Hasil Pencarian  ::  Simpan CSV :: Kembali

"ABSTRAKTelah berhasil disintesis dan dipelajari material karbon nanopori yang diperoleh dari interaksi antara padatan silikon karbida dan HCl menggunakan metode variasi ultrasonik dan pemanasan. Silion karbida dengan kemurnian lebih dari 98% dari Aldrich digunakan sebagai sumber karbon, sedangkan larutan HCl berfungsi sebagai sumber gas klor yang akan bereaksi dan mengambil silikon (Si) dari silikon karbida. Dalam penelitian ini diadakan lima variasi yang berbeda yaitu disebut sebagai CDC1, CDC2, CDC3, CDC4 dan CDC5. Metode ultrasonik dan pemanasan terhadap material CDC1, CDC2, CDC3, CDC4, CDC5 didapatkan stabil pada suhu pemanasan 1000 o C dengan perbandingan berat wt% antara silikon karbida dan pori karbon hasil sintesis adalah CDC1 wt% = SiC : C = 75% : 25%, CDC2 wt% = SiC : C = 35% : 65%, CDC3 wt% = SiC : C = 34,5% : 65,5%, CDC4 wt% = SiC : C = 30% : 70% dan CDC5 wt% = SiC : C = 25% : 75%. Pembentukan pori dan pertumbuhan kristal hanya muncul setelah proses pemanasan. Material CDC1, CDC2, CDC3, CDC4, CDC5 hasil sintesis masing-masing memiliki struktur heksagonal dengan grup ruang P6 3 mc dan parameter kisi berturut-turut yaitu a = b = 2,456 Å dan c = 12,350 Å. Pembuktian berdasarkan analisis GSAS refine Fourier memperlihatkan bahwa material CDC1, CDC2, CDC3, CDC4, CDC5 memiliki struktur rentang panjang arah sumbu c untuk CDC1 = 15Å, CDC2 = 15Å, CDC3 = 20Å, CDC4 = 30Å, CDC5 = 35Å terhadap pemanjangan parameter kisi c masing -masing CDC1 = 12,35Å, CDC2 = 15,1Å, CDC3 = 18Å, CDC4 = 20,4Å dan CDC5 = 24,1Å dan mengalami penurunan nilai densitas CDC1= 3 gr/cm 3 , CDC2 = 2,45 gr/cm 3 , CDC3 = 1,5 gr/cm 3 , CDC4 = 1,4 gr/cm 3 dan CDC5 = 1,2 gr/cm 3 . Struktur karbon m akropori - nanopori rentang panjang heksagonal tipe pori silinder memiliki ukuran pori 200 nm - 35 nm, luas permukaan 55 m 2 /gram-1250 m 2 /gram dan sangat khas muncul pada bilangan gelombang 1095, 57 cm -1 dan karenanya material tersebut diharapkan dapat digunakan sebagai media penyimpan gas.

---

ABSTRACTNanopores carbide derived carbon synthesized from silicon carbide and HCl by using ultrasonic and sintering at high temperature has been investigated. Silicon carbide with a purity better than 98% from Aldrich was used as a carbon source while HCl was used as a leaching agent.. In this investigation, five different processes were carried out, i.e. CDC1, CDC2, CDC3, CDC4 and CDC5. Ultrasonik process and sintering on these five CDC1, CDC2, CDC3, CDC4 and CDC5 materials were found to be stable at 1000 o C with the weight ratio between silicon carbide and the derived carbon CDC1 wt% = SiC : C = 75% : 25%, CDC2 wt% = SiC : C = 35% : 65%, CDC3 wt% = SiC : C = 34,5% : 65,5%, CDC4 wt% = SiC : C = 30% : 70% dan CDC5 wt% = SiC : C = 25% : 75%. Pores formation and crystal growth occur after sintering process. Each derived carbon material has the hexagonal structure and a space group of P6 3 mc and lattice parameters a = b = 2.456 Å and c = 12.350 Å. Fourier analysis by using a package program of GSAS showed that CDC1, CDC2, CDC3, CDC4 and CDC5 have an expansion on the c direction in which CDC1 = 15 Å, CDC2 = 15 Å, CDC3 = 20 Å, CDC4 = 30 Å, and CDC5 = 35 Å from the original values of CDC1 = 12.35 Å, CDC2 = 15. 1 Å, CDC3 = 18 Å, CDC4 = 20. 4 Å and CDC5 = 24.1 Å. Furthermore, the elektronic density was found to be CDC1= 3 gr/cm 3 , CDC2 = 2.45 gr/cm 3 , CDC3 = 1.5 gr/cm 3 , CDC4 = 1.4 gr/cm 3 and CDC5 = 1.2 gr/cm 3 . The long hexagonal ribbon of the derived carbon has the size of 200 nm ? 35 nm, surface area of 55 m 2 /g ? 1250 m 2 /g and occur at a wave number of 1095. 57 cm -1 . This material has the potential application as a gas storage."

