"Dye Sensitized Solar Cell DSSC berbasis TiO2 merupakan tipe sel surya yang menarik perhatian karena proses fabrikasi yang mudah, biaya pembuatan yang murah, dan efisiensi yang menjanjikan. Dalam penelitian ini dilakukan fabrikasi DSSC menggunakan TiO2 nanotube yang disintesis dengan teknik Rapid Breakdown Anodization RBA dan Ultrafast Room Temperature Cristalization URTC . TiO2 kemudian dideposisikan pada substrat kaca Fluor Tin Oxide FTO menggunakan metode doctor blade, disensitasi dengan zat warna kurkumin, dan dirangkai sebagai elektroda kerja sel surya bersama elektroda counter berbasis karbon transparan yang disintesis menggunakan metode liquid-liquid interfacial system. Karakterisasi dilakukan dengan XRD, UV-VIS DRS, SEM, FTIR, Raman Spectroscopy, dan Potensiostat EDAQ. Hasil penelitian menunjukkan, metode URTC dapat merubah bentuk TiO2 amorf menjadi fasa kristalin anatase. Fotoaktivitas TiO2-URTC pada daerah UV sebesar 0,10 mA/cm2 pun tidak terlalu jauh dari fotoaktivitas TiO2-450C. Di sisi lain, elektroda counter karbon transparan FTO/Ct berhasil disintesis dan memberikan transimisi rata-rata 58,26 pada daerah sinar tampak dengan kemampuan elektrokatalitik lebih baik dari FTO. Uji kinerja DSSC dilakukan terhadap sel surya dengan rangkaian FTO/TiO2-URTC/kurkumin//FTO/Ct. Hasilnya menunjukkan bahwa DSSC ini memberikan efisiensi sebesar 0,467 pada penyinaran depan dan 0,262 pada penyinaran belakang. Nilai efisiensi tersebut tidak berbeda jauh dengan efisiensi DSSC dengan komponen FTO/TiO2-450C/kurkumin//FTO/Pt, yaitu 0,517 untuk penyinaran depan dan 0,356 untuk penyinaran belakang.

---

based Dye Sensitized Solar Cell DSSC is one of the most attractive solar cell, because of its easy fabrication, low cost, and relatively promising efficiency. In this research, we developed solar cell using TiO2 nanotube powder that was made by Rapid Breakdown Anodization RBA and Ultrafast Room Temperature Cristalization technique. The prepared TiO2 then was sensitized using curcumin dyes and utilized to construct DSSC using carbon transparent counter electrode prepared by liquid liquid interface system technique. Characterizations of the prepared materials were done by using XRD, SEM, UV Vis DRS, FTIR, Raman spectroscopy, and Electrochemical working station. The results indicate that by using URTC technique, the freshly prepared TiO2 was transformed to anatase crystalline phase. Furthermore, photoactivity of TiO2 ndash URTC in UV 0.10 mA cm2 just equal to that was being prepared by the conventional technique 0.12 mA cm2 . On the other hand, carbon transparent electrode FTO Ct was successfully prepared and gives 58.26 transparency in visible light region but having catalytic activity better than bare FTO. Furhermore, efficiency test of constructed DSSC FTO TiO2 URTC curcumin FTO Ct showed efficiency of 0.467 for front illumination and 0.262 for back illumination. This result is still lower, but not too far than conventional DSSC with components FTO TiO2 450C curcumin FTO Pt which gives 0.517 efficiency for front illumination and 0,356 for back illumination."

"Penelitian ini adalah studi awal mengenai sel surya tersensitasi berbasis ZnO dengan zat pewarna organik. Tujuannya untuk mengetahui pengaruh dari tingkat pengisian dan besar kristalit TiO2 terhadap voltase DSSC. Hasil dari penelitian menunjukkan bahwa, besar kristalit berbanding terbalik dengan voltase yang dihasilkan. Semakin besar ukuran kristalit semakin kecil voltase yang dihasilkan dan sebaliknya semakin kecil ukuran kristalit semakin besar voltase yang dihasilkan. Sementara tingkat pengisian mempunyai pengaruh berbeda pada kristalit yang besar dan kristalit yang kecil. Selain itu, ukuran kristalit dan tingkat pengisian mempengaruh kestabilan layer oksida dan kemampuannya dalam menyerap molekul zat pewarna.

