Venty Lestari
Pengaruh Persen Deformasi dan Temperatur Perlakuan Anil terhadap Sifat Mekanik dan Struktur Mikro Paduan Al-1,06Mg-0,63Si (% berat) = Effects of Deformation and Annealing Temperature on Mechanical Properties and Microstructures of Al-1.06Mg-0.63Si (wt. %) Alloy
"Aluminium merupakan logam kedua terbanyak yang digunakan setelah baja. Salah satu aluminium yang banyak digunakan di bidang industri adalah paduan aluminium seri 6xxx, dimana unsur utama dalam paduan ini adalah Mg dan Si. Paduan Al-Mg-Si dapat ditingkatkan sifat mekaniknya melalui proses deformasi dan perlakuan panas. Penelitian ini bertujuan untuk mengetahui pengaruh persen deformasi dan temperatur anil terhadap rekristalisasi dan sifat mekanik paduan Al-1,06Mg-0,63Si (% berat).
Pembuatan paduan menggunakan metode squeeze casting. Proses homogenisasi dilakukan pada temperatur 400 oC selama 4 jam. Kemudian paduan diberi perlakuan canai dingin dengan variasi persen deformasi sebesar 5, 10 dan 20 %. Pada sampel deformasi 20 % diberi perlakuan anil dengan variasi 400, 475 dan 550 oC selama 1 jam diikuti pencelupan cepat dengan media air. Karakterisasi material yang dilakukan meliputi pengujian komposisi kimia, pengujian kekerasan mikro dan makro, pengamatan struktur mikro yang terdiri dari mikroskop optik dan Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS) dan pengujian X-Ray Diffraction (XRD).
Hasil penelitian menunjukkan bahwa terjadinya pemipihan butir seiring dengan meningkatnya persen deformasi yang diberikan. Deformasi 5, 10 dan 20 % menghasilkan rasio deformasi sebesar 1,16, 1,56 dan 2,07 secara berurutan dan meningkatkan kekerasan mikro dan makro paduan. Nilai kekerasan tertingi pada sampel deformasi 20 % dengan kekerasan mikro sebesar 49,71 VHN dan kekerasan makro sebesar 62 HRE. Perlakuan anil pada temperatur 400 dan 475 oC menyebabkan terjadinya mekanisme rekristalisasi dimana telah tumbuh butir baru yang bebas dislokasi sehingga terjadi penurunan kekerasan mikro dan makro paduan. Pada temperatur 500 oC terjadi mekanisme pertumbuhan butir yang menyebabkan terjadinya penurunan nilai kekerasan mikro dan makro dari 35,94 VHN menjadi 33,85 VHN dan 48,50 HRE menjadi 47 HRE.
Aluminium is the second most widely used metal after steel. One of them is the 6xxx series aluminum alloy, whose Mg and Si as the main elements. Mechanical properties of Al-Mg-Si can be improved through deformation processes and heat treatment. The annealing treatment after deformation will restore the alloy's ductility through recovery, recrystallization, and grain growth mechanisms. This study aimed to determine the effect of percent deformation and annealing temperature on recrystallization and mechanical properties of Al-1.06Mg-0.63Si alloy (wt. %).
The alloy was produced by squeeze casting method. The homogenization process was carried out at 400 oC for 4 hours followed by cold rolling with different deformation of 5, 10, and 20 %. The 20 % deformed samples were annealed at 400, 475 and 550 oC for 1 hour, followed by water quenching. The material characterization included chemical composition testing, micro hardness and macro hardness, and observation of microstructures by an optical microscope and Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS) and X-Ray Diffraction (XRD) testing.
The results showed that higher deformation led to more elongated grains. Deformation of 5, 10, and 20 % resulted in a grain L/d ratio of 1.16, 1.56, and 2.07, respectively, as well as an increase in microand macro hardness. The highest hardness value was observed in the 20 % deformation sample with a micro hardness of 49.71 VHN and a macro hardness of 62 HRE. The annealing treatment at 400 and 475 oC caused a recrystallization mechanism where new grains that were free of dislocations had grown, resulting in a decrease in the micro and macro hardness of the alloy. At the temperature of 500 oC, the grain growth mechanism occured, which caused a decrease in the micro and macro hardness value from 35.94 VHN to 33.85 VHN and 48.50 HRE to 47 HRE."
