"ABSTRACTTujuan: Penelitian ini bertujuan untuk mengetahui pengaruh sistem pemolesan terhadap perubahan warna resin komposit mikrohibrida setelah perendaman dalam larutan Luwakwhite coffee. Material dan Metode Penelitian: Dalam penelitian ini digunakan empat puluh dua spesimen berdiameter 6 mm dan tebal 2 mm yang dibagi menjadi 6 kelompok dengan 2 bahan yang berbeda yaitu G-aenial PosteriorTM dan Filtek Z250TM dipoles menggunakan Sof-Lex disc SuperfineTM, PoGo, dan tidak dipoles. Spesimen di polimerisasi menggunakan LED Curing Unit dengan irradiansi 700 mW/cm2 (LED Max Hilux) selama 20 detik. Setelah dipoles, spesimen direndam dalam larutan Luwak white coffee selama 7 hari. Perubahan warna diukur menggunakan colorimeter NH310 (Shenzhen 3NH) dengan sistem warna CIE Lab. Data dianalisis menggunakan uji Statistik One-Way Anova Test. Hasil: Setelah dipoles, terdapat perbedaan yang signifikan (p<0,05) pada nilai I E1 dan nilai I a1, namun untuk nilai I L1 dan nilai I b1 tidak terdapat perbedaan yang signifikan. Setelah perendaman dalam larutan Luwakwhite coffee, terdapat perbedaan yang signifikan (p<0,05) pada nilai I E2, nilai I b2. Sedangkan, nilai I L2 hampir terdapat perbedaan yang signifikan pada seluruh kelompok, kecuali G-aenial PosteriorTM yang tidak dipoles dengan Filtek Z250TM yang tidak dipoles, Filtek Z250TM yang tidak dipoles dengan Filtek Z250TM yang dipoles menggunakan Sof-LexTM Superfine, dan G-aenial PosteriorTM yang dipoles menggunakan Sof-LexTM Superfine dengan Filtek Z250TM yang dipoles menggunakan Sof-LexTMSuperfine serta nilai I a2 hampir terdapat perbedaan yang signifikan pada seluruh kelompok, kecuali Filtek Z250TM yang tidak dipoles dengan Filtek Z250TM yang dipoles menggunakan PoGo. Kesimpulan: Sistem pemolesan yang berbeda dapat mempengaruhi nilai perubahan warna resin komposit mikrohibrida. Pemolesan menggunakan PoGo menghasilkan perubahan warna paling kecil. Filtek Z250TM memiliki perubahan warna terkecil setelah perendaman dalam larutan Luwak white coffeeselama 7 hari.

---

ABSTRACTObjectives: This study aims to analyze the influence of polishing systems on color change of microhybrid composite resin after immersion in Luwak white coffee solution.Material and Methods: In this study, fourty two specimens, 6 mm in diameter and 2 mm thick, were divided into six groups with different composite types, that is G-aenial PosteriorTM and Filtek Z250TM, polished with Sof-Lex disc SuperfineTM, PoGo and unpolished. The specimens are polymerized for 20 seconds using a 700 mW/cm2irradiance LED curing unit (LED Max Hilux). After polishing, the specimens are immersed in Luwak white coffee solution for 7 days. The color change is measured using a colorimeter NH310 (Shenzhen 3NH) with the CIE Lab color system. Data were analyzed using One-Way ANOVA test. Results: After polishing, there were statistically significant differences (p<0,05) between the I E1 and I a1 groups. However, statistically significant differences were not found between the I L1 and I b1 groups. After immersed in Luwak white coffee, there were statistically significant differences (p<0,05) between the I E22 and I b1 groups. Meanwhile, almost all of the I L2 groups showed a significant increase, except for G-aenial PosteriorTM unpolished with Filtek Z250TM unpolished, Filtek Z250TM unpolished with Filtek Z250TM polished using Sof-LexTMSuperfine, G-aenial PosteriorTM polished using Sof-LexTM Superfine with Filtek Z250TMpolished using Sof-LexTM Superfine and I a2 groups showed a significant increase, except Filtek Z250TM unpolished with Filtek Z250TM polished using PoGo. Conclusions:It was concluded that different polishing systems affect color change of the microhybrid composite resins. Polishing with PoGo produces the smallest color change. Filtek Z250TM was determined to have the smallest color change after immersion in Luwak white coffee for 7 days."

