"Latar Belakang: SIK sebagai bahan restorasi memiliki kemampuan untuk berikatan secara kimiawi terhadap struktur gigi dan kemampuan melepaskan fluoride sehingga cocok digunakan pada pasien dengan risiko karies tinggi namun memiliki kekuatan mekanis yang buruk. Modifikasi bahan restorasi SIK melalui penggabungan dengan bahan bioaktif untuk mendapatkan manfaat seperti meningkatnya sifat mekanis, sifat antibakteri dan potensi remineralisasi telah di sebutkan pada beberapa literatur penelitian. Pada studi ini, bubuk carboxymetyl-chitosan (CMC) ditambahkan pada komponen bubuk dari SIK konvensional. Tujuan: Menganalisis pengaruh modifikasi material semen ionomer kaca (SIK) dengan carboxymetyl-chitosan (CMC) terhadap Kekuatan kompresi dan morfologi permukaan. Metode: Tiga puluh lubang pada cetakan akrilik silindris Diameter 4 mm tinggi 8 mm diisi dengan material SIK (FUJI IX, GC corp, Japan), modifikasi SIK dengan CMC 5% dan 10% yang di campurkan pada komponen bubuk SIK. Sampel dibagi menjadi 3 kelompok yaitu kelompok kontrol SIK (n=10) dan kelompok SIK-CMC 5% (n=10) serta kelompok SIK-CMC 10% (n=10). Kekuatan kompresi diukur dengan menggunakan Universal Testing Machine (Tensilon RTG-10Kn, A&D, Japan) dan dihitung dengan rumus KK= P/(πr2) dimana P adalah beban maksimum dan r adalah radius dari spesimen. Data dianalisis dengan analisis statistik menggunakan One-Way ANOVA dan Post hoc Bonferroni (p<0,5). Morfologi permukaan material modifikasi SIK-CMC dan kontrol di amati dengan menggunakan Scanning Electronic Microscope (EVO MA-0, Zeiss, Germany). Hasil: Terdapat perbedaan bermakna antara kelompok modifikasi SIK-CMC 5% dan SIK-CMC 10% dengan kelompok kontrol (One-Way ANOVA; p<0,05). Berdasarkan uji Post Hoc Bonferroni (p<0,5) terdapat perbedaan yang bermakna Kekuatan kompresi pada material modifikasi SIK-CMC 5 % dan SIK-CMC 10% dengan kelompok kontrol SIK. Modifikasi SIK dengan CMC mempengaruhi perubahan morfologi berupa berkurangnya porusitas dan bertambahnya permukan retakan seiring dengan penambahan persentase CMC.Kesimpulan: Modifikasi SIK dengan Penambahan CMC Mengurangi kekuatan kompresi dengan rerata hasil paling rendah pada penambahan CMC 10%. Porusitas permukaan material modifikasi SIK dengan penambahan CMC memiliki kecenderungan berkurang dan bertambahnya permukaan retakan yang melebar seiring dengan penambahan persentase CMC.

---

Background: GIC as a restorative material has the ability to chemically bond to the structure of teeth and the ability to release fluoride so that it is suitable for use in patients with a high caries risk but has poor mechanical strength. Modification of GIC restorative materials with combination with bioactive materials to obtain benefits such as increasing mechanical properties, antibacterial properties and remineralization potential has been mentioned in some research literature. In this study, Carboxymethyl-chitosan (CMC) is added to the powder phase of conventional GIC to increase the compressive strength.

Objective: to analyze the influence of modified GIC with the addition of CMC on compressive strength and surface morphology.

Methods: Thirty holes in a cylindrical acrylic mold, each hole has a diameter of 4 mm and thickness of 8 mm, were filled with conventional GIC restorative material (FUJI IX, GC corp, Japan), modified GIC with 5% CMC and 10% CMC added in the powder phase. The samples were divided into 3 groups: control group GIC (n=10), GIC-CMC 5% group (n=10) and GIC-CMC 10% group (n=10). The compressive strength measurement performed with Universal testing machine (Tensilon RTG-10Kn, A&D, Japan), and were calculated according to the following equation: CS= P/(πr2)

Where P is the maximum load and r is the radius of the cylinder-shaped specimen Statistical analysis was done by One-Way ANOVA and Post hoc Bonferroni (p<0.05). The surface morphology of the material modification of GIC-CMC and control group was observed using the Scanning Electronic Microscope (EVO MA-0, Zeiss, Germany).

