Hasil Pencarian  ::  Simpan CSV :: Kembali

"Indonesia merupakan negara yang kaya akan sumber daya alam khususnya pada bahan tambang. Pasir besi banyak ditemukan di pesisir Indonesia yang didalamnya mengandung beberapa mineral berharga seperti hematit Fe2O3, ilmenit FeTiO3 serta rutil TiO2. Studi penelitian terkait pasir besi telah dikembangkan yang bertujuan untuk mengetahui pengaruh temperatur terhadap pembentukan titanomagnetit Fe2TiO4-Fe3O4 pada proses reduksi pasir besi menggunakan reduktor batubara dan aditif sodium sulfat Na2SO4. Hasil pengujian XRD dan semi-kuantitaif pada variasi temperatur 700oC, 800oC dan 900oC diperoleh temperatur optimum yaitu temperatur 900oC dengan jumlah titanomagnetit Fe2TiO4-Fe3O4 sebesar 48.5.

---

Indonesia is a developing country that has rich deposit of natural resources particularly in mineral ores. Many of iron sand found in coastal Indonesia that contains some valuable minerals such as hematite Fe2O3, ilmenite FeTiO3 sand rutile TiO2. Research study related to iron sand has developed that aims to determine the effect of temperature against the form of titanomagnetite in reduction process using coal as reductor and sodium sulphate Na2SO4 as an additive. The results of XRD characterization and semi quantitative with temperature variable 700oC, 800oC and 900oC obtained that 900oC is an optimum temperature with amount of titanomagnetite Fe2TiO4 Fe3O4 as much as 48.5."

"Penelitian ini memiliki tujuan untuk mengetahui pengaruh penambahan sodium sulfat Na2SO4 pada proses reduksi pasir besi titan. Sampel yang digunakan merupakan pasir besi yang berasal dari daerah Sukabumi, Jawa Barat, serta menggunakan batu bara sebagai reduktor dan aditif sodium sulfat Na2SO4 yang menjadi parameter pada penelitian ini. Dari hasil pengujian XRD dan data analisa perhitungan semi-kuantitatif diperoleh peningkatan kadar senyawa titano-magnetit Fe2TiO4-Fe3O4 yang lebih tinggi setelah proses reduksi menggunakan aditif sodium sulfat Na2SO4. Dari data hasil perhitungan semi-kuantitatif untuk variasi penambahan sodium sulfat Na2SO4 sebesar 5, 15, dan 25 didapatkan bahwa pembahan sodium sulfat Na2SO4 memiliki nilai optimum pada penambahan 15 dengan jumlah senyawa titano-magnetit Fe2TiO4-Fe3O4 yang terbentuk sebesar 46,9.

---

This study aims to determine the effect of sodium sulfate Na2SO4 addition on the reduction proses of tiania iron sand. The sample that used in this research are the iron sand that taken from Sukabumi, West Java, coal as reductor, and sodium sulfate Na2SO4 as additive and primary parameter. From the result of XRD characterization and semi quantitative analysis the content of titano magnetite Fe2TiO4 Fe3O4 in the iron sand increase with addition of sodium sulfate Na2SO4. Meanwhile, from semi quantitative analysis result with the variation of sodium sulfate Na2SO4 in 5, 15, and 25 have an optimum point on the addition of 15 sodium sulfate Na2SO4 with 46,9 of titano magnetite Fe2TiO4 Fe3O4 content."

