"ABSTRAKNanopartikel Emas AuNP memiliki sifat optik dan kimia yang unik yang mana bergantung pada ukuran dan bentuknya. Meskipun berbagai metode sintesis AuNP dengan bentuk dan ukuran terkontrol sebagian besar telah dilaporkan dengan metode seed-mediated, sintesis dengan metode seedless masih tetap menantang. Disini kami melaporkan metode seedless untuk sintesis AuNP menggunakan surfaktan cetyltrimethylammonium 4-vinyl benzoate CTAVB dengan hanya mencampurkan dengan prekursor emas dalam air dengan adanya HCl. Dalam penelitian ini, pengaruh konsentrasi prekursor emas, CTAVB dan HCl terhadap hasil akhir diselidiki dan dikarakterisasi menggunakan spektroskopi UV-vis, Transmission Electron Microscopy TEM, dan Scanning Electron Microscopy SEM. Dari hasil tersebut menunjukkan bahwa konsentrasi prekursor emas 0,1 mM - 0,5 mM dan CTAVB 5 mM - 15 mM mempengaruhi ukuran akhir dari AuNP, sedangkan konsentrasi HCl 0 mM-10 mM mempengaruhi morfologi dan juga ukuran.

---

ABSTRACTGold Nanoparticles Au NPs have unique optical and chemical properties which depend on their sizes and shapes. While various methods of Au NPs synthesis with tunable shapes and sizes mostly synthesized by seed mediated method have been well reported, its synthesis for the seedless method still remains challenging. Herein we report a seedless method for the synthesis of Au NPs using cetyltrimethylammonium 4 vinyl benzoate CTAVB surfactant by simply mixing with gold precursor in water in the presence of HCl. In this study, the effects of gold precursor, CTAVB and HCl concentration upon the final product have been investigated and characterized using UV vis spectroscopy, Transmission Electron Microscopy TEM, and Scanning Electron Microscopy SEM. The results show that the concentration of gold precursor 0.1 mM 0.5 mM and CTAVB 5 mM 15 mM affect the final size of Au NPs, whereas the concentration of HCl 0 mM ndash 10 mM affects the morphology as well as their size."

"ABSTRAKPolihdedral AuNP banyak menarik perhatian para peneliti karena memiliki sifat unik yang berasal dari facet dan sharp edges. Telah dilaporkan bahwa sharp edges yang dimiliki oleh nanopartikel dapat dengan secara signifikan meningkatkan medan listrik, sehingga berpotensi untuk diaplikasikan pada surface-enchanced Raman scattering, sensor kimia dan biologi serta pembuatan nanodevices. AuNP bentuk oktahedron adalah salah satu dari polihedral Au NP yang memiliki sharp edges dan memiliki delapan facet {111} sehingga memiliki stabilitas maupun medan elektromagnetik yang tinggi. Telah dilakukan sintesis AuNP berbentuk oktahedron melalui pemanfaatan efek synergic yang dimiliki oleh cetytrimethylammonium vinyl benzoate (CTAVB) dan HCl serta penambahan zat aditif erak nitrat (AgNO3) sebagai facet blocking agent. Pada seed yang berbentuk single crystal, AgNO3 memiliki kecenderungan untuk teradsoprsi lebih kuat pada facet {100} karena memiliki surface energy yang lebih tinggi dibandingkan dengan facet {111}. Namun pada penelitian ini, AgNO3 dilaporkan teradsorpsi dengan kuat pada facet {111} karena facet {100} telah diisi CTAVB. Hal ini akan menekan laju pertumbuhan partikel pada facet {111} dan pertumbuhan partikel pada facet {100} lebih dominan sehingga akan menghasilkan AuNP berbentuk oktahedron sebagai produk akhir. Beberapa parameter yang telah dilakukan dalam sintesis nanopartikel ini adalah konsentrasi AgNO3, temperatur serta waktu reaksi. Variasi konsentrasi AgNO3 yang digunakan adalah 1%; 0.75%; 0.5% dengan variasi suhu 30 ºC dan 40 ºC. Pengamatan dilakukan sejak pembentukan partikel dan setiap 24 jam berikutnya. Hasil TEM dan SEM menunjukan hasil AuNP berbentuk oktahedron yang cukup baik dan seragam pada variasi AgNO3 0.75% di temperatur 30 ºC pada hari ke-6. Variasi 1% menghasilkan bentuk oktahedron yang rounded dengan ukuran kecil, variasi AgNO3 0.5% menghasilkan partikel berukuran paling besar dengan tingkat polidispersitas paling tinggi.