Results: There is a significant difference between the GIC-CMC 5% and GIC-CMC 10% modification groups and the control group (One-Way ANOVA; p<0.05). Based on the Post Hoc Bonferroni (p<0.5) test there is a significant difference in compressive strength in SIK-CMC modification materials of 5% and SIK-CMC of 10% with the SIK control group. Modification of SIK with CMC affects morphological changes in the form of reduced porosity and increased fractures along with the addition of CMC percentage.

Conclusion: Modification of GIC with CMC addition reduces compressive strength with the lowest average yield at 10% CMC addition. The surface porusity of SIK modification material with the addition of CMC tends to decrease and increase the surface of cracks that widen along with the addition of CMC percentage."

"Latar Belakang : SIK sebagai bahan restorasi memiliki kemampuan untuk berikatan secara kimiawi terhadap struktur gigi dan kemampuan melepaskan fluoride sehingga cocok digunakan pada pasien dengan risiko karies tinggi namun memiliki kekuatan mekanis yang buruk. Modifikasi bahan restorasi SIK melalui penggabungan dengan bahan bioaktif untuk mendapatkan manfaat seperti meningkatnya sifat mekanis, sifat antibakteri dan potensi remineralisasi telah di sebutkan pada beberapa literatur penelitian. Pada studi ini, bubuk carboxymetyl-chitosan (CMC) ditambahkan pada komponen bubuk dari SIK konvensional. Tujuan: Menganalisis pengaruh modifikasi material semen ionomer kaca (SIK) dengan carboxymetyl-chitosan (CMC) terhadap Kekuatan kompresi dan morfologi permukaan. Metode: Tiga puluh lubang pada cetakan akrilik silindris Diameter 4 mm tinggi 8 mm diisi dengan material SIK (FUJI IX, GC corp, Japan), modifikasi SIK dengan CMC 5% dan 10% yang di campurkan pada komponen bubuk SIK. Sampel dibagi menjadi 3 kelompok yaitu kelompok kontrol SIK (n=10) dan kelompok SIK-CMC 5% (n=10) serta kelompok SIK-CMC 10% (n=10). Kekuatan kompresi diukur dengan menggunakan Universal Testing Machine (Tensilon RTG-10Kn, A&D, Japan) dan dihitung dengan rumus KK= P/(πr2) dimana P adalah beban maksimum dan r adalah radius dari spesimen. Data dianalisis dengan analisis statistik menggunakan One-Way ANOVA dan Post hoc Bonferroni (p<0,5). Morfologi permukaan material modifikasi SIK-CMC dan kontrol di amati dengan menggunakan Scanning Electronic Microscope (EVO MA-0, Zeiss, Germany). Hasil: Terdapat perbedaan bermakna antara kelompok modifikasi SIK-CMC 5% dan SIK-CMC 10% dengan kelompok kontrol (One-Way ANOVA; p<0,05). Berdasarkan uji Post Hoc Bonferroni (p<0,5) terdapat perbedaan yang bermakna Kekuatan kompresi pada material modifikasi SIK-CMC 5 % dan SIK-CMC 10% dengan kelompok kontrol SIK. Modifikasi SIK dengan CMC mempengaruhi perubahan morfologi berupa berkurangnya porusitas dan bertambahnya permukan retakan seiring dengan penambahan persentase CMC.Kesimpulan: Modifikasi SIK dengan Penambahan CMC Mengurangi kekuatan kompresi dengan rerata hasil paling rendah pada penambahan CMC 10%. Porusitas permukaan material modifikasi SIK dengan penambahan CMC memiliki kecenderungan berkurang dan bertambahnya permukaan retakan yang melebar seiring dengan penambahan persentase CMC

---

Background: GIC as a restorative material has the ability to chemically bond to the structure of teeth and the ability to release fluoride so that it is suitable for use in patients with a high caries risk but has poor mechanical strength. Modification of GIC restorative materials with combination with bioactive materials to obtain benefits such as increasing mechanical properties, antibacterial properties and remineralization potential has been mentioned in some research literature. In this study, Carboxymethyl-chitosan (CMC) is added to the powder phase of conventional GIC to increase the compressive strength. Objective: to analyze the influence of modified GIC with the addition of CMC on compressive strength and surface morphology. Methods: Thirty holes in a cylindrical acrylic mold, each hole has a diameter of 4 mm and thickness of 8 mm, were filled with conventional GIC restorative material (FUJI IX, GC corp, Japan), modified GIC with 5% CMC and 10% CMC added in the powder phase. The samples were divided into 3 groups: control group GIC (n=10), GIC-CMC 5% group (n=10) and GIC-CMC 10% group (n=10). The compressive strength measurement performed with Universal testing machine (Tensilon RTG-10Kn, A&D, Japan), and were calculated according to the following equation: CS= P/(πr2)

Where P is the maximum load and r is the radius of the cylinder-shaped specimen

Statistical analysis was done by One-Way ANOVA and Post hoc Bonferroni (p<0.05). The surface morphology of the material modification of GIC-CMC and control group was observed using the Scanning Electronic Microscope (EVO MA-0, Zeiss, Germany).

