"Pendahuluan: Adanya lesi white spot setelah perawatan ortodonti cekat akan menyebabkan permukaan email semakin kasar. Peningkatan kekasaran permukaan email memudahkan penempelan plak oleh bakteri. Oleh karena itu diperlukan penatalaksanaan lesi white spot dengan teknik abrasi mikro, aplikasi Fluor dan aplikasi CPP-ACP. Tujuan: Penelitian ini bertujuan untuk menganalisis perbedaan kekasaran permukaan email lesi white spot sebelum dan setelah perlakuan teknik abrasi mikro, abrasi mikro disertai aplikasi Fluor dan abarasi mikro disertai aplikasi CPP-ACP dan menganalisis perbedaan perubahan kekasaran permukaan email diantara ketiga kelompok. Bahan dan Cara: Penelitian menggunakan 42 buah gigi premolar satu atas yang telah diekstraksi sebagai spesimen penelitian, kemudian spesimen direndam selama 96 jam dalam larutan demineralisasi pH 4, 37 C untuk membentuk lesi white spot buatan. Sampel dibagi secara acak menjadi 3 kelompok perlakuan n= 14 , yaitu A teknik abrasi mikro; B teknik abrasi mikro disertai aplikasi pasta 10 CPP-ACP dan C teknik abrasi mikro disertai aplikasi gel 1.23 APF. Pengukuran kekasaran permukaan email menggunakan alat Surface Roughness Tester merk Mitutoyo SJ-301 dalam dua waktu yaitu sebelum perlakuan dan setelah perlakuan. Hasil: Hasil penelitian menunjukkan bahwa terdapat perbedaan kekasaran permukaan email lesi white spot secara bermakna pada seluruh kelompok sebelum dan sesudah perlakuan. Ada perbedaan perubahan kekasaran permukaan email secara bermakna antar kelompok setelah perlakuan, namun yang menunjukkan perbedaan perubahan paling besar adalah kelompok teknik abrasi mikro disertai aplikasi CPP-ACP. Kesimpulan: Metode penatalaksanaan lesi white spot dengan teknik abrasi mikro disertai aplikasi CPP-ACP merupakan metode yang paling efektif menurunkan kekasaran permukaan email dibandingkan kedua metode lainnya.

---

Introduction The presence of white spot lesions after fixed orthodontic treatment will lead to increase of enamel surface roughness. The increase of enamel surface roughness accomodate the addition of plaque by bacteria. Therefore we need the management of white spot lesions.

Aim: The aim of this study was to analyze the surface roughness of white spot lesion enamel after micro abrasion technique, a combination micro abrasion technique and CPP ACP application and a combination micro abrasion technique and Fluor application.

Materials and Methods: Artificially induced white spot lesion in enamel surface of forty two extracted upper premolar one for fixed orthodontic treatment were randomly assigned into one of three treatment groups n 14 , which were A micro abrasion technique B A combination of the micro abrasion technique and CPP ACP application C a combination of the micro abrasion technique and Fluor application. Mitutoyo SJ 301 was used to measure difference before and after treatment and also the surface roughness changes compared in three groups after treatment.

Results: According to the results of this study, there was a significant difference in surface roughness of white spot lesion enamel after treatment in all groups p 0.05 . There was a significant difference in the result of surface roughness changes compared with three methods of white spot lesion treatment.

Conclusions: A combination of the micro abrasion technique and CPP ACP application significantly reduces the enamel surface roughness greater than micro abrasion alone and a combination of the micro abrasion technique and Fluor application."

