"Polimer hidrogel mampu melakukan swelling bila menyerap air serta mampu mempertahankan medium cair di dalam jaringannya. Sintesis hidrogel kitosan-cangkok-Poli N-(vinil kaprolaktam) atau kitosan-cangkok-PNVCL dilakukan melalui polimerisasi radikal dengan teknik larutan. Kemampuan swelling hidrogel kitosan-cangkok-PNVCL dilakukan dengan merendam dalam media cair selama 24 jam. Polimer diinisiasi dengan Ammonium persulfat (APS) lalu dicangkok dengan monomer N-Vinil Kaprolaktam (NVCL) dan diikat silang dengan N,N’-Metilen Bisakrilamida (MBA). Variasi konsentrasi monomer NVCL dan konsentrasi agen pengikat silang MBA serta waktu reaksi mempengaruhi rasio swelling hidrogel. Rasio swelling paling optimum sebesar 52.8% dari berat semula didapat dengan agen pengikat silang MBA 3% dan konsentrasi NVCL 0,8 g. Hidrogel tersebut dikarakterisasi dengan Fourier Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry (DSC) dan Scanning Electron Microscope (SEM).

---

Hydrogel polymer will swell if it absorbs amount of water then it can protected amount of water in his network . Hydrogel chitosan-graft-poly(Vinyl Caprolactam) or chitosan-graft-PNVCL was synthesized by radical polymerization in solution. Swelling behavior of hydrogel was carried in aqueous media for 24 hour. Hydrogel was intiated by ammonium persulfate (APS) then grafted by N-Vinyl caprolactam (NVCL) and cross linked by N’N-Metilen Bisacrylamide (MBA).

Variation of monomer concentration, cross linker concentration and reaction time will effect swelling ratio hydrogel. The best swelling ratio up to 52.8% was obtained by composition of 3% MBA and 0.8 g NVCL. The products were characterized by Fourier Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry (DSC) and Scanning Electron Microscope (SEM)."

"Hidrogel kitosan-cangkok-poli(N-vinil pirrolidon) telah disintesis melalui teknik polimerisasi radikal bebas. Dalam penelitian ini, monomer N-vinil pirrolidon (NVP) dicangkokkan pada kitosan menggunakan inisiator ammonium persulfat (APS) dan agen pengikat silang N,N’-metilen bisakrilamida (MBA) dalam sistem larutan. Untuk membuktikan bahwa monomer itu telah tercangkok, dilakukan karakterisasi dengan Fourier Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry (DSC), dan Scanning Electron Microscope (SEM) untuk mengetahui bentuk morfologi hidrogel. Pengaruh komposisi monomer NVP, agen pengikat silang, dan waktu polimerisasi terhadap kemampuan swelling telah diamati. Swelling optimum diperoleh sebesar 54,6% pada waktu polimerisasi 3 jam dengan komposisi monomer NVP 0,8 mL dan konsentrasi pengikat silang 2%.

---

Hydrogels of chitosan-graft-poly(N-vinylpyrrolidone) had been synthesized via free radical polymerization technique. In this research, monomer N-vinylpyrrolidone (NVP) was grafted onto chitosan by using APS as initiator and N,N '-methylene bisacrylamide (MBA) as crosslinking agent in the solution system. In order to prove that the monomers were grafted, FTIR spectroscopy, DSC analysis were used, and Scanning Electron Microscope (SEM) to determine the morphology of hydrogels. The influence monomer compositions, concentration of crosslinking agent, and polymerization time on the ability of swelling was observed. The optimum swelling was obtained at 54,6% in the polymerization time of 3 hours with 0.8 mL NVP monomer composition and concentration of crosslinking of 2%."