---

This research is an initial study about ZnO based dye sensitized solar cell (DSSC) with an organic dye. The purpose is to understand the effect of loading level and crystallite size to DSSC voltages.

The result of this research shows that, crystallite size is a contrary fraction with the voltages that produced by DSSC. The bigger size of crystallite the lower voltages outcome, on contrary the smaller size of crystallite the bigger voltages can be produced by DSSC. While loading level have a different affect in smaller and bigger crystallite. Afterwards, crystallite size and volume level affect the stability of the layer oxide and its ability to absorb dye molecules."

"Sel surya tersensitasi zat warna, dyes sensitized solar cell (DSSC), merupakan suatu alat fotovoltaik yang merubah sinar matahari menjadi energi listrik. Namun saat ini, sel surya yang memiliki efisiensi tertinggi menggunakan zat warna sintetik senyawa kompleks logam Ru yang mahal sebagai sensitizer. Komponen utama DSSC adalah fotoanoda berupa TiO2-nanotube TiO2-NT yang disensitasi zat warna digunakan sebagai elektroda kerja, elektrolit, dan FTO-Pt sebagai elektroda counter. Dalam penelitian ini fotoanoda TiO2-NT disensitasi dengan ekstrak curcumin. TiO2-NT dipreparasi dengan metode two-step anodization, yaitu anodisasi dua langkah dengan penggunaan voltase tinggi ke rendah dalam 0,3 NH4F; 2 H2O dalam etilen glikol kemudian dikalsinasi pada 500oC selama 2 jam untuk mendapatkan TiO2-NT dengan tabung berdiameter kecil namun panjang, sehingga kemampuan dye-loadingnya meningkat. Sebagai elektroda counter, FTO-Pt disiapkan dengan metode spray-pyrolisis lalu dideposisikan Pt pada permukaannya untuk menurunkan resistansinya. Sebagai pesensitasi zat warna curcumin diekstrak dari kunyit dengan cara maserasi dalam pelarut etanol. Karena curcumin memiliki kekurangan, yaitu sangat mudah rusak terdegradasi dan terhidrolisis saat terpapar sinar matahari, maka ekstrak curcumin yang digunakan dikomplekskan dengan ion logam Cu2 . Sistem sel surya yang dibentuk kemudian disusun dengan teknik sandwich. Karakterisasi TiO2-nanotube untuk menentukan band gap, keberadaan jejaring Ti-O-Ti , fasa Kristal, dan morfologinya dilakukan dengan UV-Vis-DRS, FTIR, XRD, dan SEM. Karakterisasi curcumin, kompleks Cu II -curcumin, TiO2-NT-curcumin dan TiO2-NT-Cu II -curcumin dilakukan dengan UV-Vis, UV-Vis-DRS dan FTIR, untuk melihat pola spektra dan ciri kromofor dan gugus fungsi. Uji photocurrent dilakukan dengan potensiostat metode LSV dan MPA. Efisiensi sel surya untuk curcumin hasil maserasi, curcumin standar, dan kompleks Cu II -curcumin berturut-turut diperoleh sebesar 0,44 ; 0,4 ; dan 0,22.

