Hasil Pencarian  ::  Simpan CSV :: Kembali

"ABSTRAKTesis ini membahas perilaku korosi dari pengelasan dissimilar antara baja karbon ASTM A36 dan baja tahan karat SS316L dengan kawat las E309L menggunakan prosedur pengelasan SMAW dan GTAW untuk dibagian root. Plat baja tahan karat dan baja karbon dengan ketebalan 10 mm dan 15 mm dilas, dipotong, diberi perlakuan panas tempering, dilakukan pengamatan mikrostruktur dan kemudian diuji secara elektrokimia. Pengujian secara elektrokimia meliputi uji electro impedance spectra (EIS), Potentiodynamic Polarization, Cyclic Voltametry. Oleh karena inti las baja tahan karat biasanya lemah terhadap korosi terlokalisasi, maka uji celup korosi sumuran ASTM G48 metode A dilakukan demi pengujian menyeluruh perilaku korosi pada pengelasan dissimilar ini. Hasilnya menunjukkan bahwa proses tempering akan meningkatkan ketahanan korosi pengelasan dissimilar. Pengelasan dissimilar tebal plat 15 mm menunjukkan ketahanan korosi yang lebih lemah dibandingkan plat 10 mm, dimana setelah diamati jumlah weld pass yang lebih banyak pada plat 15 mm mempengaruhi struktur mikro dan ketahanan korosi dari pengelasan dissimilar.

---

ABSTRACT

The focus of this study was addressed to observe corrosion behavior at dissimilar metal welding between carbon steel ASTM A36 and stainless steel 316L with E309L as weld consumables using SMAW and GTAW procedure at root weld. Stainless steel and carbon steel plate of 10 mm and 15 mm thickness were welded, cut, heat treated (tempered), observed for microstructure and then tested electrochemically. Electrochemical testing included electro impedance spectra (EIS), Potentiodynamic Polarization, Cyclic Voltametry. The core welding of stainless steels are known vulnerable to localized corrosion, hence the pitting corrosion immersion test ASTM G48 method was done for a thorough observation of welding dissimilar corrosion behavior. The results showed that the tempering process improved corrosion resistance of dissimilar weld. It was observed that dissimilar welding of 15 mm thickness was more susceptible than plate 10 mm. It is related to the number of weld passes which affect the microstructure and corrosion resistance of the weld dissimilar."

"Proses dissimilar welding dapat menguntungkan biaya operasional pada berbagai industri namun memiliki kelemahan karena timbulnya tegangan sisa dan fenomena weld decay pada material. Untuk mengatasi hal tersebut dikembangkan metode proses perlakuan panas pasca pengelasan atau post-weld heat treatment menggunakan temperatur yang berbeda pada tiap logam yang disebut sebagai PWHT terkontrol. Pada penelitian ini, akan diamati pengaruh PWHT terkontrol terhadap distribusi nilai kekerasan, struktur mikro, dan korosi batas butir pada sambungan las dissimilar baja tahan karat TP 304 dengan baja tahan panas P.11 yang dilas menggunakan metode gas tungsten arc welding (GTAW). Pengujian yang dilakukan pada daerah penyambungan meliputi pengujian hardness vickers, pengujian metalografi, dan pengujian ASTM A262 practice E. Hasil dan analisis dari penelitian ini menunjukkan bahwa PWHT terkontrol mampu mencegah terjadinya fenomena weld decay pada baja tahan karat TP 304. Hal ini ditunjukkan dari hasil pengujian dimana PWHT terkontrol mampu menstabilkan distribusi kekerasan, mencegah pembentukan presipitasi karbida pada batas butir, dan proses difusi antar logam.

---

Dissimilar welding offers operational cost benefits across various industries but is hindered by residual stress and weld decay phenomena. To mitigate these issues, a method known as controlled post-weld heat treatment (PWHT) has been developed, utilizing different temperatures for each metal. This study investigates the impact of controlled PWHT on hardness distribution, microstructure, and intergranular corrosion in dissimilar weld joints of TP 304 stainless steel and P.11 heat-resistant steel, joined using the gas tungsten arc welding (GTAW) technique. The welded joints were subjected to Vickers hardness testing, metallographic analysis, and ASTM A262 practice E testing. The results indicate that controlled PWHT effectively prevents weld decay in TP 304 stainless steel. This is evidenced by the stabilization of hardness distribution, inhibition of carbide precipitation at grain boundaries, and enhanced diffusion between the metals."

