"Grain refinement is known to lead improvements in strength of material. A complete understanding of how refinement, grain size, and processing affect the corrosion resistance of low carbon steel has not yet been fully developed. Determining a definitive „grain size-corrosion resistance‟ relationship, if one exists, in inherently complex as the processing needed to achieve grain refinement also imparts other changes to the microstructure (such as texture, internal stress, and impurities segregation). This work evaluates how variation in grain size and processing impact the corrosion resistance of SS 400 Low Carbon Steel Structural Steel. SS 400 samples with a range of grain size ~8μm to ~10.5μm, were produced using Thermomechanically Processing (TMP) with multi pass reversible method in warm rolling. Hardness measurement, tensile testing, electrochemical polarization and hydrogen embrittlement (HE) studies have been carried out to assess the mechanical and corrosion behavior of the low carbon steel. By applying rolling deformation process in warm working temperature, low carbon steel will have fine ferrite grain structures made its mechanical properties increased, its corrosion rate decreased and also its ability to absorb hydrogen decreased. The applied mechanisms of pass deformation are reversible which are 20%, 20% +20%, 20% +20% +20% and 20% +20% +20% +20% with initial thickness ho 6 mm. By applying this mechanism, it is expected that fine ferrite grains will influence the corrosion rate of low carbon steel SS 400 structural steel."

"ABSTRAKStudi terhadap penghalusan butir terus dikembangkan untuk mendapatkan sifat mekanis yang lebih baik pada baja karbon rendah. Slab baja karbon rendah berbentuk tangga dideformasi dengan metode warm rolling dengan temperature 500 0C, 550 0C, dan 600 0C untuk mendapatkan butir halus. Slab baja karbon rendah berbentuk tangga dideformasi sebesar 50 %, 66,67 %, 75 %, dan 80% di setiap temperatur, kemudian didinginkan dengan air. Rekristalisasi dinamis terjadi pada temperatur warm working di penelitian ini. Pengujian kekerasan dan hydrogen charging test dilakukan. Ketahanan baja karbon rendah terhadap serangan hidrogen dapat ditingkatkan dengan penghalusan butir ferit. Besar butir yang dihasilkan dari warm rolling mempengaruhi kekerasan dan ketahanannya terhadap serangan hidrogen.

---

ABSTRACTStudiy of grain refinement have been developed to obtain better mechanical properties in low carbon steel. Wedge Shaped low carbon steel slabs were deformed with warm rolling method at temperature 500 0C, 550 0C, and 600 0C to obtain the refine grains. Wedge Shaped low carbon steel slabs were deformed with degree of deformation 50 %, 66,67 %, 75 %, and 80%. Dynamic recrystallization was confirmed at warm working temperature in this study. Hardness and hydrogen charging test had been done. Low carbon steel resistance to hydrogen attack can be improved with grain refinement. Grain size which been resulted from warm rolling process has an effect to hardness and hydrogen attack resistance."

"Berbagai penelitian telah dilakukan terhadap proses canai untuk mendapatkan material dengan sifat mekanis yang baik namun nilai ekonomisnya tetap tinggi. Penghalusan ukuran butir ferit melalui kontrol proses termo mekanikal merupakan salah satu metode yang digunakan untuk peningkatan sifat mekanik baja karbon rendah. Pada penelitian ini slab baja karbon rendah dideformasi dengan metode warm rolling, kemudian diuji kekerasan dan ketahanan korosi-nya melalui hydrogen charging test. Salah satu penguatan material terhadap serangan difusi hidrogen adalah dengan penghalusan butir ferit melalui proses deformasi. Sehingga dapat dibuat suatu hubungan antara deformasi dengan perubahan struktur mikro ferritic dan ketahanan korosi baja karbon rendah. Ukuran butir yang diperoleh dalam penelitian ini diukur dengan metode garis intercept. Hasilnya berupa ukuran diameter butir baja karbon rendah yang lebih kecil dibanding dengan diameter butir baja karbon rendah yang tidak dideformasi. Sementara ketahanan korosi baja karbon rendah terhadap pengaruh proses difusi hidrogen untuk benda uji yang ukuran butirnya lebih kecil cenderung meningkat. Peningkatan kekuatan-nya diamati melalui pengujian kekerasan setelah sebelumnya benda uji diaplikasi ke dalam larutan 0,5M H2SO4 + 100 mg/L Thiourea CS(NH2)2 selama 10 menit.

