"Mekanisme inhibisi korosi pada ekstrak biji saga Abrus precatorius pada baja API 5L Grade B dalam larutan 1M HCl telah dipelajari menggunakan metode polarisasi potensiodinamik dan Electrochemical Impedance EIS pada variasi konsentrasi 2 ml, 4 ml, 6 ml, 8 ml, dan 10 ml. Kandungan flavonoid diidentifikasi terdapat pada ekstrak biji saga melalui pengujian FTIR. Hasil penelitian menunjukkan bahwa kenaikan laju korosi menurun seiring dengan penambahan ekstrak biji saga. Ekstrak biji saga dapat berperan sebagai inhibitor korosi dengan efisiensi maksimum 86 pada pengujian polarisasi potensiodinamik dan 66 pada pengujian EIS. Ekstrak biji saga tergolong ke dalam inhibitor campuran dengan dominan inhibitor katodik. Adsorpsi dari ekstrak biji saga pada permukaan logam sesuai isoterm adsorpsi Langmuir dengan mekanisme adsorpsi fisika.

---

Mechanism of corrosion inhibition on saga Abrus precatorius seed extract on API 5L Grade B in 1M HCl solution has been studied using potentiodynamic polarization and electrochemical impedance spectroscopy EIS with variation concentration of 2 ml, 4 ml, 6 ml, 8 ml, and 10 ml. Flavonoid content in saga seed was identified by FTIR.

The results showed corrosion rate increased with a decrease inhibitor concentration of saga seed extract. Saga seed extract acts as a corrosion inhibitor with maximum efficiency 86 using potentiodynamic polarization and 66 using EIS. Saga seed extract acts as mixed type inhibitor with cathodic inhibitor dominant. Adsorption of saga seed extract on metal surface obeyed Langmuir adsorption isotherm by physical adsorption mechanism."

"Indonesia kaya akan sumber daya alam, terutama daun salam dan cengkeh yang telah terbukti memiliki memiliki sifat antioksidant yang tinggi. Sifat antioksidan ini dapat dimanfaatkan juga sebagai inhibitor korosi ramah lingkungan. Tujuan penelitian mempelajari dan menganalisa pengaruh penambahan ekstrak daun salam dan minyak cengkeh serta campuran keduanya sebagai inhibitor ramah lingkungan pada baja karbon API 5L grade B di larutan HCl 1M. Metode pengujian adalah uji polarisasi dan EIS dengan konsentrasi penambahan ekstrak berbeda, yaitu 13 ml/L, 26 ml/L, 40 ml/L dan 53 ml/L untuk tiap ekstrak dan konsentrasi ekstrak campuran 13 ml/L dengan perbandingan komposisi yaitu 1:1, 1:2, 1:3, 2:1 dan 3:1. Pengujian FTIR juga dilakukan untuk mengetahui golongan senyawa aktif pada lapisan pelindung yang terbentuk. Hasil pengujian Polarisasi didapatkan efisiensi inhibitor tertinggi yang dari ekstrak daun salam adalah EI = 86.27 pada konsentrasi 53 ml/L dan dari minyak cengkeh adalah EI = 82.15 dengan laju pada konsentrasi 53 ml/L. Sementara itu pada ekstrak campuran dari daun salam dan minyak cengkeh didapat efisiensi inhibitor tertinggi EI = 91.51 dengan rasio pencampuran 1:2. Mekanisme inhibisinya diperkirakan secara fisik dan chemisorption. Pengujian FTIR diperkirakan lapisan senyawa aktif yang berperan sebagai lapisan pelindung pada permukaan sampel adalah Flavanoid dan Eugenol.

---

Bay leaf and clove oil are very abundant in Indonesia, and have been proven that they have antioxindant and anti aging effect. The antioxidant properties can be utilized as well as environmentall friendly corrosion inhibitor. The aim of this research is to study and analyze the effect of bay leaf extract and cloves oil and a mixture of both as an corrosion inhibitor. Electrochemical polarization test and EIS test were used ini measuring the inhibitor efficiency at a different concentration of extract i.e 13 ml L, 26 ml L, 40 ml L and 53 ml for each extracts, and 13 ml L for their mixture with a composition ratio of bay leaf extract to clove oil, 1 1, 1 2, 1 3, 2 1 and 3 1.