---

Dye sensitized solar cell DSSC is a well known photovoltaic device that convert sunlight into electricity. The DSSC is comprise of dyes sensitized TiO2 ndash nanotube photoanode used as working electrode, electrolyte, and FTO Pt is used as counter electrode. The highest efficiency of DSSC achieved so far was that used synthetic ruthenium complex dyes as sensitizer, which is expensive. In this research we prepared investigated curcumin sensitised TiO2 nanotube as photoanode. The TiO2 nanotubes TiO2 NT was prepared by two step anodization, which changed the voltage used in anodization from high to low in electrolyte containing 0,3 NH4F 2 H2O in ethylene glycol, then heated at 500oC for 2 hours to obtain TiO2 NT having small diameter but longer tube length, to improve its capability to load dyes. The FTO counter electrode was prepared by spray pyrolysis method and then the a Pt particle was deposited on its surface to improve conductivity. The curcumin, as sensitizer, was extracted from turmeric by soaked in ethanol. Unfortunately, the curcumin easily undergo degradation and hydrolized upon sun light exposure. Thus in this work, the curcumin was transformed to Cu II curcumin complex compound, to improve its stability. The TiO2 NT was characterized by UV Vis DRS, FTIR, XRD, and SEM to determine its band gap, occurrence of Ti O Ti network, crystal phase, and its morphology, respectively. The curcumin, Cu II curcumin, TiO2 NT curcumin, TiO2 NT Cu II curcumin were characterized by UV Vis, UV Vis DRS, and FTIR, to observe the spectra profile and identify the chromophore and its functional group. The photocurrent response of the photoanode was evaluated by potentiostat, under LSV and MPA method. The DSSC efficiency of curcumin extract, curcumin standard, and complex Cu II curcumin exhibits 0,44 0,4 and 0,22 respectively."

"Sel surya tersensitasi zat warna (dye-sensitized solar cell, DSSC) merupakan perangkat yang dapat mengkonversi cahaya matahari menjadi arus listrik dengan menggunakan elektroda kerja berupa semikonduktor TiO2 yang dilapisi oleh zat warna dan kaca ITO (Indium Tin Oxide) sebagai elektroda counter. Lapisan tipis TiO2 dipreparasi di atas plat Ti dengan cara anodisasi dalam larutan NH4F dalam gliserol pada bias potensial 25 volt selama 4 jam dan dikalsinasi pada suhu 500°C selama 3 jam. Karakterisasi dengan SEM menunjukkan bahwa TiO2 yang terbentuk mempunyai morfologi nanotube dengan diameter tabung yang teratur, yaitu 40-60 nm. Karakterisasi dengan XRD dan DRS UV-Vis menunjukkan bahwa kristal TiO2 yang terbentuk berupa fasa anatase. Zat warna yang digunakan sebagai photosensitizer adalah zat warna alami cyanidin yang diekstrak dari buah black mulberry (Morus nigra L) dengan pelarut metanol:HCl (99:1). Karakterisasi cyanidin dengan UV-Vis menunjukkan serapan kuat paada panjang gelombang 513 nm. Cyanidin diadsorpsikan ke dalam TiO2 nanotube menggunakan metode elektroforesis, dengan variasi bias potensial dan waktu. Plat Ti/TiO2- nanotube/cyanidin dirangkai menjadi DSSC dengan larutan elektrolit Iˉ/I3ˉ dan kaca ITO. Nilai efisiensi konversi cahaya menjadi arus listrik tertinggi adalah 0,2678 % dan 0,2672%, ditunjukkan oleh plat Ti/TiO2-nanotube/cyanidin yang masing-masing dielektroforesis pada tegangan 20 volt selama 12 menit dan 25 volt selama 8 menit.

---

Dye-sensitized solar cell (DSSC) is a device that can convert the sunlight to electrical current, by employing dyes coated TiO2 semiconductor as working electrode and ITO (Indium Tin Oxide) glass as counter electrode. TiO2 thin film was prepared by anodization of Ti plate in NH4F/glycerol at potential 25 volt for 4 hours and then heated at 500°C for 3 hours. Characterization by SEM showed the TiO2 has a nanotube morphology having internal diameter of 40-60 nm. Characterization by XRD and DRS UV-Vis indicated that the TiO2 is in anatase crystal phase. Cyanidin, a natural dye, that was used as photo sensitizer was extracted from black mulberry fruit (Morus nigra L) in methanol:HCl (99:1) solvent. The extracted cyanidin showed a strong absorption at wavelength of 513 nm, which is suitable to absorb visible light. The cyanidin is coated into TiO2 nanotube by using electrophoresis method, at various bias potential and time. The Ti/TiO2-nanotube/cyanidin plate was assembled into DSSC using Iˉ/I3ˉ electrolyte solution and ITO glass. The highest efficiency values were 0.2678 % and 0.2672%, for Ti/TiO2-nanotube/cyanidin which were prepared by electrophoresis at 20 volt for 12 minutes and 25 volt for 8 minutes, respectively."