---

ABSTRACTPolyhedral AuNP attracts many researchers because it has a distinctly sharp and inherent characteristic. It has been reported that the sharp angles possessed by nanoparticles can significantly increase the electric field which allows for many applications, such as, surface-enchanced Raman scattering, chemical and biological sensors and manufacture for nanodevices. Synthetis of AuNP has been performed through the use of synergic effects possessed by cetytrimethylammonium vinyl benzoate (CTAVB) and HCl and addition of silver nitrate additive (AgNO3) as a facet blocking agent. In single-crystalline seeds, AgNO3 has a tendency to be more adsorbed on the {100} surface because it has a higher surface energy compared to the {111} facet. However, in this study, AgNO3 was reported to be strongly adsorbed on facet of {111} because the {100} facet was already filled with CTAVB. This will suppress the particle growth rate of the {111} facets and the growth on {100} facets were more dominant resulting in an octahedral shape as a final product. Some parameters that have been varied in this nanoparticle synthesis are AgNO3 concentration, temperature and reaction time. Variations of AgNO3 concentration used in this synthesis were 1%; 0.75%; 0.5% relative to Au precursors with temperature variation of 30 º C and 40 º C. Monitoring through visual colorimetric show that a pink color was formed after 24 hours and intensified with time. The TEM and SEM measurements showed that the optimum condition for obtaining monodisperse octahedral AuNP was when the concentration of AgNO3 at 0.75%, temperature of 30 ºC, and 6 days of reaction time. Variations 1% resulted in octahedron with slightly rounded edges and smaller size. More polydisperse and bigger particle size was formed when the concentration of AgNO3 0.5%."

"Nanopartikel emas (AuNP) merupakan salah satu jenis nanopartikel yang banyak dikembangkan dalam pemanfaatannya di bidang biomedis. Berbagai metode telah diciptakan dalam proses fabrikasi AuNP. Dari berbagai metode tersebut didapatkan berbagai variasi jenis, bentuk, dan ukuran AuNP. Salah satu jenis nanopartikel emas yang cukup mendapat perhatian adalah AuNP berpori. Nanomaterial berpori memiliki perbandingan rasio volume dan luas permukaan yang tinggi juga volume pori yang besar sehingga banyak diteliti dalam berbagai aplikasi teknologi termasuk sistem penghantaran obat. Review kali ini membahas proses sintesis AuNP berpori secara cepat dan sederhana melalui berbagai metode seperti kimia basah, sacrificial template, green synthesis, filtrasi vakum, dan galvanic replacement. Dari proses sintesis nanopartikel emas berpori, dihasilkan ukuran partikel bervariasi antara 17,1-1000 nm dengan berbagai bentuk dengan kestabilan yang baik. Review ini menunjukkan bahwa nanopartikel emas berpori yang disintesis dengan sederhana dan cepat cenderung stabil untuk digunakan dalam berbagai jenis aplikasi.

---

Gold nanoparticles (GNP) are a type of nanoparticle that has been widely developed for use in the biomedical sector. Various methods have been found in the GNP fabrication process. From these various methods, various types, shapes and sizes of GNP were obtained. One type of gold nanoparticle that has received considerable attention is porous GNP. Porous nanomaterials have high volume and surface area ratios as well as large pore volumes so that they are widely studied in various applications including drug delivery systems. This review discusses the quick and simple synthesis process of porous GNP through various methods such as wet chemical, sacrificial template, green synthesis, vacuum filtration, and galvanic replacement. From the synthesis process of porous gold nanoparticles, the particle sizes varied between 17.1-1000 nm with various shapes with good stability has been produced. This review demonstrates that simple and fast synthesized porous gold nanoparticles are likely to be stable for use in a wide variety of applications."