Results: There is a significant difference between the GIC-CMC 5% and GIC-CMC 10% modification groups and the control group (One-Way ANOVA; p<0.05). Based on the Post Hoc Bonferroni (p<0.5) test there is a significant difference in compressive strength in SIK-CMC modification materials of 5% and SIK-CMC of 10% with the SIK control group. Modification of SIK with CMC affects morphological changes in the form of reduced porosity and increased fractures along with the addition of CMC percentage.Conclusion: Modification of GIC with CMC addition reduces compressive strength with the lowest average yield at 10% CMC addition. The surface porusity of SIK modification material with the addition of CMC tends to decrease and increase the surface of cracks that widen along with the addition of CMC percentage."

"Latar Belakang: Kegagalan perawatan karies gigi dapat terjadi jika mineral intrafibrillar dentin tidak teremineralisasi secara biomimetik. Semen ionomer kaca (SIK) merupakan bahan restorasi gigi dengan kemampuan melepaskan ion kalsium yang merupakan bahan baku remineralisasi. Carboxymethyl chitosan (CMC) merupakan analog protein non-kolagen alami yang terbukti dapat menstabilkan ion kalsium fosfat dalam keadaan amorf dalam proses remineralisasi biomimetik. Pencampuran kedua bahan tersebut berpotensi menghasilkan bahan restorasi baru yang dapat meremineralisasi dentin secara biomimetik. Tujuan: Mengevaluasi hasil remineralisasi dentin yang tedemineralisasi setelah aplikasi material modifikasi SIK dengan CMC 5% dan 10% dengan memeriksa perubahan morfologi dan komposisi ion kalsium dentin. Metode: Proses remineralisasi dilakukan dengan mengaplikasikan material SIK, SIK-CMC 5% dan 10% selama 14 hari pada kavitas dentin yang terdemineralisasi dengan EDTA 17% selama 7 hari. Evaluasi morfologi dilakukan dengan Scanning Electron Microscope (SEM) dan nilai komposisi ion diperiksa dengan Energy Dispersive X-ray (EDX). Hasil: Terlihat perubahan morfologi tubulus dan permukaan dentin setelah aplikasi bahan SIK, SIK-CMC 5%, dan SIK-CMC 10% selama 14 hari yang dievaluasi dengan SEM. Hasil pemeriksaan EDX memperlihatkan peningkatan kandungan ion kalsium dan pembentukan hidroksiapatit setelah aplikasi material SIK-CMC 10%. Kesimpulan: Aplikasi modifikasi SIK dengan CMC berpengaruh terhadap perubahan morfologi dan komposisi ion kalsium pada dentin yang terdemineralisasi.

---

Background: Failure of dental caries treatment can occur if intrafibrillar dentin minerals are not biomimetically mineralized. Glass ionomer cement (GIC) is a dental restoration material with the ability to release calcium ions which are the raw material for remineralization. Carboxymethyl chitosan (CMC) is a natural non-collagen protein analogue which has been proven to stabilize calcium phosphate ions in an amorphous state in a biomimetic remineralization process. Mixing these two materials has the potential to produce new restorative materials that can biomimetically remineralize dentin. Objective: To evaluate the remineralization results of demineralized dentin after application of GIC modified material with 5% and 10% CMC by examining changes in the morphology and composition of dentin calcium ions. Method: The remineralization process was carried out by applying SIK material, SIK-CMC 5% and 10% for 14 days to the demineralized dentin cavity with 17% EDTA for 7 days. Morphological evaluation was carried out using a Scanning Electron Microscope (SEM) and ion composition values were examined using Energy Dispersive X-ray (EDX). Results: Changes in tubule morphology and dentin surface were seen after application of SIK, SIK-CMC 5%, and SIK-CMC 10% for 14 days as evaluated by SEM. The EDX examination results showed an increase in calcium ion content and hydroxyapatite formation after application of 10% SIK-CMC material. Conclusion: Application of GIC modification with CMC affects changes in morphology and calcium ion composition in demineralized dentin.

