"This study aims to analyze the effect of chemical pretreatment using sodium hydroxide (NaOH) on
the capacity of coco peat in removing of copper (11) ions from aqueous solutions. The effects of
varying the molarity of NaOH, the solution pH, initial Cu(II) concentration, coco peat dosage and
contact time were studied in batch experiment. The result of the preliminary pretreatment study
shows that treatment with 0.5M NaOH greatly enhanced the metal sorption capacity of raw coco
peat. The uptake capacity for Cu of the raw coco peat was increased from 46% to 83% at pH 4.0
and from 15% to 27% uptake for initial solution pH of 2.4. The results showed that the removal
rate is directly proportional to pH, coco peat’s dosage and contact time and inversely proportional
to Cu(Il) concentration. The adsorption process is best explained by the Langmuir isotherm than
the Freundlich isotherm, indicating monolayer adsorption on a homogenous surface. The rate of
reaction follows the pseudo-second order kinetic model, signifying that chemisorption is the rate
limiting mechanism. The results of the Fourier Transform Infra-Red (FTIR) analysis indicated that
the main functional groups involved in the sorption of copper to NaOH pretreated coco peat are the
hydroxyl, carboxyl and phenolic groups. Based on the results of this study, it was found that
pretreating coco peat with NaOH significantly improve the overall efficiency of coco peat in
removing Cu(II) by adsorption process.
"
AEJ 4:1 (2015)
Artikel Jurnal  Universitas Indonesia Library
cover
Harahap, Andrea Rizky Sabrina
"Penelitian adsorben untuk menghasilkan udara dengan kemurnian oksigen tinggi dilakukan menggunakan zeolit alam yang diimpregnasi tembaga oksida. Zeolit alam yang digunakan berasal dari Sidomulyo, South Lampung, Indonesia. Zeolit alam ini termasuk di dalam tipe klinoptilolit, yang biasanya juga disebut Zeolit Alam Lampung ZAL. Teknik pemurnian oksigen yang digunakan adalah Pressure Swing Adsorption PSA dengan tekanan operasi 4 bar. Beberapa variabel divariasikan untuk mendapatkan metode yang paling optimal untuk menghasilkan oksigen, seperti ukuran ZAL 18-100 mesh, persen loading CuO 0-1 -wt, dan konsentrasi asam sulfat 1-3 M. ZAL dikarakterisasi dengan metode BET, SEM-EDX, XRF, XRD, dan FTIR. Oksigen yang diproduksi dianalisis menggunakan GC.
Hasil menunjukkan bahwa ZAL dengan ukuran 60-100 mesh dan dipreparasi menggunakan asam sulfat 2 M mempunyai luas permukaan dan volume pori paling baik 64,374 m2/g dan 0,127 cm3/g. ZAL dengan ukuran 35-60 mesh dan dipreparasi menggunakan asam sulfat 1 M mempunyai hasil adsorpsi nitrogen yang paling optimum. Impregnasi oksida tembaga pada ZAL ditemui tidak menambah performa ZAL dalam menyerap nitrogen.

Investigation of an adsorbent to produce oxygen enriched air was carried out by using copper oxide CuO which is impregnated to natural zeolite. The natural zeolite used is from Sidomulyo, South Lampung, Indonesia. It is a clinoptilolite zeolite type, namely Zeolit Alam Lampung ZAL. Oxygen purification method applied is Pressure Swing Adsorption PSA technique with operating pressure of 4 bar. Several variables are varied to get the optimum method to produce the best quality of oxygen, such as size of ZAL 18 100 mesh , CuO loading percentage 0 1 wt, and the concentration of sulfuric acid 1 3 M. ZAL will be characterized using BET, SEM EDX, XRF, XRD, and FTIR methods. The oxygen produced will be analysed using GC method.
The result showed that ZAL with size 60 100 mesh and prepared using sulfuric acid of 2 M has the best surface area and pore volume to be impregnated, which is 64,374 m2 g dan 0,127 cm3 g, respectively. ZAL with size 35 60 mesh and prepared using sulfuric acid of 1 M has the most optimum trend of nitrogen adsorption. The impregnation of oxide of metal on the adsorbent is found not supporting the adsorbent itself to adsorb nitrogen better."