"Pasir besi di Indonesia merupakan salah satu sumber daya alam yang mempunyai keberadaan cukup luas, namun belum dimanfaatkan dengan baik. Pada pasir besi terdapat kandungan senyawa yang berharga. Salah satunya adalah Titanium Ti yang berikatan dengan kandungan pasir besi. Titanium sangat dibutuhkan di Indonesia karena sifatnya yang baik sebagai paduan dan keungulan performanya. Eksperimen ini dilaksanakan dengan tujuan untuk mengetahui pengaruh penambahan additive berupa Na2SO4 dan juga jumlah batubara sebagai reductor. Pemanggangan Roasting dilakukan pada temperature 600°C untuk membuat fasa homogen, lalu dilanjutkan penambahan sodium sulfat Na2SO4 20 wt. pada sample B dan juga batubara pada proses peletisasi dengan penambahan 2 ,4 dan 6 pada sample A1-A3 dan B1-B3 berturut - turut, kemudian dilakukan proses reduksi langsung pada temperature 700°C dengan durasi selama 65 menit. Hasil reduksi dicelupkan kedalam ember berisi air dan di gerus sehingga memudahkan dalam proses pemisahan menggunakan magnet. Pada proses reduksi, hasil terbaik ditunjukan pada sample B3 dengan penambahan 1.68 gram 6 wt. batubara dan 20 wt. Na2SO4 dengan kandungan 8.95 Ti dan 43.184 Fe. Proses pemisahan dengan magnet dapat menjelaskan bahwa kandungan Ti berada pada sampel tail dan Fe pada sampel concentrate.

---

Iron Sand in Indonesia is one of the natural resources that have a wide availability, but has not been used well. In iron sand there is presents valuable compound content. One of them is Titanium Ti , which binds with iron sand content. Titanium is needed in Indonesia because it is good as alloying element and superior performance. This experiment will conduct with the aim of knowing the effect of addition Na2SO4 and also the amount of coal as reducing agent. Roasting will be implemented at a temperature of 600°C to create a homogeneous phase, and then it will be continued addition of sodium sulfate Na2SO4 20 wt. and also coal with addition 2 , 4 and 6 for sample A1 A3 and B1 B3 respectively in pelletization process then direct reduction process at temperature 700°C with duration for 65 minutes. The reduction products will quench in the water bucket and continue with crushing so it can separate easily in magnetic separation. The best result in reduction process performed by sample B3 with addition 1.86 gram 6 and 20 wt. Na2SO4 with content 8.95 of Ti and 43.184 of Fe. The magnetic separation explained if the tailing sample has rich of Ti content and Fe in concentrate."

"Indonesia merupakan negara yang dikenal memiliki sumber daya alam yang melimpah terutama di bidang cadangan mineralnya. Pasir besi merupakan salah satu mineral paling melimpah di Indonesia. Kandungan utama pasir besi adalah senyawa oksida besi, yaitu magnetit (Fe3O4), hematit (Fe2O3), titomagnetit (Fe2TiO4), dan ilmenit (FeTiO3). Ilmenite merupakan mineral yang mengandung unsur utama besi dengan pengotor lain yang memiliki harga jual tinggi yaitu titanium. Studi penelitian yang berkaitan dengan reduksi karbotermik telah dikembangkan dengan tujuan menyelidiki efek kadar natrium sulfat pada tingkat akhir terak kaya besi dan titanium. Reduksi karbotermik dilakukan dengan menggunakan muffle tube furnace pada suhu 12000C selama 1 jam. Sampel yang direduksi adalah campuran pasir besi dan arang cangkang sawit sebagai reduktor 6,91% dari massa sampel dan divariasikan aditif natrium sulfat sebesar 0%, 1,5%, 3%, dan 4,5% dari massa sampel. Hasil uji XRF menunjukkan indikasi terjadinya proses reduksi pasir besi karena terjadi peningkatan kadar unsur besi. Hasil uji SEM-EDS menunjukkan perubahan morfologi untuk setiap penambahan konsentrasi natrium sulfat sebesar 0%, 1,5%, 3%, dan 4,5%. Kondisi optimal terjadi pada penambahan 3% natrium sulfat karena terdapat senyawa besi dan TiO2 yang berbentuk anatase dan recovery mencapai 88,35%.