​

"

"Latar Belakang: Salah satu material remineralisasi yang banyak digunakan adalah semen ionomer kaca (SIK). Namun dentin terdemineralisasi sesudah aplikasi SIK memiliki sifat mekanis yang berbeda dan lebih rendah daripada dentin normal karena remineralisasi yang terjadi adalah remineralisasi interfibril. Material carboxymethyl chitosan (CMC) bertindak sebagai analog protein nonkolagen yang mampu menstabilisasi nanocluster amorphous calcium phosphate (ACP) dalam proses remineralisasi intrafibril. Tujuan: Mengetahui pengaruh aplikasi modifikasi SIK-CMC5% dan SIK-CMC10% pada dentin terdemineralisasi terhadap kekerasan mikro, fasa mineral dan derajat kristalinitas dentin. Metode: Material SIK dilakukan pencampuran dengan CMC pada rasio 5% dan 10% menghasilkan SIK-CMC5% dan SIK-CMC10%. Kemudian, demineralisasi pada kavitas dentin terdemineralisasi dilakukan dengan aplikasi material SIK, SIK-CMC5% dan SIK-CMC10%. Akar gigi direndam dalam cairan phosphate-buffered saline selama 14 hari. Remineralisasi dentin dievaluasi dari kekerasan mikro melalui uji Vickers dan penilaian fasa mineral dan derajat kristalinitas dentin dari uji X-Ray Diffraction (XRD). Hasil: Kekerasan mikro dentin pada kelompok SIK-CMC5% dan SIK-CMC10% meningkat dibandingkan pada kelompok SIK. Pembentukan kristal hidroksiapatit ditemukan pada sampel SIK dan SIK-CMC, dengan derajat kristalinitas tertinggi pada sampel SIK-CMC10%. Kesimpulan: Semen Ionomer Kaca modifikasi Carboxymethyl Chitosan 10% lebih efektif dalam meningkatkan nilai kekerasan mikro dan mempengaruhi pembentukan fasa mineral kristal hidroksiapatit dan derajat kristalinitas.

---

Background: One of the widely used remineralization materials is glass ionomer cement (GIC). However, demineralized dentine after GIC application has different and lower mechanical properties than normal dentin because the remineralization that occurs is interfibril remineralization. Carboxymethyl chitosan (CMC) acts as noncollagenous protein analog that can stabilize amorphous calcium phosphate (ACP) nanoclusters in intrafibril remineralization. Objective: To determine the effect of the application of modified GIC-CMC5% and GIC-CMC10% on the microhardness, mineral phase and degree of crystallinity of demineralized dentin. Methods: GIC material was mixed with CMC at ratio 5% and 10% to produce GIC-CMC5% and GIC-CMC10%. Remineralization of demineralized dentin cavity was carried out by applying GIC, GIC-CMC5% and GIC-CMC10% for 14 days. Remineralization was evaluated from microhardness value through Vickers test and assessment of mineral phase and degree of dentin crystallinity from X-Ray Diffraction (XRD) test. Results: Dentin microhardness in the GIC-CMC5% and GIC-CMC10% was increasing compared to the CIC group. The formation of hydroxyapatite crystals was found in the GIC and GIC-CMC samples with the highest degree of crystallinity in the GIC-CMC10% sample. Conclusion: Modified Glass Ionomer Cement with 10% Carboxymethyl Chitosan is more effective in increasing the microhardness value and affecting the formation of the hydroxyapatite crystalline mineral phase and the degree of crystallinity."

"Latar Belakang: Semen ionomer kaca (SIK) merupakan bahan tumpat berbahan dasar air yang cukup populer, tetapi memiliki kelemahan pada sifat mekanisnya. Seiring perkembangan teknologi, ditemukan bahan tumpat baru yaitu Giomer. Keduanya memiliki keunggulan berupa sifat pelepasan fluoride, sehingga diharapkan Giomer dapat menutupi kekurangan SIK yang terletak pada sifat mekanisnya, salah satunya kekuatan tekan. Beberapa penelitian menyatakan bahwa sifat mekanis suatu material berhubungan dengan morfologi permukaan dan komposisi kimia. Tujuan: Mengetahui perbandingan kekuatan tekan SIK dan Giomer, serta hubungannya dengan morfologi permukaan dan komposisi kimia. Metode: 16 spesimen SIK dan Giomer disiapkan untuk uji kekuatan tekan lalu dianalisis dengan uji Independent T-test. Kemudian spesimen SIK dan Giomer disiapkan untuk analisis morfologi permukaan dan komposisi kimia menggunakan SEM-EDX. Hasil Penelitian: Terdapat perbedaan bermakna nilai kekuatan tekan antara SIK dan Giomer dengan nilai kekuatan tekan Giomer lebih tinggi (204,67 MPa) dibandingkan dengan SIK (118,59 MPa). SIK memiliki permukaan eksternal yang lebih tidak beraturan, ukuran partikel lebih besar, dan lebih banyak porus. Kandungan silika pada Giomer lebih tinggi. Kesimpulan: Giomer memiliki kekuatan tekan lebih tinggi dibandingkan dengan SIK. Material restorasi dengan morfologi permukaan yang lebih beraturan, lebih sedikit porus, dan ukuran partikel yang lebih kecil dengan susunan yang rapat, serta kandungan silika dan karbon yang lebih tinggi berhubungan dengan kekuatan tekan yang lebih tinggi.