"ABSTRAKTujuan: Untuk mengetahui pengaruh pemaparan gel ekstrak belimbing wuluh terhadap kekasaran permukaan enamel gigi.Metode: Spesimen berupa 36 gigi premolar yang dibagi ke dalam 4 kelompok (n = 9), kemudian dipaparkan dengan gel asam fosfat 37% (pH = 1) selama 15 detik sebagai kelompok kontrol, dan gel ekstrak belimbing wuluh dengan konsentrasi 80% (pH = 1,8) selama 15 detik, 20 detik, dan 25 detik sebagai kelompok perlakuan.Hasil: Analisa statistik uji T berpasangan dan tidak berpasangan menunjukkan bahwa semua kelompok perlakuan mengalami perubahan bermakna (p<0,05). Permukaan enamel mengalami perubahan kekasaran terbesar setelah dipaparkan gel ekstrak belimbing wuluh dengan konsentrasi 80% selama 25 detik, namun perubahan kekasaran yang dihasilkan gel asam fosfat 37% lebih besar.Kesimpulan: Terdapat hubungan antara nilai kekasaran pada permukaan enamel gigi dengan lama pemaparan gel belimbing wuluh dengan konsentrasi 80%.Kata kunci: enamel, belimbing wuluh (Averrhoa bilimbi L.), asam fosfat, kekasaran permukaan

---

ABSTRACT

Objective: To analyze the effect of Belimbing Wuluh Gel Extract to surface roughness of enamel.

Methods: Thirty-six premolars teeth divided into 4 groups (n = 9), were exposed to 37% phosphoric acid gel (pH = 1) for 15 seconds as a control group, and belimbing wuluh extract gel with a concentration of 80% (pH = 1.8) for 15 seconds, 20 seconds, and 25 seconds as the treatment groups.

Results: The statistical analysis of paired and unpaired T-test shows that all treatment groups experiment were significant change (p <0.05). The greatest changes in surface roughness of enamel occurred after exposed by belimbing extract gel with an exposure duration of 25 seconds, but the roughness of 37% phosphoric acid gel was still greater.

Conclusions: There was a corelation between roughness on the surface of tooth enamel with prolonged exposure belimbing wuluh extract gel with a concentration of 80%."

"Pendahuluan : Debonding dan permbersihan sisa bahan adesif setelah perawatan ortodonti cekat menyebabkan permukaan email menjadi kasar. Peningkatan kekasaran permukaan email memudahkan akumulasi plak yang dapat menyebabkan demineralisasi email. Tujuan: Menganalisis perubahan kekasaran permukaan email pasca debonding setelah aplikasi bahan infiltrasi resin, bahan pelapis nano resin, dan kombinasi bahan infiltrasi resin dengan bahan pelapis nano resin serta menganalisis perbedaan perubahan kekasaran permukaan email ketiga kelompok tersebut. Material dan Metode : 30 buah gigi premolar digunakan sebagai spesimen penelitian. Setiap spesimen direkatkan braket standard Edgewise premolar di bagian bukal mahkota gigi, lalu direndam dalam aquades selama 24 jam. Selanjutnya dilakukan proses debonding braket dan sisa bahan adesif dibersihkan menggunakan dome tapered tungsten carbide bur highspeed 30.000rpm. Spesimen dibagi menjadi 3 kelompok perlakuan n= 10 , yaitu : R aplikasi bahan infiltrasi resin; N aplikasi bahan pelapis nano resin; RN aplikasi bahan infiltrasi resin bahan pelapis nano resin. Kekasaran permukaan email diukur menggunakan alat Surface Roughness Tester merk Mitutoyo SJ-301 saat sebelum perlakuan dan setelah perlakuan. Hasil : Terdapat perubahan kekasaran permukaan email pasca debonding yang bermakna setelah aplikasi bahan seluruh kelompok. Perbedaan perubahan kekasaran permukaan email pasca debonding paling besar terjadi pada kelompok RN aplikasi bahan infiltrasi resin bahan pelapis nano resin Kesimpulan : Aplikasi bahan infiltrasi resin bahan pelapis nano resin merupakan metode yang paling efektif untuk menurunkan kekasaran permukaan email pasca debonding dibandingkan aplikasi bahan infiltrasi resin atau bahan pelapis nano resin saja.

---

Background Debonding and removal of adhesive remnants after orthodontic treatment will increase the surface roughness of enamel, This condition promotes plaque accumulation which leads to enamel demineralization. Objective Analyzing surface roughness changes of enamel after debonding using resin infiltration system, nano filled resin coating, and the combination of both materials. We also analyze the differences in surface roughness changes of enamel between the three groups. Material and Method 30 extracted upper first premolar tooth specimens were bonded with standard Edgewise bracket and stored in distilled water for 24 hours. Then the brackets were debonded, and adhesive remnants were removed using highspeed dome tapered tungsten carbide bur at 30.000rpm. Afterwards, each specimen was randomly assigned into one of the three treatment groups n 10 , which were R resin infiltration system N nano filled resin coating RN A combination of resin infiltration system nanofilled resin coating. The surface roughness of enamel was measured using Mitutoyo SJ 301 Surface Roughness Tester before and after the treatment."