"Kemajuan teknologi mendorong berbagai industri untuk menggunakan sambungan material baja tahan karat asutenitik AISI 316L dan baja karbon feritik ASTM A36, yang dapat mengoptimalkan kinerja dan mengurangi biaya produksi. Namun, perbedaan material pada dissimilar welding ini pastinya akan memiliki kecenderungan terjadinya korosi galvanik berkaitan dengan potensial elektrokimia dan komposisi kimia yang berbeda. Salah satu metode penyambungan yang umum digunakan adalah pengelasan TIG yang memakai filler metal untuk menyambungkan kedua material. Pada penelitian ini menggunakan tiga jenis logam pengisi yang berbeda, yaitu ER308LSi, ER309L, dan ER316L. Variasi logam pengisi yang digunakan untuk penyambungan kedua material tersebut telah diteliti dan ditelaah hubungannya terhadap perilaku korosi. Untuk mendukung analisis dan pembahasan penelitian, dilakukan pengujian komposisi kimia, pengamatan mikrostruktur, dan pengujian Linear Polarization Resistance (LPR). Hasil penelitian menunjukkan bahwa logam pengisi ER309L memberikan kinerja korosi yang paling optimal dibandingkan dengan ER308LSi dan ER316L. Analisis hasil penelitian ini mengungkapkan bahwa komposisi kimia, terutama unsur Cr dan Mo, serta fasa mikrostruktur yang terbentuk pada logam pengelasan berperan penting dalam menentukan perilaku korosi, khususnya pada hasil daerah pengelasan.

---

Technological advancements are driving various industries to use the joint materials of austenitic stainless steel AISI 316L and ferritic carbon steel ASTM A36 to optimize performance and reduce production costs. However, the material differences in dissimilar welding tend to induce galvanic corrosion due to differing electrochemical potentials and chemical compositions. One commonly used joining method is TIG welding, which employs filler metal to connect the two materials. This study utilized three different filler metals, ER308LSi, ER309L, and ER316L, to examine their effects on corrosion behaviour in the welded joint. Chemical composition testing, microstructure observation, and Linear Polarization Resistance (LPR) testing were conducted to support the analysis and discussion. The results indicated that the ER309L filler metal provided the most optimal corrosion performance compared to ER308LSi and ER316L. The study revealed that chemical composition, particularly the elements Cr and Mo, as well as the microstructural phases formed in the weld metal, play a crucial role in determining corrosion behaviour, especially in the weld area."

"ABSTRAKKemajuan Teknologi dalam hal ini mendorong pertumbuhan industriindustrialat berat beserta fasilitas-fasilitas lainnya. Proses penyambungan materialdengan pengelasan memegang peran penting dalam proses pembuatan danperawatan fasilitas-fasilitas di industri. Material yang digunakan dalam pembuatanalat-alat di industri tentunya tidak hanya satu jenis saja, begitupun prosespengelasan yang dilakukan tidak dalam satu posisi saja. Baja tahan karataustenitik 304 banyak digunakan dalam aplikasi di industri karena harganya yangmurah, memiliki ketahanan korosi yang baik, dan kemampulasan yang bagus.Akan tetapi, baja tahan karat austenitik 304 akan menurun ketahanan korosinyajika mengalami sensitisasi, yaitu terbentuknya senyawa krom karbida di batasbutir, yang menyebabkan serangan korosi di sekitar batas butir. Dalam Penelitianini, dilakukan percobaan pengelasan antara pelat baja tahan karat austenitik 304dengan baja karbon A36 dengan variasi ketebalan pelat 6 mm, 8 mm, 10 mm, dan12mm, dengan variasi posisi pengelasan 1G (datar), 2G (horisontal), dan 3G(vertikal). Hasil percobaan akan dilihat pengaruhnya terhadap terbentuknyasensitisasi dengan mengacu pada standar ASTM A262. Hasilnya menunjukkansensitisasi paling minim terjadi pada pengelasan pelat 10 mm dan 12 mm denganposisi 1G dan pada ketebalan 10 mm dan 12 mm dengan posisi 2G. Sedangkantingkat sensitisasi akan maksimum pada proses pengelasan dengan posisi 3G disemua ketebalan 6mm, 8 mm, 10 mm, dan 12 mm.

