer matrix can reduce the mechanical properties of the composites were affected by the weak interaction interface so that the necessary of surface treatment. Hyacinth will be treated first with hot press, then treated with alkali, silane, and combinations of alkali-silane. Then, hyacinth mixed with polyester to make composites by hand lay-up method. For observation of the quality of bonding fibers and matrix was observed by Scanning Electron Microscopy and FTIR.

The results showed that the fibers with the surface treatment has better wettability and mechanical properties than the untreated fibers. With the surface treatment, the contact angle formed becomes smaller from 55.9⁰ to be 40.9⁰; 29.8⁰; and 23⁰ so the wettability of the fiber to the matrix be better. In addition, the bending strength without surface treatment increased from 21.99 MPa to: 36.86 MPa by treatment with alkali; 43.10 MPa by silane treatment; and 52.78 MPa by combination of alkali-silanes"

"Restorasi porselen untuk mahkota tiruan cekat semakin sering dijumpai pada pasien. Masalah yang mungkin terjadi saat bonding braket pada restorasi tersebut adalah braket mudah terlepas dan terjadi kerusakan pada porselen. Penggunaan bahan silane coupling agent dilaporkan dapat meningkatkan kekuatan rekat dan menjaga integritas porselen. Penelitian ini bertujuan untuk melihat perbedaan kuat rekat geser pada pemakaian tiga bahan silane coupling agentdengan komposisi organosilane yang berbeda. Penelitian ini menggunakan 21 plat porselen yang dibagi menjadi 3 kelompok, yaitu yang menggunakan bahan silane coupling agent Monobond-Plus (Ivoclar vivadent), Ultradent Silane (Ultradent product) dan Porcelain Repair Primer (Ormco). Permukaan 21 plat porselen diberi etsa asam fosfat 37%, bahan silane coupling agent dan bahan adhesif Transbond XT (3M Unitek). Setelah braket direkatkan pada permukaan plat porselen dilakukan perendaman dalam aquadest selama 24 jamdan dilakukan pengujian kuat rekat geser dengan alat uji Universal Testing Machine Shimazu AG-5000. Hasil yang diperoleh terdapat perbedaan kuat rekat geser yang signifikan secara statistik dari ketiga bahan silane coupling agent. Bahan A mempunyai kuat rekat geser tertinggi (12,827 ± 1,228 MPa) dan B mempunyai kuat rekat geser terendah (6,295 ± 0,642 MPa). Ketiga bahan tersebut memenuhi kriteria kuat rekat geser minimal yaitu 6-8 MPa. Skor ARI pada bahan B memperlihatkan permukaan porselen yang bersih, sedangkan bahan A dan C memperlihatkan adanya bahan adhesif yang merekat seluruhnya di permukaan porselen. Kesimpulan : Bahan A dan C baik digunakan jika porselen akan diganti, sedangkan bahan B baik digunakan jika porselen tidak akan diganti.

---

Porcelain crown restorations are more often found in patients. Problems that may occur when bonding the bracket on the restoration is easily dislodged bracket and there is damage to the porcelain. The use of silane coupling agent has been reported to increase the bond strength and maintain the integrity of the porcelain. This study aimed to see differences of shear bond strength using three materials of silane coupling agent with different organosilane composition. This study uses 21 porcelain plates that are divided into three groups, they are using silane coupling agent material Monobond-Plus (Ivoclar Vivadent), Ultradent Silane (Ultradent product) and Porcelain Repair Primer (Ormco). The surface of 21 porcelain plates are given a 37% phosphoric acid etching, silane coupling agent material and Transbond XT adhesive (3M Unitek). Once the bracket is bonded on the surface of the porcelain plate and soaking in distilled water for 24 hours and tested the shear bond strength with test equipment Universal Testing Machine Shimazu AG-5000. The results obtained there are statistically significant differences in shear bond strength from three silane coupling agent material. Material A has the highest shear bond strength (12.827 ± 1.228 MPa) and B has the lowest shear bond strength (6.295 ± 0.642 MPa). Those three ingredients meet the minimum criteria of shear bond strength,which is 6-8 MPa. ARI scores on material B showed a clean porcelain surface, while the materials A and C show the presence of bonding adhesive on the entire surface of the porcelain.