---

Indonesia is a country known to have abundant natural resources, especially in the field of mineral reserves. Iron sand is one of the most abundant minerals in Indonesia. The main content of iron sand is iron oxide compounds, namely magnetite (Fe3O4), hematite (Fe2O3), titomagnetite (Fe2TiO4), and ilmenite (FeTiO3). Ilmenite is a mineral that contains the main element iron with another impurity that has a high selling price, namely titanium. Research studies related to carbothermic reduction have been developed with the aim of investigating the effect of sodium sulfate levels on the final levels of iron and titanium rich slag. Carbothermic reduction was carried out using a muffle tube furnace at a temperature of 12000C for 1 hour. The sample that was reduced was a mixture of iron sand and palm shell charcoal as a reducing agent of 6.91% of the sample mass and varied with sodium sulfate additives of 0%, 1.5%, 3%, and 4.5% of the sample mass. XRF test results indicate an indication of an iron sand reduction process due to an increase in iron content. SEM-EDS test results showed morphological changes for each addition of sodium sulfate concentration of 0%, 1.5%, 3%, and 4.5%. The optimal condition occurs in the addition of 3% sodium sulfate because there are iron and TiO2 compounds in the form of anatase and recovery reaches 88.35%."

"Sumber daya alam yang melimpah di Indonesia menuntut industri pertambangan dan pengolahan mineral untuk dapat mengolah sumber daya yang ada menjadi bahan baku untuk kelancaran siklus industri di Indonesia. Salah satu sumber daya yang dibutuhkan dalam industri adalah bahan baku mineral berupa pasir besi. Pasir besi merupakan salah satu mineral paling melimpah di Indonesia. Kandungan utama pasir besi adalah senyawa oksida besi yaitu magnetit (Fe3O4), hematit (Fe2O3), titanomagnetit (Fe2TiO4), dan ilmenit (FeTiO3). Mineral ini mengandung unsur utama besi dengan pengotor lain yang memiliki harga jual tinggi seperti titanium. Kajian penelitian terkait reduksi karbotermik telah dikembangkan dengan tujuan untuk mengetahui pengaruh proses distribusi ukuran bahan baku terhadap reduksi karbotermik pasir besi dengan arang tempurung kelapa sawit dan natrium sulfat. Hasil penelitian menunjukkan bahwa terjadi perubahan kadar sebelum dan sesudah reduksi sehingga bisa dikatakan terjadi proses reduksi. Selain itu, tampilan visual metode milling 60 menit lebih baik daripada metode lainnya. Persentase perolehan kembali Fe tertinggi dicapai pada sampel 3 yang diberi perlakuan bubuk selama 4 menit tanpa penambahan Na2SO4 sebesar 91%.

---

The abundant natural resources in Indonesia require the mining and mineral processing industries to be able to process existing resources into raw materials for the smooth running of the industrial cycle in Indonesia. One of the resources needed in the industry is mineral raw material in the form of iron sand. Iron sand is one of the most abundant minerals in Indonesia. The main content of iron sand is iron oxide compounds, namely magnetite (Fe3O4), hematite (Fe2O3), titanomagnetite (Fe2TiO4), and ilmenite (FeTiO3). This mineral contains the main element iron with other impurities that have a high selling price such as titanium. Research studies related to carbothermic reduction have been developed with the aim of knowing the effect of the raw material size distribution process on the carbothermic reduction of iron sand with palm oil shell charcoal and sodium sulfate. The results showed that there was a change in levels before and after the reduction so that it could be said that there was a reduction process. In addition, the visual display of the 60 minute milling method is better than other methods. The highest percentage of Fe recovery was achieved in sample 3 which was treated with powder for 4 minutes without the addition of Na2SO4 by 91%."