"ABSTRAKPenelitian bertujuan untuk mengetahui pengaruh sistem pemolesan terhadap perubahan warna Nano-ionomer. Nano-ionomer dibagi menjadi empat kelompok; dipoles dengan Sof-LexTM XT, PoGOTM, OptraPol®, dan tidak dipoles. Seluruh spesimen direndam dalam larutan kopi selama tujuh hari. Perubahan warna dinilai dengan sistem CIELAB. Hasil dianalisis dengan uji One Way Anova dan PairedSamples T Test. Nilai L* mengalami penurunan yang signifikan (p < 0,05) setelah dilakukan pemolesan. OptraPol® mengalami perubahan warna terkecil. Setelah perendaman, terjadi perubahan nilai L*, a*, dan b* yang signifikan (p < 0,05) pada seluruh kelompok. OptraPol® mengalami perubahan warna terkecil namun tidak berbeda bermakna terhadap PoGOTM dan tidak dipoles.

---

ABSTRACTThe aim of this study was to assess the influence of polishing systems on color change of Nano-ionomer. Specimens were divided into four groups; polished with Sof-LexTM XT, PoGOTM, OptraPol® and unpolished. Color values were evaluated using CIELAB system. Data were analyzed using One Way Anova and Paired Samples T Test. L* values were significantly lowered (p < 0,05) after polishing procedures. OptraPol® showed the least colour change. After immersion, therewere significant changes in L*, a* and b* values (p < 0,05) in all groups.OptraPol® showed the littlest colour change but it was not statistically significant compared to PoGOTM and unpolished."

"Resin kompositterus dikembangkan untuk meningkatkan performa estetiknya. Resin komposit terbaru yaitu nanofiller dan nanohybrid yang masih diperdebatkan ketahanannya terhadap zat warna minuman kopi. Penelitian ini bertujuan membandingkan perubahan warna permukaan resin komposit nanofiller dan nanohybrid setelah perendaman kopi. Terdapat 36 sampel yang dibagi dalam 6 kelompok dengan ukuran diameter 6 mm, tebal 3 mm. Pengukuran warna menggunakan vita easyshade classic yang diurutkan berdasarkan value. Hasil data dianalisis menggunakan Wilcoxon Test dan Mann-Whitney Test. Didapatkan Perubahan warna pada nanohybrid lebih sedikit dibandingkan pada nanofiller dan secara statistik berbeda bermakna (p<0,05). Sehingga nanohybrid memiliki ketahanan terhadap zat warna yang lebih baik daripada nanofiller.

---

Resin composites continue developed to improve aesthetic performance. The newest composite resin are nanofiller and nanohybrid where color resistance to coffee drinks still debating. The aim of this study is to compare surface discoloration nanofiller and nanohybrid resin composites after immersion coffee. There are 36 samples were divided into 6 groups with a diameter of 6 mm, thickness 3 mm. Color measurements using vita easyshade classic that is sorted by value.Results data were analyzed using the Wilcoxon test and Mann-Whitney Test. Changes in color on nanohybrid lower than the nanofiller and statistically significant (p<0.05). Therefore nanohybrid has resistance to color better than nanofiller."

"Tujuan: Penelitian ini bertujuan untuk mengetahui perubahan warna dari resin komposit mikrohibrida setelah perendaman dalam minuman cokelat Indonesia. Metode Penelitian: Dalam penelitian ini digunakan resin komposit mikrohibrida G-aenial Anterior™. Spesimen berbentuk silinder dengan ukuran diameter 6 mm dan tebal 2 mm. Selembar mylar strip diletakkan diatas permukaan resin komposit sebelum dilakukan proses curing. Polimerisasi dilakukan menggunakan Light Curing Unit (Ledmax Hilux Model 450) selama 20 detik dengan irradiansi 700 mw/cm2. Setelah polimerisasi, spesimen direndam dalam akuades pada suhu 37oC selama 24 jam. Spesimen dibagi menjadi tujuh kelompok (n = 6) yaitu; perendaman pada larutan kakao asal Aceh, Lampung, Jawa Timur, Bali, Flores, Kendari dan Akuades. Spesimen direndam dalam larutan cokelat dengan durasi 24 jam selama 7 hari dengan penggantian larutan setiap harinya. Warna spesimen diukur menggunakan Colorimeter NH310 (Shenzhen 3NH) menurut sistem warna CIE L*a*b* setelah perendaman pada akuades selama 24 jam dan setelah direndam dalam larutan cokelat Indonesia selama 7 hari. Indeks perubahan warna (ΔE*) antara setiap kelompok dihitung. Data dianalisis menggunakan uji One-Way Anova untuk menilai perbedaan warna antar kelompok perendaman. pH larutan cokelat diukur menggunakan pH meter (Thermo Scientific Orion Star A211 Benchtop). Hasil: Resin komposit G-aenial Anterior™ yang telah direndam di dalam enam larutan cokelat selama 7 hari menunjukkan perubahan warna yang signifikan antar kelompok (p<0,05). Larutan cokelat menyebabkan perubahan warna yang signifikan hanya pada satu kelompok yaitu kelompok G-aenial Anterior™ yang direndam dalam larutan cokelat Lampung. Perubahan warna yang paling rendah didapatkan pada kelompok resin komposit yang direndam dalam larutan cokelat Bali. Kesimpulan: Disimpulkan bahwa seluruh larutan cokelat tidak menyebabkan perubahan warna secara signifikan, kecuali pada larutan cokelat asal Lampung.