"Penelitian ini bertujuan untuk mengetahui karakteristik material untuk pengganti fantom polymethyl methacrylate PMMA dan fantom air dengan menggunakan metode dual-energy computed tomography DECT dan metode analisis stoikiometri. Metode DECT dilakukan dengan memindai sampel menggunakan dua jenis energi yaitu 80 kV dan 130 kV, sedangkan metode analisis stoikiometri dilakukan melalui uji energy dispersive x-ray spectroscopy EDX untuk mendapatkan informasi mengenai komposisi atomnya. Material yang digunakan untuk membuat sampel terdiri dari bahan organik lilin Gondorukem, lilin Cecek, dan tepung beras yang komposisinya divariasikan sesuai dengan kebutuhan. Parameter yang digunakan sebagai alat untuk mengkarakterisasi sampel adalah CT number Hounsfield Unit, densitas massa, densitas elektron, dan nomor atom efektif Zeff. Metode DECT menunjukkan hasil yang lebih akurat dibandingkan dengan metode analisis stoikiometri dengan kesalahan literatur kurang dari 4, kecuali untuk Zeff pada sampel ekuivalen-air dengan kesalahan literatur 22,22. Hasilnya, sampel ekuivalen-PMMA dinilai memiliki karakteristik yang serupa dengan PMMA, namun sampel ekuivalen-air dinilai belum memiliki karakteristik yang serupa pada energi rendah.

---

The purpose of this research is to obtain information of the material characteristics of polymethyl methacrylate PMMA phantom and water phantom replacement using dual energy computed tomography DECT method and stoichiometry analysis method. DECT method is performed by scanning the samples using two types of energy 80 kV and 130 kV, and stoichiometry analysis is performed by using the Energy Dispersive X ray Spectroscopy EDX to obtain the atomic composition of the sample. The basic material used to produce the samples are made from organic materials Gondorukem wax, Cecek wax, and rice flour, which compositions are varied according to the required material equivalent needed. The parameters used to characterize the sample are CT number Hounsfield Unit, mass density, electron density e, and effective atomic number Zeff. DECT method shows more accurate results compared to stoichiometry analysis method with the literature error less than 4, except for the Zeff for water equivalent sample that have 22,22 of literature error. The final results show the equivalent PMMA sample has similar characteristics to the PMMA, yet the water equivalent does not have similar characteristics with water in a low energy. "