"Indonesia memiliki sejumlah besar deposit bijih laterit, salah satunya dalam bentuk bijih limonit. Namun, bijih limonit jarang digunakan sebagai bahan baku pembuatan feronikel karena konsentrasi Ni relatif rendah (<1,5%) sehingga dianggap tidak menguntungkan. Feronikel umumnya dihasilkan melalui jalur tanur tiup atau tungku putar-tugku busur listrik yang membutuhkan energi yang besar (temperatur 1300-1400°C). Dengan permasalahan tersebut, penelitian ini bertujuan untuk mengolah bijih nikel laterit menjadi feronikel menggunakan suatu metode proses selektif reduksi dengan biaya (energi) yang relatif lebih rendah. Proses reduksi selektif dilakukan menggunakan muffle furnace dengan temperatur rendah dan diikuti pemisahan magnetik basah untuk mendapatkan kembali nikel dalam bentuk logam paduan (feronikel). Untuk mengurangi temperatur reduksi, Na2SO4 sebagai aditif ditambahkan ke dalam proses. Proses ini diharapkan dapat membebaskan nikel dari mineral pengganggunya sehingga akan meningkatkan kadar nikel dalam konsentrat. Proses reduksi selektif dilakukan pada rentang temperatur 950-1150°C, waktu reduksi 60-120 menit, jumlah reduktor 5-15% berat, dan 10% aditif Na2SO4. Karakterisasi bijih laterit hasil reduksi dilakukan menggunakan X-ray Diffraction (XRD), mikroskop optik dan Scanning Electron Microscope (SEM) yang dilengkapi Energy Dispersive X-ray Spectroscopy (EDS) serta konsentrat feronikel dan tailing diidentifikasi menggunakan X-ray Fluororescene (XRF). Hasil penelitian menunjukkan seiring meningkatnya temperatur dan waktu reduksi, kadar dan perolehan nikel dari bijih nikel yang telah direduksi dengan penambahan aditif Na2SO4 lebih tinggi jika dibandingkan dengan tanpa penambahan aditif. Sedangkan semakin banyak jumlah reduktor yang ditambahkan menyebabkan kadar dan perolehan nikel menurun. Kondisi proses yang ekonomis dan efisien diperoleh pada proses reduksi selektif bijih nikel laterit dengan 10% Na2SO4 pada temperatur 1150oC selama 60 menit dengan penambahan 5% berat reduktor dimana kadar dan perolehan nikelnya adalah 6,1% dan 70,3% dengan kadar dan perolehan besi yang rendah, yaitu 56,18% dan 17,98%. Kehadiran Na2SO4 akan meningkatkan laju reduksi kinetik dan memfasilitasi pembentukan FeS yang dapat menurunkan metalisasi besi dan meningkatkan selektifitas reduksi nikel dan besi sehingga perolehan nikel meningkat, sedangkan perolehan besi menurun.

---

Indonesia has large amounts of laterite ore deposits, one of them in the form of limonite ore. However, limonite ore is rarely used as raw materials for produce ferronickel, since the concentration of Ni is relatively low 1,5 so it is not considered beneficial. Ferronickel is generally produced through blast furnace or electric arc furnace which required a large amount of energy temperature 1300 ndash 1400 C . With the issues, this research aims to process limonite ore into ferronickel using a selective reduction method with low cost energy . The selective reduction process was carried out in a muffle furnace with lower temperature and followed by wet magnetic separation in order to recover nickel in the form of ferronickel. To reduce the reduction temperature, sodium sulfate as an additive was added to the process. This process is expected can liberate nickel from the impurities minerals so it will increase the nickel grade in the concentrate. The selective reduction process was carried out at temperature range of 950 ndash 1150 C for 60 120 minutes, 5 15 wt. reductant, and 10 wt. additive.

The characterization of reduced ore was performed by using by X ray Diffraction XRD, optical microscope and Scanning Electron Microscope SEM with Energy Dispersive X ray Spectroscopy EDS and ferronickel concentrate was identified by X ray Fluororescene XRF. The results showed that as the temperature and reduction time increases, the nickel grade and recovery of the reduced ore with the addition of Na2SO4 was higher than without the additive. While the more amount of reductant added causes the nickel grade and recovery decrease. The economical and efficient process conditions were obtained in a selective reduction of laterite ore with 10 wt. Na2SO4 at temperature of 1150 C for 60 minutes and 5 wt. reductant with the nickel grade of 6.1 and nickel recovery of 70.3 and low iron grade and recovery 56,18 and 17,98 . The presence of Na2SO4 increase the kinetic reduction rate and facilitate the formation of FeS that can decrease iron metallization and increase the selectivity of nickel and iron reduction thus increase the nickel recovery, while decrease the iron recovery."