---

Various studies have been carried out on rolling process to achieve materials with good mechanical properties but its economic value remains high. Grain refinement through thermo-mechanical process control is one of many methods used to improve low carbon steel mechanical properties. On this paper, low carbon steel is deformed with warm rolling method, then the deformed material is applied to hardness test and corrosion resistance test against hydrogen charging. Hydrogen introduction into material may occur in many ways and one of physical properties of material against this introduction is through microstructure refinement of ferrite grain size by deformation process. So there is a connection between the deformation with the change in ferritic microstructure and corrosion resistance of low carbon steel.

The grain size was measured by intercept line method. The result is grain size of the deformed steel is smaller than the undeformed one. In addition, there is an improvement of corrosion resistance of low carbon steel with smaller grain size against hydrogen diffusion. The improvement can be seen from the result of hardness test. Before the hardness test began, the deformed specimen are introduced to 0,5M H2SO4 + 100 mg/L Thiourea CS(NH2)2 solution for 10 minutes."

"Metode fabrikasi material komposit paduan Al 6061 dengan penambahan partikel mikro SiC dipilih menggunakan metode pengecoran aduk karena mampu mendistribusikan partikel penguat SiC dan memiliki nilai ekonomis yang baik. Material ini kemudian diharapkan memiliki sifat mekanis yang baik dengan densitas yang relatif rendah.Pada penelitian ini dilakukan variasi penambahan volume fraksi dari partikel miro SiC sebesar 2%, 4%, 6%, 8%, dan 10% untuk mengetahui nilai optimal dari penambahan partikel penguat. Penambahan Mg sebesar 10 wt.% dilakukan untuk meningkatkan kemampubasahan dan penambahan Sr dan TiB dilakukan untuk meningkatkan sifat mekanis dari material komposit. Kemudian didapatkan nilai kekuatan tarik, elongasi, dan kekerasan memiliki nilai maksimal pada penambahan partikel penguat SiC sebesar 10 wt.% dengan nilai masing-masing 230 MPa, 6,5%, dan 62,2 HRB. Sedangkan nilai kekuatan impak memiliki nilai optimum pada penambahan partikel penguat sebesar 4% dengan nilai 0.0294 Joule/mm2. Kemudian juga didapatkan bahwa persentase porositas terus meningkat seiring dengan peningkatan volume fraksi dari partikel penguat.

---

Manufacturing of composite material Aluminum Alloy (Al-Mg-Si) with the addition of micro SiC particles reinforcement chosen using stir casting method because it can be able to evenly distribute the SiC particles reinforcement and has a good economic value. Then this addition of SiC particles predicted will improved the mechanical properties and density of the materials.

In this study, the addition of micro particles volume fraction in the amount of SiC 2%, 4%, 6%, 8%, and 10% were used in order to know the optimum volume fraction. The addition of Mg 10 wt.% were used as wetting agent to increase the wettability between matrix and reinforce and the addition of AlSr and TiB were used to increase the mechanical properties. As a result, the ultimate tensile strength, elongation, and hardness value has a maximum value in addition of micro particles volume fraction in the amount of SiC 10 wt.%with the value up to 230 MPa, 6,5%, dan 62,2 HRB. However, the impact value and hardness value has a optimum value in addition of micro particles volume fraction in the amoung of SiC 4% with the value 0.0294 Joule/mm2. The percentages of porosity were increased along with the increase of micro particles volume fraction."