---

Objectives: The aim of this study was to analyse the color change of resin composite microhybrid after immersion in Indonesian Chocolate Drink. Material and Methods: G-aenial Anterior™ resin composite was used in this study. All materials were prepared and polymerized into disk-shaped specimens of 6 mm in diameter and 2 mm in thickness. A piece of mylar strip was placed on top of the specimens just before the polymerization. Polymerization was done using Light Curing Unit (Ledmax Hilux Model 450 for 20 seconds with irradiance of 700 mw/cm2. Specimens were immersed in 37oC aquadest solution for 24 hours after polymerization was done. Specimens were divided into seven groups (n=6); immersion in chocolate drink from Aceh, Lampung, Jawa Timur, Bali, Flores, Kendari, and Aquadest. Specimens were immersed in chocolate drink for 7 days (with the duration being 24 hours daily). The chocolate drink solutions were changed daily. Color of the specimens were measured using Colorimeter NH310 (Shenzhen 3NH) according to the CIE L*a*b* color system after immersion in aquadest solution for 24 hours and after immersion in Indonesian chocolate drink for 7 days. Color change (ΔE*) of every groups was calculated. Data were analysed using One-Way Anova to assess the significant differences among immersion groups. pH levels of all chocolate drink was measured using a pH meter. (Thermo Scientific Orion Star A211 Benchtop). Results: G-aenial Anterior™ resin composite showed significant color differences among each groups after immersion in chocolate drink for 7 days (p<0,05). G-aenial Anterior™ resin composite that has been immersed in Lampung chocolate drink was the only group with significant color change. The least amount of color change was found in G-aenial Anterior™ resin composite immersed in Bali chocolate drink. Conclusions: It was concluded that none of the chocolate drink from Indonesia caused significant color change, except for Lampung chocolate drink."