The highest efficiency inhibitor of indonesian bay leaf extract was 86.27 at concentration 53 ml L and for clove oil extract obtained 82.15 at concentration 40 ml L. The addition of their mixture showed good interaction with efficiency inhibitor 91.51 at composition ratio 1 2. FTIR test result on sample which was immersed in HCl 1 M solution had identified primarily the presence of phenolic compound group tannin, flavanoid with bay leaf extract and eugenol compound on clove oil extract."

"Efek penghambatan dari ekstrak Curcuma xanthorhizza pada korosi baja API 5L Grade X42 dalam larutan HCl 1M diselidiki dengan menggunakan metode kehilangan berat, polarisasi tafel, dan metode electrochemical impedance spectroscopy EIS . Uji FTIR digunakan untuk menyelidiki senyawa antioksidan yang berperan penting dalam menghambat korosi. Dalam penelitian ini konsentrasi ekstrak temulawak yang digunakan adalah 0 ppm, 100 ppm, 250 ppm, 500 ppm, dan 1000 ppm.Hasilnya menunjukkan bahwa temulawak dapat menghambat korosi pada baja dan bertindak sebagai penghambat tipe campuran. Laju korosi menurun seiring dengan meningkatnya konsentrasi inhibitor. Sedangkan efisiensi inhibisi meningkat dengan meningkatnya konsentrasi inhibitor. Adsorpsi ekstrak pada permukaan baja mengikuti Langmuir isotherm. Nilai energi bebas ?Gads menunjukkan bahwa adsorpsi molekul inhibitor secara fisika. Dapat disimpulkan bahwa ekstrak Curcuma xanthorhizza dapat digunakan sebagai penghambat alternatif dan ramah lingkungan untuk baja API 5L Grade X42 di lingkungan asam.

---

The inhibitory effect of the extract of Curcuma xanthorhizza on the corrosion of API 5L Grade X42 steelin HCl 1M solution was investigated by using weight loss, tafel polarization, and electrochemical impedance spectroscopy methods.FTIR test was used to investigate the antioxidant compound that plays an important role to inhibit corrosion.In this study the concentration of Curcuma xanthorhizza extract used was 0 ppm, 100 ppm, 250 ppm, 500 ppm, and 1000 ppm.

The results show that Curcuma xanthorhizza inhibit the steel corrosion and act as mixed type inhibitors. The corrosion rate decreases with the increasing of inhibitors concentrations. At the same time, inhibition efficiency increases with the increase of inhibitors concentrations.The adsorption of extract on the steel surface was found to obey Langmuir rsquo s adsorption isotherm. The free energy value Gads indicated that the adsorption of inhibitor molecules was typical of physisorption.It can be concluded that Curcuma xanthorhizza extract could be used as an alternative and environmental friendly inhibitor for API 5LGrade X42 steel in acidic environment."

"Ekstrak daun jati cina Cassia angustifolia sebagai inhibitor ramah lingkungan pada Baja API 5L di lingkungan HCl diinvestigasi. Pengujian yang dilakukan adalah polarisasi dan kehilangan berat. Senyawa yang terkandung pada ekstrak adalah senyawa flavonoid, xanthone, dan anthraquinone. Senyawa tersebut diinvestigasi melalui pengujian FTIR. Variabel pengujian merupakan konsentrasi inhibitor, meliputi 10 ml, 20 ml, 30 ml, 40 ml, dan 50 ml. Kemampuan inhibitor untuk menginhibisi optimum pada konsentrasi 40 ml. Ekstrak daun jati cina berperan sebagai inhibitor campuran dengan dominan katodik. Mekanisme adsorpsi pada ekstrak daun jati cina merupakan mekanisme adsorpsi isotherm Langmuir dengan tipe adsorpsi physisorption.

---

Cassia angustifolia leaves extract as green inhibitor for API 5L steel pipe in HCl environment was investigated. This study was experimented by using different types of test, such as polarization and weight loss. The compound in cassia angustifolia are flavonoid, xanthone, and anthraquinone. These compound was investigated by using FTIR. This experiment was investigated with different number of concentrations as its variables, which are 10 ml, 20 ml, 30 ml, 40 ml, and 50 ml inhibitor extracts. The optimum capability of the inhibitor to inhibit the steel surface was in 40 ml concentrations. Cassia angustifolia leaves extract is found to be a mixed type inhibitor with predominant cathodic effectiveness. The adsorption mechanism of cassia angustifolia leaves extract was Langmuir with physisorption as the types of adsorption. "