Conclusion: Materials A and C both used if the porcelain will be replaced, while materials B is good to use if the porcelain will not be replaced."

"Latar Belakang: Bleaching merupakan prosedur mencerahkan warna gigi dengan bantuan bahan kimia yang memiliki efek samping berupa perubahan pada permukaan material resin komposit. Sementara itu, kekasaran permukaan memainkan peran penting dalam penentuan interaksi material restorasi dengan lingkungan rongga mulut karena tekstur permukaan yang tidak baik dapat meningkatkan retensi akumulasi plak dan dapat menimbulkan penyakit lainnya. Namun, penelitian mengenai efek bleaching agent pada kekasaran permukaan melaporkan hasil yang kontroversial. Tujuan: Penelitian ini bertujuan untuk menganalisis pengaruh in-home bleaching agent terhadap kekasaran permukaan resin komposit nanofilled dan microhybrid. Metode: Resin komposit nanofilled FiltekTM Z350 XT Universal Restorative (3M ESPE) dan resin komposit microhybrid FiltekTM Z250 Universal Restorative (3M ESPE) digunakan pada penelitian ini. Sebanyak 16 spesimen disiapkan dari masing-masing jenis resin komposit yang dinyatakan oleh kelompok A resin komposit nanohybrid dan kelompok B resin komposit microhybrid (jumlah total spesimen adalah 32). Seluruh spesimen dibuat dengan penumpatan material ke dalam mould dengan diameter 6 mm dan ketebalan 2 mm menggunakan kaca preparat dengan strip seluloid kemudian diberikan beban 500 gram. In-home bleaching agent (Opalescence Tooth Whitening Systems 10% Carbamide Peroxide Concentrations) diaplikasikan selama 8-10 jam/hari. Seluruh perlakuan dilakukan pada suhu 37°C dan in-home bleaching agent dibilas setiap hari selama 1 minggu dan disimpan dalam air saline steril selama periode hiatus. Kemudian, seluruh spesimen diuji dan dicatat nilai kekasaran permukaan (Ra) dalam satuan μm dengan menggunakan alat uji surface roughness tester (Surtronic® S-128) sebelum dan sesudah perlakuan. Data dianalisis secara statistik dengan uji Paired T-Test dan Independent T-Test. Hasil: Terdapat perbedaan bermakna antara kekasaran permukaan resin komposit nanofilled dan microhybrid sebelum dan sesudah aplikasi in-home bleaching agent (p<0,005). Terdapat perbedaan bermakna antara resin komposit nanofilled dan microhybrid sesudah aplikasi in-home bleaching agent (p<0,005). Kesimpulan: In- home bleaching agent secara signifikan meningkatkan nilai kekasaran permukaan pada kedua jenis material resin komposit dengan resin komposit nanofilled lebih rendah dari resin komposit microhybrid. Kekasaran permukaan pada kedua jenis resin komposit masih dapat diterima secara klinis karena menunjukkan nilai di bawah ambang batas kritis 0,2 μm.