"Modifikasi elektroda karbon, glassy carbon (GC) dan boron-doped diamond (BDD), menggunakan nanopartikel emas (AuNP) dilakukan dengan menggunakan teknik self-assembly. Teknik ini dipilih berdasarkan interaksi elektrostatik antara AuNP yang terperangkap ion sitrat dengan gugus amina yang dimodifikasikan pada BDD dan GC. Material yang diperoleh, AuNP-GC dan AuNP-BDD, kemudian digunakan sebagai elektroda pendeteksi As 3+ menggunakan teknik anodic stripping voltammetry (ASV). Anodic stripping voltammograms dari kedua elektroda menunjukkan puncak potensial oksidasi As °pada ~0.21 V (vs. Ag/AgCl) pada kondisi optimum potensial deposisi -500 mV, waktu deposisi 180 s, dan scan rate 100 mV/s. AuNP-BDD memiliki daerah pengukuran yang lebih luas (0-20 mM) dan limit deteksi yang lebih rendah (0.39 μ M atau 4.64 ppb), sedangkan AuNP-GC linier pada daerah konsentrasi 0-10 mM dengan limit deteksi 0.14 μ M (13.12 ppb). Keberulangan yang baik ditunjukkan dengan RSDs (n=20) 2.93% pada AuNP-BDD dan 4.54% pada AUNP-BDD. Meskipun demikian penurunan yang lebih banyak pada pengukuran 6 hari berturut-turut ditemukan pada AuNP-BDD (~20.1%) daripada pada AuNP-GC (~2.8%).

---

Modification of carbon, including boron-doped diamond (BDD) and glassy carbon (GC), using gold nanoparticle (AuNP) was developed by self-assembly technique. This technique is based on electrostatic interaction between citrate-capped AuNP to amine terminal groups after surface modification of BDD and GC. The fabricated materials, AuNP-BDD and AuNP-GC, were then utilized as electrodes for As 3+ detection using anodic stripping voltammetry (ASV) technique. Anodic stripping voltammograms of both Au NP-BDD and AuNP-GC electrodes showed similar peak potentials of As ° oxidation at ~0.21 V (vs. Ag/AgCl) in optimum conditions of -500 mV, 180 s, and 100 mV/s for deposition potential, deposition time, and scan rate, respectively. AuNP-BDD shows better performances in the case of wide linear concentration range (0-20 mM) and low limit of detection (0.39μM or 4.64 ppb), whereas those of AuNP-GC were linear in the concentration range of 0-10mM with a detection limit of 0.14μ M (13.12 ppb). Excellent reproducibility was shown with RSDs (n=20) of 2.93% and 4.54% at AuNP-BDD and AuNP-GC, respectively. However, decreasing of current responses in 6-concecutive days was found more at AuNP-BDD (~20.1%) than that at AuNP-GC (~2.8%)."

"Telah dilaporkan bahwa nanopartikel emas terbukti dapat digunakan untuk terapi kanker dengan memanfaatkan efektermal. Pembunuhan sel kanker dapat pula dilakukan dengan memanfaatkan radiasi radioisotop. Untuk itu, telah dilakukan kajian pembuatan nanopartikel emas radioaktif dengan aktivasi neutron di central irradiation position (CIP) reaktor nuklir G.A. Siwabessy dengan fluks neutron 1,26 x 1014 neutron s-1cm-2. Dari kajian ini diketahui bahwa dari iradiasi neutron pada emas alam dihasilkan 1 jenis radioisotop yaitu 198Au. Hasil perhitungan menunjukkan bahwa radioaktivitas 198Au yang dihasilkan dari iradiasi selama 12 hari sebesar 0,366 Bq, 2,93 Bq, 9,90 Bq dan 23,4 Bq untuk partikel emas berukuran 100, 200, 300 dan 400 nm. Dengan iradiasi selama 12 hari, tingkat kejenuhan radioaktivitas198Au sebesar 96,5%. Setelah peluruhan selama 10 hari, radioaktivitas 198Au di dalam partikel dengan diameter 100, 200, 300, 400 nm sebesar 0,027 Bq, 0,223 Bq, 0,753 Bq dan 1,78 Bq. Pengotor radioisotop yang dapat dihasilkan di dalam partikel emas adalah 108Ag, 110mAg, 64Cu, 66Cu, 205Pb dan 209Pb dengan total radioaktivitas sebesar 4,31 x 10-5 % dari radioaktivitas 198Au pada saat akhir iradiasi.