"Latar Belakang: White spot merupakan salah satu efek samping perawatan ortodonti dengan piranti cekat. Keberadaan lesi ini setelah debonding menimbulkan masalah estetik. Tujuan: Penelitian ini bertujuan untuk menilai perubahan warna white spot paska debonding setelah aplikasi fluor dan CPP-ACP. Metode: Pada penelitian ini digunakan empat puluh dua gigi premolar atas yang telah diekstraksi guna perawatan ortodonti, lalu dipasang braket, kemudian spesimen direndam dalam larutan demineralisasi untuk membentuk lesi white spot artifisial, dan selanjutnya braket dilepas. Sampel dibagi menjadi 3 kelompok (n= 14) secara acak untuk diberi perlakuan: (1) Aplikasi gel 1.23% APF; (2) Aplikasi pasta 10% CPP-ACP, dan (3) kontrol. Pengukuran perubahan warna dengan menggunakan spektrofotometer dilakukan pada 3 waktu yaitu pada sebelum dan setelah white spot artifisial dibentuk, dan setelah white spot diberi perlakuan. Hasil: Hasil penelitian ini memperlihatkan bahwa terdapat perbedaaan warna white spot yang bermakna secara statistik sesudah perlakuan pada seluruh kelompok sampel. Tidak terdapat perbedaan bermakna secara statistik pada banyaknya perubahan warna white spot setelah aplikasi gel 1.23% APF dan pasta 10% CPP-ACP. Simpulan: CPP-ACP memberikan hasil perubahan warna white spot yang lebih baik secara visual, namun tidak berbeda bermakna secara statistik dengan fluor.

---

Background: White spot are common side effect in orthodontic treatment. The presence of the lesions after the removal of orthodontic aplliances still remains an esthetic problem.

Objective: The aim of this study was to quantify color changes in post-debonding white spot lesions after fluor and CPP-ACP aplication.

Methods: Forty-two upper premolars which were extracted for orthodontic reasons, were selected as the sample teeth. Universal premolar brackets were bonded to the facial surfaces of the sample and the sample were exposed to demineralization solution to create artificial white spot lesions, and then brackets were debonded. The sample were randomly allocated into 1 of 3 groups (n= 14) and were assigned to this following treatment: (1) 1.23% APF gel; (2) 10% CPP-ACP paste, and (3) control group. Then all groups were assigned to pH cycling for 14 days. Color change measurements were determined using a spectrophotometer 3 times: before and after production of the artificial white spot lesions, and after the artificial white spot lesions were treated.

Results: This study showed that there was significant difference in the color of the artificial white spot lesions after treatment in all groups. There was not significant difference in the result of color changes between after aplication with 1.23% APF gel and 10% CPP-ACP paste.

Conclusions: CPP-ACP were giving better result in changing the color of white spot lesions, but it was not significantly different from the fluoride."

"Latar Belakang: Karies gigi merupakan penyakit gigi dengan prevalensi tinggi di Indonesia.Tujuan: Mengetahui pengaruh susu sapi dan protein whey terhadap kekerasan email gigi setelah demineralisasi.Metode : Dua puluh satu email gigi diukur kekerasannya sebelum perlakuan, setelah demineralisasi dengan asam sitrat 1%, serta setelah perendaman dengan susu sapi, protein whey, dan aquades selama 90 menit.Hasil: Semua kelompok perlakuan remineralisasi menunjukkan peningkatan nilai kekerasan yang bermakna (p<0,05). Kelompok yang direndam dengan susu sapi dan kelompok protein whey menunjukkan hasil yang tidak berbeda bermakna (p>0,05). Kesimpulan: Susu sapi maupun protein whey dapat meremineralisasi gigi.