---

Background: Glass ionomer cement (GIC) is a water-based filling material that is quite popular, but has a weakness in its mechanical properties. Along with the development of technology, a new filling material was discovered, namely Giomer. Both have advantages in the form of fluoride release properties, so it is hoped that Giomer can cover the shortcomings of GIC which lie in their mechanical properties, one of which is compressive strength. Several studies have stated that the mechanical properties of a material are related to the surface morphology and chemical composition. Objective: To determine the comparison of the compressive strength of GIC and Giomer, as well as their relationship to surface morphology and chemical composition. Methods: 16 specimens of GIC and Giomer were prepared for compressive strength test and then analyzed by Independent T-test. Then the GIC and Giomer specimens were prepared for analysis of surface morphology and chemical composition using SEM-EDX. Research Results: There is a significant difference in the compressive strength value between GIC and Giomer with a higher Giomer compressive strength value (204.67 MPa) compared to GIC (118.59 MPa). GICs have a more irregular external surface, larger particle size, and more porosity. The silica content in Giomer is higher. Conclusion: Giomer has higher compressive strength than GIC. A restorative material with a more regular surface morphology, less porous and smaller particle size with a denser arrangement, and higher silica and carbon content is associated with higher compressive strength."

"Latar belakang: Semen MTA telah digunakan dalam berbagai prosedur endodontik karena memiliki sealing ability yang baik, biokompatibel, bioaktif, dan bersifat antibakteri. Namun, semen MTA memiliki beberapa kelemahan seperti waktu pengerasan yang lama, konsistensi berpasir sehingga sulit untuk dimanipulasi serta kekuatan mekanik yang relatif rendah. Polimer sintetik dan alami telah diteliti sebagai material aditif pada semen MTA dan diketahui dapat meningkatkan sifat manipulasi material. Kitosan larut air merupakan polimer alami yang memiliki keunggulan bioaktivitas, biokompatibilitas dan biodegradabilitas serta dapat larut pada pH fisiologis.Tujuan: Penelitian ini bertujuan untuk mengetahui pengaruh penambahan kitosan larut air terhadap kekuatan kompresi semen MTA. Metode: Spesimen penelitian dibagi menjadi tiga kelompok; MTA, MTA dengan penambahan kitosan larut air 5% (MTA-CW5), dan MTA dengan penambahan kitosan larut air 10% (MTA-CW10). Pengukuran kekuatan kompresi dilakukan dengan alat universal testing machine setelah diinkubasi selama empat hari pada temperatur 37°C dan kelembabab relatif 100%. Hasil: Terdapat perbedaan bermakna dari nilai rerata kekuatan kompresi ketiga kelompok perlakuan (Uji one-way ANOVA). Hasil uji Post Hoc Bonferroni menunjukkan perbedaan kekuatan kompresi yang bermakna antara kelompok MTA-CW5 dengan MTA, kelompok MTA-CW10 dengan MTA serta MTA-CW 5 dengan MTA-CW10. Kesimpulan: Penambahan kitosan larut air konsentrasi 5% dan 10% dapat meningkatan kekuatan kompresi semen MTA.

---

Background: Mineral trioxide aggregates have been used in various endodontic treatments because of the sealing ability, biocompatibility, bioactivity, and antibacterial properties. However, MTA cement has several disadvantages such as long setting time, sandy consistency, and relatively low mechanical strength. Synthetic and natural polymers have been investigated as additives in MTA cement and could improve its handling characteristic. Water soluble chitosan is a natural polymer with excellent bioactivity, biocompatibility, biodegradability and soluble at physiological pH. 

Objectives: This study aimed to determine the effect of adding water-soluble chitosan to the compressive strength of MTA

Methods: The specimens were divided into three groups; MTA, MTA with the addition of 5% water soluble chitosan (MTA-CW5), and MTA with the addition of 10% water soluble chitosan (MTA-CW10). The compressive strength measurement was carried out using a universal testing machine after four days incubation at 37°C and 100% humidity.

Result: There were significant different mean values of the compressive strength between three groups (one-way ANOVA test). Post Hoc Bonferroni test showed significant differences in compressive strength between the MTA-CW5 and MTA group, the MTA-CW10 and MTA group, also the MTA-CW 5 and MTA-CW10 group.