---

AbstractIt was reported that gold nanoparticle could be used for cancer therapy using thermal effect. It is possible to kill cancer cells using radiation of radioisotope. Study on preparation of radioactive gold by neutron activation at central irradiation position (CIP) of G.A. Siwabessy reactor with neutron flux 1.26 x 1014 neutron s-1cm-2 has been carried out. It was revealed that a radioisotop of gold (198Au) was produced by neutron activation from natural gold. Calculation results showed that 198Au with radioactivity of 0.366 Bq,2.93 Bq, 9.90 Bq and 23.4 Bq was produced for nanoparticle with diameter of 100, 200, 300 and 400 nm by neutron irradiation for 12 days. The saturation factor was 96.5%. After 10 days of decay, the radioactivity was 0.027 Bq, 0.223 Bq, 0.753 Bq and 1.78 Bq in nanoparticle with diameter of 100, 200, 300 and 400 nm. The radionuclide impurities were 108Ag, 110mAg, 64Cu, 66Cu, 205Pb and 209Pb with the total radioactivity was 4.31 x 10-5 % of the total radioactivity of 198Au at the end of irradiation."

"Nanopartikel emas semakin diminati oleh para peneliti karena sifat elektronik, optik, dan kimia yang unik dari partikel emas berskala nano. Namun, dalam pembuatan AuNP, bahan kimia yang dapat merusak lingkungan digunakan, sehingga dalam beberapa tahun terakhir pendekatan sintesis hijau telah dikembangkan. Dalam penelitian ini, AuNP dibuat dengan menggunakan ekstrak kacip fatimah yang memiliki karakterisasi dan stabilitas yang baik. Sintesis AuNP menggunakan larutan HAuCl4 30% dan ekstrak kernip fatimah dengan konsentrasi 5%, 10%, dan 15%, diaduk selama 5 menit dengan kecepatan 300 rpm, dan ditambahkan larutan natrium sitrat sebagai capping agent. Karakterisasi dilakukan dengan menggunakan alat pengukur pH, spektrofotometer UV-VIS, Particle Size Analyzer (PSA), dan Transmission Electron Microscopy (TEM). Uji stabilitas dilakukan. AuNP disimpan pada suhu kamar selama 56 hari. Hasil sintesis AuNP dengan konsentrasi ekstrak 5% terbentuk pada 535,50 nm dengan daya serap 0,720 A, pH 3,83, ukuran partikel 59,93 ± 1,35 nm, nilai polidispersitas 0,463 ± 0,06, a Potensi zeta -31,0 ± 7,44 mV, dan ditemukan morfologi berbentuk bola, pentagonal, dan tidak beraturan. Pada uji stabilitas AuNP dengan konsentrasi ekstrak 5%, 10%, dan 15% selama 56 hari yang diamati menggunakan spektrofotometer UV-VIS dan PSA, ditemukan bahwa AuNP dengan konsentrasi ekstrak 5% memiliki stabilitas yang lebih baik daripada AuNP dengan konsentrasi ekstrak 10% dan 15%. . Sintesis AuNP menggunakan ekstrak kacip fatimah memiliki karakterisasi dan stabilitas yang baik pada konsentrasi ekstrak 5%, diaduk selama 5 menit dengan kecepatan 300 rpm dan ditambahkan natrium sitrat sebagai capping agent.