---

Background: Caries has high prevalence oral problem in Indonesia.

Objective: To evaluate the effect of bovine milk and protein whey on the enamel hardness after demineralization.

Methods: Twenty one tooth enamel measured its hardness before the treatment, after demineralized with 1% citric acid, and after immersed in bovine milk, whey protein and aquades for 90 minutes.

Results: Significant increase of enamel hardness in all remineralization groups (p<0,05). There was no significant differences between group with immersed in bovine milk and whey protein group (p>0,05).

Conclusion: Bovine milk and whey protein can remineralize enamel surface."

"Resin komposit merupakan material tumpat yang sensitif dan membutuhkan area kerja yang kering. Penelitian ini bertujuan untuk mengetahui efek kontaminasi saliva dan darah setelah bonding terhadap kekuatan ikat geser resin komposit dengan email dan membandingkan beberapa metode pembersihan kontaminan. 25 spesimen gigi premolar dibagi ke dalam 5 kelompok berdasarkan tipe kontaminasi dan metode pembersihan kontaminan. Kelompok kontrol menunjukkan rerata kekuatan ikat tertinggi dan rerata nilai paling rendah terdapat pada kelompok kontaminasi darah-alkohol. Terdapat perbedaan bermakna antara kelompok kontrol dengan kelompok kontaminasi saliva dan darah. Dapat disimpulkan, kontaminasi saliva dan darah setelah bonding menurunkan kekuatan ikat geser resin komposit dengan email.

---

Composite resin is sensitive material that needs dry operative area. This study aimed to determine the effect of saliva and blood contamination after bonding on shear bond strength of composite resin to enamel and to compare several cleansing methods. 25 samples of human premolars were divided into 5 groups based on type of contamination and cleansing procedures. The highest bond strength was seen in control group, while group blood-alcohol showed the lowest bond strength. Significant differences were seen between control group, compared to contamination groups. In conclusion, contamination of saliva and blood after bonding decreased the shear bond strength of composite resin to enamel."

"[ABSTRAKResin komposit merupakan bahan restorasi direk dengan teknik aplikasi yang sangat sensitif. Penelitian ini bertujuan untuk menganalisis efek kontaminansi saliva dan darah setelah etsa terhadap kekuatan ikat geser antara resin komposit dan email. Dua puluh lima spesimen email (n=25) secara acak dibagi dalam lima kelompok berdasarkan bahan kontaminasi dan metode pembersihan kontaminan. Hasil penelitian menunjukkan nilai rerata kekuatan ikat geser tertinggi adalah kelompok kontrol, sedangkan yang terendah adalah kelompok kontaminasi darah dengan etsa ulang. Antara kelompok kontrol dengan kelompok kontaminasi terdapat perbedaan yang signifikan. Sebagai kesimpulan, kontaminasi saliva dan darah menyebabkan penurunan kekuatan ikat geser antara resin komposit dan email;Composite resin is a direct restorative material with highly sensitive application technique.ABSTRACTThis study aimed to analyze the effect of saliva and blood contamination after etching procedure to shear bond strength between composite resin and enamel. Twenty five samples of enamel (n=25) were randomly divided into five group based on contamination agent and decontamination procedures. The result showed the mean value of shear bond strength was highest on control group and the lowest on blood contamination group with re-etching procedure. Between control group and contamination group were significantly different. In conclusion, saliva and blood contamination can decrease shear bond strength between composite resin and enamel, Composite resin is a direct restorative material with highly sensitive application technique. This study aimed to analyze the effect of saliva and blood contamination after etching procedure to shear bond strength between composite resin and enamel. Twenty five samples of enamel (n=25) were randomly divided into five group based on contamination agent and decontamination procedures. The result showed the mean value of shear bond strength was highest on control group and the lowest on blood contamination group with re-etching procedure. Between control group and contamination group were significantly different. In conclusion, saliva and blood contamination can decrease shear bond strength between composite resin and enamel]"