"Daun salam dan buah salak sangat melimpah di Indonesia, dan dipercaya masyarakat memiliki sifat antioksidan dan anti penuaan. Namun belum ada penelitian mengenai penggunaanya sebagai inhibitor korosi ramah lingkungan. Penelitian ini bertujuan untuk mempelajari dan menganalisa pengaruh penambahan ekstrak daun salam (syzygium polyanthum),, buah salak banjarnegara (salacca zalacca var banjarnegara) dan campuran keduanya sebagai inhibitor ramah lingkungan terhadap baja karbon API 5L grade B dalam larutan HCl 1M. Pengujian polarisasi dan EIS dilakukan untuk mengukur efisiensi inhibitor pada konsentrasi penambahan ekstrak yang berbeda yaitu 2ml/L, 4ml/L, 6ml/L dan 8ml/L untuk masing-masing ekstrak daun salam dan buah salak, dan konsentrasi ekstrak campuran 6ml/L dengan perbandingan komposisi ekstrak daun salam dan buah salak yaitu 1:1, 1:2, 1:3, 3:1 dan 2:1. Pengujian FTIR dilakukan untuk mengetahui golongan senyawa aktif yang terkandung pada ekstrak daun salam dan buah salak, dan mengetahui golongan senyawa aktif yang membentuk lapisan protektif pada permukaan logam. Adsorption isotherm digunakan untuk mengidentifikasi mekanisme adsorpsi dari inhibitor ekstrak daun salam, buah salak dan campuran pada permukaan baja. Hasil pengujian polarisasi pada penambahan inhibitor ekstrak daun salam dan buah salak secara tunggal, sama-sama menunjukan nilai efisiensi inhibitor (EI) tertinggi dan laju korosi (CR) terendah diperoleh pada konsentrasi 6ml/L yaitu masing-masing EI = 58.56%, CR=1.36 mm/tahun untuk ekstrak daun salam dan EI = 74.90%, CR = 0.82 mm/tahun untuk ekstrak buah salak. Hasil pengujian EIS pada penambahan inhibitor ekstrak daun salam dan buah salak secara tunggal juga menunjukan nilai efisiensi inhibitor (EI) tertinggi diperoleh pada konsentrasi 6ml/L yaitu masing-masing EI=76.60% untuk ekstrak buah salak dan EI=66.07% untuk ekstrak daun salam. Sedangkan untuk campuran ekstrak daun salam dan buah salak diperoleh efisiensi inhibitor (EI) tertinggi dan laju korosi (CR) terendah pada perbandingan komposisi 1:1 (50% : 50%) yaitu sebesar EI=73.54% dan CR=0.87 mm/year, berdasarkan pengujian polarisasi dan EI=74.83% berdasarkan pengujian EIS. Pengujian FTIR menunjukkan keberadaan golongan senyawa fenolik (tannin) pada penambahan inhibitor ekstrak daun salam dan keberadaan golongan senyawa alkaloid pada penambahan ekstrak salak dipermukaan logam yang direndam dalam HCl 1M. Kedua jenis ekstrak apabila dicampurkan tidak menunjukan adanya efek sinergis dan juga antagonis sehingga dapat disimpulkan keduanya tidak saling mempengaruhi satu sama lain. Kedua inhibitor ekstrak menunjukan korelasi sesuai dengan Langmuir dan Frumkin Isotherm yang mengindikasinya mekanisme adsorpsi fisik dan chemisorption

---

Bay leaves and snake fruits are very abundant in Indonesia, and have been believed by local community that they have antioxidant properties and anti-aging effect. However, no studies regarding its use as a enviromental friendly corrosion inhibitor. The aim of this research is to study and analyze the effect of indonesian bay leaf extract (syzygium polyanthum), snake fruit (salacca zalacca var banjarnegara) extract and also these mixed extract as enviromental friendly inhibitor on carbon steel API 5L grade B in hydrochoric acid 1M solution.

Electrochemical polarization test and EIS test were used in measuring the inhibitor efficiency at a different concentration of extract i.e. 2ml/L, 4ml/L, 6ml/L dan 8ml/L for indonesia bay leaf extract and snake fruit extract as single inhibitor, and 6ml/L for their mixture with a composition ratio of indonesian leaf extract to snake fruit extract , 1:1, 1:2, 1:3, 3:1 dan 2:1. FTIR was also used to identify the active compound group contained in both extracts and identify the active compound group which formed protective film on the metal surface. Adsorption isotherm was used to study inhibition mechanism of indonesia bay leaf extract, snake fruit extract and their mixture on metal surface.