---

Gold nanoparticles are increasingly in demand by researchers due to the unique electronic, optical and chemical properties of nanoscale gold particles. However, in the manufacture of AuNP, chemicals that can damage the environment are used, so in recent years a green synthesis approach has been developed. In this study, AuNP was prepared using an extract of the fatimah kacip which has good characterization and stability. Synthesis of AuNP using 30% HAuCl4 solution and kernip fatimah extract with a concentration of 5%, 10%, and 15%, stirred for 5 minutes at a speed of 300 rpm, and sodium citrate solution was added as a capping agent. Characterization was performed using a pH measuring device, UV-VIS spectrophotometer, Particle Size Analyzer (PSA), and Transmission Electron Microscopy (TEM). Stability test was carried out. AuNP was stored at room temperature for 56 days. The results of the synthesis of AuNP with a concentration of 5% extract were formed at 535.50 nm with an absorption capacity of 0.720 A, pH 3.83, a particle size of 59.93 ± 1.35 nm, a polydispersity value of 0.463 ± 0.06, a zeta potential of -31, 0 ± 7.44 mV, and the morphology is spherical, pentagonal, and irregular. In the AuNP stability test with an extract concentration of 5%, 10%, and 15% for 56 days, which was observed using a UV-VIS and PSA spectrophotometer, it was found that AuNP with an extract concentration of 5% had better stability than AuNP with an extract concentration of 10% and 15%. . Synthesis of AuNP using kacip fatimah extract has good characterization and stability at a 5% extract concentration, stirred for 5 minutes at a speed of 300 rpm and sodium citrate is added as a capping agent."

"Deteksi adanya As(III) dan As(V) dapat dilakukan dengan metode anodic stripping voltammetry. Elektroda pembanding berupa Ag/AgCl, elektroda pendukung berupa kawat platina, dan elektroda kerja yang digunakan merupakan elektroda glassy carbon dan screen printed electrode termodifikasi nanopartikel emas. Modifikasi kedua elektroda ini dengan nanopartikel emas dilakukan melalui teknik self-assembly menggunakan NH4OH sebagai aktivator. Nanopartikel emas dibuat dengan cara mereduksi HAuCl4 yang telah mengandung sitrat menggunakan pereduksi NaBH4. Kehadiran sitrat berguna untuk menstabilkan ukuran nanopartikel emas yang terbentuk. Karakterisasi dengan PSA menunjukkan ukuran nanopartikel emas sekitar 8-11 nm. Pada penelitian ini telah dilakukan modifikasi elektroda glassy carbon dan screen printed electrode dengan nanopartikel emas serta dilakukan pengujian terhadap larutan As(III) dan As(V). Hasil pengukuran larutan As(III) dan As(V) menggunakan screen printed electrode termodifikasi nanopartikel emas (SPE-AuNP) belum menunjukkan adanya puncak arus oksidasi. Sebaliknya, pengukuran menggunakan elektroda glassy carbon termodifikasi nanopartikel emas (GC-AuNP) memperlihatkan adanya puncak arus oksidasi. Respon arus terhadap As(III) pada elektroda GC-AuNP menunjukkan linearitas yang baik (r2=0,996) pada rentang konsentrasi 5-80 μM. Demikian juga untuk As(V) pada rentang konsentrasi 10-100 μM (r2=0,995). Hal ini menunjukkan bahwa elektroda GC-AuNP dapat digunakan sebagai elektroda kerja menggantikan elektroda Au bare.

---

Detection of arsenic in the form of As(III) and As(V) can be done by anodic stripping voltammetry method. The reference electrode used is Ag/AgCl, with platinum counter electrode, and as a working electrode glassy carbon and screen printed electrodes modified with gold nanoparticle were used. Modification of both working electrode was conducted through self-assembly technique in which gold nanoparticle is attached to the surface of the electrode activated by NH4OH. Gold nanoparticle was synthesized by reduction of HAuCl4 using NaBH4 in the presence of citrate. Citrate is used to prevent aggregation of gold nanoparticles. PSA characterization indicates that the size of gold nanoparticles are 8-11 nm. In this study, we investigate the possibility of modified glassy carbon electrode with gold nanoparticle to analyze As(III) and As(V). The determination of As(III) and As(V) using gold nanoparticle-modified screen printed electrode (SPE-AuNP) did not show the current oxidation peak. On the other hand, the gold nanoparticle-modified glassy carbon electrode (GC-AuNP) show current oxidation peak when used to analyze As(III) and As(V). Current response for the concentration of As(III) on GC-AuNP electrode gives linear response in the range of 5-80 μM (r2=0,996) whereas for As(V) in the range 10-100 μM (r2=0,995). This indicates that GC-AuNP electrode can replace the Au bare as a working electrode."

