"ABSTRAKKemampuan ekstrak daun Physalis angulata daun ciplukan sebagai inhibitor ramah lingkungan di lingkungan HCl 1 M diinvestigasi menggunakan pengujian polarisasi linear dan weight loss. Adapun diinvestigasi flavonoid dan antioksidan yang menginhibisi permukaan Baja API 5L melalui pengujian FTIR. Variabel bebas yang dipakai yaitu ekstrak konsentrasi inhibitor dalam HCl 1 M, yakni 10 mL, 20 mL, 30 mL, 40 mL, dan 50 mL. Ekstrak daun ciplukan mengandung senyawaan flavonoid yang merupakan inhibitor campuran yang dominan katodik. Inhibitor ini mampu mencegah kerusakan catastrophic akibat agresivitas HCl 1 M dengan mekanisme physisorption hingga 192 jam. Efisiensi inhibitor yang paling tinggi ada di konsentrasi 50 mL sebesar 98,9. Inhibitor ekstrak daun ciplukan berpotensi sebagai inhibitor ramah lingkungan bagi Baja API 5L dilingkungan HCl 1 M.

---

ABSTRACTThe ability of Physalis angulata leaves extract as green inhibitor in HCl 1 M environment has been investigated with linear polarization measurement and weight loss method. FTIR analysis was used to investigate flavonoid and antioxidant compound that plays an important role to inhibit corrosion. The free variable that has been used in this study was 10 mL, 20 mL, 30 mL, 40 mL, dan 50 mL. Physalis angulata leaves extract that contain flavonoid play role as mixed inhibitor that predominantly cathodic. This inhibitor can prevent cathasthropic damage due to aggressiveness of HCl 1 M with physisorption mechanism up to 192 hours. The concentration that showed highest efficiency 98.9 was 50 mL. It can be concluded that Physalis angulata leaves extract could be used as an alternative and environmental friendly inhibitor for API 5L in HCl 1 M environment."

"Pengaruh kombinasi ekstrak daun Physalis angulata daun ciplukan dan daun Cassia angustifolia daun jati cina sebagai inhibitor ramah lingkungan dengan perbandingan 50:50 pada baja karbon API 5L diinvestigasi. Pengujian dilakukan dalam lingkungan HCl 1M. Pengujian yang dilakukan meliputi polarisasi potensiodinamik, kehilangan berat, dan EIS. Senyawa antioksidan diinvestigasi melalui pengujian FTIR. Sesuai dengan pengujian FTIR, senyawa antioksidan yang terkandung pada kombinasi ekstrak ini adalah flavonoid. Variabel yang digunakan adalah konsentrasi inhibitor, yaitu 10 ml, 30 ml, dan 50 ml. Diketahui bahwa semakin tinggi konsentrasi yang diberikan, maka semakin tinggi kemampuan inhibitor dalam menginhibisi permukaan baja dimana efisiensi inhibitor paling tinggi didapatkan dengan konsentrasi 50 ml. Kombinasi ekstrak daun ciplukan dan daun jati merupakan inhibitor jenis campuran yang lebih dominan ke katodik. Metode adsorpsi inhibitor ini mengikuti adsorpsi isotherm Langmuir dengan tipe adsorpsi fisika atau physisorption.

---

The effect of combination of Physalis angulata leaf and Cassia angustifolia leaf extract as green inhibitor with a 50:50 ratio for API 5L steel was investigated. This experiment was carried in 1M HCl solution by using different concentrations as variables which is 10 ml, 30 ml, and 50 ml inhibitor extracts. This experiment was evaluated using potentiodynamic polarization, EIS, and weight loss. The antioxidant compound was investigated using FTIR and was found to be flavonoid. It was found that the capability of the inhibitor to inhibit the steel surface from the environment increases with increasing concentration, which 50 ml concentration is found to have the best efficiency of all concentrations. Combination of physalis angulata leaf and cassia angustifolia leaf extract is found to be a mixed type inhibitor with predominant cathodic effectiveness. The adsorption of this inhibitor on the steel surface was predominantly through physisorption and obeyed Langmuir adsorption isotherm."