"Bijih besi menjadi salah satu sumber daya mineral yang sangat berpotensial di Indonesia untuk dilakukan proses pengolahan dan diproduksi sehingga menjadi logam mineral yang memiliki nilai guna Proses pengolahan bijih besi sudah banyak dikembangkan dengan cara reduksi langsung maupun reduksi tidak langsung dimana kedua proses tersebut membutuhkan reduktor untuk mereduksi bijih besi menjadi logam murni Reduktor yang digunakan pada proses reduksi bijih besi dalam bentuk padatan seperti batu bara dan kokas maupun dalam bentuk gas seperti gas metana Pada penelitian kali ini dilakukan pengembangan proses reduksi bijih besi menggunakan reduktor biomassa yaitu cangkang kelapa sawit yang merupakan limbah dari hasil perkebunan buah kelapa sawit Dalam penelitian digunakan bijih besi laterit Kalimantan dan cangkang kelapa sawit dari sisa perkebunan di Palangkaraya Kalimantan Tengah Bijih besi direduksi ukurannya hingga membentuk partikel serbuk 18 Tujuan dalam penelitian ini adalah untuk mengetahui pengaruh variabel temperatur reduksi dengan waktu dan rasio massa yang konstan terhadap hasil reduksi bijih besi Variasi temperatur yang diuji dalam penelitian adalah 600oC 700oC 800oC 900oC dan 1 000oC Seluruh sampel diuji dalam waktu 120 menit dan rasio bijih besi dengan cangkang kelapa sawit 1 3 yang dimasukkan ke sebuah krusibel dan perlakuan reduksi langsung dilakukan di dalam muffle furnace Hasil XRD menunjukkan bahwa pada 1 000oC merupakan temperatur optimum dengan waktu reduksi selama 120 menit karena kandungan bijih besi seluruhnya berupa peak Fe metallic tanpa adanya kehadiran peak peak besi oksida lainnya.

---

Iron ore become one of minerals source that very pottential in Indonesia for process to have result value metallic mineral Iron steel making process have been developed by direct reduction and indirect reduction process which both of them need solid reducing agent for reduction iron ore like coal and coke or gas reduction agent like methane gas In this research it develop renewable reduction iron ore process use biomass reductor palm kernell shell is waste from palm tree plantation The research was conducted laterite ore from Kalimantan and palm kernel shell from residue plantation in Palangkaraya Central Kalimantan Before reduction process is started iron ore must be crushing to reduce particle size forming powder particles with size about 18 The purpose of the research is to determine the effect of reduction temperature with optimum time and mass ratio to result of reduction iron ore Variation of temperature that be examined is 600oC 700oC 800oC 900oC and 1 000oC All of samples is tested in 120 minutes and mass ratio 1 3 for iron ore and palm kernell shell Mixed samples are put in crucible and reduction process take place in muffle furnace XRD results showed that in 1 000oC is optimum temperature during 120 minutes because all composition of iron ore is Fe metallic peaks without other iron oxide peaks."