"Dye Sensitized Solar Cell DSSC adalah perangkat yang digunakan untuk mengubah energi sinar matahari menjadi energi listrik. Pada penelitian ini digunakan TiO2-NT yang disensitasi dengan antosianin dari ekstrak kulit manggis Garcinia mangostana L sebagai elektroda kerja dan kaca FTO-Pt sebagai elektroda counter. TiO2-NT ditumbuhkan pada plat titanium dengan metode two step anodization dengan potensial 30V pada tahap pertama dan 15V pada tahap kedua menggunakan elektrolit yang mengandung etilen glikol, NH4F dan H2O, kemudian dikalsinasi pada suhu 500oC selama 2 jam untuk mendapatkan TiO2-NT dengan fasa anatase. FTO dipreparasi dengan metode spray pyrolysis kemudian Pt dari H2PtCl6 dideposisikan pada permukaan FTO. Dilakukan kopigmentasi terhadap antosianin hasil ekstraksi dengan penambahan asam benzoat untuk meningkatkan serapan sinar tampak dan meningkatkan stabilitas antosianin. Karakterisasi yang digunakan adalah SEM untuk mengetahui morfologi permukaan, XRD untuk mengetahui fasa kristal yang terbentuk, FTIR untuk mengetahui vibrasi ikatan dari molekul, UV-Vis DRS untuk mengetahui energi celah TiO2. Uji photocurrent menggunakan teknik LSV dan MPA, menunjukkan bahwa TiO2-NT aktif pada daerah UV dan setelah disensitasi dengan antosianin, TiO2-NT menjadi aktif pada daerah sinar tampak. Karakterisasi antosianin yang diekstrak dari kulit manggis menggunakan UV-Vis menunjukkan terdapat serapan pada daerah visible pada daerah panjang gelombang 400-600nm dan setelah antosianin dikopigmentasi dengan asam benzoat, terjadi peningkatan absorbansi. Efisiensi sel surya yang dihasilkan menggunakan sensitizer antosianin adalah sebesar 0.2273 , dan menggunakan antosianin yang dikopigmentasi dengan asam benzoat adalah sebesar 0.2297 1:0,5 , 0.2884 1:0,8 , and 0.3709 1:1 .Dari hasil yang didapatkan, dapat diketahui bahwa penggunaan antosianin yang dikopigmentasi dengan asam benzoat sebagai sensitizer dapat meningkatkan effisiensi sel surya.

---

Dye Sensitized Solar Cell DSSC is a device that convert solar energy to electric energy. In this research, the TiO2 nanotube TiO2 NT which was sensitized by anthocyanin, extracted from mangosteen pericarp, was used as working electrode and FTO Pt Fluor Doped Tin Oxide Platinum as counter electrode. TiO2 NT were growth on titanium plate by two step anodization method with 30V potential on the first step and 15V potential on the second step using etilen glycol NH4F H2O electrolyte, then heated at 500oC for 2 hours. FTO prepared by spray pyrolysis method then Pt from H2PtCl6 solution deposited on FTO surface. Anthocyanin extract was copigmented with benzoic acid to increase absorbance on visible light and its stabilization. Prepared TiO2 was characterized using SEM to determined surface morphology, XRD to know crystal phase formed, FTIR to know vibration bonding molecule and UV DRS to determine band gap. Photocurrent evaluation using LSV and MPA method showed that TiO2 NT active at UV light, and after being sensitized with anthocyanin benzoic acid did active toward visible light. Anthocyanin extract which was characterized by UV Vis showed absorbance at visible wavelength region 400nm 600nm and after being copigmented using benzoic acid, the absorbance was increased. Evaluation of DSSC efficiency showed that those using anthocyanin and anthocyanin copigmented benzoic acid with ratio 1 0,5 1 0,8 and 1 1 v w as sensitizer were 0.2273 , 0.2297 , 0.2884 , and 0.3709 respectively. The results shows that the addition of benzoic acid to anthocyanin can improve the DSSC performance."