"ABSTRAKPenggunaan nanopartikel emas di bidang kosmetik cukup diminati, salah satunya sebagai antipenuaan. Aktivitas antipenuaan dalam suatu zat dapat diuji menggunakan uji efek anti-replikasi. Penelitian ini bertujuan untuk mengetahui efek anti glikasi nanopartikel emas hasil sintesis ekstrak Kacip Fatimah (Labisia pumila) dan membandingkannya dengan efek anti glikasi ekstrak Kacip Fatimah (Labisia pumila). Metode sintesis nanopartikel emas yang aman bagi manusia dan lingkungan adalah metode sintesis hijau dengan menggunakan ekstrak tumbuhan. Kacip Fatimah (Labisia pumila) merupakan tumbuhan yang dapat digunakan sebagai bahan baku sintesis nanopartikel emas dan telah terbukti memiliki aktivitas antioksidan. Setelah nanopartikel emas disintesis, kemudian nanopartikel emas dikarakterisasi menggunakan spektrofotometer UV-Vis dan Particle Size Analyzer (PSA). Terakhir dilakukan uji efek anti glikasi secara in vitro pada nanopartikel emas dan ekstrak Kacip Fatimah dengan menghitung% penghambatan pembentukan AGEs, dimana pembentukan AGEs dapat dideteksi dengan melihat intensitas fluoresensi yang terbentuk. Hasil karakterisasi yang diperoleh adalah serapan nanopartikel emas sebesar 0,668 pada panjang gelombang 535,60 nm dan rata-rata ukuran partikel yang terbentuk adalah 65,46 nm dengan nilai indeks polidispersitas (PdI) 0,443 dan nilai potensial zeta -35,1 mV. Hasil uji efek anti glikasi menunjukkan bahwa nanopartikel emas yang disintesis dengan ekstrak Kacip Fatimah (Labisia pumila) 5% memiliki efek anti glikasi yang lebih tinggi dibandingkan ekstrak Kacip Fatimah (Labisia pumila) 5%, dimana% penghambatan nanopartikel emas yang disintesis dengan ekstrak Kacip Fatimah (Labisia pumila) 5% adalah 89,94 ± 6,12% dan% penghambatan ekstrak Kacip Fatimah (Labisia pumila) 5% adalah 64,24 ± 5,63%. Dengan demikian, nanopartikel emas yang disintesis dengan ekstrak Kacip Fatimah (Labisia pumila) telah terbukti memiliki efek anti-glikasi dan dapat digunakan sebagai agen antipenuaan.

---

ABSTRACTThe use of gold nanoparticles in the cosmetic sector is quite attractive, one of which is as antiaging. Antiaging activity in a substance can be tested using an anti-replication effect test. This study aims to determine the anti-glycation effect of the gold nanoparticles synthesized from Kacip Fatimah (Labisia pumila) extract and compare it with the anti-glycation effect of Kacip Fatimah (Labisia pumila) extract. The gold nanoparticle synthesis method that is safe for humans and the environment is a green synthesis method using plant extracts. Kacip Fatimah (Labisia pumila) is a plant that can be used as raw material for the synthesis of gold nanoparticles and has been shown to have antioxidant activity. After the gold nanoparticles were synthesized, the gold nanoparticles were characterized using a UV-Vis spectrophotometer and Particle Size Analyzer (PSA). Finally, an in vitro anti-glycation effect test was carried out on gold nanoparticles and Kacip Fatimah extract by calculating the% inhibition of AGEs formation, where the formation of AGEs can be detected by looking at the intensity of fluorescence formed. The characterization results obtained were gold nanoparticle absorption of 0.668 at a wavelength of 535.60 nm and the average particle size formed was 65.46 nm with a polydispersity index (PdI) 0.443 and a zeta potential value of -35.1 mV. The results of the anti-glycation effect test showed that gold nanoparticles synthesized with 5% Kacip Fatimah (Labisia pumila) extract had a higher anti-glycation effect than 5% Kacip Fatimah (Labisia pumila) extract, where% inhibition of gold nanoparticles synthesized with Kacip Fatimah extract (Labisia pumila) 5% was 89.94 ± 6.12% and the% inhibition of Kacip Fatimah extract (Labisia pumila) 5% was 64.24 ± 5.63%. Thus, gold nanoparticles synthesized with Kacip Fatimah (Labisia pumila) extract have been shown to have anti-glycation effects and can be used as an antiaging agent."