Depok: Fakultas Teknik Universitas Indonesia, 2017
S68091
UI - Skripsi Membership  Universitas Indonesia Library
cover
Muhammad Irfan Hasan
"Nanopartikel perak (NPP) hasil biosintesis telah diketahui mampu mendeteksi keberadaan logam berat secara kolorimetri, namun belum cukup selektif karena menghasilkan perubahan warna yang serupa pada beberapa logam. Selain itu, stabilitas dari indikator kolorimetri berbasis NPP hasil biosintesis masih harus ditingkatkan. Telah diketahui bahwa modifikasi NPP dengan ligan berupa polimer dapat berfungsi sebagai penstabil sekaligus mempengaruhi agregasi antarpartikel dengan larutan analit yang dikenal sebagai sensor agregasi. Penelitian ini dilakukan untuk meningkatkan selektivitas dan stabilitas indikator kolorimetri keberadaan logam dan melakukan pengembangan pada NPP yang telah termodifikasi agar meningkat sensitivitasnya secara kolorimetri. Biosintesis NPP dilakukan dengan cara mereaksikan larutan AgNO3 1 mM dengan air rebusan daun kering bisbul (Diospyros discolor Willd.) dengan rasio 10:1 (v:v). NPP yang terbentuk dimodifikasi dengan larutan polivinil alkohol (PVA) 1% (b/v) dan 2% (b/v). Prosedur peningkatan sensitivitas dari indikator dilakukan dengan penambahan garam Natrium Klorida (NaCl) 1 M. Selektivitas terbaik didapatkan di larutan nanopartikel perak yang dimodifikasi dengan PVA 1% (b/v) dengan perubahan warna menjadi ungu muda secara selektif pada analit Cu2+. NPP termodifikasi PVA juga ditingkatkan sensitivitasnya dengan prosedur terpilih, yaitu dengan mereaksikan NPPtermodifikasi dengan NaCl 1 M pada rasio 10:2 (v:v), diaduk dengan pengaduk magnetik selama 15 menit, lalu langsung digunakan untuk pengujian pada analit. Larutan indikator terbukti mampu mendeteksi keberadaan ion Cu2+ hingga 0,1 ppm secara visual dengan LOD 0,459 ppm berdasarkan kurva regresi spektrofotometer UV-Vis. Percobaan dilakukan berdasarkan perbedaan warnanya dengan larutan blangko (tanpa ion Cu2+) serta spektrofotometer UV-Vis. Aplikasinya pada sampel, diujicoba menggunakan sampel makroalga merah (Kappaphycus alvarezii) dengan preparasi menggunakan metode destruksi basah.

Silver nanoparticles, derived from biosynthesis method, have been known to detect heavy metals with colorimetry method, but their selectivity is not sufficient because they make similar changes in color to some metals. Besides, stability of colorimetric indicator, based on biosynthesized silver nanoparticles, still needed to be improved. It has been known that modification of silver nanoparticles with ligand, such as polymers, can be functioned as stabilizer and affects aggregation between particles and analyte solution. This research was conducted to improve the selectivity of colorimetric indicator for metals in analyte solution and to implement the development of modified silver nanoparticles to improve their sensitivity in colorimetry method. Biosynthesis of silver nanoparticles was conducted by reaction of AgNO3 1 mM solution with boiled water of velvet apple (Diospyros discolor Willd.) leaves in 10:1 (v:v) ratio. Then, silver nanoparticles are modified with polyvinyl alcohol (PVA) 1% (w/v) and 2% (w/v). Procedures to improve the sensitivity of indicator was conducted by addition of sodium chloride (NaCl) 1 M. Best selectivity was reached in silver nanoparticles solution that modified with PVA 1% (w/v) based on selective changes in color of Cu2+ analytes. Modified-silver nanoparticles? sensitivity has also been improved by chosen procedure, which is by reacted modified-silver nanoparticles with NaCl 1 M in 10:2 (v:v) ratio, stirred by magnetic stirrer in 15 minutes, then directly used to examine analyte solution. The indicator solution also has been proven that was able to detect Cu2+ ions up to 0,1 ppm as lowest concentration, and with LOD 0,459 ppm based on spectrophotometer UV-Vis. This test based on comparison with blank solution (without Cu2+ ions) and UV-Vis spectrophotometer in trial with red macroalga (Kappaphycus alvarezii) sample, which is prepared by wet destruction method."