"Penelitian mengenai alat dan kendaraan militer selalu dilakukan untuk meningkatkan kendaraan tempur untuk meningkatkan kekuatan militer. Salah satu tujuannya adalah untuk menciptakan bahan yang lebih ringan yang dapat menahan benturan balistik. Pada penelitian ini dibuat material komposit hybrid laminate dengan paduan aluminium 5052 sebagai matriks dan Kevlar diresapi dengan titanium karbida sebagai penguat. Kevlar diresapi menggunakan cairan penebalan geser (STF). Varietas lapisan Kevlar adalah 20, 30, dan 40 lapisan. Uji balistik dilakukan dengan standar NIJ 0108.01. Penambahan STF dapat meningkatkan balistik dan kekuatan impak sampel dengan mengisi rongga antar setiap serat Kevlar. Kekuatan impak material meningkat dengan semakin tebal lapisan kevlar. Semua sampel dapat menahan uji balistik level II dan hanya 40 lapisan sampel yang diresapi TiC yang dapat menahan uji balistik level III/

---

Great amount of effort is always made to improve combat vehicles in order to increase military strength. One of the goals is to create a lighter material that can withstand ballistic impact. In this study, hybrid laminate composite material is made with aluminum alloy 5052 as a matrix and Kevlar impregnated with titanium carbide as reinforcement. The Kevlar is impregnated using shear thickening fluid (STF). The varieties of Kevlar layers are 20, 30, and 40 layers. The ballistic test was carried out with NIJ 0108.01 standard. The addition of STF can improve the ballistic and impact strength of the sample by filling the cavity between each Kevlar fibers. The impact strength of the material increases with the thicker the kevlar layer. All of the samples can withstand level II ballistic test and only 40 layers of TiC-impregnated sample can withstand level III ballistic test. "

"Komposit Aluminium 6061 berpenguat nanopartikel SiC dibuat menggunakan metode pengecoran aduk, dimana ditambahkan unsur Mg 10% untuk mengoptimalkan pembasahan antara matriks dan penguat serta penambahan grain refiner Al-TiB untuk meningkatkan sifat mekanik dari material. Penambahan fraksi volume nanopartikel sebesar 0,05%, 0,10%, 0,15%, 0,20%, dan 0,30% dilakukan untuk mengetahui fraksi volume optimal.Data hasil penelitian menunjukkan nilai kekuatan tarik maksimum sebesar 217,2 Mpa pada penambahan 0,15%vf dengan elongasi optimal 6% pada penambahan 0,20%vf. Nilai kekerasan terus meningkat seiring dengan penambahan fraksi volume, akan tetapi harga impak terus menurun seiring dengan penambahan fraksi volume. Porositas yang terbentuk semakin meningkat seiring dengan penambahan fraksi volume nanopartikel SiC. Penambahan unsur Al-TiB menghasilkan ukuran butir yang lebih kecil dan persebaran partikel serta porositas yang lebih merata.

---

Aluminium 6061 composite reinforced with nanoparticles SiC produced by stir casting with the addition of Magnesium 10% as wetting agent to optimize wettability between matrix and reinforcement and addition of Titanium Boron as grain refiner to increase mechanical properties. In this study, addition of nano-particles volume fraction in the amount of SiC 0.05 %, 0.10 %, 0.15 %, 0.20 %, and 0.30 % were used in order to known the optimum volume fraction.As the result, the maximum of ultimate tensile strength is 271,2 Mpa in addition of 0,15%vf, with maximum elongation up to 6% in additon of 0,20%vf. Hardness value continues to rise with the addition of volume fraction, but the impact properties declines steadily with the addition of volume fraction. Porosity percentage increase with the addition of nanoparticles SiC."

"Material untuk aplikasi peralatan militer (balistik) didesain untuk menahan tembakan peluru yang pada aplikasinya dibutuhkan sifat tangguh terhadap beban impak balistik. Selain itu diperlukan sifat yang kuat dan ringan. MMC dengan matriks aluminium sangat populer untuk dikembangkan karena aluminium memiliki berat yang ringan dan sifat mekanis yang baik. Untuk mendapatkan kekerasan tanpa mengorbankan ketangguhan, diperlukan penambahan elemen paduan pada matriks.Dalam penelitian ini dikembangkan material variasi paduan 0, 1 dan 3 wt.% Cu pada matriks Al–8Zn–4Mg dengan penguat 15 vol.% SiC hasil squeeze casting yang diharapkan dapat memberikan karakteristik baik untuk aplikasi material balistik. Karakterisasi material dilakukan untuk melihat efek penambahan Cu pada komposit. Karakterisasi material yang dilakukan diantaranya pengujian kekerasan dengan metode Rockwell B, pengujian impak, analisis mikrostruktur menggunakan mikroskop optik dan Scanning Electron Microscopy (SEM), analisis distribusi kuantitatif partikel SiC, analisis komposisi menggunakan Optical Emission Spectroscopy (OES) kemudian dilakukan pengujian balistik dengan peluru tipe III berkaliber 7.62 mm.Hasil pengujian menunjukkan bahwa semakin tinggi kadar Cu yang diberikan maka kekerasan meningkat hingga 79.05 HRB yang diikuti dengan turunnya keuletan sehingga harga impak menurun menjadi 29332.78 J/m2 akibat kegetasan material. Komposisi komposit belum mampu menahan beban impak balistik akibat sifat yang terlalu getas. Hasil pengujian balistik untuk ketiga komposisi menunjukkan bahwa semakin banyak Cu yang ditambahkan, kemampuan pelat untuk menahan beban impak balistik akan semakin buruk. Kegagalan ini juga diakibatkan oleh partikel SiC yang mengkluster dan adanya cacat pengecoran seperti porositas dan retak panas.