Polarization test result of addition of indonesian bay leaf extract and snake fruit extract as single inhibitor in 1M HCl solution showed the highest inhibitor efficiency value (IE) and lowest corrosion rate (CR) IE=58.56%, CR=1.36 mm/year for bay leaf extract, and IE=74.90%, CR=0.82 mm/year for snake fruit extract at concentration 6ml/L, as well as EIS test showed the highest inhibitor efficiency value respectively IE=66.07% for bay leaf extract and IE=76.6% for snake fruit extract at concentration 6ml/L. And the addition of their mixture showed the highet inhibitor efficiency value achieved at a composition ratio 1:1 (50% : 50%) i.e. IE=73.54%, CR=0.87 mm/year based on polarisation test and 74.83% based on EIS test.

FTIR test result on steel sample which was immersed in HCl 1M solution had identified primarily the presence of phenolic compound group (tannin) on the metal surface with an addition of indonesian bay leaf extract and alkaloid compound group on the metal surface with an addition of snake fruits extract. The mixture of the extracts showed no sinergistic and antagonistic interaction. Thus, it can be concluded that these extracts do not interact to each other when they are mixed. These two extracts showed a correlation to Langmuir and Frumkin Isotherm that indicated physical adsorption as well as chemisorption."

"80% kegagalan material baja pada fasilitas produksi industri minyak dan gas bumi disebabkan oleh proses korosi. Salah satu pengendalian proses korosi material baja API 5L Grade X60 dengan menggunakan inhibitor ramah lingkungan. Pada penelitian ini, ekstrak kayu secang (Caesalpinia Sappan L.) dievaluasi sebagai inhibitor ramah lingkungan untuk baja API 5L X60 di lingkugan HCl 1M dengan variasi volume ekstrak 0,5 ml, 1 ml, 1,5 ml, 2 ml, 3ml dan variasi temperatur 302K, 312K, 322K, dan 332K menggunakan metode polarisasi tafel, Electrochemical Impedance Spectroscopy (EIS), Fourier Transform Infra-red Spectroscopy (FTIR), dan Stimultaneous Thermal Analysis (STA). Hasil dari pengujian polarisasi tafel dan EIS menunjukan ekstrak kayu secang bertindak sebagai inhibitor campuran (Mixed Inhibitor). Efisiensi optimal dihasilkan dari penambahan volume ekstrak sebesar 1,5 ml dalam 400 ml HCl 1M. sebesar 91 % polarisasi tafel, dan sebesar 94% EIS. Rapat arus korosi material pada volume 1,5 ml ekstrak kayu secang sebesar 57 µA/cm2 dan nilai resistivitas larutan 841 ?.cm2. Kenaikan temperatur lingkungan sebesar 332 K menaikan rapat arus korosi material menjadi 139 µA/cm2 dan menurunkan nilai resistivitas larutan sampai 121 ?.cm2, sehingga nilai efisiensi inhibitor turun sampai 50%. Gugus fungsi keton (C=O) muncul dari hasil karakterisasi pengujian FTIR yang menandakan keberadaan senyawa brazilein dan dan sappanchalcone.

---

80 % failure of carbon steel at oil and gas production facility was caused by corrosion. One of corrosion mitigation of carbon steel was used green inhibitor. In this study, Caesalpinia Sappan L. extract has been evaluated as green inhibitor corrosion for API 5L X60 in HCl 1M environment with variation of volume extract 0,5 ml, 1ml, 1,5 ml, 2ml, 3ml and variation of temperature 302K, 312K, 322K, and 332K using Tafel polarization and Electrochemical Impedance Spectroscopy (EIS), Fourier Transform Infra-red Spectroscopy (FTIR), dan Stimultaneous Thermal Analysis (STA).The Result show the tafel polarization and EIS show caesalpinia sappan extract acts for inhibit corrosion process in the system with mixed type inhibitor. Optimal inhibiton efficiency occurs at volume 1.5 ml extract caesalpinnia sappan/400 ml HCl 1M, 91% for tafel polarization and 94% for EIS. Current density at volume extract 1,5 ml was 57 µA/cm2 and resistivity of solution 841 ?.cm2. Increasing temperatur of environment will increase current density to 139 µA/cm2 and decrease resistivity to 121 ?.cm2. So, the inhibition efficiency decrease to 50%. Keton fuctional group was found showed exisstance of showed that brazilein dan dan sappanchalcone"