Depok: Fakultas Farmasi Universitas Indonesia, 2012
S42115
UI - Skripsi Open  Universitas Indonesia Library
cover
Zelayna Claudia
"Dalam penelitian ini pengamatan berfokus pada penyelidikan peran ozone pada penyisihan tembaga (Cu) dari air limbah dengan adsorpsi menggunakan kitosan. Kitin adalah salah satu polisakarida alami yang paling melimpah yang dihasilkan oleh banyak organisme hidup, biasanya ditemukan sebagai komponen krustasean, setelah menjalani isolasi tertentu kitin dapat berubah menjadi kitosan (β-Poly (1-4) - 2-Amino-2-deoksi-ß-D-Glucan) yang memiliki sifat kimia yang lebih baik yang diperlukan sebagai bioadsorben. Pemisahan tembaga dari limbah cair menggunakan metode flotasi dan ozon sebagai diffuser, penggunaan ozon dikarenakan sifat oksidasi dan kelarutannya dalam air lebih besar dari udara. Selain itu, proses penyisihan tembaga yang dilakukan dibagi menjadi tiga variasi utama; ozonasi, kitosan dan gabungan kitosan dan ozon, dengan konsistensi kitosan; 1g/L, 2g/L dan 3 g/L. dan variasi konsentrasi tembaga pada 100 ppm, 200ppm, 300ppm dan 400 ppm. Hasil penelitian menunjukkan bahwa prosentase penyisihan tembaga dalam proses ozonisasi dan kitosan masing-masing hanya mencapai titik tertinggi pada 14,15% dan 44,58%, dimana kombinasi kedua metode mencapai 51,42%.

In this study the observation were mainly focus on the investigation of the significance of the copper (Cu) removal from wastewater by adsorption using chitosan and ozonation process. Furthermore, chitin is one of the most abundant natural polysaccharides produced by many living organisms; it is usually found as a component of crustacean shell, after undergoing specific isolations process chitin can be transform into the chitosan (β Poly-(1-4)-2-Amino-2-deoxy-ß-D- Glucan) which has a better chemical properties which necessary as a bioadsorbent Furthermore, separation of copper from wastewater was conducted by flotation method, ozone is used as diffuser because it is a stronger oxidant and more dissolvable in water than oxygen. Moreover, the process of the copper removal that is carried out is using a varied of ozone, chitosan and ozon-chitosan process, with the variation of chitosan used consitency at 1g/L, 2g/L and 3 g/L. and the variation of copper concentration at 100 ppm, 200ppm, 300ppm and 400 pm. The results indicated that the precentage removal of copper in ozonation process only and chitosan only reach its highest point at 14.15% and 44.58% respectivelly, where the combination of both method reach 51.42%."
Depok: Fakultas Teknik Universitas Indonesia, 2013
S47713
UI - Skripsi Membership  Universitas Indonesia Library
cover
cover
Mahfuzhoh Karimah
"Pemilihan jenis adsorben merupakan hal penting dalam proses adsorpsi. Adsorben yang paling sering digunakan adalah karbon aktif karena memiliki luas permukaan yang besar sehingga daya adsorpsinya lebih besar dari pada adsorben lainnya. Pada penelitian pembuatan karbon aktif dari ampas tebu ini dilakukan dengan metode aktivasi menggunakan gas CO2. Dengan laju alir gas CO2 300 ml/menit, 400 ml/menit, dan 500 ml/menit. Aktivasi dilakukan pada temperatur 700 °C, 800 °C,dan 900 °C selama 2 jam. Ampas tebu dipilih karena mengandung karbon yang cukup. Selain itu, ketersediaan ampas tebu melimpah di Indonesia dan sebagai representatif dari sumber daya alam yang terbarukan. Karbon aktif yang diperoleh dikarakterisasi luas permukaannya. Proses dengan aktivasi CO2 ini diharapkan dapat diperoleh karbon aktif dengan luas permukaan yang cukup tinggi sehingga akan membantu dalam proses adsorpsi. Hasil yang diperoleh menunjukkan bahwa semakin tinggi waktu aktivasi dan laju alir CO2, maka luas permukaan yang direpresentasikan dengan bilangan iod semakin meningkat. Luas permukaan karbon aktif tertinggi yang direpresentasikan dengan bilangan iod sebesar 730 mg/g diperoleh dengan aktivasi pada laju alir CO2 sebesar 500 mL/menit dan temperatur aktivasi 900°C.