"Sel surya tersensitisasi-pewarna merupakan jenis sel surya yang dapat menjadi alternatif sumber energi murah dan mudah dibuat. Prinsip kerjanya relatif berbeda dengan sel surya yang sudah dikenal saat ini. Umumnya, DSSC berbasis titanium (IV) oksida (TiO2). Telah dibuat partikel nano ZnO dengan metode presipitasi yang diharapkan menjadi basis sel surya tersensitisasi pewarna. NaOH diberikan pada prekursor seng asetat dihidrat dalam pelarut etanol dengan rasio molar NaOH : Zn(CH3COO)2 · 2H2O 3,6, 1,8, dan 0,9. Penambahan NaOH menghasilkan endapan, kemudian dicuci dengan etanol, dan diproses lanjut dengan pemanasan (anil) dan pascahidrotermal. Partikel yang dicuci pada pengujian XRD memberikan sifat amorf. Keteraturan meningkat dengan perlakuan anil, lalu pascahidrotermal. Sifat elektronik berupa energi celah pita juga diamati dan memberi kecenderungan mengecil dengan ukuran yang meningkat. Kecenderungan berbeda diamati pada sampel dengan rasio molar 1,8. Tegangan sel yang diamati pada setiap rasio molar adalah 30, 67, dan 27 mV.

---

Dye-sensitised solar cell (DSSC) is a solar cell that may become an economically feasible and easily manufactured alternative source of energy. The principle is different from conventional silicon solar cell. Such solar cells generally based on titanium (IV) oxide (TiO2). In this research, ZnO nanoparticles was made via precipitation method. The material in question was expected to be the basis of DSSC. NaOH wasadded to zinc acetate dihydrate precursor in ethanol with the molar ratios of 3.6, 1.8, and 0.9 respectively. It was observed that the addition of NaOH gave rise to precipitate that was washed with ethanol and subsequently processed by heating (annealing) and post-hydrothermal treatment. After XRD examination, the as-washed particle showed the amorphous tendency, but the internal order was improved after the annealing and post- hydrothermal treatment. The band-gap energy was also observed and gave tendency to be lower with the increasing size, although the nanoparticle with 1.8 molar ratio gave slightly different result. The voltage observed (per molar ratio) was 30, 67, and 27 mV."