"Ekstrak areca flower telah diteliti sebagai inhibitor korosi pada baja API 5L Gr. B pada lingkungan 1 M HCl dengan menggunakan pengujian Linear Polarisasi dan Electrochemical Impedance Spectroscopy EIS. Penambahan konsentrasi inhibitor 4 ml, 8 ml, 12 ml, 16 ml, dan 20 ml dapat meningkatkan efisiensi inhibitor. Efisiensi inhibitor optimum terjadi pada saat penambahan konsentrasi inhibitor 20 ml sebesar 96.6 pada pengujian Electrochemical Impedance Spectroscopy EIS. Senyawa polifenol dan flavonoid yang terkandung dalam areca flower dapat menginhibisi korosi secara adsorpsi fisika yang membentuk lapisan monolayer yang dapat menghambat terjadinya korosi. Adsorpsi terjadi secara spontan sesuai dengan adsorpsi isotermal Langmuir. Sesuai hasil pengujian polarisasi menunjukkan ekstrak areca flower memiliki tipe inhibisi campuran mixed-type . Nilai energi bebas adsorpsi -7.026 kJ/mol menunjukkan bahwa adsorpsi molekul inhibitor adalah adsorpsi fisika.

---

Areca flower has been investigated as green corrosion inhibitor on API 5L Gr B in solution 1 M HCl acidic using Linear polarization and Electrochemical Impedance Spectroscopy EIS . Addition of 4 ml, 8 ml, 12 ml, 16 ml, and 20 ml inhibitor corrosion increase efficiency of the inhibitor. Optimum inhibition efficiency occurs at addition at concentration 20 ml is 96.6 on Electrochemical Impedance Spectroscopy EIS testing. Polyphenolic and flavanoid compounds contained in the areca flower inhibit corrosion by physical adsorption, to form a monolayer which can inhibit corrosion. Adsorption occurs spontaneously in accordance with Langmuir isothermal adsorption. The polarization showed that the areca flower extract acts through mixed ndash type inhibition. The value of the free energy 7.026 kJ mol of adsorption indicated that the adsorption of inhibitor molecules was typical of physical adsorption."

"Ekstrak daun jati cina Cassia angustifolia sebagai inhibitor ramah lingkungan pada Baja API 5L di lingkungan HCl diinvestigasi. Pengujian yang dilakukan adalah polarisasi dan kehilangan berat. Senyawa yang terkandung pada ekstrak adalah senyawa flavonoid, xanthone, dan anthraquinone. Senyawa tersebut diinvestigasi melalui pengujian FTIR. Variabel pengujian merupakan konsentrasi inhibitor, meliputi 10 ml, 20 ml, 30 ml, 40 ml, dan 50 ml. Kemampuan inhibitor untuk menginhibisi optimum pada konsentrasi 40 ml. Ekstrak daun jati cina berperan sebagai inhibitor campuran dengan dominan katodik. Mekanisme adsorpsi pada ekstrak daun jati cina merupakan mekanisme adsorpsi isotherm Langmuir dengan tipe adsorpsi physisorption.

---

Cassia angustifolia leaves extract as green inhibitor for API 5L steel pipe in HCl environment was investigated. This study was experimented by using different types of test, such as polarization and weight loss. The compound in cassia angustifolia are flavonoid, xanthone, and anthraquinone. These compound was investigated by using FTIR. This experiment was investigated with different number of concentrations as its variables, which are 10 ml, 20 ml, 30 ml, 40 ml, and 50 ml inhibitor extracts. The optimum capability of the inhibitor to inhibit the steel surface was in 40 ml concentrations. Cassia angustifolia leaves extract is found to be a mixed type inhibitor with predominant cathodic effectiveness. The adsorption mechanism of cassia angustifolia leaves extract was Langmuir with physisorption as the types of adsorption. "