Conclusion: The addition of 5% and 10% water-soluble chitosan could increase the compressive strength of MTA cement. "

"SIK modifikasi resin dapat mengalami penurunan kekerasan permukaan pada pH kritis rongga mulut 5,5 yang dapat dicegah dengan pemberian ion kalsium dan fosfat. Ion tersebut bersumber dari CPP ACP. Pengaplikasian CPP ACP pada SIK modifikasi resin diketahui mampu mencegah terjadinya penurunan kekerasan permukaan SIK modifikasi resin. Saat ini telah ada penggabungan propolis pada CPP ACP yang bertujuan untuk meningkatkan sifat antibakteri tetapi diketahui penambahan propolis mengurangi pelepasan ion kalsium dan fosfat dari CPP ACP sehingga berpengaruh terhadap kemampuannya dalam melindungi SIK modifikasi resin dari penurunan kekerasan permukaan. Namun belum diketahui efek pengaplikasian CPP ACP yang ditambahkan propolis terhadap kekerasan permukaan SIK modifikasi resin.Tujuan: penelitian ini bertujuan untuk membandingkan pengaruh aplikasi pasta CPP ACP dengan dan tanpa kombinasi propolis terhadap kekerasan permukaan semen ionomer kaca modifikasi resin.Metode: Tiga puluh spesimen semen ionomer kaca modifikasi resin berbentuk silinder berukuran 6 x 3 mm, di polimerisasi menggunakan LED curing unit irradiansi 700 mW/cm2, selama 20 detik kemudian disimpan selama 1 hari kering dalam inkubator. Spesimen diuji kekerasan awalnnya dengan Knoop Hardness Tester (50 g selama 15 detik) dengan penjejasan 5 kali di 5 lokasi permukaan yang berbeda kemudian diambil nilai rata-ratanya untuk mempresentasikan permukaan spesimen. Spesimen dibagi menjadi tiga kelompok yaitu spesimen tanpa dan dengan pengolesan CPP ACP yang didiamkan 30 menit dan dengan pengolesan CPP ACP propolis yang didiamkan 30 menit. Seluruh spesimen direndam dalam larutan asam laktat pH 5,5 selama 24 jam dan diuji nilai kekerasan permukaan akhirnya. Data dianalisis menunggunakan uji statistik Kruskal Wallis dan uji Post Hoc Mann Whittney.Hasil: hasil menunjukkan bahwa kekerasan awal seluruh spesimen adalah 30,68, 0,03 dan setelah diberi perlakuan kelompok A menjadi 24,96, 0,07, kelompok B menjadi 27,9, 0,01 dan kelompok C menjadi 26.5, 0,03. Pengaplikasian CPP ACP propolis pada SIK modifikasi resin menyebabkan penurunan kekerasan permukaan yang lebih besar dibandingkan dengan yang hanya diaplikasikan CPP ACP.

---

The surface hardness of Resin modified glass ionomer cement can be decrease at the critical pH of the oral cavity 5.5 which can be prevented by giving calcium and phosphate ions. These ions can be sourced from CPP ACP. Aplication CPP ACP is known to be able to prevent a decrease in the surface hardness of resin modified glass ionomer cement. Now there has been the addition of propolis to CPP ACP which functions as an antibacterial but it is known the further addition of propolis reduces ion calcium and phosphate release from CPP ACP which influences its capability in protecting RMGIC from further reduction of surface hardnes. However, the effect of CPP ACP application that added propolis is not yet known on resin modified glass ionomer cement.

Objective: this study aims to compare the effect of CPP ACP paste application with it and without a combination of propolis against the surface hardness of glass ionomer cement modified resin.

Methods: thirty specimens of Resin Modified Glass Ionomer Cement in cylindrical shape (6 x 3 mm), 1 day dray storage in the incubator and the specimen are polymerized for 20 seconds using a 700 mW/cm irradiance LED curing unit. The initial specimens were tested for hardness with Knoop Hardness Tester (50 g for 15 seconds) with 5 times of crushing in 5 different surface locations then the average value was taken to present the specimen surface. The specimens were divided into three groups: without CPP ACP application, CPP ACP and CPP ACP Propolis application which were allowed to stand for 30 minutes. All specimens were immersed in lactic acid pH 5.5 for 24 hours and tested for final surface hardness values. Data obtained analyzed using Kruskal Wallis dan Mann Whittney.