Depok: Fakultas Teknik Universitas Indonesia, 2022
T-pdf
UI - Tesis Membership  Universitas Indonesia Library
cover
Maya Putri Agustianingrum
Studi pengaruh temperatur anil dan persen deformasi terhadap sifat mekanik dan struktur mikro paduan al-4.5zn-1.5mg-0.9cr berat hasil squeeze casting dan canai dingin = Effect of annealing temperature and deformation on the mechanical properties and microstructure of al 4zn 1 5mg 0 9cr wt alloy fabricated by squeeze casting
" ABSTRAK
Paduan aluminum telah dikenal sebagai material utama untuk berbagai aplikasi yang membutuhkan kombinasi antara kekuatan dan massa jenis yang rendah. Paduan aluminium yang sering diaplikasikan yaitu paduan seri 7xxx. Kebanyakan paduan ini digunakan untuk aplikasi pesawat terbang yang membutuhkan kekuatan yang tinggi dan keuletan. Dalam industri penerbangan, paduan Al-Zn-Mg mengalami proses pembentukan untuk menghasilkan produk struktural. Salah satu masalah yang sering muncul dari produk hasil pembentukan adalah peripheral coarse grain PCG dan hot tearing yang dapat mengurangi sifat mekanik dan ketahanan korosi paduan. Penambahan paduan mikro dapat digunakan untuk mengatasi masalah ini. Penambahan kromium Cr pada paduan Al-Zn-Mg dapat menekan pertumbuhan butir dan mengontrol ukuran butir dengan mencegah rekristalisasi lanjutan. Tujuan dari studi ini yaitu untuk mengetahui pengaruh deformasi melalui proses canai dingin pada paduan Al-4.5Zn-1.5Mg-0.9Cr berat dan untuk mengetahui pengaruh kromium terhadap struktur mikro dan sifat mekanik selama rekristalisasi melalui proses anil.Dalam studi ini, paduan dihasilkan melalui squeeze casting. Kemudian, paduan dilakukan homogenisasi selama 4 jam dengan temperatur 400 C. Paduan kemudian dicanai dingin dengan persen deformasi 5, 10 dan 20 . Proses anil dilakukan pada sampel deformasi 20 dengan variasi temperatur 300, 400 dan 500 C selama 2 jam. Karakterisasi yang dilakukan terdiri dari analisis struktur mikro oleh mikroskop optik dan Scanning Electron Microscope SEM - Energy Dispersive Spectroscopy EDS dan pengujian sifat mekanik dengan uji keras Microvickers. Hasilnya, terjadi pemipihan struktur diikuti dengan peningkatan reduksi ketebalan 5, 10 dan 20 dengan nilai rasio butir terdeformasi berturut-turut yaitu, 1.6, 2.84 dan 2.99. Struktur yang semakin pipih ini efektif untuk meningkatkan kekerasan. Selain itu, proses anil hasil canai dingin 20 pada temperatur 300 C dan 400 C belum menunjukkan adanya proses rekristalisasi. Proses rekristalisasi baru terjadi pada proses anil dengan temperatur 500 C. Sementara, pada paduan tanpa Cr, rekristalisasi baru terjadi pada temperatur 400 C. Hal ini dikarenakan adanya dispersoid Cr dalam bentuk Al, Zn 7Cr dengan ukuran kurang dari 1 m menghambat pergerakan dislokasi dan proses rekristalisasi. Hal ini ditandai dengan pembentukan butir baru berawal dari intermetalik Al, Zn 7Cr dengan ukuran lebih dari 1 m yang telah terdeformasi melalui mekanisme particle stimulated nucleation PSN .