"Nanopartikel emas memiliki masalah kestabilan yaitu mudah beragregasi sehingga dibutuhkan agen penstabil untuk mencegah agregasi. Tujuan penelitian ini adalah untuk memperoleh nanopartikel emas yang stabil dengan menggunakan Polietilen Glikol. Nanopartikel emas disintesis dengan menggunakan metode Turkevich, lalu ditambahkan PEG sebagai agen penstabil dan dikonjugasikan dengan resveratrol sebagai model obat. Konjugat yang terbentuk kemudian dikarakterisasi dengan PSA, FTIR, dan spektrofotometer UV-Vis. Pembuatan RSV-AuNP-PEG menghasilkan larutan jernih berwarna ungu kemerahan, ukuran partikel 83,93 nm dengan indeks polidispersitas 0,562, zeta potensial sebesar -22,9 mV, dan efisiensi penjerapan 75,86 0,66. Sedangkan konjugat AuNP-RSV menghasilkan larutan keruh berwarna ungu, ukuran partikel 51,97 nm dengan indeks polidispersitas 0,694 dan zeta potensial -24,6 mV. Hasil uji stabilitas RSV-AuNP-PEG dalam penyimpanan lebih stabil dibandingkan AuNP-RSV. Namun pada uji stabililitas di dalam medium, RSV-AuNP-PEG paling stabil berada dalam BSA 2 dan tidak stabil pada Sistein 1 , NaCl 0,9 , PBS pH 7,4, dan PBS pH 4. Sedangkan AuNP-RSV paling stabil pada BSA 2 , PBS pH 7,4 dan tidak stabil pada Sistein 1 , NaCl 0,9 , dan PBS pH 4. Penggunaan PEG dalam Konjugat resveratrol-nanopartikel emas mampu mencegah agregasi dalam penyimpanan namun belum mampu melindungi nanopartikel dari agregasi di medium.

---

The gold nanoparticles have a stability problem which is easy to aggregate. Thus, the stabiliser agent is required to prevent aggregation. The purpose of this research was to obtain stable gold nanoparticles by using polyethene glycol. The initial step utilised the Turkevich method to synthesised the gold nanoparticles, then PEG was added as stabiliser agent and conjugated with resveratrol as a drug model. The forming conjugates were characterised by PSA, FTIR, UV Vis spectrophotometers and HPLC. Therefore, RSV AuNP PEG resulted in a clear purple reddish fluid with measurement of particle size by 83.93 nm, polydispersity index 0.562, zeta potential at 22.9 mV, and highest entrapment efficiency of 75.86 0.66. As a comparison, AuNP RSV appeared in a purple turbidity fluid, with the measurement of the particle size by 51.97 nm, a polydispersity index is 0.694, and zeta potential value at 24.6 mV.

The results of the stability test of RSV AuNP PEG in storage were more stable than AuNP RSV. However, in the medium stability test, the RSV AuNP PEG were more stable in 2 BSA and unstable in 1 Cysteine, 0.9 NaCl, PBS pH 7.4, and PBS pH 4. On the other hand, the AuNP RSV were most stable at 2 BSA, PBS pH 7.4 and unstable in 1 cysteine, 0.9 NaCl, and PBS pH 4. The application of PEG in conjugate resveratrol gold nanoparticles proficient in preventing aggregation in storage, but unable to preserve the nanoparticles from aggregation in some mediums."