---

Background: Bleaching is a procedure that involves lightening the color of a tooth through the application of a chemical agent, which has a side effect in the form of changes to the surface of the composite resin material. Meanwhile, surface roughness plays a vital role in determining a material’s interaction with the oral environment due to the poor surface texture of dental materials. It has a significant influence on plaque accumulation and causes other diseases. However, studies on the effect of bleaching agents on the surface roughness of dental materials have reported controversial results. Objectives: This study aimed to analyze the effect of in-home bleaching agents on the surface roughness of nanofilled and microhybrid composite resin. Methods: Nanofilled composite resin FiltekTM Z350 XT Universal Restorative (3M ESPE) and microhybrid composite resin FiltekTM Z250 Universal Restorative (3M ESPE) were used in the present study. Sixteen specimens were prepared from each type of composite resin that represented by group A for nanofilled composite resin and group B for microhybrid composite resin (total number of specimens were 32). Each specimen was prepared by compressing a sufficient amount of material into a mold of 6 mm in diameter and 2 mm in thickness using glass slides with celluloid strip, then given a load of 500 grams. In-home bleaching agents (Opalescence Tooth Whitening Systems 10% Carbamide Peroxide Concentrations) were applied 8-10 hours/day. All treatment was conducted at 37°C temperature, and an in-home bleaching agent was applied and rinsed off daily for one week and stored in distilled water during the hiatus period. Then, the surface roughness of all specimens was measured and recorded (Ra) value in μm using a surface roughness tester (Surtronic® S-128) before and after being treated. Data were statistically analyzed with Paired T-Test and Independent T-Test. Result: There was a statistically significant difference between the surface roughness of nanofilled and microhybrid composite resin before and after being bleached with an in-home bleaching agent (p<0,005). There was a statistically significant difference between nanofilled and microhybrid composite resin after being bleached with an in-home bleaching agent (p<0,005). Conclusion: In-home bleaching agent significantly increased the surface roughness value of both types of composite resin with nanofilled composite resin is lower than microhybrid composite resin. Surface roughness for both composite resins is still clinically acceptable because values tested below the critical threshold of 0,2 μm."

"Studi prihal pengaruh surfaktan anionik terhadap interaksi permukaan minyak dan air dilakukan dengan cara membandingkan volume segmen-segmen dua buah tetesan yang terbuat dari dua bahan yang berbeda yaitu larutan sodium dodesil sulfat 0.01 molar dan air suling. Penelitian ini dilakukan didalam tabung yang terbuat dari plexiglass yang dirancang oleh penulis bersama tim. Penelitian ini dilakukan dalam dua tahap, yang pertama adalah perancangan tabung percobaan dan fabrikasi tabung percobaan. Tahap kedua adalah pemilihan bahan kimia yang cocok dan di tahap kedua ini percobaan surfaktan anionik dilakukan. Bahan-bahan yang digunakan dalam penelitian ini adalah air suling, minyak paraffin, dan sodium dodesil sulfat. Tabung yang digunakan dalam percobaan ini terbuatdari plexiglass dan memiliki penampang tampak atas berbentuk bujur sangkar untuk meminimalisasi distorsi foto kedua jenis tetesan. Penelitian ini menemukan bahwa sodium dodesil sulfat dengan konsentrasi 0.01 molar mampu menurunkan tegangan permikaan tetesan air suling sehingga menghasilkan bentuk tetesan yang ellipsoid. Lebih lagi, sifat amfifilik yang dimiliki oleh sodium dodesil sulfat diperkuat kecendrungan lipofiliknya untuk menempel pada minyak paraffin karena bertambahnya luas penampang tetesan yang semula berbentuk bola menjadi ellipsoid akibat berkurangnya tegangan permukaan tetesan. Rasio volume segmen-segmen kedua tetesan menunjukkan bahwa sodium dodesil sulfat memiliki kecendrungan untuk sedikit lebih lipofilik daripada hidrofilik.

---

The study of the influence of anionic surface active agent (surfactant) on the interactions between oil and water interfaces was done by comparing the volumes of droplet which were divided into segments in a controlled environment using a column designed by the team. The experiment involves two phases; the first were column design and fabrication while the next were the selection of suitable chemicals and the commencement of the anionic surface active agent experiment. The substances used in this experiment were deionised water, paraffin oil, and sodium dodecyl sulphate 0.01 molar solution. The column was made of plexiglass with rectangular cross-section to minimise optical distortion of the droplet image.