ABSTRACT Aluminum alloys have been known as the main material for various application which requires the combination of strength and low density. One of the alloys that widely used is 7xxx series aluminum alloy. Most of the alloys are commonly used in aircraft industries for their high strength and ductility. In aircraft industries, Al Zn Mg alloys undergo many kinds of forming processes to create structural product. Problems that are usually found in the forming process include peripheral coarse grain PCG and hot tearing which decrease mechanical properties and corrosion resistance of the alloys. Microalloying element can be used to overcome these problems. The addition of chromium Cr in Al Zn Mg alloys can supress the grain growth and control the grain size by preventing excess recrystallization. The aim of this study is to understand the effect of deformation by cold rolling and Cr addition on the microstructure and mechanical properties of Al 4.5Zn 1.5Mg 0.9Cr wt. during recrystallization by annealing process.The Al 4Zn 1.5Mg 1Cr wt. alloy was fabricated by squeeze casting process and was subsequently homogenized at 400 oC for 4 hours. The samples were cold rolled for 5, 10 and 20 . The 20 deformed samples were then annealed at 300, 400 and 500 oC for 2 hours. The material characterization consisted of microstructure analysis by optical microscope and Scanning Electron Microscope SEM Energy Dispersive Spectroscopy EDS and also mechanical testing by Microvickers hardness test. The results showed that the deformed grain ratio was found to be 1.6, 2.84 dan 2.99 in the 5, 10 and 20 deformed samples, rexspectively. The elongated dendrites were effective to increase the hardness of the alloy. No recrystallization was detected during annealing at 300 oC and 400 oC. Recrystallization was observed in the annealing process at 500 oC. Whereas, for the samples without Cr addition, recrystallization occurred at 400 oC. It means the addition of Cr was found to increase the recrystallization temperature of the alloy. It occurred because Cr dispersoid in Al, Zn 7Cr with size less than 1 m impedes the dislocation motion. However, the presence of Al, Zn 7Cr intermetalics with size more than 1 m promote the formation of new grains around them by particle stimulated nucleation PSN mechanism. "
Depok: Fakultas Teknik Universitas Indonesia, 2016
S63574
UI - Skripsi Membership  Universitas Indonesia Library
cover
Desrilia Nursyifaulkhair
Studi pengaruh temperatur penuaan terhadap sifat mekanik dan struktur mikro paduan Al-5.1Zn-1.8Mg-0.4Ti (% berat) hasil squeeze casting = Effect of ageing temperature on mechanical properties and microstructure of Al-5.1Zn-1.8Mg-0.4Ti alloy (wt.%) fabricated by squeeze casting
"Paduan Al-Zn-Mg (Seri 7xxx) telah banyak dikembangkan dalam berbagai aplikasi, terutama dalam industri penerbangan sebab memiliki kekerasan yang tinggi sementara densitasnya rendah. Paduan tersebut umumnya diperkuat melalui perlakuan penuaan, di mana terjadi difusi atom-atom Zn dan Mg dari larutan padat sangat jenuh sehingga terbentuk presipitat metastabil. Selain itu, paduan dapat diperkuat pula dengan penambahan Ti yang akan memperhalus butir. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh Ti dalam penguatan presipitasi paduan Al-5.1Zn-1.8Mg-0.4Ti (% berat) pada berbagai temperatur.
Paduan ini dibuat dengan proses squeeze casting. Kemudian dilakukan homogenisasi pada temperatur 400 oC selama 4 jam dan laku pelarutan pada 440 oC selama 1 jam yang dilanjutkan dengan pencelupan air hingga temperatur ruang. Penuaan dilakukan pada temperatur 90, 130 dan 200 oC selama 200 jam. Untuk mengetahui respon penuaan, dilakukan pengujian kekerasan Rockwell, sementara itu perubahan struktur mikro diamati dengan menggunakan Mikroskop Optik dan Scanning Electron Microscope (SEM) - Energy Dispersive Spectroscopy (EDS).
Hasil penelitian menunjukkan bahwa kekerasan tertinggi dihasilkan setelah penuaan di temperatur 90 oC, bahkan pada temperatur ini, kekerasan terus meningkat setelah 200 jam. Semakin tinggi temperatur penuaan, semakin rendah kekerasan puncak yang dihasilkan, tapi waktu yang dibutuhkan untuk mencapai kekerasan puncak akan berkurang. Penambahan Ti diketahui dapat menahan penguatan dengan memperlambat kinetika presipitasi melalui penurunan jumlah kekosongan kompleks zat terlarut. Urutan presipitasi yang terbentuk adalah GP zone  ƞ?  ƞ (MgZn2).