"Larutan kayu manis dapat menjadi obat kumur alternatif, namun kandungan taninnya dapat menyebabkan diskolorasi. Untuk mengetahui pengaruh perendaman dengan larutan kayu manis terhadap perubahan warna email, duabelas gigi premolar direndam dalam larutan kayu manis konsentrasi 4% dan 12,5% (masing-masing n=6) selama 60 menit, 120 menit, dan 180 menit. Terdapat peningkatan perubahan warna seiring lama perendaman dan besarnya konsentrasi. Seluruh sampel menunjukkan perubahan warna yang tidak dapat diterima secara klinis (ΔE>3,5). Uji antar kelompok waktu menunjukkan perubahan bermakna (p<0,05) sedangkan antar konsentrasi perubahannya tidak bermakna (p>0,05). Larutan kayu manis menyebabkan perubahan warna email yang tidak dapat diterima secara klinis.

---

Cinnamon solution can be used as an alternative mouthwash. However, its tannin can cause discoloration. To identify the effect of cinnamon solution immersion to color change of tooth enamel, twelve premolar teeth were immersed in 4% and 12% cinnamon solution concentration (each n=6) for 60 minutes, 120 minutes, and 180 minutes. There were higher changes at longer time of immersion and bigger concentration. All samples showed clinically unacceptable color changes result (ΔE>3,5). Test between time groups showed significant changes (p<0,05) and no significant changes between concentration groups (p>0,05). Cinnamon solution can cause a clinically unacceptable color changes to tooth enamel."

"[Chitosan memiliki gugus amino dan hidroksil yang diduga reaktif terhadap ion asam sehingga dapat meningkatkan pH lingkungan dan menghambat proses demineralisasi email. Penelitian ini bertujuan menganalisis kelarutan email yang diberi chitosan pada suasana asam serta mekanisme kerja chitosan. Sebelas gigi pascaekstraksi dibagi menjadi kelompok baseline, kelompok kontrol negatif, kelompok perlakuan asam+chitosan, dan kelompok perlakuan chitosan. Hasil penelitian menunjukkan peningkatan pH lingkungan dan penurunan kerusakan permukaan email yang diberi chitosan dalam suasana asam dibanding kelompok kontrol negatif. Chitosan terbukti menghambat proses demineralisasi email in vitro, Chitosan’s amino and hydroxyl groups are assumed to react with acid ions, increase environmental pH level, and thereby interfere enamel demineralization process. This research aims to analyze the enamel surface damage after chitosan application in acidic environment and chitosan’s mechanism of action. Eleven postextraction teeth are categorized as baseline, negative control, acid+chitosan application, and chitosan application group. Results showed that there is an increase in environmental pH level and a decrease in enamel surface damage after chitosan application in acidic environment compared to negative control group. Chitosan is proven to interfere enamel demineralization process in vitro]"

"Daun sirih mengandung komponen utama yaitu polifenol, yang lebih dikenal dengan nama tanin. Tanin berpengaruh terhadap kekerasan permukaan email gigi. Cara aplikasi pada email adalah dengan topikal gel. Pada penelitian ini digunakan 18 spesimen gigi sapi yang ditanam dalam resin akrilik dan dibagi dalam 3 kelompok, gel ekstrak daun sirih 15%, 25% dan 35% selama 1 bulan, 3 bulan dan 6 bulan. Kekerasan email diukur menggunakan alat uji Shimadzu Microhardness Tester HMV-2. Hasil dianalisis dengan menggunakan Repeated ANOVA dan One Way ANOVA. Terdapat perbedaan yang bermakna pada seluruh kelompok perlakuan (p<0.05). Terdapat peningkatan nilai kekerasan email setelah aplikasi gel ekstrak daun sirih 15% selama 6 bulan.

---

Betel leaf (Piper betle Linn) contains a main component, known as Tannin. Tannin can affect enamel`s hardness. 18 specimens of bovine teeth were embedded in acrylic resin, divided into 3 groups of gel application betel leaf extract 15%, 25% and 35% for 1 month, 3 months and 6 months. Enamel`s hardness measured by Shimadzu Microhardness Tester HSV-2. Statistical analysis was done by Repeated ANOVA and One Way ANOVA. There was significantly increase (p<0.05) of micro hardness number after 6 months gel application with 15% betel leaf extract. Gel with betel leaf extract can significantly affect the enamel`s hardness."