It was found that sodium dodecyl sulphate solution reduces the surface tension of deionised water of droplet resulting in an ellipsoid shaped droplet. In addition to the amphiphilic nature of sodium dodecyl sulphate; the ellipsoid shape of sodium dodecyl sulphate droplet caused by the reduced surface tension has greater surface area compared to the spherical deionised water droplet which further increased its affinity toward paraffin oil. The volumetric ratio of the droplet segments suggest that sodium dodecyl sulphate has a slight tendency to be more lipophilic that hydrophilic."

"Isolator polimer epoxy resin memiliki kelebihan diantaranya beban lebih ringan, sifat rugi dielektrik yang lebih kecil, serta resistivitas volume yang lebih tinggi. Kelebihan lain adalah proses produksi yang relatif lebih cepat dan biaya produksi yang lebih murah. Selain kelebihan tersebut isolator jenis epoxy resin juga memiliki kekurangan, yaitu menurun nya kinerja isolator apabila digunakan pada daerah berpolutan tinggi. Skripsi ini dilakukan percobaan terhadap isolator epoxy resin dengan memberikan polutan buatan. Isolator pada transmisi tegangan tinggi yang terkontaminasi akan memiliki konduktansi yang berbeda-beda. Semakin besar konduktansi dari lapisan pengotor maka arus bocor yang terjadi akan semakin besar. Penelitian ini dilakukan untuk mengetahui sejauh mana isolator epoxy resin dipengaruhi oleh polutan-polutan yang ada.Pengujian dilakukan terhadap bahan-bahan seperti garam-garaman (NaCl),debu(CaCO3), dan Carbon sebagai polutan asap kendaraan bermotor. Dari penelitian yang dilakukan dapat diperoleh kesimpulan antara lain, berkurangnya tahanan pada permukaan konduktor selain dipengaruhi oleh konsentrasi endapan garam juga dipengaruhi oleh daya higroskopis dan daya rekat polutan pada permukaan isolator, semakin jauh jarak antar elektroda yang diambil untuk mengukur tahanan permukaan, maka tahanan akan bertambah, pada kadar 100 gram dan 300 gram, CaCO3 memiliki tahanan permukaan yang paling rendah, sedangkan pada kadar 500 gram, Carbon merupakan polutan yang menyebabkan kadar permukaan terendah.

---

Polimer epoxy resin Isolator have many advantage, one of them it is more lite, smaller dielektrik loses, and higher resistivity volume. other advantage is a rather fast production process and a cheap cost. other than those advantage epoxy resin isolator also have disadvantage that is, the decrease of isolator function if it is used in a high pollutan area. in this research an experiment to epoxy resin isolator have been done with giving synthetic pollutn. the high voltage transimission isolator which were contaminated will have different conductance. the bigger the conductance from the polluted layer, the bigger the leaking stream will become.

This research is done to know how far epoxy resin isolator is influenced from pollutans. the testing is done to ingridients such as salts (NaCl), dust (CaCO3), and carbon as motor vehicle pollutan. from the research that is done, a conclusion were made that, the decrease of resistivity on the conductor surface other than influenced by endapan salt also influenced by higroscopic power and the pollutan daya rekat to the isolator surface, the more distance between electrode that is taken to measure the surface resistivity, the larger the resistivity will be, in 100 gram and 300 gram dosage, CaCO3 have the lowest surface resistivity, while the meantime pada kadar 500 gram, Carbon were the lowest surface resistivity pollutan."

"Pelapisan merupakan salah satu cara yang paling umum dan mudah digunakan untuk menghindari dan mengurangi terjadinya korosi pada baja karbon rendah. Namun sering terjadi kegagalan pada pelapisan ini dikarenakan daya lekat cat yang kurang baik serta metode preparasii yang kurang tepat. Penelitian ini bertujuan untuk mengetahui pengaruh perlakuan permukaan pada material yang akan dilindungi dengan cat epoksi primer terhadap ketahanan korosi dan daya lekatnya pada substrat baja karbon rendah. Untuk menganalisa terhadap ketahanan korosinya maka metode yang dilakukan yaitu sembur kabut garam dan untuk daya lekat dilakukan pengujian pengujian adhesi. Untuk meningkatkan ketahanan korosi dan daya lekat, maka material benda uji yang akan dilapisi cat epoksi primer dilakukan perlakuan permukaan grit 800, SA 1, dan SA 2,5. Hasil yang didapat yaitu peringkat ketahanan korosi adalah 9 atau sangat baik untuk semua sampel. Kemudian dengan perlakuan permukaan yang tinggi dan permukaan yang lebih kasar akan meningkatkan nilai daya lekat dari cat epoksi primer.

