Hasil Pencarian  ::  Simpan CSV :: Kembali

"The influence of oxidation soaking time on the micro-strain of oxidation product of rejected UO2 sintered pellet. The possibility of unexpected rejected UO2 sintered pelet from fabrication process came from, such as crack sintered pellet, the size of pore,unacceptable pellet dimension, therefore those pellet was called rejected sintered pewllet...."

"Penelitian dilakukan untuk mengetahui pengaruh berbagai kondisi oksidasi terhadap penurunan kandungan sterol dari lemak coklat (BC) murni dan yang ditambah dengan 100 ppm (RTc), 750 ppm (RTm) �?�-tokoferol, 5,00 ppm Cu(II) atau Fe(III). Oksidasi dilakukan pada temperatur 45, 60 atau 90 oC tanpa sinar atau pada temperatur kamar dengan adanya sinar (L). Hasil analisis menunjukkan bahwa kenaikan temperatur lebih meningkatkan laju oksidasi dibanding sinar. Laju penurunan kandungan sterol sedikit berbeda antar jenis sterol. Secara umum penambahan �?�-tokoferol akan menghambat laju oksidasi, namun penambahan sangat berlebih malah bertindak sebagai prooksidan. Penambahan Cu(II) dan Fe(III) mempercepat laju oksidasi, dimana sifat katalis Cu(II) sedikit lebih kuat dibanding Fe(III). Analisis dengan ANOVA dua arah menunjukkan bahwa perbedaan kondisi dan lama oksidasi berpengaruh terhadap kandungan sterol secara signifikan, kecuali pengaruh lama oksidasi untuk kondisi Tm-L.

---

The influence of different oxidation condition to the sterolic content of cocoa butter. The influence of different oxidation conditions to the variation of sterolic compound of refined cacao butter (BC) was observed. BC was also treated by addition of 100 ppm (RTc), 750 ppm (RTm) �?�-tocopherol, 5.00 ppm Cu (II) or Fe(III). Oxidation was carried out at 45, 60 or 90oC in the dark or in day light at room temperature (L). The analysis showed that the temperature is more accelerate oxidation rate than light at room temperature. The disappearance rate of sterol is slight difference among each other. In general, addition of �?�-tocopherol inhibited the degradation of sterol, but in excess it was seem to be a prooxidant. The other hand Cu (II) or Fe (III) was a catalyst where the influence of Cu (II) was stronger than Fe (II). Two ways ANOVA shown that the condition and time of oxidation influenced sterol content significantly, except for time oxidation of Tm-L condition."

"Telah dilakukan studi penelitian pengaruh filamen platina pada oksidasi parsial metana dengan menggunakan reaktor baja tahan karat SS 316 berlapis gelas pyrex. Tujuan dari studi penelitian ini untuk mempelajari pengaruh filamen ini terhadap produk reaksinya. Filamen ini ditempatkan didalam preheater. Filamen ini dipanaskan dengan mengalirkan arus listrik. Kandungan oksigen dalam gas umpan antara 2,5 % - 31 %. Temperatur operasinya antara 350°C - 550°C dan tekanan operasinya antara 15 atm - 40 atm. Hasil yang diperoleh dari pengoperasian dengan dan tanpa filamen secara kualitatif tidak berbeda namun secara kuantitatif nampak ada perbedaan. Produk reaksinya berupa metanol, air, karbon dioksida, karbon monoksida dan formaldehid, sama dengan hasil tanpa menggunakan filamen. Secara umum filamen ini tidak banyak mempengaruhi konversi metana pada setiap kondisi. Pengaruhnya terhadap selektifitas dan yield metalol terlihat bahwa pada kondisi P=20 atm ; 9,6% 02 untuk kisaran temperatur dari 425°C- 500°C memberikan kenaikan selektifitas dan yield metanol rata-rata 15%. Kenaikan selektifitas dan yield metanol diikuti dengan menurunnya selektivitas CO."

"ABSTRAKDalam meningkatnya kebutuhan nikel di dunia dan menurunnya deposit nikel sulfida, pengolahan nikel jenis nikel oksida merupakan tantangan baru dengan metode reduksi selektif aditif Na 2SO4 dan reduktor batu bara. Penelitian ini bertujuan untuk mengetahui parameter preparasi persiapan pelet sebelum reduksi dalam peningkatan redusibilitas dan perolehan nikel laterit . Sampel dipersiapkan dengan membuat pelet dengan variasi ukuran massa 5 gram, 10 gram, dan 15 gram. Sampel dengan hasil perhitungan reducibilitas setelah reduksi selektif dikarakterisasi dengan BET- luas permukaan untuk mengetahui perubahan luas permukaan specifik, Uji XRD untuk mengetahui fasa yang terbentuk, dan uji AAS untuk mengetahui perolehan kadar setelah reduksi selektif. Nilai redusibilitas yang besar dan penurunan luas permukaan specifik terjadi pada pelet yang berukuran massa besar, hasil uji XRD menunjukkan pembentukan Magnetite pada pelet ukuran massa 5 gram, akan tetapi terjadi pembentukan fasa fayalite di setiap ukuran massa pellet yang diuji. Nilai perolehan besi dan nikel terbesar dimiliki oleh pelet yang berukuran kecil.