---

Materials for military equipment application (ballistic) designed to withstand bullets, so that they need high toughness. Beside that, they also need strong and light weight materials. MMC with aluminum matrix is very popular to be developed because aluminum has a light weight and good mechanical properties. To obtain high hardness without sacrifiying the toughness, alloying elements are added in the matrix.

This study evaluate Al-8Zn-4Mg alloy added with 0, 1 and 3 wt. % Cu with 15 vol. % SiC as reinforcement. Manufacturing process was squeeze casting to assume good mixing of SiC particulates. Materials characterization included composition analysis using Optical Emission Spectroscopy (OES), hardness testing (Rockwell B), impact testing (charpy method), microstructure analysis using optical microscopy and Scanning Electron Microscopy (SEM), quantitative analysis of SiC particles distribution then ballistic testing with type III bullets of 7.62 mm callibre.

The test result showed that the higher level of Cu give higher hardness up to 79.05 HRB followed by reduction in ductility, so the impact value decrease to 29332.78 J/m2. The composites were not able to withstand ballistic impact load due to its brittleness. Ballistic testing showed that all composite plates with varied Cu content could not stop the bullets. The higher Cu content, the more shattered the plates. The failure is due to SiC clustering and casting defects such us porosity and hot cracking."

"Metal Matrix Composites (MMC) merupakan salah satu contoh material lanjut yang terus berkembang khususnya yang berbasis logam aluminium. MMC memiliki sifat-sifat yang haik yang merupakan perpaduon dari sifat mekonis logam sebagai matriks dan keramik sebagai penguatnya. Sifat mekanis yang beruhah antara lain kekerasan, ketahanan aus, ketahanan fatik, ketahanan korasi, nilai resistivitas dan lain-lain. Metal Matrix Composites At-SiC pada penelitian ini dibuat menggunakan metodik PRIMEX (Pressureless Metal Infiltration) otau infiltrasi logam tanpa tekanan yang dipatenkan oleh Ltmxide. Ingot aluminium jenis AC2B (sebagai matriks) pada temperatur proses 750'C, 800'C, 9011'C, 1OO1'C, 11O1'C alam melebur dan terinfiltrasi ke dalam serbuk lepas SiC (sebagai reiriforcement), yang berada pada suatu tray. Waktu tahan yang diberikan selama 10 jam dengan kodar Mg I WAiwt, untuk setiap temperatur proses. Serbuk magnesium ber:fongsi sebagai wetting agent agar /erjadi pembasahan antar muka logam-keramik. MMC Al~SiC hasil dari proses PRIMEX ini menunjukkan perubahan yang baik.Peningkalan temperaJur firing menyebabknn kenaikan densilas dan kekerasan sedangkan porosilas dan Juju aus menurun. sehingga sifol mekanis lvi.MC Al-SiC dari liap-tiap lemperatur firing terus membaik. Dari strukturmikro yang diamali, lerlilwt bahwa distribusi SiC semakin banyak."