"Latar Belakang: Perendaman resin komposit nanohibrid dan mikrohibrid di dalam jus berbagai buah menunjukkan perubahan warna total (ΔE) lebih gelap, namun tidak disertai dengan nilai-nilai komponen warna yang lain, yaitu kecerahan (L*), kroma merah-hijau (a*), dan kroma kuning-biru (b*). G-aenial Anterior merupakan resin komposit mikrohibrid dengan estetika berkualitas tinggi. Tujuan: Menganalisis pengaruh perendaman resin komposit nanohibrid dan mikrohibrid G-aenial Anterior dalam larutan-larutan yang mengandung klorofil, bit, dan kolagen terhadap perubahan warna total (ΔE), kecerahan (ΔL), kroma merah-hijau (Δa), dan kroma kuning-biru (Δb). Metode: Spesimen (21spesimen) dipersiapkan dengan memolimerisasi resin komposit nanohibrid dan mikrohibrid G-aenial Anterior selama 20 detik dengan iradiansi 1000 mW/cm2 untuk masing-masing jenis resin komposit. Spesimen dibagi menjadi 3 kelompok, masing-masing kelompok dilakukan perendaman selama 7 hari dengan setiap larutan-larutan klorofil, bit, atau kolagen. Pengukuran warna dilakukan dengan menggunakan kolorimeter CIE untuk menghasilkan L*a*b*. Perubahan warna spesimen yang dilakukan sebelum dan sesudah perendaman menghasilkan ΔL, Δa, Δb dan ΔE dengan perhitungan dari rumus CIE. Signifikasi perbedaan warna spesimen sebelum (L*1; a*1; b*1) dan sesudah (L*2; a*2; b*2) setelah dilakukan perendaman dilakukan dengan uji t-test. Signifikansi perbedaan perubahan warna ΔL, Δa, Δb, dan ΔE setelah perendaman antar larutan atau antar resin komposit dilakukan dengan Uji One-Way ANOVA. Signifikansi perbedaan data yang homogen (ΔL dan Δb) menggunakan post hoc Bonferroni sedangkan data yang heterogen (Δa dan ΔE) menggunakan post hoc Tamhane. Hasil: Resin komposit nanohibrid dan mikrohibrid G-aenial Anterior setelah perendaman di dalam larutan klorofil, bit, dan kolagen memberi perbedaan signifikan (p<0,05) antara L*1-L*2 dan b*1-b*2 yang signifikan (p<0,05). Resin komposit nanohibrid dan mikrohibrid G-aenial Anterior setelah perendaman di dalam larutan klorofil memberi ΔL kurang cerah (p<0,05), Δa semakin kehijauan (p<0,05), Δb semakin kekuningan (p<0,05) dan ΔE> 3,3. Setelah perendaman resin komposit di dalam larutan bit, terlihat ΔL kurang cerah (p<0,05), Δa semakin kemerahan (p<0,05), Δb semakin kekuningan (p<0,05),dan nilai ΔE>3,3. Setelah perendaman resin komposit dalam larutan kolagen, ΔL kurang cerah, Δa semakin kemerahan, dan Δb kekuningan, yang mana perubahan kurang signifikan; dan nilai ΔE<1. Kesimpulan: Perendaman spesimen di dalam larutan klorofil, bit, dan kolagen menurunkan kecerahan dan meningkatkan warna kekuningan. Larutan klorofil menampilkan perubahan warna lebih kehijauan, sedangkan, larutan bit dan kolagen menyebabkan perubahan warna lebih kemerahan. Namun, perubahan warna oleh larutan kolagen kurang signifikan. Perendaman spesimen di dalam larutan klorofil, bit menampilkan ΔE di luar kisaran batas perubahan warna.

---

Background: Immersion of nanohybrid and microhybrid composite resins in various fruit juices showed a darker total color change (ΔE), but was not accompanied by other color component values, namely brightness (L*), red-green chroma (a*), and yellow-blue chroma (b*). G-aenial Anterior is a microhybrid composite resin with high quality aesthetics. Objective: To analyze the effect of immersion of nanohybrid and microhybrid composite resins G-aenial Anterior in solutions containing chlorophyll, beetroot, and collagen on total color changes (ΔE), brightness (ΔL), red-green chroma (Δa), and yellow-blue chroma (Δb). Method: Specimens (21 specimens) were prepared by polymerizing nanohybrid and microhybrid composite resins G-aenial Anterior for 20 seconds with an irradiance of 1000 mW/cm2 for each type of composite resin. The specimens were divided into 3 groups, each group was soaked for 7 days with each chlorophyll, beetroot, or collagen solution. Color measurements were performed using a CIE colorimeter to produce L*a*b*. The color changes of the specimens before and after immersion produced ΔL, Δa, Δb and ΔE with calculations from the CIE formula. The significance of the color differences of the specimens before (L*1; a*1; b*1) and after (L*2; a*2; b*2) after immersion was performed using the t-test. The significance of the differences in color changes ΔL, Δa, Δb, and ΔE after immersion between solutions or between composite resins was performed using the One-Way ANOVA Test. The significance of the differences in homogeneous data (ΔL and Δb) used the Bonferroni post hoc while the heterogeneous data (Δa and ΔE) used the Tamhane post hoc. Results: Nanohybrid and microhybrid composite resin G-aenial Anterior after immersion in chlorophyll, beetroot, and collagen solution gave significant differences (p<0.05) between L*1-L*2 and b*1-b*2 which were significant (p<0.05). Nanohybrid and microhybrid composite resin G-aenial Anterior after immersion in chlorophyll solution gave ΔL less bright (p<0.05), Δa more greenish (p<0.05), Δb more yellowish (p<0.05) and ΔE> 3.3. After immersion of the composite resin in beetroot solution, ΔL was less bright (p<0.05), Δa more reddish (p<0.05), Δb more yellowish (p<0.05), and ΔE>3.3. After immersion of composite resin in collagen solution, ΔL was less bright, Δa was more reddish, and Δb was yellowish, which were less significant changes; and the ΔE value <1. Conclusion: Immersion of specimens in chlorophyll, beetroot, and collagen solutions decreased brightness and increased yellowish color. Chlorophyll solution displayed a more greenish color change, while beetroot and collagen solutions caused a more reddish color change. However, the color change by collagen solution was less significant. Immersion of specimens in chlorophyll, beetroot solutions displayed ΔE outside the range of color change limits."