"ABSTRAKPhysalis angulata L. merupakan tanaman yang banyak digunakan sebagai obattradisional, oleh karena itu untuk menjaga ketersediaannya perlu dilakukanbudidaya, salah satunya dengan kultur in vitro. Penelitian yang dilakukanbertujuan untuk mengetahui respons eksplan daun P. angulata pada medium MSvitamin MS + 2,4-D 0,3 mg l -1 (M1); MS vitamin MS + 2,4-D 0,4 mg l -1 (M2);MS vitamin MS + NAA 0,5 mg l-1 & BAP 0,5 mg l-1 (M3), MS vitamin B5 + 2,4-D 0,3 mg l -1 (M4); MS vitamin B5 + 2,4-D 0,4 mg l-1 (M5); MS vitamin B5 +kombinasi NAA 0,5 mgl & BAP 0,5 mg l-1 (M6). Eksplan dikultur denganfotoperiodesitas 12 jam. Terdapat 4 kategori respons, yaitu terbentuknya kalus(K), Akar adventif (A), kalus yang kemudian diikuti dengan tumbuhnya akaradvenif (KA), serta kalus yang kemudian juga diikuti dengan tumbuhnya akaradventif dan tunas adventif (KAT). Eksplan dapat membentuk K dan KAdiseluruh medium, sedangkan eksplan yang membentuk A saja hanya terlihat dimedium M2. Sementara itu, eksplan yang membentuk KAT juga hanya terlihat dimedium M3 dan M6. Secara keseluruhan, eksplan menunjukkan respons banyakterbentuk di medium M6. Pada penelitian ini, eksplan dapat merespons mediaperlakuan melalui tahapan kalogenesis dan organogenesis.

---

ABSTRACTPhysalis angulata L. is plant widely used in traditional medicines, therefore tokeep its availability the cultivation is required, one way to ensure its availability isby using in vitro culture. Research aims to know response of P. angulata?s leavesexplant on medium MS supplemented with MS vitamins + 2,4-D 0,3 mg l -1 (M1);MS supplemented with MS vitamins + 2,4-D 0,4 mg l -1 (M2); MS supplementedwith MS vitamins + NAA 0,5 mg l-1 & BAP 0,5 mg l-1 (M3), MS supplementedwith B5 vitamins + 2,4-D 0,3 mg l -1 (M4); MS supplemented with B5 vitamins +2,4-D 0,4 mg l-1 (M5); MS supplemented with B5 vitamins + kombinasi NAA 0,5mgl & BAP 0,5 mg l-1 (M6). The explant were cultured with photoperiodisity in12 hours. The result show there are four categories response, the first, explantresponse to form a callus (K), explant response to form adventitious root (A), nextis the callus formation that followed by the growth of adventitious root (KA), andthe last one callus formation that followed by the growth of adventitious root andadventitious shoot. The explant could form K and KA in every medium, but theone that form A only found in M2. However, the explant that form KAT onlyfound in several medium, which are medium M3 and M6. Overall, the explantshow response many formed in medium M6. By this research, the explant couldresponse to several action, such as through organogenesis and calogenesis."