"Keberadaan obat di lambung tidak dapat bertahan lama dikarenakan terpengaruh oleh proses pengosongan lambung. Salah satu sistem yang dapat digunakan untuk menahan obat berada dalam lambung dalam waktu yang cukup lama yaitu dengan menggunakan floating drug delivery system (FDDS). Pada penelitian ini obat amoxicillin trihidrat digunakan untuk menguji hidrogel kitosan-cangkok-poli(N-vinil kaprolaktam) sebagai sediaan pengantar obat sistem mengapung yang dipengaruhi oleh efek agen pembentuk pori. Enkapsulasi obat amoxicillin trihidrat ke dalam sediaan mengapung menggunakan metode in situ loading. Komposisi hidrogel yang digunakan pada penelitian ini adalah sebanyak 0,2 g kitosan, 0,8 g monomer NVCL, 0,02 g inisiator APS, 0,012 g agen pengikat silang MBA. Selain itu juga ditambahkan variasi konsentrasi dari agen pengikat silang CaCO3 dan NaHCO3, yaitu 0; 5; 7.5; 10 dan 15%. Penelitian ini dikaji berdasarkan jenis pembentuk pori, konsentrasi pembentuk pori, jenis kualitas obat, dan jenis hidrogel. Uji pelepasan obat dilakukan di dalam larutan pH 1,2. Karakterisasi dilakukan dengan menggunakan spektrofotometer Fourier Transform Infrared (FTIR) untuk melihat gugus fungsi yang ada pada hidrogel, dan Mikroskop Stereo Optik untuk melihat morfologi permukaan hidrogel. Dari hasil penelitian didapatkan hasil optimum pada matriks hidrogel kitosan-cangkok-poli(N-vinil kaprolaktam) dengan agen pembentuk pori NaHCO3 pada konsentrasi 15%.

---

The existence of the drug in the stomach can not last long due to be affected by the process of gastric emptying. One of the systems can be used to retain the drug in the stomach in a long time by using floating drug delivery system (FDDS). In this study, the drug amoxicillin trihydrate was used to test the hydrogel chitosan-graft-poly (N-vinyl caprolactam) as a floating drug delivery systems which is influenced by the effects of pore-forming agent. Amoxilin trihydrate was encapsulated in matrix using in situ loading. Hydrogel composition used in this study was 0.2 grams of chitosan, 0.8 g NVCL monomer, 0.02 g initiator APS, and 0,012 g MBA crosslinking agent. It also added varying concentrations of crosslinking agent CaCO3 and NaHCO3, which is 0; 5; 7.5; 10 and 15%.

This study assessed based on the type of forming the pores, pore-forming concentration, the type of drug quality, and type of hydrogel. Drug release test was conducted in a solution of pH 1.2. The characterization was conducted by using Fourier Transform Infrared (FTIR) spectrofotometry to see the existing functional groups on the hydrogel, and Stereo Optical Microscope to the hydrogel surface morphology. Obtainable from the optimum results of observe matrix hydrogel chitosan-graft-poly (N-vinyl caprolactam) with a pore-forming agent NaHCO3 at a concentration of 15%."

"Hidrogel merupakan polimer superabsorben yang dapat menyerap dan menahan sejumlah besar medium cair. Hidrogel kitosan-graft-poli(N-vinil pirrolidon) atau kitosan-graft-PNVP disintesis melalui proses polimerisasi radikal bebas. Polimer ini diikatsilangkan pada rantai cabang, rantai PNVP, dengan agen pengikat silang yang berbeda, yaitu N,N’-Metilen Bisakrilamida (MBA) dan Etilen Glikol Dimetakrilat (EGDMA). Kemampuan swelling hidrogel kitosan-graft-PNVP terikat silang dilakukan dengan merendamnya dalam media cair. Pengaruh jenis dan konsentrasi agen pengikat silang serta waktu reaksi terhadap daya absorbsi air telah diamati. Hidrogel yang terikat silang dengan EGDMA memperlihatkan rasio swelling lebih besar dibandingkan dengan hidrogel yang terikat silang dengan MBA. Kemampuan menyerap hidrogel yang terikat silang dengan EGDMA dapat mencapai 50% dari berat sebelum menyerap air. Produk ini dikarakterisasi menggunakan Fourier Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry (DSC) dan Scanning Electron Microscope (SEM).

---

Hydrogels are superabsorbent polymer that it can be able to absorb and retain large amounts of aqueous fluids. Hydrogel chitosan-graft-poly(N-vinyl pirrolidone) or chitosan-graft-PNVP has been synthesized by free radical polymerization. It is synthesized by crosslinking in the branch chains, PNVP chains, with different crosslinking agents, i.e. N,N’-Methylene Bisacrylamide (MBA) dan Ethylene Glycol Dimethacrylate (EGDMA). The swelling behavior of the crosslingked chitosan-graft-PNVP was measured by immerse it in the water. The effect of different and concentration of crosslinked agents and also reaction time on water absorbency have been investigated. Crosslinked hydrogel by using crosslinker EGDMA had showed that swelling ratio is higher than crosslinked hydrogel by using crosslinker MBA. The swelling behavior of crosslinked hydrogel by using crosslinker EGDMA can absorb water until 50% from its weight before absorbed. Resulted hydrogels were characterized by Fourier Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry (DSC) and Scanning Electron Microscope (SEM)."