"Teknik Metalurgi dan MaterialJudul : Studi Ketahanan Korosi Pipa Baja API 5L X42 dengan Green Inhibitor Ekstrak Bawang Dayak Eleutherine americanna Merr. dalam Lingkungan 1M HCl. Ketahanan korosi pipa baja API 5L X42 dengan inhibitor ramah lingkungan ekstrak bawang dayak Eleutherine americanna Merr. dalam lingkungan 1M HCl diinvestigasi dengan pengujian polarisasi tafel, weight loss, dan Electrochemical Impedance Spectroscopy EIS . Senyawa flavonoid yang bersifat antioksidan yang berperan untuk menginhibisi korosi diinvestigasi melalui pengujian FTIR. Variabel yang digunakan adalah konsentrasi inhibitor, yaitu 0 ppm, 100 ppm, 250 ppm, 500 ppm, dan 1000 ppm. Ekstrak bawang dayak yang mempunyai gugus flavonoid merupakan inhibitor jenis campuran, dan dominan katodik. Efisiensi inhibisi paling tinggi didapatkan dengan konsentrasi 1000 ppm. Inhibitor ekstrak bawang dayak dapat digunakan sebagai alternatif inhibitor ramah lingkungan untuk baja API 5L X42 pada lingkungan 1M HCl.

---

Metallurgy and Materials EngineeringTitle Study of Corrosion Resistance of Pipeline API 5L X42 Using Green Inhibitor Bawang Dayak Eleutherine americanna Merr. in 1M HCl. This study aimed to investigate the ability of Eleutherine americanna Merr. extract as an environment friendly inhibitor for API 5L X42 in 1M HCl. Corrosion inhibition ability of this extract was tested using tafel polarization, weight loss and electrochemical impedance spectroscopy methods. FTIR test was used to investigate flavonoid and antioxidant compound that plays an important role to inhibit corrosion. In this study the concentration of Eleutherine americanna Merr. extract used was 0 ppm, 100 ppm, 250 ppm, 500 ppm, and 1000 ppm. It can be concluded that Eleutherine americanna Mer. extract can be used as an alternative and environmental friendly inhibitor for API 5L X42 in 1M HCl. "

"Ekstrak areca flower telah diteliti sebagai inhibitor korosi pada baja API 5L Gr. B pada lingkungan 1 M HCl dengan menggunakan pengujian Linear Polarisasi dan Electrochemical Impedance Spectroscopy EIS. Penambahan konsentrasi inhibitor 4 ml, 8 ml, 12 ml, 16 ml, dan 20 ml dapat meningkatkan efisiensi inhibitor. Efisiensi inhibitor optimum terjadi pada saat penambahan konsentrasi inhibitor 20 ml sebesar 96.6 pada pengujian Electrochemical Impedance Spectroscopy EIS. Senyawa polifenol dan flavonoid yang terkandung dalam areca flower dapat menginhibisi korosi secara adsorpsi fisika yang membentuk lapisan monolayer yang dapat menghambat terjadinya korosi. Adsorpsi terjadi secara spontan sesuai dengan adsorpsi isotermal Langmuir. Sesuai hasil pengujian polarisasi menunjukkan ekstrak areca flower memiliki tipe inhibisi campuran mixed-type . Nilai energi bebas adsorpsi -7.026 kJ/mol menunjukkan bahwa adsorpsi molekul inhibitor adalah adsorpsi fisika.

---

Areca flower has been investigated as green corrosion inhibitor on API 5L Gr B in solution 1 M HCl acidic using Linear polarization and Electrochemical Impedance Spectroscopy EIS . Addition of 4 ml, 8 ml, 12 ml, 16 ml, and 20 ml inhibitor corrosion increase efficiency of the inhibitor. Optimum inhibition efficiency occurs at addition at concentration 20 ml is 96.6 on Electrochemical Impedance Spectroscopy EIS testing. Polyphenolic and flavanoid compounds contained in the areca flower inhibit corrosion by physical adsorption, to form a monolayer which can inhibit corrosion. Adsorption occurs spontaneously in accordance with Langmuir isothermal adsorption. The polarization showed that the areca flower extract acts through mixed ndash type inhibition. The value of the free energy 7.026 kJ mol of adsorption indicated that the adsorption of inhibitor molecules was typical of physical adsorption."