---

ABSTRACTDuring the needs increase of nickel and the deposit decline of nickel sulfide, the processing of nickel oxide is a new challenge with selective aditive reduction Na 2SO4 and coal redactor. The purpose of this research is to identify the parameter of pellet preparation before reduction in order to increase the reducibility and the gain of nickel laterite. Samples are prepared by creating pellets which mass variation are within 5, 10, and 15 gram. The samples with the results of the reducibility after selective reduction was characterized by BET surface area to identify the specific survey area change, XRD test to determine the formed phase, and the AAS test to determine the acquisition of content after selective reduction. The large reducibility value and the decrease of specific surface area occur in large pellets, XRD test results show the formation of Magnetite in 5 gram pellets. However, the forming of fayalite phase occurred in every tested pallets. The largest iron and nickel recovery value is owned by small pellets"

"Gas alam dan batu bara merupakan sumber daya yang terbatas, sehingga transisi ke energi terbarukan sangat penting untuk masa depan. Hidrogen, alternatif yang bersih dan berlimpah, menawarkan potensi yang signifikan, tetapi metode yang efektif untuk penyimpanan dan pengangkutannya masih menjadi tantangan. Proyek Me2H2 mengatasi masalah ini dengan menggunakan proses uap-besi, sebuah metode yang memungkinkan penyimpanan dan pengangkutan hidrogen melalui oksidasi dan reduksi siklik besi. Tesis ini berfokus pada aspek oksidasi dari proses steam-iron, menyelidiki bagaimana waktu dan suhu mempengaruhi oksidasi besi. Eksperimen melibatkan pemanasan serbuk besi pada suhu 600°C hingga 800°C selama 40 hingga 360 menit. Hasil penelitian menunjukkan bahwa suhu 725°C menghasilkan peningkatan massa tertinggi karena tingkat oksidasi yang optimal, sementara suhu yang sangat tinggi, seperti 800°C, menyebabkan oksidasi permukaan yang cepat sehingga mencegah penetrasi yang seragam. Penelitian ini juga mengidentifikasi pembentukan wüstite, magnetite, dan hematite sebagai oksida besi utama selama proses tersebut. Untuk menganalisis oksida-oksida ini, alat canggih seperti Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray (EDX), dan Electron Backscatter Diffraction (EBSD) digunakan untuk memeriksa struktur mikro dan komposisinya. Temuan ini berkontribusi pada optimalisasi proses steam-iron, mendukung kemajuan dalam teknologi penyimpanan hidrogen dan mempromosikan solusi energi yang berkelanjutan dan ramah lingkungan.

---

Natural gas and coal are finite resources, making the transition to renewable energy crucial for the future. Hydrogen, a clean and abundant alternative, offers significant potential, but effective methods for its storage and transportation remain a challenge. The Me2H2 project addresses this issue using the steam-iron process, a method that enables hydrogen storage and transport through the cyclic oxidation and reduction of iron. This thesis focuses on the oxidation aspect of the steam-iron process, investigating how time and temperature influence iron oxidation. Experiments involved heating iron powder at temperatures from 600°C to 800°C for 40 to 360 minutes. Results showed that 725°C yielded the highest mass increase due to optimal oxidation rates, while extremely high temperatures, such as 800°C, caused rapid surface oxidation, preventing uniform penetration. The study also identified the formation of wüstite, magnetite, and hematite as key iron oxides during the process. To analyze these oxides, advanced tools like Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray (EDX), and Electron Backscatter Diffraction (EBSD) were used to examine their microstructure and composition. The findings contribute to the optimization of the steam-iron process, supporting advancements in hydrogen storage technologies and promoting sustainable, eco-friendly energy solutions."

"Proses oksidasi langsung metana menjadi metanol mulai banyak diteliti dalam rangka pemanfaatan cadangan gasbumi yang masih cukup banyak. Namun faktor penyulit utama dalam proses tersebut adalah tingginya stabilitas molekul-molekul metana dan reaktivitas produk terhadap oksigen yang sangat tinggi. Penggunaan katalis yang tepat adalah salah satu cara untuk mengatasi kendala tersebut.Penggunaan katalis Cu-Sick, V-Si42 dan Pb-SiO2 telah diteliti untuk mengoksidasi metana menjadi metanol. Katalis yang dipreparasi melalui metoda sol-gel ini mempunyai luas permukaan BET 130-215 m²/g, volume pori sekitar 2x10-³ - 7x10-³ cm³/g, berupa padatan yang porous dan sifat-sifat lain yang menunjang terbentuknya metanol. Pengujian kinerja ketiga katalis pada oksidasi metana menjadi metanol dilakukan pada temperatur 400-440°C, tekanan 54.4 atm dan waktu kontak semu 0.24 detik dan dari ketiga katalis tersebut, katalis V-Sid menunjukkan kinerja yang lebih baik dengan menghasilkan konversi CH4 maksimum sebesar 4% mol pada 440°C dan selektivitas terhadap metanol maksimum sebesar 18.22% mol pada 420°C."