"Daun salam dan buah salak sangat melimpah di Indonesia, dan dipercaya masyarakat memiliki sifat antioksidan dan anti penuaan. Namun belum ada penelitian mengenai penggunaanya sebagai inhibitor korosi ramah lingkungan. Penelitian ini bertujuan untuk mempelajari dan menganalisa pengaruh penambahan ekstrak daun salam (syzygium polyanthum),, buah salak banjarnegara (salacca zalacca var banjarnegara) dan campuran keduanya sebagai inhibitor ramah lingkungan terhadap baja karbon API 5L grade B dalam larutan HCl 1M. Pengujian polarisasi dan EIS dilakukan untuk mengukur efisiensi inhibitor pada konsentrasi penambahan ekstrak yang berbeda yaitu 2ml/L, 4ml/L, 6ml/L dan 8ml/L untuk masing-masing ekstrak daun salam dan buah salak, dan konsentrasi ekstrak campuran 6ml/L dengan perbandingan komposisi ekstrak daun salam dan buah salak yaitu 1:1, 1:2, 1:3, 3:1 dan 2:1. Pengujian FTIR dilakukan untuk mengetahui golongan senyawa aktif yang terkandung pada ekstrak daun salam dan buah salak, dan mengetahui golongan senyawa aktif yang membentuk lapisan protektif pada permukaan logam. Adsorption isotherm digunakan untuk mengidentifikasi mekanisme adsorpsi dari inhibitor ekstrak daun salam, buah salak dan campuran pada permukaan baja. Hasil pengujian polarisasi pada penambahan inhibitor ekstrak daun salam dan buah salak secara tunggal, sama-sama menunjukan nilai efisiensi inhibitor (EI) tertinggi dan laju korosi (CR) terendah diperoleh pada konsentrasi 6ml/L yaitu masing-masing EI = 58.56%, CR=1.36 mm/tahun untuk ekstrak daun salam dan EI = 74.90%, CR = 0.82 mm/tahun untuk ekstrak buah salak. Hasil pengujian EIS pada penambahan inhibitor ekstrak daun salam dan buah salak secara tunggal juga menunjukan nilai efisiensi inhibitor (EI) tertinggi diperoleh pada konsentrasi 6ml/L yaitu masing-masing EI=76.60% untuk ekstrak buah salak dan EI=66.07% untuk ekstrak daun salam. Sedangkan untuk campuran ekstrak daun salam dan buah salak diperoleh efisiensi inhibitor (EI) tertinggi dan laju korosi (CR) terendah pada perbandingan komposisi 1:1 (50% : 50%) yaitu sebesar EI=73.54% dan CR=0.87 mm/year, berdasarkan pengujian polarisasi dan EI=74.83% berdasarkan pengujian EIS. Pengujian FTIR menunjukkan keberadaan golongan senyawa fenolik (tannin) pada penambahan inhibitor ekstrak daun salam dan keberadaan golongan senyawa alkaloid pada penambahan ekstrak salak dipermukaan logam yang direndam dalam HCl 1M. Kedua jenis ekstrak apabila dicampurkan tidak menunjukan adanya efek sinergis dan juga antagonis sehingga dapat disimpulkan keduanya tidak saling mempengaruhi satu sama lain. Kedua inhibitor ekstrak menunjukan korelasi sesuai dengan Langmuir dan Frumkin Isotherm yang mengindikasinya mekanisme adsorpsi fisik dan chemisorption

---

Bay leaves and snake fruits are very abundant in Indonesia, and have been believed by local community that they have antioxidant properties and anti-aging effect. However, no studies regarding its use as a enviromental friendly corrosion inhibitor. The aim of this research is to study and analyze the effect of indonesian bay leaf extract (syzygium polyanthum), snake fruit (salacca zalacca var banjarnegara) extract and also these mixed extract as enviromental friendly inhibitor on carbon steel API 5L grade B in hydrochoric acid 1M solution.

Electrochemical polarization test and EIS test were used in measuring the inhibitor efficiency at a different concentration of extract i.e. 2ml/L, 4ml/L, 6ml/L dan 8ml/L for indonesia bay leaf extract and snake fruit extract as single inhibitor, and 6ml/L for their mixture with a composition ratio of indonesian leaf extract to snake fruit extract , 1:1, 1:2, 1:3, 3:1 dan 2:1. FTIR was also used to identify the active compound group contained in both extracts and identify the active compound group which formed protective film on the metal surface. Adsorption isotherm was used to study inhibition mechanism of indonesia bay leaf extract, snake fruit extract and their mixture on metal surface.

Polarization test result of addition of indonesian bay leaf extract and snake fruit extract as single inhibitor in 1M HCl solution showed the highest inhibitor efficiency value (IE) and lowest corrosion rate (CR) IE=58.56%, CR=1.36 mm/year for bay leaf extract, and IE=74.90%, CR=0.82 mm/year for snake fruit extract at concentration 6ml/L, as well as EIS test showed the highest inhibitor efficiency value respectively IE=66.07% for bay leaf extract and IE=76.6% for snake fruit extract at concentration 6ml/L. And the addition of their mixture showed the highet inhibitor efficiency value achieved at a composition ratio 1:1 (50% : 50%) i.e. IE=73.54%, CR=0.87 mm/year based on polarisation test and 74.83% based on EIS test.