---

Coating is the most common and easy way to avoid and reduce the corrosion rate of low carbon steel. But failure often happened due to insufficient coating adhesion and low preparation method. This study aimed to understand the effect of surface preparation on prime epoxy coated low carbon material corrosion resistence and its adhesion level. The low carbon material which will be coated with epoxy prime coating is subjected to 800 grade grinding, SA 1, amd SA 2,5 sand-blasting before tested in salt spray machine and adhesion test to analyse the corrosion resistance and the adhesion level. The result shows that the corrosion resistance rating is 9 which is very good for every sample, but more specificly higher surface treatment produce higher roughness levelm higher corrosion resistance, and an increase on prime epoxy adhesion level."

"Limbah plastik adalah salah satu permasalahan klasik yang dialami Negara dengan konsumsi plastik yang besar, seperti Indonesia. Selain itu, industri kertas Indonesia banyak menghasilkan limbah pengolahan kertas lignin yang tidak dimanfaatkan karena bernilai rendah. Oleh karena itu, metode baru diperlukan untuk mengurangi pencemaran plastik serta meningkatkan nilai lignin agar Industri tidak langsung membuangnya, yang salah satunya adalah mencampurkan kedua bahan ini sebagai bahan tambahan pada material penyusun aspal, yaitu bitumen. Bitumen yang ditambahkan polipropilena disebut polypropilene modified bitumen PPMB. Penelitian ini membahas pengaruh pencampuran bitumen dengan limbah plastik PP sebagai zat pengisi dan lignin termodifikasi sebagai coupling agent atau kompatibiliser. PPMB dibuat dengan menggunakan alat hot melt mixer dengan rasio masa 19:1 untuk bitumen dan PP yang diaduk dengan kecepatan 80 round per minute rpm. Pencampuran dilakukan pada temperatur 160oC, 180oC, dan 200oC selama 15, 30, dan 45 menit dengan penambahan komposisi lignin termodifikasi sebesar 0.1, 0.3, dan 0.5 berat. Kemudian sampel dianalisis kandungan senyawaan, morfologi, serta sifat mekanisnya menggunakan FT-IR, SEM, uji penetrasi dan daktilitas. Hasil pengujian menunjukkan bahwa lignin termodifikasi memiliki kompabilitas yang lebih baik dibanding lignin murni serta sifat mekanis PPMB yang lebih baik dibandingkan bitumen murni.

---

Plastic waste is one of classic problem which are experienced by Country with huge plastic consumption, like Indonesia. Other than that, Indonesias Paper Industries produce much paper processing waste lignin which isnt utilized because of its low value. Because of these reasons, a new method was needed to reduce plastic pollution and also to increase the value of lignin so industries wont throw it away, which one of the method is to mix these substances as an addition in asphalt material, that is bitumen. Bitumen, in which polypropylene is added is called polypropylene modified bitumen PPMB . This research discusses the effect of bitumen mixing with polypropylene as filler and modified lignin as coupling agent or compatibilizer. PPMB was created with hot melt mixer machine with mass ratio of 19 1 for bitumen and PP which are mixed in 80 rpm. Mixing was done at the temperature of 160oC, 180oC, and 200oC for 15, 30 and 45 minutes with 0.1, 0.3, and 0.5 total weight addition of modified lignin. Lastly, samples rsquo compound content, morphology, and mechanical properties were analyzed using FT IR, SEM, penetration and ductility test. Result showed that modified lignin has better compatibility compared to pure lignin, and also PPMB rsquo s mechanical properties are better than pure bitumen."