"Kemampuan inhibisi korosi senyawa fenolik minyak zaitun pada baja API 5L Grade B di lingkungan NaCl 3,5 % diinvestigasi dengan menggunakan pengujian Tafel polarisasi dan Electrochemical Impedance Spectroscopy (EIS). Senyawa fenolik minyak zaitun yang berperan dalam menginhibisi korosi diinvestigasi dengan pengujian FTIR. Senyawa oleuropein dalam minyak zaitun berperan dalam menginhibisi korosi pada sistem dengan tipe mixed inhibitor. Efisiensi inhibisi optimal terjadi pada konsentrasi 1 ml minyak zaitun/100 ml NaCl. Efisiensi inhibisi akan menurun seiring dengan kenaikan temperatur. Senyawa oleuropein menginhibisi korosi dengan cara adsorpsi fisika (interaksi elektrostatis) pada permukaan logam membentuk lapisan tunggal yang akan menghambat transfer muatan dan massa. Adsorpsi senyawa fenolik minyak zaitun pada permukaan logam terjadi spontan mengikuti Langmuir adsorpsi isoterm. Adsorpsi senyawa fenolik minyak zaitun akan meningkatkan energi aktivasi proses korosi. Hasil pengujian menunjukkan bahwa senyawa fenolik minyak zaitun dapat digunakan sebagai alternatif inhibitor ramah lingkungan pada baja API 5L Grade B di lingkungan NaCl 3,5 %.

---

Corrosion inhibition ability of olive oil phenolic compounds on API 5L Grade B steel in 3.5% NaCl environment was investigated using Tafel polarization and Electrochemical Impedance Spectroscopy (EIS) test. Olive oil phenolic compounds that acts for inhibit corrosion process was investigated by FTIR test. Oleuropein compounds in olive oil acts for inhibit corrosion process in the system with mixed type inhibitors. Optimal inhibition efficiency occurs at a concentration 1 ml olive oil/100 ml NaCl. Inhibition efficiency decreases with increasing temperature. Oleuropein compounds inhibit corrosion by physisorption (electrostatic interactions) on the metal surface to form a single layer that will inhibit the charge and mass transfer. Adsorption of olive oil phenolic compounds on the metal surface occurs spontaneously follow the Langmuir adsorption isotherm. Adsorption of olive oil phenolic compounds will increase the activation energy of the corrosion process. The results showed that olive oil phenolic compounds can be used as an alternative green corrosion inhibitor on API 5L Grade B steel in 3.5% NaCl environment."

"Tesis ini mempelajari mengenai pengaruh injeksi ekstrak Andaliman dan Alpha-Tocopherol sebagai green corrosion inhibitor pada baja API 5L dalam larutan HCl 1M. Dengan pengujian weight loss diperlihatkan bahwa inhibitor campuran antara ekstrak Andaliman dan Alpha-Tocopherol mampu menurunkan laju korosi dengan efisiensi 92.07 pada konsentrasi inhibitor 2 ml Andaliman 0.5 ml Alpha-Tocopherol. Dari pengujian polarisasi ditunjukkan bahwa inhibitor campuran antara ekstrak Andaliman dan Alpha-Tocopherol menggeser kurva polarisasi kearah atodik dan katodik mixed type inhibitor , yang menunjukkan ciri utama sebagai inhibitor dari bahan organik. Pengujian dengan FTIR dan GCMS memperkuat dugaan bahwa inhibitor ekstrak Andaliman dan Alpha-Tocopherol sebagai inhibitor adsorpsi/film forming.

---

This thesis is intended to study the influences of Andaliman extract and Alpha- Tocopherol injection as green corrosion inhibitor for API 5L steel in HCl 1M solution. By weight loss analysis, it show that mixed inhibitor from andaliman extract and Alpha-Tocopherol can reduce corrosion rate with efficiency up to 92.07 % under inhibitor injection about 2 ml Andaliman + 0.5 ml Alpha- Tocopherol. By polarization, it is shown that inhibitor shift polarisation curves for both of anodic and cathodic polarisation (mixed type inhibitor), shows that inhibitor have characteristic as inhibitor from organic material. By FTIR and GCMS analysis can be concluded that inhibitor from Andaliman and A- Tocopherol act inhibition by adsorption/film forming corrosion inhibitor."