"[Dye Sensitized Solar Cell (DSSC) dalam konfigurasi tabung telah berhasil dibuat. DSSC dirakit menggunakan Inner Wall Conductive Glass Tube (IWCGT) yang mengandung SnO2-F (Fluorine Tin Oxide) sebagai lapisan konduktif. IWCGT dipreparasi menggunakan tehnik penguapan dan spray nebulizer, menghasilkan kaca transparan berpenghantar yang memiliki hambatan jenis antara 11-80 Ω/cm2.Sol TiO2 dilapiskan pada IWCGT dengan tehnik dip coating, dilanjutkan dengan kalsinasi pada suhu 500° C dan 550° C. Terhadap TiO2 hasil sintesis dilakukan karakterisasi menggunakan UV-Vis Diffuse Reflectance Spectrometry (DRS), Xray Diffraction (XRD), Fourier Transform Infra Red (FTIR) dan spektrofotometerRaman. Lapisan tipis yang diimobilisasi pada IWCGT dikarakterisasi menggunakan Field Emission Scanning Electron Microscope (FE-SEM) dan sistem elektrokimia. Berdasar spektrum UV-Vis dapat diketahui TiO2 yang dihasilkan memiliki energi celah (band gap) sebesar 3,01 dan 3,04 eV. Hasil pengukuran spektroskopi Raman dan XRD menunjukkan bahwa film yang dihasilkan didominasi oleh TiO2 dalam bentuk anatase dan mempunyai ukuran kristal sebesar 9,79 nm (kalsinasi pada suhu 500° C) dan 10,59 nm (kalsinasi pada suhu 550° C). Hasil FE-SEM menunjukkan bahwa lapisan TiO2 yang dipreparasi dengan bantuan template PEG memiliki ketebalan sebesar 496,56 nm. Sistem DSSC dalam konfigurasi tabung yang disiapkan dengan menggunakan TiO2 dan zat warna Rhodamin B, Klorofil dan campuran keduanya mampu menghasilkan efisiensi (η) antara 0,03 – 0,91%.;Dye Sensitized Solar Cell (DSSC) dalam konfigurasi tabung telah berhasil dibuat. DSSC dirakit menggunakan Inner Wall Conductive Glass Tube (IWCGT) yang mengandung SnO2-F (Fluorine Tin Oxide) sebagai lapisan konduktif. IWCGT dipreparasi menggunakan tehnik penguapan dan spray nebulizer, menghasilkan kaca transparan berpenghantar yang memiliki hambatan jenis antara 11-80 Ω/cm2.Sol TiO2 dilapiskan pada IWCGT dengan tehnik dip coating, dilanjutkan dengan kalsinasi pada suhu 500° C dan 550° C. Terhadap TiO2 hasil sintesis dilakukan karakterisasi menggunakan UV-Vis Diffuse Reflectance Spectrometry (DRS), Xray Diffraction (XRD), Fourier Transform Infra Red (FTIR) dan spektrofotometerRaman. Lapisan tipis yang diimobilisasi pada IWCGT dikarakterisasi menggunakan Field Emission Scanning Electron Microscope (FE-SEM) dan sistem elektrokimia. Berdasar spektrum UV-Vis dapat diketahui TiO2 yang dihasilkan memiliki energi celah (band gap) sebesar 3,01 dan 3,04 eV. Hasil pengukuran spektroskopi Raman dan XRD menunjukkan bahwa film yang dihasilkan didominasi oleh TiO2 dalam bentuk anatase dan mempunyai ukuran kristal sebesar 9,79 nm (kalsinasi pada suhu 500° C) dan 10,59 nm (kalsinasi pada suhu 550° C). Hasil FE-SEM menunjukkan bahwa lapisan TiO2 yang dipreparasi dengan bantuan template PEG memiliki ketebalan sebesar 496,56 nm. Sistem DSSC dalam konfigurasi tabung yang disiapkan dengan menggunakan TiO2 dan zat warna Rhodamin B, Klorofil dan campuran keduanya mampu menghasilkan efisiensi (η) antara 0,03 – 0,91%.

---

A dye sensitized solar cell (DSSC) having tube geometry has been successfully constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT) containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is 11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared by a dip-coating technique from titania sol-gel, followed by heat treatment at 500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission scanning electron microscopy (FE-SEM). Characterization results indicated that the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis); predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of 0.03 to 0.91 %.;A dye sensitized solar cell (DSSC) having tube geometry has been successfully

constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT)

containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared

by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is

11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared

by a dip-coating technique from titania sol-gel, followed by heat treatment at

500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission

scanning electron microscopy (FE-SEM). Characterization results indicated that

the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis);

predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and

having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its

mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of

0.03 to 0.91 %.;A dye sensitized solar cell (DSSC) having tube geometry has been successfully

constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT)

containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared

by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is

11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared

by a dip-coating technique from titania sol-gel, followed by heat treatment at

500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission

scanning electron microscopy (FE-SEM). Characterization results indicated that

the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis);

predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and

having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its

mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of

0.03 to 0.91 %., A dye sensitized solar cell (DSSC) having tube geometry has been successfully

constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT)

containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared

by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is

11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared

by a dip-coating technique from titania sol-gel, followed by heat treatment at

500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission

scanning electron microscopy (FE-SEM). Characterization results indicated that

the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis);

predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and

having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its

mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of

0.03 to 0.91 %.]"