"Latar Belakang: Resin komposit single-shade merupakan resin komposit yang dapat menghasilkan warna menyerupai berbagai shade gigi tanpa tambahan pigmen. Resin komposit single-shade tetap memiliki potensi perubahan warna saat terpapar zat pewarna. Teh hitam dan oolong memiliki kadar tanin yang dapat mempengaruhi stabilitas warna resin komposit. Maka, dilakukan pengujian perubahan warna resin komposit single-shade setelah perendaman dalam larutan teh hitam dan oolong. Tujuan: Mengetahui perbedaan perubahan warna antara resin komposit single-shade yang direndam dalam larutan teh hitam dan oolong. Metode: Spesimen resin komposit single-shade dan konvensional nanohybrid (n = 42) dibagi ke dalam 6 kelompok, kemudian direndam dalam larutan teh hitam dan oolong selama 24 jam/hari dalam waktu 7 hari. Pengukuran perubahan warna dilakukan dengan colorimeter. Hasil: Perendaman dalam larutan teh hitam menghasilkan perubahan warna yang tidak sesuai pada resin komposit single-shade. Terdapat perbedaan perubahan warna signifikan antara resin komposit konvensional dalam kedua larutan teh, serta antara resin komposit single-shade dalam kedua larutan teh (p < 0.05). Kesimpulan: Perendaman resin komposit dalam teh hitam atau oolong menyebabkan perubahan warna resin komposit konvensional dan single-shade. Teh hitam menyebabkan perubahan warna lebih besar dibandingkan teh oolong pada kedua jenis resin komposit.

---

Single-shade composite resin is a composite resin that produces various teeth shades without additional pigments. Single-shade composite resin still has its color change potential when exposed to colorants. Black and oolong tea possess tannin contents that influence composite resin’s color stability. Therefore, single-shade resin composite’s color change was evaluated after its immersion in black and oolong tea solutions. Objective: To determine color change difference of single-shade composite resin after its immersion in black and oolong tea solutions. Methods: Single-shade and conventional nanohybrid composite resin specimens (n = 42) were divided into 6 groups, then immersed in black and oolong tea solutions for 24 hours/day for 7 days. Color change measurements were taken with a colorimeter. Results: Immersion in black tea resulted in unacceptable color change in single-shade composite resin. Significant difference in color change was found between conventional composite resin immersed in black and oolong tea, and between single-shade composite resin immersed in black and oolong tea (p < 0.05). Conclusions: Black and oolong tea immersion causes color change in conventional and single-shade composite resins. Black tea causes larger color change compared to oolong tea in both composite resins."

"Tujuan: Untuk mengetahui pengaruh perendaman resin komposit mikrohibrida Filtek Z250™ di dalam larutan cokelat Indonesia asal Aceh, Lampung, Jawa Timur, Bali, Flores, dan Kendari terhadap perubahan warna. Metode dan Material: Digunakan 42 spesimen resin komposit mikrohibrida Filtek Z250TM berdiameter 6 mm dan tebal 2 mm serta minuman cokelat Indonesia asal Aceh, Lampung, Jawa Timur, Bali, Flores, dan Kendari. Spesimen dipolimerisasi menggunakan LED Curing Unit iradiansi 700 mW/cm2 (LED Max Hilux) selama 20 detik kemudian direndam di dalam larutan cokelat selama 7 hari yang diganti setiap harinya. Perubahan warna diukur menggunakan colorimeter NH310 (Shenzhen 3NH) dengan sistem CIE L*a*b kemudian dianalisis menggunakan uji statistik One-Way Anova. pH larutan media perendaman diukur menggunakan pH meter (Thermo Scientific Orion Star A211 Benchtop). Hasil: Terdapat perubahan warna sebelum dan sesudah direndam dalam larutan cokelat yang signifikan (p<0,05) pada nilai ΔE*, ΔL*, Δa* dan Δb* nya. Larutan cokelat asal Lampung dengan pH yang paling rendah menyebabkan perubahan warna paling besar pada resin komposit Filtek Z250TM sedangkan larutan cokelat Kendari dengan pH yang paling tinggi menyebabkan perubahan warna yang paling kecil. Seluruh spesimen resin komposit Filtek Z250TM berubah menjadi lebih gelap. Kesimpulan: pH larutan coklat Indonesia mempengaruhi besarnya perubahan warna pada resin komposit mikrohibrida Filtek Z250TM.