Selection type of adsorbent is important in the adsorption process. The most commonly used adsorbent is activated carbon because it has a large surface area so that the adsorption energy is greater than the other adsorbents. To study the manufacture of activated carbon from bagasse was carried out by the method of activation using carbon dioxide gas. With CO2 flow rate 300 mL/min, 400 mL/min, and 500 mL/min. Activation is done at a temperature of 700 °C, 800 °C, and 900 °C. Bagasse chosen because they contain enough carbon. Moreover, the availability of bagasse abundant in Indonesia and as a representative of a renewable natural resource. Activated carbon were then characterized its surface area. With carbon dioxide activation process is expected to obtain activated carbon with high surface area that will help in the process of adsorption. The results showed that the higher the activation time and the flow rate of CO2, the surface area represented by the iodine number is increasing. The surface area of activated carbon is represented by the highest iodine number of 730 mg / g obtained by activation of the CO2 flow rate of 500 mL / min and a temperature of 900 ° C."
Depok: Fakultas Teknik Universitas Indonesia, 2013
S46855
UI - Skripsi Membership  Universitas Indonesia Library
cover
Minhatul Maula
"Pencemaran air merupakan dampak negatif dari berkembangnya aktivitas perindustrian. Limbah dari proses industri dapat mengandung zat warna hingga mencapai 10 %. Oleh karena itu, penting untuk mengetahui metode penanganan limbah tersebut. Adsorpsi merupakan metode yang efektif dan efisien untuk menangani kontaminasi zat warna dalam lingkungan perairan. Kertas koran bekas berpotensi menjadi adsorben zat warna karena banyak mengandung selulosa. Pada penelitian ini, serat koran bekas (WNF) dimodifikasi dengan nanokitosan (NCH) untuk meningkatkan kemampuannya dalam mengadsorpsi zat warna congo red. WNF diperoleh setelah proses deinking menggunakan NaOH 4 %. NCH dengan ukuran partikel 123,8 nm dibuat dengan melarutkan kitosan dalam larutan asam asetat 1,67 x 10-2 M. Modifikasi WNF dengan NCH mencapai kondisi optimum pada rasio 0,01 g WNF/mL NCH. Proses adsorpsi congo red menggunakan WNF/NCH berlangsung baik pada pH 5,0. Kondisi kesetimbangan proses adsorpsi tercapai dalam waktu 10 menit. Kapasitas adsorpsi maksimum dari WNF/NCH sebesar 33,502 mg g-1 dengan menggunakan massa WNF/NCH 0,075 g dan konsentrasi awal congo red 400 mg L-1. Proses adsorpsi mengikuti model isoterm adsorpsi Langmuir dan kinetika adsorpsi orde dua semu. Hasil menunjukkan WNF/NCH dapat menjadi alternatif adsorben rendah biaya dalam penanganan limbah zat warna.

Water pollution is a negative effect emerged by industrial activities. These industries produce wastewater containing about 10 % dye stuffs. Adsorption has been considered to be the most effective and efficient process for treating dye contaminants in wastewater. Waste newspaper which is mainly consists of cellulose was found to be a potential adsorbent for dye removal. In this research, waste newspaper fiber (WNF) was modified by nanochitosan (NCH) to improve its ability for removal of congo red from aqueous medium. WNF was obtained after deinking treatment using 4 % NaOH. NCH with particle size of 123.8 nm was formed by dissolving chitosan particle in 1.67 x 10-2 M acetic acid solution. Modification of WNF using NCH reached optimum condition at ratio 0.01 g WNF/mL NCH. Adsorption study indicated that pH 5.0 favored the adsorption of congo red using WNF/NCH. The equilibrium condition was reached within 10 minutes. The maximum capacity of WNF/NCH for adsorption of congo red was 33.502 mg g-1 under dose of 0.075 g and initial concentration of 400 mg L-1. The adsorption process and equilibrium of congo red were well fitted by a pseudo-second order kinetic model and Langmuir isotherm, respectively. The results showed that nanochitosan-modified waste newspaper fiber may be utilized as a low cost adsorbent for dye-contaminated wastewater treatment."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