"Sel surya tersensitasi zat warna dye-sensitized solar cell, DSSC merupakan perangkat yang dapat mengkonversi sinar matahari menjadi arus listrik dengan menggunakan elektroda kerja berupa semikonduktor TiO2 yang dilapisizat warna dan kaca FTO Fluorine Tin Oxide sebagai elektroda counter. Lapisan tipis TiO2 dipreparasi pada plat Ti dengan cara anodisasi dalam larutan NH4F dalam gliserol pada bias potensial 25 volt selama 4 jam dan dikalsinasi pada suhu 450oC selama 2 jam. Karakterisasi menggunakan DRS UV-Vis dan FTIR menunjukkan bahwa TiO2 yang terbentuk berupa fasa anatase. Zat warna yang digunakan sebagai photosensitizer adalah zat warna alami yang diekstrak dari daun suji, wortel dan alga hijau-biru Spirulina platensis sebagai klorofil, '-karoten dan fikosianin. Optimasi dilakukan dengan memodifikasi klorofil dengan penambahan '-karoten dan fikosianin cocktail dyes dengan perbandingan 1:1 dan 1:2. Zat warna diadsorpsikan ke dalam TiO2-nanotube dengan metode elektroforesis pada bias potensial 20 volt selama 12 menit. Plat Ti/TiO2-nanotube/dyes dirangkai menjadi DSSC dengan larutan I-/I3- dan kaca FTO. Nilai efisiensi konversi cahaya menjadi arus listrik tertinggi ditunjukkan oleh plat Ti/TiO2-nanotube/cocktail dyes klorofil-fikosianin 1:1 sebesar 1.04926.

---

Dye sensitized solar cell DSSC is a device that can convert the sunlight to electrical current by employing dyes coated semiconductor as working electrode and FTO Fluorine Tin Oxide glass as counter electrode. TiO2 thin film was prepared by anodization of Ti plate in NH4F glycerol at potential 25 volt for 4 hours and heated at 450oC for 2 hours. Characterization by DRS UV Vis and FTIR showed that the TiO2 is in anatase crystal phase. Dye that was used as photosensitizer were natural dyes extracted from suji leaf, carrot and green blue algae Spirulina platensis as chlorophyll, carotene and phycocyanin. Optimization was done by modified the chlorophyll added by carotene and phycocyanin cocktail dyes with ratio 1 1 and 1 2. Dyes was coated into TiO2 nanotube by using electrophoresis method at 20 volt for 12 minutes. Ti TiO2 nanotube dyes was assembled into DSSC using I I3 electrolyte solution and FTO glass. The highest efficiency value was showed by Ti TiO2 nanotube cocktail dyes chlorophyll phycocyanin 1 1 was 1.04926."

"Sel surya perovskite berbasis timbal menunjukkan efisiensi dan stabilitas yang tinggi dengan metode sintesis mudah dan murah, namun penggunaan timbal sangat dikhawatirkan karena tingkat toksisitas tinggi dan dapat mencemari lingkungan. Baru-baru ini disintesis bismuth perovskite yang stabil, non-toksik dan dapat disintesis dengan metode sederhana pada temperatur rendah namun persen efisiensinya hanya mencapai 0,19%. Berbagai riset membuktikan bahwa titania anatase dengan persen eksposur (001) yang besar mampu meningkatkan arus listrik, tegangan, meningkatkan injeksi elektron dan memperkecil rekombinasi. Sehingga pada penelitian ini, disintesis TiO₂ nanopartikel dengan tingkat pemaparan faset (001) berbeda menggunakan capping agent fluorin dan mendapatkan persentase faset (001) menurut karakterisasi XRD 17% , 18% dan 23% dan menurut karakterisasi raman 12% , 14% dan 25%. Menurut hasil dari karakterisasi dengan UV-DRS seiring dengan penambahan volume HF reflektan dari TiO2 di daerah sinar UV meningkat. Dari hasil perhitungan, didapatkan energi celah pita untuk variasi HF 5 ml, HF 10 ml dan HF 15 ml adalah 3,25 eV; 3,25 eV dan 3,3 eV.