"Emas (Au) merupakan logam transisi yang saat ini banyak dikembangkan dalam berbagai aplikasi termasuk obat, diagnosis penyakit, dan terapi kanker. Nanopartikel emas dibuat dengan cara mereduksi larutan hidrogen tetrakloroaurat (HAuCl4) menggunakan gom arab. Gom arab juga digunakan sebagai penstabil pada pembuatan nanopartikel emas untuk mencegah terjadinya agregasi. Nanopartikel emas dimurnikan dengan menggunakan metode sentrifugasi ultrafiltrasi. Nanopartikel emas dikarakterisasi dengan menggunakan alat Spektrofotometer UV-Vis, FTIR, PSA dan TEM. Uji stabilitas nanopartikel emas secara in vitro dalam berbagai lingkungan yaitu aquabides, dapar pH 3, pH 7,4, pH 11, NaCl 0,35%, NaCl 0,5%, NaCl 0,9%, Sistein 1%, dan BSA 2% diamati selama 3 minggu dengan menggunakan alat Spektrofotometer UV-Vis. Hasil penelitian menunjukkan bahwa nanopartikel emas sebagian besar berbentuk sferis, memiliki ukuran partikel 25,2 nm ±3,99 nm, indeks polidispersitas 0,299 ±0,013, potensial zeta +46,95 mV ±2,78 mV. Hasil uji stabilitas nanopartikel emas secara in vitro selama 3 minggu menunjukkan bahwa nanopartikel emas stabil di dalam aquabides, dapar pH 3, dapar pH 11, larutan NaCl 0,35%, NaCl 0,5%, NaCl 0,9%, dan tidak stabil dalam larutan dapar pH 7,4, larutan sistein 1%, dan BSA 2%. Hasil pengukuran partikel nanopartikel emas setelah uji stabilitas secara in vitro menunjukkan perubahan ukuran partikel menjadi 38,35 nm ±2,05 nm dan memiliki indeks polidispersitas 0,347 ±0,035. Hasil penelitian tersebut menunjukkan bahwa gom arab efektif digunakan sebagai penstabil maupun pereduksi pada pembuatan nanopartikel emas yang menghasilkan larutan koloid nanopartikel emas yang stabil.

---

Gold (Au) is a transition metal which has been developed in various applications including drug, disease diagnostic, and therapy of cancer. Gold nanoparticles were prepared by reducing HAuCl4 using gum arabic solution. Gum arabic also used as a stabilizer in the preparation of gold nanoparticles to prevent aggregation. Gold nanoparticles were purified by centrifugation ultrafiltration method. Gold nanoparticles were characterized by UV-Vis spectroscopy, FTIR, PSA, and TEM. In vitro stability studies of gold nanoparticles in various environment of aquabidest, buffer pH 3, pH 7,4, pH 11, NaCl solution 0,35%, NaCl 0,5%, NaCl 0,9%, sistein 1%, and BSA 2% was observed for 3 weeks by using UV-Vis spectrophotometer. The results showed that the spherical gold nanoparticles, have a particle sizes of 25,2 nm ±3,99 nm, polydispersity index 0,299 ±0,013, and zeta potential +46,95 mV ±2,78 mV. Stability test results of gold nanoparticles in vitro studies for 3 weeks showed that gold nanoparticles were stable in aquabidest, buffer pH 3, buffer pH 11, NaCl solution 0,35%, NaCl 0,5%, NaCl 0,9%, and unstable in buffer solution pH 7,4, cysteine solution 1%, and BSA 2%. Result of particle sizes after in vitro stability studies of gold nanoparticles showed changes in particle where the size became 38,35 nm ±2,05 nm and polydispersity index was 0,347 ±0,035. The result showed that gum arabic effectively used as stabilizer and reductant in the preparation of gold nanoparticles produces a solution of colloidal gold nanoparticles which were stable."