S57191
UI - Skripsi Membership  Universitas Indonesia Library
cover
Ricky Yuwono Pahlawan
"Kadmium merupakan salah satu logam berat bersifat toksik bagi kehidupan manusia. Dalam konsentrasi yang sangat rendah, logam kadmium tidak dapat ditentukan menggunakan instrumen dengan mudah. Ion Imprinted Polymer (IIP) digunakan untuk mengenali dan memisahkan logam berat. Prinsip kerja dari IIP adalah dengan metode trapping dalam matriks polimer yang terikat silang dengan agen pengkelat. Dalam penelitian ini, IIP melalui metode polimerisasi bulk dengan ion logam kadmium sebagai template, 8-hydroxyquinoline sebagai ligan, MMA sebagai monomer fungsional, EGDMA sebagai crosslinker, dan AIBN sebagai inisiator berhasil disintesis. Pengaruh rasio campuran ligan dan monomer (1:1, 1:2, dan 1:3) terhadap IIP dipelajari pada penelitian ini. Produk IIP dikarakterisasi menggunakan AAS, FTIR, SEM, dan TGA. Kapasitas adsorpsi IIP mencapai kemampuan optimumnya pada pH 6 dengan waktu kontak 60 menit. IIP dengan rasio 1:2 memiliki mekanisme adsorpsi sesuai dengan persamaan Freundlich dengan R2 0.9214 dan kapasitas adsorpsi maksimum sebesar 335.58 mg/g untuk IIP dan 105.46 untuk NIP. Model kinetika adsorpsi dari IIP dan NIP mengikuti model kinetika orde pseudo pertama dengan R2 0.9722. Hasil tersebut menunjukkan mekansime adsorpsi IIP terjadi pada tahap awal reaksi. IIP menunjukkan selektifitas yang baik terhadap ion Cd(II) dengan adanya interferensi logam Pb dan Cr.

Cadmium become one of toxic heavy metals that can be dangerous for human lives. At very low concentration, cadmium cannot be determined by instrument easily. Ion Imprinted Polymer (IIP) is used to recognize and separating heavy metal ion that works with trapping method in polymer matrices that are crosslinked with chelating agent. In this research, IIP via bulk polymerization with cadmium ion as template, 8-Hydroxyquinoline as ligand, methyl methacrylate as functional monomer, EGDMA as Crosslinker, and AIBN as Initiator was successfully synthesized. The effect of ratio of ligand and monomer (1:1, 1:2, 1:3) to IIP was studied. The synthesized IIP was characterized by AAS, FTIR, SEM, and TGA. Adsorption capacity of IIP reach optimum capacity at pH 6 with 60 minutes contact time. IIP with ratio 1:2 has the adsorption mechanism of both IIP and NIP followed to the Freundlich equation with R2 0.9214 and maximum adsorption capacity of Cd(II) was 335.58 mg/g for IIP and 105.46 mg/g for NIP respectively. Furthermore the kinetics model followed the pseudo first order with R2 0.9722, this results show that the adsorption mechanism took place on initial time of adsorption. IIP exhibited good selectivity to Cd2+ ions in the presence of Pb2+ and Cr3+ interferences."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Sitorus, Paulus Pardamean Rinaldo
"Zeolit alam Lampung telah berhasil dimodifikasi menjadi TETA-Zeolit dengan menggunakan triethylenetetramine. Karakterisasi senyawa dilakukan menggunakan FTIR, XRD dan EDS. Studi adsorpsi ion logam dilakukan menggunakan AAS dan UV-Visible. Sebelum preparasi, dilakukan aktivasi zeolit menggunakan teknik aktivasi fisik dan kimia, lalu kationnya diseragamkan dengan Na+ (menjadi Na-zeolit). Dengan menggunakan metode kompleks tembaga amin diperoleh nilai KTK Na-zeolit sebesar 0,5318 mek/100 gram zeolit dan dengan metode metilen blue diperoleh nilai KTK sebesar 0,0939 mek/100 gram zeolit.
Keberhasilan modifikasi zeolit menggunakan triethylenetetramine dapat dilihat dari karakterisasi yang dilakukan membuktikan adanya atom karbon dalam senyawaan. Aplikasinya sebagai adsorben dilakukan dengan 3 variasi. Variasi konsentrasi triethylenetetramine dimana konsentrasi terbesar merubah pola daya adsorpsi zeolit secara signifikan. Variasi waktu dimana pada menit diatas 30 menit, daya serap TETA-Zeolit sudah tidak banyak berubah. Dan variasi konsentrasi adsorbat, dimana kemampuan adsorbsi TETA-Zeolit lebih tinggi dibandingkan zeolit lainnya.