"Pada penelitian ini, amoksisilin trihidrat telah berhasil dienkapsulasi ke dalam hidrogel kitosan-cangkok-poli(N-vinil pirrolidon) mengapung dengan agen pembentuk pori CaCO3 dan NaHCO3 untuk menghasilkan suatu sistem penghantaran obat mengapung. Komposisi agen pembentuk pori yang digunakan divariasikan 10%; 15%, 20% dan 25% terhadap total massa reagen. Karakterisasi matriks hidrogel dilakukan dengan spektrofotometer FTIR dan mikroskop stereo. Hidrogel yang mengandung CaCO3 mengalami perubahan sifat fisik dan kimia yang lebih nyata dibandingkan hidrogel yang mengandung NaHCO3 dan kontrol. NaHCO3 menghasilkan daya apung, porositas, dan efisiensi penjeratan obat yang lebih baik dari CaCO3. Semakin besar komposisi agen pembentuk pori, porositas (%) dan daya apung matriks hidrogel semakin meningkat tetapi efisiensi penjeratan obatnya menurun. Matriks hidrogel mengapung memiliki kemampuan mengapung di atas 180 menit dengan porositas tertinggi (47%) diperoleh pada komposisi NaHCO3 25%. Uji pelepasan amoksisilin trihidrat dilakukan pada larutan pH 1,2 dan karakter pelepasan obat pada hidrogel yang mengandung CaCO3 menunjukkan sifat yang lebih terkendali dibandingkan hidrogel yang mengandung NaHCO3. Formulasi matriks hidrogel mengapung optimum diperoleh pada komposisi 10% NaHCO3 dengan efisiensi penjeratan obat sebesar 57% dan total pelepasan obat sebesar 43%.

---

In this research, the floating drug delivery system of amoxicillin trihydrate encapsulated in floating chitosan-graft-poly(N-vinyl pyrrolidone) hydrogels containing CaCO3 and NaHCO3 as pore forming agents has been successfully prepared. Pore forming agents used was varied 10%; 15%; 20%; and 25% in respect to total mass of the used materials. Characterization of the hydrogels were carried out using FTIR spectrophotometer and stereo microscope. Hydrogels containing CaCO3 exhibited profound physical and chemical differences over NaHCO3 containing hydrogels and control. NaHCO3 showed better floating properties, porosity, and drug entrapment efficiency than CaCO3. As pore forming agents compositions increased, the porosity (%) and floating properties increase but followed by decrease in drug entrapment efficiency. The floating hydrogel possessed floating abilities longer than 180 minutes and the highest porosity was found in hydrogel containing 25% NaHCO3. Amoxicillin trihydrate release was performed in pH 1,2 solution and hydrogel containing CaCO3 showed better drug release profile than hydrogel containing NaHCO3. The optimum formulation was achieved at composition of 10% NaHCO3 with 57% of drug entrapped within the hydrogel and 43% drug released."

"Hidrogel termosensitif N-vinil kaprolaktam (NVCL) disintesis dengan metode polimerisasi radikal bebas ikat silang. Agen pengikat silang etilen glikol dimetakrilat (EGDMA) dan N,N?-metilen bis akrilamida (MBA) digunakan untuk menentukan pengaruh dari jenis dan konsentrasi pengikat silang pada nilai persen fraksi gel dan swelling saat setimbang. Spektrum Fourier Transform Infra Red Spectroscopy (FTIR) membuktikan pemutusan dari ikatan C=C untuk berpolimerisasi sebagai hidrogel. Hasil menunjukkan bahwa semakin tinggi konsentrasi pengikat silang, semakin tinggi fraksi gel namun rasio swelling semakin rendah. Ditemukan bahwa MBA merupakan agen pengikat silang yang lebih efektif dari EGDMA dengan nilai fraksi gel 35,72% pada MBA 5%. Kondisi optimal yang diperoleh yaitu waktu reaksi 24 jam dengan nilai persen gelation sebesar 14,29%.

---

Thermosensitive N-vinyl caprolactam (NVCL) hydrogels were synthesized by a free radical crosslinking polymerization. Ethylene glycol dimethacrylate (EGDMA) and N,N?-methylene bisacrylamide (MBA) crosslinking agents were employed in order to determine the effects of crosslinker type and concentration in percentage of gel fraction and equilibrium swelling value (ESV). Fourier Transform Infra Red Spectroscopy (FTIR) spectrum confirmed the breaking bond of C=C to polymerize as hydrogel.