FTIR test result on steel sample which was immersed in HCl 1M solution had identified primarily the presence of phenolic compound group (tannin) on the metal surface with an addition of indonesian bay leaf extract and alkaloid compound group on the metal surface with an addition of snake fruits extract. The mixture of the extracts showed no sinergistic and antagonistic interaction. Thus, it can be concluded that these extracts do not interact to each other when they are mixed. These two extracts showed a correlation to Langmuir and Frumkin Isotherm that indicated physical adsorption as well as chemisorption."

"Kemampuan kombinasi ekstrak temulawak Curcuma Xanthorrhiza dan bawang Dayak Eleutherine Americana sebagai inhibitor ramah lingkungan untuk baja karbon API 5L X42 pada lingkungan HCl 1M diinvestigasi dengan pengujian tafel, weight loss, polarisasi, Electrochemical Impedance Spectroscopy EIS , dan Fourier Transform Infrared Spectroscopy FTIR . Senyawa flavonoid dan antioksidan yang berperan untuk menginhibisi korosi diinvestigasi melalui pengujian FTIR. Selain itu, lapisan yang terbentuk di permukaan logam juga dipelajari dengan menggunakan metode adsorpsi Langmuir isotherm. Campuran ekstrak temulawak dan bawang Dayak merupakan inhibitor jenis campuran, dan dominan pada katodik. Efisiensi inhibisi paling tinggi didapatkan dengan persentase 80 :20 yaitu 91,78 . Campuran ekstrak temulawak dan bawang Dayak dapat digunakan sebagai alternatif inhibitor ramah lingkungan untuk baja karbon API 5L X42 pada lingkungan asam.

---

This study aimed to investigate the ability of combination from Curcuma Xanthorrhiza and Eleutherine Americana extract as an environment friendly inhibitor for API 5L X42 steel in 1M HCl environment. Corrosion inhibition ability of this extract was tested using weight loss, tafel polarization, electrochemical impedance spectroscopy methods, and fourier transform infrared spectroscopy. FTIR test was used to investigate flavonoid and antioxidant compound that plays an important role to inhibit corrosion. In addition, formed layer on the metal surface was also studied using Langmuir isotherm adsorption methode. It can be concluded that combination from Curcuma Xanthorrhiza and Eleutherine Americana extract could be used as an alternative and environmental friendly inhibitor for API 5L X42 steel in acidid environment."

"Bawang dayak mengandung naphtoquinon sedangkan herba ceplukan mengandung quersetin dan physalin yang memiliki efek antihipertensi. Penelitian ini bertujuan untuk menguji efektivitas antihipertensi kombinasi ekstrak bawang dayak dan herba ceplukan. Deksametason 0,02mg dan larutan NaCl 2,5% digunakan sebagai penginduksi hipertensi. Kelompok normal: akuades, kontrol negatif: CMC-Na 1%, kontrol positif: kaptopril 0,45mg, ekstrak bawang dayak 121,5mg, ekstrak herba ceplukan 232,5mg, dosis kombinasi 1 (BD 40.5mg + HC 77,5mg), dosis kombinasi 2 (BD 81mg + HC 155mg), dan  dosis kombinasi 3 (BD 121,5 mg + HC 232,5mg). Tekanan darah dan berat badan diukur setiap minggu selama 49 hari. Hasil uji antihipertensi menunjukan bahwa, dosis kombinasi 1, 2, dan 3 efektif menurunkan hipertensi dengan p<0,05 dibandingkan dengan tekanan darah pada hari 28. Dosis kombinasi 1 menurunkan tekanan sistolik 32 mmHg (27%), diastolik 29 mmHg (37%), dan MAP 30 mmHg (33%). Dosis kombinasi 1 sudah  cukup untuk menurunkan tekanan darah, kadar angiotensin 2, malondialdehid, VEGF, dan kaveolin-1 dalam plasma serta mengurangi penebalan dinding aorta. 