"ABSTRAKBijih besi di Indonesia digolongkan menjadi tiga jenis yaitu besi primer, besi laterit dan pasir besi. Penelitian ini bertujuan untuk mengetahui hasil reduksi langsung bijih besi laterit dari pulau Sebuku, Kalimantan Selatan dan besi goethite sintetik secara karbotermik. Proses pembuatan komposit bijih besi laterit dimulai dari pulverisasi bijih besi laterit dan batubara, pengeringan oven pada temperatur 120 C, pencampuran, peletisasi, dan roasting dalam furnace pada temperatur 400 C. Reduksi langsung dilakukan menggunakan tube furnace dengan dua periode waktu yang berbeda yaitu 30 dan 60 menit serta tiga variasi temperatur yaitu 1000 C, 1100 C, dan 1200 C. Variasi komposisi batubara, temperatur, dan waktu tahan reduksi memberikan pengaruh terhadap hasil reduksi langsung yaitu penurunan derajat reduksi dan derajat metalisasi pada temperatur 1100oC dan kenaikan pada temperatur 1200oC. Derajat reduksi tertinggi dihasilkan oleh bijih besi goethite sintetik dengan komposisi batubara 24 pada temperatur 1000oC dan waktu tahan 60 menit sebesar 88,91 dan derajat reduksi terendah dihasilkan oleh bijih besi dari Sebuku dengan komposisi 16 batubara pada temperatur 1100oC dan waktu tahan 30 menit sebesar 69,81. Derajat metalisasi tertinggi dihasilkan dari bijih besi goethite sintetik dengan komposisi batubara 24 pada temperatur 1000oC dan waktu tahan 60 menit sebesar 94,35 dan derajat metalisasi terendah dihasilkan oleh bijih besi dari Sebuku dengan komposisi batubara 16 pada temperatur 1100oC dan waktu tahan 30 menit sebesar 72,53.

---

ABSTRACTIron ore in Indonesia has been classified into three types such as primary iron, iron laterite and iron sand. This study aimed to determine the results of direct reduction of Sebuku Lateritic Iron Ore from South Kalimantan and synthetic goethite iron with carbothermic reaction. Laterite ore composite making process was started from pulverizing of coal and laterite iron ore, drying oven in 120 C, mixing, pelletizing, and roasting. Direct reduction performed using tube furnace with two different time periods are 30 and 60 minutes and three temperature variation there are 1000 C, 1100 C, and 1200 C. Variation of coal compositions, temperature, and holding time have an influence on the results of direct reduction which is decreasing reduction degree and metallization degree in 1100oC and increasing in 1200oC. The highest of reduction degree is synthetic goethite with 24 coal composition in 1000oC and 60 minutes holding time at 88,91 and the lowest of reduction degree is lateritic iron ore from Sebuku with 16 coal composition in 1100oC and 30 minutes holding time at 69,81. The highest metallization degree is synthetic goethite with 24 coal composition in 1000oC and 60 minutes holding time at 94,35 and the lowest of metallization degree is iron ore from Sebuku with 16 coal composition in 1100oC and 30 minutes holding time at 72,53. "

"ABSTRACTBijih besi kadar rendah dari Lampung direduksi menggunakan biomassa tadah kosong kelapa sawit yang sudah dipirolisis sebagai reduktor pada temperatur 1400 dan 1450 oC selama 30 dan 40 menit. Hanya hasil reduksi besi pada temperatur 1450 oC selama 40 menit yang terpisah dari kotorannya, dengan derajat reduksi sebesar 98.5 dan derajat metalisasi 80.85 . Mikrostrukturnya adalah besi metalik dengan beberapa inklusi. Sementara hasil reduksi besi lainnya yang tidak terpisah dari pengotornya terdiri dari dua dominan fasa: besi metalik putih dan fayalite Fe2SiO4 dalam bentuk lamellar. Di mana persentase terak fayalite lebih besar daripada besi metalik.

---

ABSTRACTLow grade iron ore from Lampung is reduced using biomass pyrolyzed palm oil empty fruit bunch as reductant at temperature 1400 and 1450 oC for 30 and 40 minutes. Only iron nugget that is reduced at 1450 oC for 40 minutes that is completely separated from its slag, with reduction degree 98.5 and metallization degree 80.85 . The microstruture has metallic iron as base with some inclusions. On the other hand, the other iron nuggets that are not separated from its slag consist of two prominent phases white metallic iron and lamellar fayalite Fe2SiO4 . Where the percentage of fayalite slag is greater than the metallic iron."