Results: the test showed that the initial hardness of all specimens were 30,68, 0,03 and after treatment group A becomes 24,96, 0,07, group B becomes 27,9, 0,01 and group C becomes 26.5, 0,03. There was a decrease surface hardness of the resin modified glass ionomer cement before and after immersion at all groups. The initial hardness of all specimens were 30,68, 0,03 and after treatment group A becomes 24,96, 0,07, group B becomes 27,9, 0,01 and group C becomes 26.5, 0,03. The application of CPP ACP propolis to RMGIC caused."

"[Latar Belakang : Semen Ionomer Kaca Modifikasi Resin (SIKMR) merupakan salah satu material restorasi yang terdiri dari bubuk dan cairan yang kestabilannya dipengaruhi oleh shelf life. Hal ini masih belum diperhatikan oleh pengguna maupun penjual. Tujuan : Mengetahui pengaruh shelf life terhadap nilai kuat tekan SIKMR. Metode : 30 spesimen berbentuk silinder (d=4mm dan t=6mm) SIKMR (Fuji II LC dari GC, Tokyo) dibagi menjadi tiga kelompok berdasarkan lama penyimpanan dan dilakukan uji kuat tekan dengan universal testing machine. Data kemudian dianalisis statistik dengan uji One-Way ANOVA. Hasil : Terdapat perbedaan bermakana (p<0,05) antara ketiga kelompok SIKMR. Kesimpulan : Terdapat penurunan nilai kuat tekan seiring dengan lamanya penyimpanan, Background : Resin Modified Glass Ionomer Cement (RMGIC) is one of restoration materials composed by powder and liquid that their stability is affected by shelf life. This thing hasn’t been taken as a consideration by customers or sellers. Objective : To observe the influence of shelf life on compressive strength of RMGIC. Methods: 30 cylindrical (d = 4mm and t = 6mm) specimens RMGIC (Fuji II LC of GC, Tokyo) are divided into three groups with different storage time and compressive strength tested with universal testing machine. Results were statistically analyzed with One-Way ANOVA test. Results: There are significant differences (p< 0.05) between three groups of RMGIC. Conclusion: There is a decrease in compressive strength value along with the length of storage time]"

"Latar Belakang: Saat ini perawatan pulpa vital mengacu pada konsep minimal intervensi, yaitu dengan meninggalkan lapisan affected dentin saat ekskavasi karena masih terdapat ikatan silang kolagen sehingga dapat dilakukan upaya remineralisasi. Remineralisasi melalui aplikasi material bioaktif Mineral Trioxide Aggregate (MTA) belum dapat menghasilkan karakteristik dentin menyerupai dentin normal karena pembentukan mineral hanya terjadi pada ruang ekstrafibrillar. Penggunaan material analog protein non kolagen dibutuhkan untuk menstabilkan nano Amorphous Calcium Phosphate (ACP) agar dapat memasuki ruang intrafibrillar, salah satunya menggunakan Carboxymethyl Chitosan (CMC).Tujuan: mengevaluasi remineralisasi dentin pada permukaan dentin terdemineralisasi setelah aplikasi material MTA dan material modifikasi MTA-CMC dengan melihat morfologi permukaan dan komposisi ion pada dentin.Metode: remineralisasi dilakukan melalui aplikasi material MTA, MTA-CMC 5% dan 10% selama 14 hari pada permukaan sampel dentin yang terdemineralisasi. Pengamatan morfologi dilakukan dengan Scanning Electron Microscope (SEM) dan konfirmasi komposisi ion dengan Energy Dispersive X-ray Spectroscopy (EDX).Hasil: terdapat perbedaan morfologi pada permukaan dentin setelah dilakukan remineralisasi melalui aplikasi MTA, MTA-CMC 5%, dan MTA-CMC 10% selama 14 hari yang dievaluasi menggunakan SEM. Hasil analisis EDX mengonfirmasi adanya peningkatan kandungan kalsium dan fosfor pada permukaan dentin yang diremineralisasi dengan material MTA-CMC.Kesimpulan: remineralisasi melalui aplikasi material modifikasi MTA-CMC dapat memengaruhi morfologi permukaan dan komposisi ion pada permukaan dentin yang terdemineralisasi.

---

Background: Vital pulp treatment refers to the concept of minimal intervention by preserving the affected dentin layer in the excavation process because there are still collagen cross-linked to induce remineralization. Remineralization through the application of bioactive material Mineral Trioxide Aggregate (MTA) produce different dentin characteristics to normal dentin because mineral formation only occurs in the extrafibrillar space. The use of non-collagen protein analog materials is needed to stabilize the nano Amorphous Calcium Phosphate (ACP) to get into the intrafibrillar space, one of which is Carboxymethyl Chitosan (CMC).

Objective: To evaluate dentin remineralization on the surface of demineralized dentin after the application of MTA and MTA-CMC modified material by looking at the surface morphology and ionic composition of the dentin.