---

Dayak onions contain naphtoquinone while herba ceplukan  contain quercetin and physalin which have antihypertensive effects. This study aimed to test the antihypertensive effectiveness of a combination of dayak onion extract and herba ceplukan. Dexamethasone 0.02mg and 2.5% NaCl solution are used as inducers of hypertension. Normal group: aquades, negative control: CMC-Na 1%, positive control: captopril 0.45mg, dayak onion extract 121.5 mg, herba ceplukan  extract 232.5 mg, combination dose 1 (BD 40.5mg + HC 77.5mg), combination dose 2 (BD 81 mg + HC 155 mg), and combination dose 3 (BD 121.5 mg + HC 232.5mg). Blood pressure and weight were measured weekly for 49 days. The results of the antihypertensive test showed that the combined dose of 1, 2, and 3 was effective in reducing hypertension by p<0.05 compared to blood pressure on day 28. The combination dose 1 lowered systolic pressure by 32 mmHg (27%), diastolic by 29 mmHg (37%), and MAP by 30 mmHg (33%). A combination dose of 1 is sufficient to lower blood pressure, levels of angiotensin 2, malondialdehyde, VEGF, and kaveolin-1 in plasma and reduce thickening of the aortic wall. "

"

Penelitian ini dilakukan untuk mempelajari mekanisme ekstrak daun kelor (Moringa Oleifera) dan ekstrak ubi ungu (Ipomoea Batatas) sebagai inhibitor korosi ramah lingkungan untuk API 5L pada lingkungan 0,2 M HCl. Karakterisasi kedua inhibitor dilakukan dengan pengujian FTIR dan menunjukkan bahwa senyawa yang terdapat pada kedua inhibitor tersebut adalah senyawa flavonoid. Pengujian polarisasi potensiodinamik dan EIS dengan variasi penambahan inhibitor serta campuran antara kedua inhibitor dilakukan untuk mempelajari sifat inhibisi, dari penelitian ini dapat diketahui bahwa masing- masing kedua inhibitor dapat digunakan sebagai inhibitor ramah lingkungan sedangkan campuran antara kedua inhibitor tersebut tidak dapat melindungi logam API 5L pada lingkungan 0,2 M HCl. Dari pengujian polarisasi potensiodinamik menunjukkan bahwa dengan penambahan konsentrasi inhibitor ekstrak daun kelor maka laju korosi akan semakin menurun dan nilai efisiensi inhibisi semakin naik dengan nilai tertinggi adalah 73,08%, sedangkan dengan penambahan konsentrasi inhibitor ekstrak ubi ungu laju korosi semakin turun dengan nilai efisiensi inhibisi maksimal sebesar 65,31%. Namun hasil pengujian polarisasi potensiodinamik untuk kombinasi kedua inhibitor menunjukkan nilai laju korosi yang semakin meningkat. Hasil pengujian EIS menunjukkan bahwa kedua inhibitor ini dapat melindungi logam dengan membentuk sebuah lapisan film yang melapisi permukaan logam. Mekanisme adsorpsi inhibitor menunjukkan sebagai mekanisme adsorpsi secara fisik serta sesuai dengan model dari Langmuir untuk inhibitor ekstrak daun kelor dan Temkin untuk ekstrak ubi ungu.

---

This research was conducted to study the mechanism of Moringa Oleifera leaf extract and purple sweet potato extract (Ipomoea Batatas) as green corrosion inhibitors for API 5L in the environment of 0.2 M HCl. The characterization of the two inhibitors was carried out by FTIR testing and showed that the compounds contained in the two inhibitors were flavonoids. Testing of potentiodynamic polarization and EIS with variations in inhibitor addition and mixtures between the two inhibitors was carried out to study the inhibitory properties, from this study it can be seen that each of the two inhibitors can be used as green corrosion inhibitors while the mixture between the two inhibitors cannot protect the API 5L environment of 0.2 M HCl. From the potentiodynamic polarization test showed that by increasing the concentration of Moringa leaf extract inhibitors, the corrosion rate will decrease and the inhibition efficiency value increases with the highest value is 73.08%, whereas with the addition of the purple yam extract inhibitor concentration the corrosion rate decreases with the inhibition efficiency value maximum of 65.31%. However, the results of the potentiodynamic polarization test for the combination of the two inhibitors showed an increasing corrosion rate. The EIS test results show that these two inhibitors can protect the metal by forming a layer of film that lines the metal surface. The adsorption inhibitor mechanism shows as a mechanism of physical adsorption and in accordance with the model from Langmuir for Moringa leaf extract inhibitors and Temkin for purple sweet potato extract.