"ABSTRAKSenyawa Annonaceous acetogenin (asetogenin) dari daun sirsak telah terbukti memiliki sifat antikanker. Gugus asetogenin terdiri dari berbagai senyawa, salah satunya adalah Annonacin yang banyak terdapat di bagian daun tanaman sirsak. Adapun tujuan dari isolasi ini adalah untuk mendapatkan senyawa annonacin yang dapat digunakan sebagai standar untuk penelitian lebih lanjut. Isolasi annonacin terdiri dari tiga tahap yaitu maserasi, fraksinasi, dan isolasi. Pelarut yang digunakan antara lain etanol, etil asetat, heksana, kloroform, dan air. Hasil isolasi tersebut diuji dengan menggunakan kedde reagent untuk mengetahui ada atau tidaknya gugus lakton serta jumlah konsentrasi lakton yang dikandung. Hasil uji reagen kedde menunjukkan adanya gugus lakton dengan perubahan warna menjadi pink-ungu. Jumlah konsentrasi lakton terkandung dari F4.4 241,86 mg/gr. Sitotoksisitas annonacin diuji menggunakan metode Brine Shrimp Test dengan menghitung LC50. Didapat nilai LC50 sebesar 1,04 ppm. Analisis kualitatif hasil isolasi dilakukan menggunakan HPLC dan LC-MS menghasilkan terdapat senyawa annonacin dari F4.4 dengan berat molekul 597,23.

---

ABSTRACT

Compounds of Annonaceous acetogenin (asetogenin) from soursop leaf has been shown to have anticancer properties. Asetogenin group consists of a variety of compounds, one of which is that many Annonacin located on the leaves of the soursop plants. The purpose of isolation is to get annonacin compounds that can be used as a standard for further research. Isolation of annonacin consists of three phases, namely maceration, fractionation, and isolation. Solvents used include ethanol, ethyl acetate, hexane, chloroform, and water. isolation results were tested using kedde reagent to determine the presence or absence of the lactone group and the number concentration of lactones contained. Kedde reagent test results indicate the presence of the lactone group to change into a pink-purple color. Total concentrations of F4.4 lactone contained 241.86 mg / g. Annonacin cytotoxicity was tested using Brine Shrimp Test method by calculating the LC50. Obtained LC50 values of 1.04 ppm. Qualitative analysis of the results was performed using HPLC isolation and LC-MS produces compounds contained annonacin F4.4 with a molecular weight of 597.23."

"Telah dilakukan isolasi senyawa (-)- asam usnat dalam bentuk kristal kuning sebesar 727 mg dari ekstrak aseton kasarnya, dengan mengekstraksi serbuk kering dari talus lichen Usnea flexuosa Tayl, lichen tersebut dikumpulkan dari kaki gunung Bambapuang, Kecamatan Anggeraja, Kabupaten Enrekang, Sulawesi Selatan. Ekstraksi dilakukan secara sinambung dengan menggunakan soxhlet dan dengan pelarut aseton selama 8 jam, kemudian ekstrak kasar dipisahkan / dimurnikan menggunakan kromatografi kolom dengan fasa diam kiesegel 60 dan eluen campuran diklorometana dan metanol. Kristal (-)- asam usnat direkristalisasi dengan pelarut diklorometana dan penentuan struktur molekul dilakukan dengan membandingkan senyawa hasil isolasi tersebut dengan sifat-sifat fisika dan data spektrum dari UV-Vis, IR dan GC-MS dari asam usnat yang sudah diketahui, hasil uji aktivitas larvasida dari senyawa (-)- asam usnat terhadap Larva nyamuk Aedes aegypti instar III memberikan LC50 sebesar 0,1904 ppm.

---

It has been carried out the isolation of (-)- usnic acid as yellow crystal from aceton extract, from dried powders of lichen thallus of Usnea flexuose Tayl. The yield of extraction was 727 mg. This lichen was collected from Bambapuang mount, Anggeraja region, Enrekang, province of South Sulawesi. The extraction is performed by using continuous extraction apparatus (soxhlet) for 8 hours and aceton as solvent. Than, the raw aceton extract were, purified with coloumn chromatography filling with kieselgel 60 as stationary phase and using a mixture of dichloromenthane and methanol as eluent. Pure (-)- usnic acid crystals were crystalised using dichloromethare as solvent and followed by structure elucidation using physical ? and spectroscophycal data (UV-Vis, Ir and Mass) comparison with related data of (+)- usnic acid. Larvacidal activity test was ferformanced against 3rd phase of Aedes aegypti Larvae and, (-)- Usnic acid possesed positive result with LC50=0,1904 ppm."