---

AbstractTechnology Advancement in this regard encourages the growth of heavyindustries along with other facilities. Joining material in the welding process playsan important role in the process of manufacture and maintenance facilities in theindustry. Materials used in the manufacture of tools in the industry is certainly notjust one type, as well as the welding process is carried out not in one positiononly. 304 austenitic stainless steels are widely used in industrial applicationsbecause it is cheap, has good corrosion resistance, and good weldability.However, corrosion resistance of austenitic stainless steels 304 will be reduced ifexperience sensitization, it is the formation of chromium carbide compounds inthe grain boundaries, leading to corrosion attack around the grain boundaries. Inthis study, conducted experiments the welding of austenitic stainless steel plate304 with A36 carbon steel plate with thickness 6 mm, 8 mm, 10 mm, and 12mm,with a variety of welding positions 1G (flat), 2G (horizontal), and 3G (vertical).The experimental results will be looked its influence on the formation ofsensitization with reference to ASTM A262 standards. The results show the mostminimal sensitization occurs in the welding plates 10 mm and 12 mm with theposition of 1G and the thickness of 10 mm and 12 mm in 2G position. While thelevel of sensitization will be maximum at the position of the welding process with3G in all the thickness of 6 mm, 8 mm, 10 mm, and 12 mm."

"Pembangunan infrastruktur di Indonesia membutuhkan banyak penyambungan material dengan berbagai metode pengelasan yang efektif. Teknologi ini dikembangkan untuk dapat melakukan pengelasan logam berbeda jenis atau umum disebut Dissimilar Metal Welding (DMW), seperti baja karbon dengan baja tahan karat. Proses ini dapat dilakukan menggunakan metode pengelasan Gas Tungsten Arc Welding (GTAW) dengan kontrol masukan panas yang efisien. Penyambungan A36 dengan SS316L menggunakan logam pengisi ER309L menjadi opsi yang dapat dilakukan untuk membentuk material unggul yang benefisial dan aplikatif. Hasil pengelasan DMW akan mempengaruhi sifat mekanik yang dihasilkan dengan memperhatikan dilusi dan sudut kampuh sebagai faktor yang mempengaruhinya, seperti V Groove 75 ̊, V Groove 60 ̊, dan Single Bevel Groove 30 ̊. Berdasarkan hasil pengujian, didapatkan bahwa semakin besar sudut kampuh akan menghasilkan persentase dilusi yang semakin rendah dengan pembentukan kandungan delta ferit yang semakin besar.

---

Infrastructure development in Indonesia requires a lot of material joining with various effective welding methods. This technology was developed to be able to weld different types of metals or commonly called Dissimilar Metal Welding (DMW), such as carbon steel with stainless steel. This process can be performed using Gas Tungsten Arc Welding (GTAW) method with efficient heat input control. Joining A36 with SS316L using ER309L filler metal is an option that can be done to form superior materials that are beneficial and applicable. DMW welding results will affect the mechanical properties produced by considering dilution and the angle of the seam as influencing factors, such as V Groove 75 ̊, V Groove 60 ̊, and Single Bevel Groove 30 ̊. Based on the test results, it is found that the larger the angle of the groove will result in a lower percentage of dilution with the formation of a larger delta ferrite content. "