"Energi yang besar diperlukan untuk menghasilkan feronikel melalui proses pengolahan bijih nikel laterit. Pengolahan bijih nikel laterit kadar rendah akan menjadi tidak ekonomis. Saat ini, reduksi selektif dianggap sebagai proses yang potensial untuk menghasilkan nikel berkadar tinggi dalam pembuatan feronikel dan mulai banyak dilakukan penelitian untuk mendapatkan metode reduksi selektif yang ekonomis. Pada penelitian ini digunakan natrium sulfat, natrium karbonat, dan natrium klorida sebagai aditif dengan variasi dosis 5, 10, dan 15 berat. Batu bara antrasit dari Padang digunakan sebagai reduktor pada penelitian ini sebanyak 5 berat. Reduksi dilakukan pada variasi temperatur 950, 1050, dan 1150oC selama 60 menit. Proses separasi magnetik basah dengan kekuatan magnet 500 Gauss dilakukan pada tahapan setelah reduksi selektif untuk memisahkan konsentrat feronikel yang bersifat magnetik dan tailing pengotor yang bersifat non-magnetik. Karakterisasi bijih laterit hasil reduksi dilakukan menggunakan X-ray Diffraction XRD , mikroskop optik, dan Scanning Electron Microscope SEM yang dilengkapi Energy Dispersive X-ray Spectroscopy EDS . Konsentrat dan tailing hasil separasi magnetik diidentifikasi menggunakan X-ray Fluororescene XRF . Hasil penelitian ini menunjukkan bahwa pada penambahan 15 berat aditif dengan variasi temperatur reduksi, terlihat bahwa terjadi peningkatan yang signifikan pada kadar nikel yang dihasilkan dari proses separasi magnetik. Kadar nikel optimum didapatkan pada temperatur reduksi 1150 C dengan nilai 15,06 untuk penambahan aditif natrium sulfat; 2,18 untuk penambahan aditif natrium karbonat; dan 2,27 untuk penambahan aditif natrium klorida. Pada reduksi selektif yang dilakukan pada temperatur reduksi 1150 C selama 60 menit dengan variasi penambahan persentase berat aditif, terlihat bahwa terjadi peningkatan yang signifikan pada kandungan nikel. Dosis aditif optimum untuk masing-masing aditif diperoleh pada penambahan 15 berat.

---

The extraction process of lateritic nickel ores to produce ferronickel required high energy. It will not be economical to process low grade lateritic nickel ores. Nowadays, selective reduction process is being a potential process to produce high grade nickel from low grade nickel ores and there are many reasearches to gain an economical method of this process. The recent work used sodium sulfate, sodium carbonate, and sodium chloride as additives with the variative dossage of 5, 10, and 15w.t. Antrachite coal from Padang used as reductant with the dossage of 5w.t. The reduction was done with variation reduction temperature of 950, 1050, and 1150oC for 60 minutes. Wet magnetic separation process was done afterwards to separate the magnetic particle feronickel as concentrate and the non magnetic particle gangue as tailing. It was done by 500 Gauss of magnet. The caracterization of reduced ore had been done using X ray Diffraction XRD, optical microscope, and Scanning Electron Microscope SEM completed by Energy Dispersive X ray Spectroscopy EDS. Concentrate and tailing of magnetic separation process had been observed by X ray Fluororescene XRF . The results of the recent work shows that the addition of 15w.t. of additive with the variation of reduction temperature obtained significantly increasing of nickel grade from magnetic separation process. The optimum nickel grade from the reduction temperature of 1150 C are 15,0625 for the addition of sodium sulfate, 2,1855 for the adition of sodium carbonate, and 2,2695 for the addition of sodium chloride. The result of selective reduction process at the reduction of temperature of 1150 C for 60 minutes with variation of additive dossage shows that the optimum dossage for each additive is 15w.t. "