Methods: The remineralization was carried out through the application of MTA,MTA-CMC 5%, MTA-CMC 10% materials for 14 days on the surface of demineralized dentin samples. Morphological observations were carried out by Scanning Electron Microscope (SEM) and confirmation of ion composition by Energy Dispersive X-ray Spectroscopy (EDX). Results: there were morphological differences on the dentin surface after remineralization through the application of MTA, MTA-CMC 5%, and MTA-CMC 10% for 14 days which were evaluated using SEM. The results of the EDX analysis confirmed an increase in the content of calcium and phosphorus on the dentin surface remineralized with MTA-CMC material.

Conclusion: remineralization through the application of MTA-CMC modified material can affect the surface morphology and ion composition on the demineralized dentin surface."

"Tujuan: Penelitian ini bertujuan untuk mengetahui pengaruh penyikatan dengan dantanpa pasta gigi charcoal terhadap kekerasan permukaan material restorasi semenionomer kaca modifikasi resin. Metode penelitian: Dalam penelitian ini digunakansemen ionomer kaca modifikasi resin Fuji II LC. Sejumlah 24 spesimen berbentuksilinder dengan ukuran diameter 6 mm dan tebal 2 mm yang dipolimerisasi denganmenggunakan LED light cured LEDMAX-Hilux selama 20 detik dengan irradiansi 800mW/cm2. Setelah polimerisasi, spesimen direndam dalam akuades pada suhu 37Cselama 24 jam. Spesimen diukur kekerasan permukaan awal dengan dengan KnoopMicrohardness tester Shimatzu HMV-G21 DT yang diindentasikan dengan beban 50 gfselama 15 detik. Selanjutnya, specimen dibagi menjadi tiga kelompok (n=8) denganperlakuan penyikatan dengan akuades, pasta gigi tanpa charcoal Colgate TotalProfessional Clean®, dan pasta gigi dengan charcoal Colgate Total Charcoal DeepClean® selama 4 menit 40 detik setara satu bulan penyikatan dengan beban 150 grammenggunakan Oral-B DB4010 Advance Power Battery Toothbrush. Spesimen kemudiandibersihkan dengan ultrasonic cleaner selama 20 detik dan diuji kekerasan permukaanakhir. Data dianalisis menggunakan uji One Way Anova untuk menilai perbedaankekerasan permukaan antara kelompok penyikatan. Hasil: Semen ionomer kacamodifikasi resin yang diberikan penyikatan dengan akuades, pasta gigi tanpa charcoal,dan pasta gigi charcoal menunjukkan peningkatan kekerasan permukaan yang signifikanantar kelompok (p<0,5). Peningkatan kekerasan permukaan paling tinggi terjadi padapenyikatan dengan pasta gigi charcoal. Kesimpulan: Semen ionomer kaca modifikasiresin setelah penyikatan menggunakan pasta gigi yang mengandung charcoal memilikikekerasan permukaan yang lebih tinggi dibandingkan pasta gigi yang tidak mengandungcharcoal

---

Objective: The aim of this study was to determine the effect of brushing with and without

charcoal toothpaste to surface hardness changes of resin modified glass ionomer cement.

Method: Resin modified glass ionomer cement Fuji II LC was used in this study. 24

specimens of 6 mm in diameter and 2 mm in thinkness with disk-shaped were prepared

and polymerized using LED light cured LEDMAX-Hilux in 20 seconds with irradiance

800 mW/cm2. After polymerization, specimens were immersed in 37C aquadest solution

for 24 hours. Specimens were measured initial surface hardness using Knoop

Microhardness tester Shimatzu HMV-G21 with 50 gf indentation in 15 seconds.

Futhermore, specimens were divided into three groups (n=8); brushed using distilled

water (group A), toothpaste without charcoal Colgate Total Professional Clean® (group

B), and toothpaste with charcoal Colgate Total Charcoal Deep Clean® (group C) for four

minutes and 40 seconds (equivalent to a month brushing) using Oral-B DB4010 Advance

Power Battery Toothbrush with a load of 150 gr. Specimens were cleaned with ultrasonic

cleaner in 20 seconds and were measured for final surface hardness. Data were anylized

using One Way Anova to assess the significant differences between brushed groups.

Result: The value of surface hardness of resin modified glass ionomer cement specimens

were increased significantly between groups (p<0,05). The enhancement of surface

hardness value of charcoal toothpaste was highest between brushed groups. Conclusion:

It was concluded that resin modified glass ionomer cement specimens after brushed with

charcoal toothpaste have a higher surface hardness than toothpaste without charcoal"