Results showed that higher concentration of crosslinking agent, higher fraction gel but swelling ratio decreased. It was found that MBA more effective than EGDMA in synthesis PNVCL hydrogel with 35,72% gel fraction at 5% MBA. Optimum condition was 24 hour reaction time with percentage of gelation 14,29%."

"Metode IPN (Interpenetrating Polymer Network) baik semi maupun full IPNdapat digunakan untuk mensintesis hidrogel superabsorben (HSA) kitosan dan poli(N-vinil-kaprolaktam) (PNVCL) atau HSA kitosan-PNVCL. Pada metode full IPN jaringan polimer disintesis secara bertahap (sequential). Tahap pertama adalah sintesis jaringan polimer kitosan terikat silang asetaldehida dan homogenisasi dengan monomer N-vinil-kaprolaktam (NVCL) Tahap kedua adalah sintesis jaringan polimer PNVCL terikat silang N Nmetilenbisakrilamida (MBA) melalui polimerisasi radikal bebas monomer NVCL dengan inisiator amonium persulfat (APS) Hasil sintesis HSA kitosan-PNVCL full-IPN memiliki kekuatan struktur ikat silang dan kemampuan swelling yang baik Kekuatan struktur ikat silang meningkat dengan bertambahnya waktu reaksi, konsentrasi agen pengikat silang, inisiator, dan dipengaruhi rasio kitosan-PNVCL Kemampuan swelling HSA kitosan-PNVCL dengan kekuatan struktur ikat silang yang baik didapat pada rasio kitosan/PNVCL 70:30 (b/b %). HSA kitosan-PNVCL full-IPN memberikan persen derajat ikat silang yang tinggi (78,2%) dan kemampuan swelling yang baik (390,2%) Karakterisasi.

---

The IPN (Interpenetrating Polymer Network) method, both semi and full IPN, can be used to synthesize chitosan and poly (N-vinyl-caprolactam) (PNVCL) superabsorbent hydrogels or HSA chitosan-PNVCL. In the full method of IPN polymer networks are synthesized sequentially. The first stage is the synthesis of crosslinked acetaldehyde chitosan polymer tissue and homogenization with N-vinyl-caprolactam (NVCL) monomer The second stage is synthesis of PNVCL polymer network bound by N Nmetilenbisakrilamida (MBA) through NVCL monomer free polymerization with ammonium persulfate (APS) initiator Synthesis of HSA chitosan-PNVCL full-IPN has crosslinked structure strength and good swelling ability The strength of crosslinking structure increases with increasing reaction time, concentration of crosslinking agent, initiator, and influenced by chitosan-PNVCL ratio Swelling ability of HSA chitosan-PNVCL with good cross-link structure strength is obtained at the chitosan / PNVCL ratio of 70:30 (b / b%). Full-IPN HSA chitosan-PNVCL gives a high percentage of crosslinking (78.2%) and good swelling ability (390.2%) Characterization Characterization."

"Hidrogel kitosan-graft-poli(N-vinil kaprolaktam) disintesis dengan metode polimerisasi radikal bebas dengan larutan yang diikat silangkan. Agen pengikat silang etilen glikol dimetakrilat (EGDMA) dan N,N’-metilen bisakrilamida (MBA) digunakan untuk menentukan pengaruh dari jenis dan konsentrasi pengikat silang pada rasio swelling saat setimbang. Spektrum Fourier Transform Infra Red Spectroscopy (FTIR) dan Differential Scanning Calorimetry (DSC) membuktikan terbentuknya polimer graft yang terikat silang. Hasil menunjukkan semakin tinggi konsentrasi pengikat silang, semakin besar rasio swelling yang dihasilkan. Ditemukan bahwa MBA merupakan agen pengikat silang yang lebih efektif dari EGDMA dengan nilai rasio swelling 46,70% pada MBA 2% pada waktu optimal yang diperoleh yaitu tiga jam.

---

Chitosan-graft-poly(N-vinyl caprolactam) Hydrogels were synthesized by free radical crosslinking polymerization with solvent. Ethylene glycol dimethacrylate (EGDMA) and N,N’-methylene bisacrylamide (MBA) crosslinking agent were employed to determine the effect of crosslinker type and concentration in equilibrium swelling rate (ESV). Fourier Transform Infra Red Specstrocopy (FTIR) spectrum confirm the formation of crosslinking graft polymer. Result showed that higher concentration of crosslinker, the swelling rate produced was increase. It was found that MBA more effective than EGDMA with swelling rate up to 46,70% at 2% MBA with optimum reaction time is three hours."