"Penelitian ini didasarkan pada kebutuhan untuk menggabungkan material dengan sifat mekanik yang berbeda guna memperoleh sifat mekanik gabungan yang lebih baik dan biaya yang lebih rendah, yang sering digunakan dalam berbagai industri, seperti industri petrokimia, minyak dan gas, pembangkit listrik, serta otomotif. Penelitian ini dilakukan untuk memahami pengaruh variasi logam pengisi terhadap mikrostruktur dan nilai kekerasan pada penyambungan baja tahan karat 316L dan baja karbon rendah A36 menggunakan metode pengelasan Tungsten Inert Gas (TIG). Pengelasan dua jenis material dilakukan dengan menggunakan tiga variasi logam pengisi, yaitu ER309L, ER316L, dan ER308LSi. Pengujian yang dilakukan meliputi pengujian mikrostruktur menggunakan mikroskop optik, pengujian kekerasan dengan metode microvickers, serta analisis unsur kimia menggunakan pengujian OES. Hasil penelitian menunjukkan bahwa variasi logam pengisi mempengaruhi mikrostruktur dan nilai kekerasan pada daerah lasan dan Heat Affected Zone (HAZ). Salah satu hasil signifikan dari penelitian ini adalah bahwa penggunaan logam pengisi ER309L menghasilkan nilai kekerasan yang lebih tinggi dan mikrostruktur yang lebih halus pada sambungan las dibandingkan dengan logam pengisi lainnya. Hal ini menunjukkan bahwa pemilihan logam pengisi yang tepat sangat penting untuk meningkatkan kualitas sambungan las pada material dengan karakteristik yang berbeda.

---

This research is based on the necessity to combine materials with different mechanical properties to achieve better combined mechanical properties and lower costs, which are frequently used in various industries, such as petrochemical, oil and gas, power generation, and automotive industries. This study aims to understand the effect of filler metal variation on the microstructure and hardness values in the welding of 316L stainless steel and low carbon steel A36 using the Tungsten Inert Gas (TIG) welding method. The welding of the two types of materials was conducted using three variations of filler metals, namely ER309L, ER316L, and ER308LSi. The tests conducted included microstructure analysis using an optical microscope, hardness testing using the microvickers method, and chemical element analysis using OES testing. The results showed that the variation in filler metals affects the microstructure and hardness values in the weld area and the Heat Affected Zone (HAZ). One of the significant findings of this study is that the use of ER309L filler metal resulted in higher hardness values and a finer microstructure in the weld joint compared to the other filler metals. This indicates that the appropriate selection of filler metal is crucial for improving the quality of weld joints in materials with different characteristics."

"Penyambungan dua jenis material merupakan salah satu tantangan dalam industri manufaktur. Salah satu aplikasinya dilakukan pada penyambungan antara pipa baja tahan karat Dupleks 2205 disambungkan dengan pelat baja HY80 yang banyak dipakai bahan bakar kapal selam. Pengelasan menggunakan SMAW (Shielded Metal Arc Welding) dilakukan karena merupakan pengelasan yang paling efisien dan baik bagi baja paduan. Setelah proses pengelasan dilakukan pengujian radiografi menggunakan sinar X, pengukuran tegangan sisa dengan hamburan neutron untuk mengukur ketahanan sisa di dalam serta menggunakan hamburan sinar X untuk pengukuran tegangan sisa di permukaan, selanjutnya untuk melengkapi data dilakukan juga pengujian kekerasan material dan pengambilan gambar struktur mikro atau metalografi, serta uji tekuk untuk mengetahui kekuatan hasil lasan. Hasil pengujian menunjukkan bahwa masukan panas yang lebih tinggi selain menghasilkan ukuran butir yang lebih besar, ternyata juga menghasilkan karbida yang lebih banyak sehingga kekerasannya lebih tinggi. Tingginya nilai kekerasan akan memberikan efek terhadap nilai tegangan sisa, kekerasan yang tinggi dihasilkan dari tegangan yang bersifat kompresi, sementara tegangan sisa bersifat tarik akan menghasilkan kekerasan yang rendah.

 

---

Joining two types of material is one of the challenges in the manufacturing industry. One application is carried out on the connection between HY80 steel plates connected with Duplex 2205 stainless steel pipes which are widely used as submarine fuel. Welding using SMAW (Shielded Metal Arc Welding) is done because it is the most efficient and good welding for alloy steel. After the welding process, radiographic testing using X-rays is carried out, the residual stress measured at the surface (using X ray diffraction) and in the middle of the metal (using neutron diffraction), hardness checked, metallography, and buckling test are also done to determine the strength of weld results. The test results show that higher heat input in addition to producing larger grain sizes, it also produces more carbides so that the hardness is higher. The high value of hardness will have an effect on the value of residual stress, high hardness is produced from compressive stress, while the tensile residual stress will produce low hardness.

 

"