"Material komposit sangatlah populer dalam beberapa dekade terakhir karena massanya yang ringan dan harganya yang relatif murah disertai dengan kekuatan mekanik yang tinggi. Penelitian ini memiliki tujuan untuk membandingkan sifat mekanik dan kerusakan yang terjadi dari komposit sandwich dengan inti honeycomb polipropilen dan kulit epoksi/serat karbon yang difabrikasi dengan CPA (Cold-Press Adhesive) dan VARI (Vacuum-Assisted Resin Infusion). Terdapat empat pengujian yang dilakukan dalam penelitian ini, yaitu uji densitas, uji tarik, uji tekan, dan uji lentur. Pengamatan kerusakan dilakukan sebelum dan sesudah pengujian dilakukan. Kedua komposit sandwich memiliki nilai densitas yang rendah, yaitu; (0,42 ± 0,03) g/cm3 dan (0,56 ± 0,04) g/cm3 masing-masing untuk komposit sandwich yang dibuat dengan teknik fabrikasi Cold-Press Adhesive (CPA) dan VARI. Komposit sandwich CPA dan VARI mempunyai kekuatan mekanik yang relatif sama, yaitu (14,79 ± 6,11) MPa dan (13,09 ± 2,53) MPa untuk kuat lentur; (1,87 ± 0,17) MPa dan (1,5 ± 0,17) MPa untuk kuat tekan; dan (0,36 ± 0,06) MPa dan (0,33 ± 0,04) MPa untuk kuat tarik. Kerusakan pada inti terjadi pada sampel setelah pengujian lentur dan tekan, sedangkan kerusakan pada kulit terjadi pada sampel setelah pengujian lentur dan tarik. 

---

Composite materials are so popular in the last few decades as lightweight and relatively cheap with high mechanical properties. The purpose of this research was to compare the mechanical properties and failures of sandwich composites with polypropylene honeycomb as core and epoxy/carbon fiber as skin fabricated with CPA (Cold-Press Adhesive) and VARI (Vacuum-Assisted Resin Infusion). Four testing methods were used in this research, namely density measurement, tensile, compressive, and bending tests. Failure observation was conducted before and after mechanical tests. Densities of the two sandwich composites were (0,42 ± 0,03) g/cm3 and (0,56 ± 0,04) g/cm3 for CPA and VARI consecutively. Sandwich composites fabricated with CPA and VARI had a relatively similar mechanical strength values; in the amount of (14,79 ± 6,11) MPa and (13,09 ± 2,53) MPa for bending strengths, (1,87 ± 0,17) MPa and (1,5 ± 0,17) MPa for compressive strengths, and (0,36 ± 0,06) MPa and (0,33 ± 0,04) MPa for tensile strengths. Failure of the core was occurred in the bending and compressive test samples, meanwhile failure of the skin was occurred in the bending and tensile test samples."

"Komposit merupakan salah satu material yang saat ini sedang dikembangkan karena memiliki keunggulan seperti memiliki kekuatan yang baik dengan bobot yang ringan. Proses pembuatan material dengan menggunakan metode thixoforming memberikan keunggulan berupa perbaikan struktur dan meningkatkan kekuatan material. Pada penelitian ini, dilakukan pengamatan terhadap material komposit dengan matriks paduan Al-5%Cu-4%Mg dengan penguat partikel SiC sebanyak 20-25% hasil pengecoran biasa dan hasil proses thixoforming. Hasil pengujian kekerasan memperlihatkan peningkatan nilai kekerasan seiring penambahan kadar penguat dan proses thixoforming pada komposit. Pengamatan struktur mikro juga dilakukan untuk mengamati pengaruh proses thixoforming pada komposit dalam mengubah bentuk dendritik menjadi globular yang menghasikan kekerasan yang lebih baik dari pada komposit hasil pengecoran biasa.

---

Composite is one of materials that recently being developed because it has the advantages such as good strength with light weight. Materials forming with the thixoforming process has the advantages such as structure refinement and materials properties improvement. In this study, we making an observation about composite materials with Al-5%Cu-4%Mg alloys matrix and 20-25% SiC particle reinforcement as a common casting process and thixoforming process. From the hardness test, the result shows that the hardness increasing as the reinforcement increase and the influence of thixoforming process on composite. The observation on the microstructure conducted to see the influence of thixoforming process on composite in modify the dendritic structure into globular structure that give the better hardness than the as-cast composite."