"

"Indonesia memiliki potensi cengkeh yang melimpah,daunnya dapat gugur setiap minggunya 0.96 kg/pohon. Inhibitor yang digunakan adalah ekstrak daun cengkeh dengan konsentrasi 1ml,2ml,3ml,4ml,5ml dan minyak cengkeh dengan konsentrasi 2ml,4ml,6ml,8ml,10ml. Pengujian dilakukan dengan metode linear polarisasi, Fourier Transform Infrared Spectroscopy ( FTIR ), Gas Chromatography Mass Spectroscopy ( GCMS ), dan Eletrochemical Impedance Spectroscopy ( EIS ). Konsentrasi optimum pada ekstrak daun cengkeh berada pada konsentrasi 4 ml dengan laju korosi 0.042 mm/year dan efisiensi 46.6 % sedangkan minyak cengkeh konsentrasi optimumnya berada pada konsentrasi 8 ml dengan laju korosi 0.001 mm/year dengan efisiensi 98.6 %. FTIR menunjukkan gugus - gugus fungsi yang berada di dalam inhibitor dan diperkuat dengan hasil GCMS untuk mengetahui senyawa aktif yang berada dalam inhibitor. Pengujian FTIR juga menunjukkan bahwa gugus - gugus fungsi pada inhibitor menempel pada permukaan sampel ketika sampel di rendam. Mekanisme adsorpsi dari kedua inhibitor adalah physical adsorption dengan nilai ΔGads pada inhibitor ekstrak daun cengkeh sebesar -7.575 kJ/mol, dan - 12.142 kJ/mol untuk inhibitor minyak cengkeh. EIS menunjukkan adanya peningkatan nilai tahanan charge transfer pada setiap kenaikan konsentrasi inhibitor dan nilai dari Cdl menurun yang menunjukkan bahwa terjadi pembentukan lapisan protektif. Nilai charge transfer dari inhibitor minyak cengkeh lebih besar yang berarti minyak cengkeh memiliki kemampuan inhibisi lebih baik dan ini diperkuat dari hasil polarisasi. Kedua jenis inhibitor ini termasuk dalam jenis inhibitor campuran (mix type inhibitor).

---

Indonesia has abundant potential clove, leaves can fall every week 0.96 kg/tree. Inhibitor which used on this research are clove leave extract with concentration 1ml,2ml,3ml,4ml,5ml and clove oil with concentration 2ml,4ml,6ml,8ml,10ml. Inhibitor are examined by linear polarization, Fourier Transform Infrared Spectroscopy ( FTIR ), Gas Chromatography Mass Spectroscopy ( GCMS ), and Electrochemical Impedance Spectroscopy ( EIS ). The result show that optimum concentration of clove leave extract is at 4 ml with corrosion rate 0.042 mm/year and efficiency 46.6% where as optimum concentration of clove oil is at 8 ml with corrosion rate 0.001 mm/year and efficiency 98.6 %. FTIR obtain functional group which contained in inhibitor and GCMS result also show active compound in inhibitor. FTIR show that functional group in inhibitor adsorp on the metal surface when sample is soaked in inhibitor. Adsorption mechanism of these inhibitor is physical adsorption with ΔGads of clove leave extract inhibitor is -7.575 kJ/mol, and - 12.142 kJ/mol for clove oil inhibitor. EIS show increasing charge transfer resistance with increasing inhibitor concentration and decreasing Cdl also show there are protective film forming. The charge transfer resistance of clove oil inhibitor higher, means clove oil has better inhibition than clove leaves extract. Both of these inhibitor are included in mix type inhibitor."