---

Objective: To analyze the influence of Indonesian (Aceh, Lampung, East Java, Bali, Flores, and Kendari) chocolate drink immersion on color change of microhybrid composite resin. Materials and Method: 42 specimens with 6 mm diameter and 2 mm thick, chocolate drink from Aceh, Lampung, East Java, Bali, Flores, and Kendari were prepared. The specimens were polymerized for 20 seconds using a 700 mW/cm2 irradiance LED curing unit (LED Max Hilux). Specimens were immersed in Indonesia chocolate drink for 7 days and the chocolate were changed everyday. The color changes of specimens were measured using colorimeter NH310 (Shenzhen 3NH) following CIE L*a*b system then being analyzed using statistic One-Way Anova Test. pH solutions was measured by pH meter (Thermo Scientific Orion Star A211 Benchtop). Results: There were significant color change ΔE*, ΔL*, Δa* and Δb* (p<0,05) before and after immersed in Indonesia chocolate. Lampung chocolate drink which has the lowest pH makes the most significant color changes on Filtek Z250TM, meanwhile Kendari chocolate drink which has the highest pH most likely has no effect on color changes. All composite resin colors are darker after being immersed in all solutions. Conclusions: Color changes on microhybrid composite resin Filtek Z250TM are influenced by pH."

"Skripsi ini membahas pengaruh teknik inkremental dan aplikasi re-etch re-bond terhadap pencegahan perubahan warna tepi restorasi resin komposit nanohybrid setelah perendaman dalam larutan kopi, dengan cara membagi 24 gigi molar 3 menjadi 4 kelompok. Sample dibuat kavitas berbentuk lingkaran dengan diameter 2 mm kemudian ditumpat resin komposit nanohybrid dengan teknik inkremental (kelompok I-II) dan bulk (kelompok III-IV),pada kelompok I juga diaplikasikan re- etch re-bond setelah finishing lalu direndam dalam larutan kopi. Hasilnya, kelompok I menunjukkan nilai pewarnaan tepi tumpatan yang terendah dan pewarnaan tepi bermakna secara statistik (p<0,05) terjadi pada penghitungan hari ke-6 dan ke-12. Kesimpulannya, teknik penumpatan inkremental dan pengaplikasian re-etch re-bond dapat meminimalkan perubahan warna tepi tumpatan.

---

This study discusses the influence of incremental technique and re-etch re-bond applications to the prevention of marginal discoloration nanohybrid composite resin after immersed in a solution of coffee, by dividing the 24 third molars into 4 groups. Sample made a circular cavity with a diameter of 2 mm then restored by nanohybrid composite resin with incremental technique (group I-II) and bulk (group III-IV), in group I also applied re-etch re-bond after finishing and then immersed in a solution of coffee . As a result, group I showed the lowest value of marginal discoloration and the marginal discoloration statistically significant (p <0.05) occurred in the counting day 6 and 12. In conclusion, incremental techniques and application of re-etch re- bond can minimize marginal discoloration of composite resin"