---

Lead-based perovskite solar cells exhibit high efficiency and stability with an easy and inexpensive synthesis method, but the use of lead is a great concern because of its high toxicity and pollution. Recently bismuth perovskite with stable, non-toxic and simple synthesis low temperature method has been synthesized but the efficiency is only 0,19%. Various studies have shown that anatase titania with a large percentage of exposure (001) facet can increase electric current, voltage, electron injection and reduce recombination. In this study, TiO₂ nanoparticle were synthesized with different facet (001) exposure using fluorine as capping agents and obtained (001) facet percentage according to XRD characterization of 17%, 18% and 23% and according to raman characterization of 12%, 14% and 25%. According to UV-DRS characterization along with the addition of the volume of HF reflectant from TiO2 in the UV light region increases. From the calculation results, band gap energy for 5 ml HF variation, 10 ml HF and 15 ml HF is 3.25 eV; 3.25 eV and 3.3 eV."

"Material karbon menjadi alternatif material yang dapat digunakan sebagai elektroda pada sel surya perovskite. Karbon memiliki keberagaman pada jenis alotropinya berdasarkan ikatan atom. Namun, hingga saat ini belum ada penelitian penggunaan karbon aktif yang berasal dari material biomassa sebagai elektroda pada sel surya perovskite. Pada riset ini, karbon aktif yang digunakan berasal dari arang batok kelapa. Ukuran partikel dari karbon aktif berbentuk bubuk, yaitu 30 mikrometer mesh 500 dan 15 mikrometer (mesh 1000) serta rentang waktu pembuatan elektroda karbon aktif akan diteliti pada skripsi ini untuk mengetahui unjuk kerja sel surya perovskite yang menggunakan karbon aktif arang batok kelapa sebagai elektrodanya dengan metode yang digunakan adalah powder pouring. Perbedaan jenis prekursor titanium Ti juga akan diteliti pengaruhnya terhadap unjuk kerja dari sel surya perovskite yang dihasilkan. Prekursor Ti yang digunakan untuk membentuk lapisan penghantar elektron TiO2 pada penelitian ini adalah Titanium Isopropoxide TTIP dan Titanium Diisopropoxide Bis Acetylacetonate TTDB dengan metode yang digunakan spin coating dan annealing. Hasil dari skripsi ini, unjuk kerja sel surya perovskite terbaik adalah sel surya perovskite yang menggunakan prekursor TTIP pada lapisan penghantar elektron TiO2 dan elektroda karbon aktif dengan ukuran partikel mesh 1000 serta pembuatan elektroda dilakukan pada hari yang sama dengan proses fabrikasi dengan unjuk kerja yang dihasilkan adalah VOC sebesar 1,28 volt; ISC sebesar 8,04 mA; fill factor sebesar 0,512; dan efisiensi sebesar 2,85%.

---

Carbon can be an alternative material as the electrode of perovskite solar cells (PSCs). According to the different atom bonded, there are several allotropes of carbon which makes carbon as the diversity material. However, there is no research that uses activated carbon derived from biological materials as the electrode of PSCs. In this research, the activated coconut shell charcoal will be used as the electrode of PSCs. Effect of the particle size of coconut shell charcoal which is 30 micrometer mesh 500 and 15 micrometer mesh 1000, as well as the lifespan of the activated carbon based electrode, towards the performance of PSCs, was investigated. The method in depositing activated carbon is powder pouring. This research also investigated the effect of Ti precursors for the TiO2 based electron transport layer. Ti precursors that used in this research consists of Titanium Isopropoxide TTIP and Titanium Diisopropoxide Bis Acetylacetonate TTDB. The best performance of PSCs in this research is the PSCs that use TTIP precursor for the TiO2-based electron transport layer, the particle size of the activated carbon-based electrode is mesh 1000, and the lifespan of the activated carbon based electrode is 0 days. The device produced VOC of 1.28 volt; ISC of 8.04 mA; fill factor of 0.512; and efficiency of 2.85%."