Natural zeolit obtained from Lampung, has been modified into TETA-Zeolit using triethylenetetramine. Compound characterization performed using XRD, FTIR and EDS. Adsorption studies performed using AAS and UV-Visible. Before preparation, zeolit is activated using physical and chemical activation. After that, all cation from zeolit exchanged with Na+. Using copper amine complex method and methylene blue, the cation exchange capacity obtained are 0,5318 meq/100 gram zeolite and 0,0939 meq/100 gram zeolite, respectively.
The success of modification triethylenetetramine into zeolite can be seen from characterization where carbon atoms can be seen in compounds. Its application as an adsorbent is done with three variations. Variation of triethylenetetramine concentration, where the biggest concentration of triethylenetetramine changing adsorption power of zeolite significantly. Variation in time, where in minutes over 30 minutes, TETA-Zeolite adsorption has not changed much. Variation of the concentration of adsorbate, where TETA-Zeolite adsorption capability is higher than other zeolite.
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
S57140
UI - Skripsi Membership  Universitas Indonesia Library
cover
Fuaddilabib Muhammad
"Pencemaran lingkungan merupakan salah satu masalah yang di Indonesia, salah satunya ialah pencemaran lingkungan air oleh zat warna dari industri tekstil dan pakaian. Zat warna merupakan salah satu polutan organik yang keberadaannya sangat berbahaya bagi lingkungan dan ekosistem air karena dapat menyebabkan keracunan, perubahan mutagenik pada makhluk hidup bahkan kematian. Metode adsorpsi dinilai paling efektif untuk mengurangi pencemaran air dan memiliki berbagai macam adsorben dengan penggunaan dan bahan yang mudah serta memiliki nilai efesiensi tinggi. Pada penelitian ini disintesis karbon aktif berasal dari bahan alam, yaitu limbah tandan kosong kelapa sawit yang dimodifikasi ukuran porinya menggunakan silika gel bekas sebagai template dan menggunakan gugus sulfonat di permukaannya. Pada penelitian ini sintesis karbon aktif dengan metode hard template dan untuk pori diisi oleh ekstrak silika dari kaolin. Hasil sintesis diaplikasikan sebagai adsorben dengan methylene blue dan rhodamine B dalam air. Hasil sintesis dikarakterisasi menggunakan FTIR, XRD, BET, dan SEM-EDX untuk mengetahui ikatan kimia, morfologi, dan luas permukaan. Aplikasi adsorpsi zat warna methylene blue dan rhodamine B mencapai kapasitas adsorpsi maksimum pada pH 9 dan waktu kontak 60 menit pada adsorpsi karbon aktif dan karbon aktif tersulfonasi pada methylene blue dan pada pH 5 dan waktu kontak 60 menit pada adsorpsi karbon aktif dan karbon aktif tersulfonasi.

Environmental pollution is one of the problems in Indonesia, one of which is the pollution of the water environment by dyes from the textile and clothing industry. Dyes are one of the organic pollutants whose existence is very dangerous for the environment and aquatic ecosystems because they can cause poisoning, mutagenic changes in living things and even death. The adsorption method is considered the most effective for reducing water pollution and has various kinds of adsorbents with easy use and materials and has a high efficiency value. In this study, activated carbon was synthesized from natural materials, namely empty palm fruit bunches waste which modified its pore size using used silica gel as a template and using sulfonate groups on its surface. In this study, the synthesis of activated carbon was carried out using the hard template method and the pores were filled with silica extract from kaolin. The result of the synthesis was applied as an adsorbent with methylene blue and rhodamine B in water. Synthesis results were characterized using FTIR, XRD, BET, and SEM-EDX to determine chemical bonding, morphology, and surface area. The adsorption application of methylene blue and rhodamine B dyes achieved maximum adsorption capacity at pH 9 and a contact time of 60 minutes for the adsorption of activated carbon and sulfonated activated carbon on methylene blue and at pH 5 and a contact time of 60 minutes for the adsorption of activated carbon and sulfonated activated carbon.
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2022
S-pdf
UI - Skripsi Membership  Universitas Indonesia Library
<<   1 2 3 4 5 6 7 8 9 10   >>