"Latar Belakang: Perubahan warna masih menjadi masalah utama kegagalan klinis restorasi resin komposit. Perubahan warna dapat disebabkan oleh konsumsi teh yang tingkat konsumsinya tinggi, terutama teh hitam. Estetika merupakan indikator keberhasilan klinis yang berkaitan dengan kehalusan permukaan. Oleh karena itu, penting untuk menerapkan pemolesan yang tepat. Untuk mengetahui pengaruh teknik pemolesan terhadap perubahan warna resin komposit, perlu dilakukan evaluasi terhadap resin komposit nanohibrid dan spherical filler setelah perendaman dalam teh hitam selama 7 hari. Perendaman selama 7 hari dilakukan untuk mengevaluasi performa klinis restorasi resin komposit selama 2 tahun. Tujuan: Penelitian ini bertujuan untuk mengetahui perbedaan nilai perubahan warna resin komposit nanohibrid dan spherical filler yang dipoles menggunakan polishing disc serta polishing disc diikuti wool brush dan diamond polishing paste setelah perendaman dalam larutan teh hitam. Metode: Dua puluh satu spesimen dari masing-masing resin komposit nanohibrid (Filtek Z250 XT shade A2) dan spherical filler (PALFIQUE OMNICHROMA) dipersiapkan dengan bentuk silinder berdiameter 6mm dan tebal 2mm. Total keempat puluh dua spesimen dibagi ke dalam 4 kelompok perlakuan dan 2 kelompok kontrol. Perlakuan pertama adalah pemolesan menggunakan polishing disc (Pd) dan perlakuan kedua menggunakan polishing disc diikuti wool brush dan diamond polishing paste (PdP). Spesimen yang tidak dipoles berfungsi sebagai kontrol (K). Warna awal spesimen diukur menggunakan colorimeter. Spesimen lalu direndam dalam larutan teh hitam selama 7 hari. Warna akhir diukur menggunakan colorimeter kemudian data dianalisis secara statistik menggunakan uji One-Way ANOVA dan uji Post Hoc Tamhane. Hasil: Perendaman dalam larutan teh hitam menghasilkan perubahan warna yang tidak dapat diterima secara klinis, kecuali pada kelompok N-PdP. Kelompok N-K menunjukkan nilai ∆E* terbesar, sementara kelompok N-PdP menunjukkan nilai ∆E* terkecil. Terdapat perbedaan bermakna antara kelompok N-K dengan kelompok SF-K, kelompok N-Pd, dan kelompok N-PdP; antara kelompok SF-K dengan kelompok SS-PdP; antara kelompok N-Pd dengan kelompok N-PdP; serta antara kelompok N-PdP dengan kelompok SF-PdP (p < 0.05). Kesimpulan: Penggunaan pasta dalam pemolesan dapat mengurangi perubahan warna pada resin komposit akibat perendaman dalam larutan teh hitam. Resin komposit nanohibrid yang dipoles menggunakan disc diikuti pasta menunjukkan ketahanan terhadap perubahan warna yang lebih baik daripada resin komposit spherical filler.

---

Color change remains a primary concern in the clinical failure of composite resin restorations. Color change can be attributed to the high consumption of tea, especially black tea. Aesthetics serve as a clinical success indicator that is related to low surface roughness. Therefore, it is crucial to apply appropriate polishing procedures. To assess the effect of polishing procedures on the color change of composite resin, an evaluation of nanohybrid and spherical filler composite resins after immersion in black tea for 7 days is necessary. The 7-day immersion aims to evaluate the clinical performance of composite resin restorations over a 2-year period. Objective: This study aims to determine the differences in color change values between nanohybrid and spherical filler composite resins polished using a polishing disc and using a polishing disc followed by a wool brush and diamond polishing paste after immersion in black tea. Methods: Twenty one specimens were prepared from each nanohybrid (Filtek Z250XT shade A2) and spherical filler composite resin (PALFIQUE OMNICHROMA), shaped as cylinders with a diameter of 6mm and a thickness of 2mm. The forty-two specimens were divided into 4 treatment groups and 2 control groups. The first treatment involved polishing with a polishing disc (Pd), and the second treatment involved polishing with a polishing disc followed by a wool brush and diamond polishing paste (PdP). Unpolished specimens served as controls (K). Initial specimen color was measured using a colorimeter. Specimens were then immersed in a black tea solution for 7 days. The final color was measured using a colorimeter and data were statistically analyzed using One-Way ANOVA and Tamhane's Post Hoc test. Results: Immersion in black tea solution resulted in clinically unacceptable color changes, except for the N-PdP group. The N-K group exhibited the highest ∆E* value, while the N-PdP group showed the smallest ∆E* value. There were significant differences between N-K and SF-K, N-Pd and N-PdP group, SF-K and SF-PdP group, N-Pd and N-PdP group, as well as N-PdP and SF-PdP group (p < 0.05). Conclusion: The use of paste in polishing can reduce color changes in composite resin due to immersion in black tea solution. Nanohybrid composite resin polished with a disc followed by paste demonstrates better resistance to color changes than spherical filler composite resin."