Hasil Pencarian  ::  Simpan CSV :: Kembali

"Skripsi ini membahas mengenai perancangan perangkat akustik untuk getaran hama wereng agar dapat mengatasi permasalahan tanaman. Pemanfaatan teknologi ini memiliki aplikasi yang cukup mudah dan murah dan diharapkan dapat meningkatkan produktivitas tanaman pangan Indonesia. Perangkat ini berupa bambu yang memiliki lubang-lubang dengan ketentuan dan parameter tertentu yang menghasilkan frekuensi yang dibutuhkan untuk dapat membunuh jenis hama yang diinginkan dan dalam hal ini adalah hama wereng.

---

This essay discusses the design of acoustic devices for vibration planthopper in order to overcome the problems of plants. Utilization of this technology has applications that are easy and inexpensive and is expected to increase the productivity of food crops in Indonesia. The device is in the form of bamboo that has holes with certain rules and parameters that produce frequencies that is required to kill the pests you want and in this case is planthopper."

"ABSTRAKPada uji tak rusak (non-destructive testing, NDT) metode ultrasonik, dikenal adanya gelombang ruah (bulk wave) dan gelombang terarah (guided wave). Salah satu jenis gelombang terarah yang memiliki potensi untuk mendeteksi dan mengkarakterisasi cacat adalah gelombang Lamb. Gelombang Lamb memiliki profil mode gelombang antisymmetical dan symmetrical, berdasarkan profil displacement saat merambat dalam suatu pelat tipis, dalam penelitian ini digunakan metode kontak teknik pulse-echo untuk menghasilkan gelombang symetris mode nol. Gelombang ini dirambatkan pada pelat aluminium baik yang bebas cacat maupun yang telah diberi cacat fatik simulasi. Setelah itu dilakukan analisis signal menggunakan time dan frekuensi-domain.Hasil penelitian menunjukkan bahwa cacat fatik dapat dideteksi oleh gelombang Lamb simetris mode nol. Analisis time-domain menunjukkan perbedaan amplitudo antara pelat non-cacat dan cacat fatik sebesar 91,11%, sementara pada frekuensi-domain, perbedaan amplitudonya 80,96%. Perhitungan lokasi cacat dengan menggunakan Time-of-flight (TOF) signal menunjukkan bahwa lokasi cacat menyimpang 19,42% dari lokasi sebenarnya. Dari penelitian ini dapat disimpulkan bahwa gelombang Lamb simetris mode nol dapat digunakan secara independen untuk mendeteksi dan mengkarakterisasi cacat fatik.

---

ABSTRACT

In the field of Non-Destructive Test (NDT) using ultrasonic method, it is known that there are bulk waves and guided waves. The type of guided waves that has the potential to detect and characterize defect is the Lamb waves. Lamb waves have antisymmetrical and symmetrical profile modes, based on the profile displacement when it propagated inside a thin plate. In this research, the pulse-echo contact method was being used to produce the zero order symmetrical wave. This wave was propagate inside the aluminium plate with both no defect and with simulated fatique defect. Then, the data was analyzed by using time-domain and frequency-domain.

The results showed that a fatique defect can be detected by zero order symmetrical Lamb wave. Time-Domain analysis showed that the difference of ampliudes between fatique defect and non-defect is 91,11% while by using frequency-domain, the difference is 80,96%. The calculation of the defected location using the Time-of Flight signal showed that the amount of deviation to the distance of this simulation defects is 19.42% from the real location. From the abovementioned results, it can be concluded that the zero order symmetrical Lamb wave, can be used independently to detect and characterize the fatique defect."

"ABSTRAKBaja ODS (Oxide Dispersion Strengthened) merupakan paduan dengan ketahanan temperatur dan korosi yang baik. Penggunaan metode iradiasi ultrasonik di dalam larutan toluene merupakan metode baru yang dapat memberikan keuntungan berupa ukuran butir yang halus, dapat membentuk microalloying di dalam serbuk, dan dapat meminimalisasi pembentukan fasa oksida. Penelitian ini mempelajari tentang pengaruh amplitudo terhadap reduksi ukuran partikel, homogenitas serbuk, dan pembentukan microalloying Fe-Cr pada preparasi serbuk Fe-15Cr-0.5Y2O3. Serbuk dibagi menjadi 4 sampel dengan perlakuan pencampuran mortar (sampel A), iradiasi ultrasonik dengan amplitudo 40% (sampel B), 50% (sampel C), dan 60% (sampel D) yang kemudian dikarakterisasi menggunakan SEM, EDS, dan XRD. Hasil dari penelitian ini adalah peningkatan amplitudo akan menurunkan ukuran butir dengan nilai sampel B>sampel C>sampel D adalah 4.63 μm>3.44 μm>3.09 μm. Sampel C menghasilkan partikel Fe-Cr sementara sampel B dan D terbentuk partikel paduan Fe-Cr-Y2O3. Nilai komposisi Fe-Cr terbesar dicapai pada amplitudo 40% dengan nilai sampel A:sampel B:sampel C: sampel D adalah 0.00%:20.5%:10.06%:5.2% tanpa pembentukan oksida dengan ukuran crystallite Fe-Cr sampel B:sampel C:sampel D berukuran 16.79 nm:30.13 nm: 55.69 nm. Nilai lattice strain sampel B:sampel C: sampel D adalah 0.0055:0.0030:0.0016.