"ABSTRAKHidrogel poli(N-vinil pirrolidon) terikat silang telah disintesis dengan menggunakan agen pengikat silang etilen glikoldimetakrilat (EGDMA) dan NN?-metilenbisakrilamid (MBAm), inisiator benzoil peroksida dan pelarut etanol melalui teknik polimerisasi radikal bebas. Dilakukan variasi jenis dan konsentrasi agen pengikat silang serta waktu reaksi. Hidrogel yang terbentuk dikarakterisasi menggunakan FT-IR dan analisa gravimetri. Ditemukan bahwa hidrogel PNVP terikat silang dengan baik jika digunakan MBAm 5% sebagai agen pengikat silang daripada EGDMA dengan waktu reaksi 24 jam. Hidrogel PNVP-MBAm ini memiliki derajat ikat silang yang lebih tinggi daripada PNVP-EGDMA yaitu 28,8% dengan kemampuan menyerap air sekitar 250%. Derajat ikat silang berbanding terbalik dengan kemampuan hidrogel menyerap air atau mengembang (swelling). Semakin lama waktu reaksi, semakin banyak ikatan silang yang terbentuk. Semakin tinggi derajat ikat silang maka semakin rendah kemampuan hidrogel dalam menyerap air.

---

ABSTRACTThis article describes about the synthesis of chemically crosslinked hydrogels poly(N-vinyl pirrolidone) (PNVP) by free radical polymerization in solution technique. Ethylene glycoldimethacrylate and NN?-methylenebisacrylamide were used as crosslinker, benzoyl peroxide was used as initiator and ethanol was used as a solvent. Hydrogels were prepared by varying the type and concentration of crosslinker, and also reaction time. Resulted hydrogels were characterized by FT-IR and gravimetry analysis. Crosslinked hydrogels PNVP by using crosslinker MBAm 5% with 24 hours reaction time had the highest degree of crosslinking about 28,8% and 250% for its swelling ratio. The degree of crosslinking inversely proportional with hydrogels ability to absorp water (swelling). The longer reaction time was, the higher degree of crosslink was. The higher degree of crosslink was, the lower swelling ability of the hydrogels was."

"Metode semi-Interpenetrating Polymer Network (semi-IPN) dapat digunakan untuk mensintesis hidrogel. Pada metode ini, jaringan kitosan terikat silang formaldehida akan berinteraksi dengan poli(N-vinil pirolidon) linear. Secara umum, rasio sweling dan derajat ikat silang hidrogel semi-IPN dipengaruhi oleh komposisi kitosan-PVP, konsentrasi formaldehida, dan waktu reaksi. Rasio swelling dan derajat ikat silang dari hidrogel kitosan-poli(N-vinil pirolidon) semi-IPN didapatkan sebesar 553,70% dan 58,82% pada rasio kitosan-poli(N-vinil pirolidon) 70:30 (%b/b), konsentrasi formaldehida 2% (%b/b), dan waktu reaksi 3 jam. Hidrogel kitosan-poli(N-vinil pirolidon) semi-IPN menunjukkan penurunan rasio swelling dan peningkatan derajat ikat silang dibandingkan hidrogel kitosan nonkovalen.

---

Semi-Interpenetrating Polymer Network (semi-IPN) method was used to synthesize hydrogel. In this method, chitosan was crosslinked with formaldehyde and blended with Poly(N-vinyl pyrrolidone) to form crosslinked chitosan network that interracts with linear polymer of Poly(N-vinyl pyrrolidone). Generally, swelling ratio and degree of crosslinking of semi-IPN hydrogel were influenced by Poly(N-vinyl pyrrolidone) amount, concentration of formaldehyde, and reaction time. Swelling ratio and degree of crosslinking of semi-IPN hydrogel was obtained at 553,70% and 58,82% in the ratio of chitosan- Poly(N-vinyl pyrrolidone) 70:30 (%w/w), formaldehyde concentration of 2%, and 3 hours of reaction time. Semi-IPN hydrogel of chitosan-Poly(N-vinyl pyrrolidone) has lower swelling ratio and higher degree of crosslinking compared to hydrogel of chitosan."