---

ABSTRACTODS Steel (Oxide Dispersion Strengthened) is an alloy with good corrosion and high temperature resistance. The utilization of ultrasonic irradiation method in toluene solution is a new method giving benefits like producing fine grain-size, forming micro-alloying on powder, and minimizing the oxide phase formation. This research investigates the influence of amplitude on the reduction of the particle size, the homogeneity of the powder, and the formation of Fe-Cr microalloying on Fe-15Cr-0.5Y2O3 powder preparation. The powder was divided into 4 samples with various treatments such as mortar mixing (sample A) and ultrasonic irradiation with an amplitude of 40% (sample B), 50% (sample C) and 60% (sample D). After that, each sample was characterized by SEM, EDS and XRD. This research shows that increasing the amplitude will decrease the grain size with the value of sample B> sample C> sample D is 4.63 μm>μm 3:44> 3:09 μm. Sample C produced Fe-Cr particles meanwhile samples B and D formed Fe-Cr-Y2O3 alloy particle. The highest composition value of Fe-Cr is reached on the amplitude of 40% to the composition value of sample A: sample B: sample C: sample D is 0.00%: 20.5%: 10:06%: 5.2% without the oxide formation. The size of crystalline Fe-Cr sample B: sample C : sample D size of 16.79 nm: 30.13 nm: 55.69 nm. The lattice strain value of the sample B: the sample C: sample D was 0.0055: 0.0030: 0.0016.;"

"ABSTRAKBaja ODS (Oxide Dispersion Strenghtened) merupakan salah satu advancedmaterial yang memiliki struktur stabil dan tahan terhadap temperatur tinggi yangberguna sebagai aplikasi nuklir atau pembakaran biomassa. Dengan serbuk Fe, Cr,dan Y2O3, Paduan Baja ODS memiliki standard pengolahan yang terdiri atasatomisasi gas dari pre-alloy, mechanical alloying, perlakuan thermal/mekanis. Padapengolahan tipe powder metallurgy, pengolahan baja ODS masih perlu dikaji dalamhal homogenitas, dan mechanical properties, dengan menyelidiki baja ODS pascaperlakuan microalloying dengan ultrasonic pada media toulene. Perlakuandiberikan dalam bentuk serbuk dengan variabel amplitudo, kemudian tekanankompaksi pada 7500 hingga 8000 Psi, serta proses sintering yang dilakukan padasuhu 1300oC dengan proses I tahap yang ditahan selama 2 jam dan proses II tahappada suhu tahan 1000oC, dan 1300oC dengan masing-masing 1 jam tahan yangkemudian diteiti dengan SEM-EDS, XRD, microhardness, serta density. Hasil dariPenelitian ini menunjukkan bahwa Nilai kekerasan berada pada rentang 87,42 HVNHingga 163,77 HVN dengan nilai densitas serbuk, 5,13 gr/cc, 5,76 gr/cc, 5,23gr/cc, serta 5,5 gr/cc yang secara berurutan Sampel A hinga D. selain itu, hasilpenyelidikan menyebutkan bahwa, pada pengujian kompaksi, terjadi perbedaanNilai kekerasan sebesar 62,24 HVN. Kemudian, dari Hasil morfologi bongkah dariproses sintering, menghasilkan fasa Ferrite dengan struktur kristal Cubic yangmemiliki nilai homogenitas yang tinggi melalui pembuktian grafik XRD dengankomposisi Fe-Cr tertinggi pada amplitudo 40% 1-step sintering sebesar 94,5%.

---

ABSTRACTODS (Oxide Dispersion Strengthened) Steel is one of the AdvancedMaterial that has a stabilized structure and Heat Resistance as Nuclear Applicationor Combustion of Biomass. With the basic Element Fe-Cr-Y2O3, ODS Alloy SteelObtain standard of processing consisting Pre-Alloy, Mechanical Alloying, andMechanical/Thermal Treatment. In the type of Powder Metallurgy Processing,ODS Steel indicated a obstacles that need to discuss in the concern of Homogeneityand Mechanical Properties with investigating ODS Steel Characterization afterMicro alloying treatment with ultrasonic using Toulene as a media. The treatmentgiven by a various Amplitude, and then gain the Compacting Pressure from 7500Psi to 8000 Psi, also sintering Processes for the first step in 1300OC with 2 hours ofholding time, and the second one the 2 step of sintering process, which has holdingtime in 1000OC and 1300OC with 1 hours each. After that, the result of the processesbeing characterized by SEM-EDS, XRD, Micro hardness, and Density. Effect ofcompaction pressure prove the difference between pressure of compaction wasgiven by 62.24 HVN. the result of this research Prove that the range of Hardnessare from 87,42 HVN to 163,77 HVN in the manner score of density in powdershape, 5,13 gr/cc, 5,76 gr/cc, 5,23 gr/cc, and 5,5 gr/cc that sequentially from sampleA to D. the Bulk Morphology, as a result of sintering Process, describes Ferritewhich has cubic structure, contain high homogeneity result that proved by XRDgraph with highest composition of Fe-Cr at 40% amplitude in 1-step sintering in theamount of 94,5%"