Al-Zn-Mg alloys (7xxx series Al alloys) have been widely used in many applications, especially in aerospace industry because of their high strength and low density. These alloys are commmonly hardened upon ageing treatment, in which diffusion of Zn and Mg atoms from super saturated solid solution results in formation of metastable precipitates. To further increase the strength of the alloys, Ti is added to decrease the grain size. The objective of this study is to investigate the role of Ti in the precipitation strengthening of Al-5Zn-1.8Mg-0.4Ti (wt.%) alloy.
The alloy was fabricated by squeeze casting process. Then, the alloy was homogenized at 400 oC for 4 hours. Subsequent solution treatment was employed at 440 oC for 1 hour and followed by water quenching to room temperature. The ageing was conducted at 90, 130 and 200 oC for 200 hours. The ageing response was followed by Rockwell hardness testing, while the microstructural evolution was observed by using Optical Microscope (OM) and Scanning Electron Microscope (SEM) - Energy Dispersive Spectroscopy (EDS).
The results showed that the highest hardness was achieved after ageing at 90 oC, and even at this temperature, the hardness remained increase after 200 h of ageing. The higher the ageing temperature, the lower the achieved peak hardness but the time needed to peak hardness reduced. Addition of Ti retarded the strengthening by slowering kinetics of precipitation through decreasing number of solute-vacancy complexes. The suggested major precipitation sequence was GP zones  ƞ?  ƞ (MgZn2)."
Depok: Fakultas Teknik Universitas Indonesia, 2017
S66089
UI - Skripsi Membership  Universitas Indonesia Library
cover
Rachman Kurnia
Studi pengaruh canai dingin dan temperatur anil terhadap sekristalisasi serta sifat mekanik paduan Al-4.7Zn-1.8mg (% berat) hasil squeeze casting = Effect of cold rolling and annealing temperatur on recrystallization and mechanical properties of Al-4.7Zn-1.8mg (wt. %) produced by squeeze casting
"Aluminium dan paduannya tengah dikembangkan sebagai badan pesawat terbang karena sifatnya yang lebih ringan daripada baja dan mudah dibentuk. Paduan aluminium 7XXX yang mengandung Zn dan Mg dapat ditingkatkan sifat mekanisnya melalui proses deformasi. Persentase deformasi yang diberikan akan meningkatkan kekerasan paduan melalui mekanisme penguatan regang. Proses anil yang dilakukan setelah deformasi akan mengembalikan keuletan paduan melalui mekanisme stress relieve, rekristalisasi dan pertumbuhan butir. Penelitian ini bertujuan untuk mengetahui pengaruh persen deformasi dan temperatur anil terhadap rekristalisasi dan sifat mekanik paduan Al-4.7Zn-1.8Mg berat.
Pembuatan paduan dilakukan dengan proses squeeze casting. Proses homogenisasi dilakukan pada temperatur 400 oC selama 4 jam. Paduan hasil homogenisasi kemudian diberikan canai dingin dengan persen deformasi 5, 10 dan 20 . Selanjutnya paduan dengan deformasi 20 diberi perlakuan panas anil dengan temperatur 300, 400 dan 500 oC selama 2 jam. Karakterisasi meliputi pengujian kekerasan untuk melihat pengaruh canai dingin dan temperatur anil terhadap sifat mekanik paduan, pengamatan struktur mikro dengan mikroskop optik dan Scanning Electron Microscope SEM yang dilengkapi dengan Energy Dispersive Spectroscopy EDS.
Hasil penelitian menunjukkan bahwa peningkatan persen deformasi sebesar menyebabkan terjadinya pemipihan butir. Deformasi 5, 10 dan 20 menghasilkan rasio deformasi butir sebesar 2.19, 3.19 and 4.59 dan meningkatkan kerasan paduan dari 69.5 HV menjadi sebesar 95.3, 100.1 dan 105.4 HV. Perlakuan panas anil pada temperatur 300 oC menyebabkan terjadinya recovery sedangkan rekristalisasi terjadi pada temperatur 400 oC dgrain 290 ?m. Grain growth terjadi pada temperatur 500 oC dgrain 434 ?m yang menyebabkan penurunan kekerasand dari 105.4 HV menjadi 71.5, 96.8 and 95.3 HV berturut turut. Rekristalisasi sempurna diprediksi pada temperature anil 375 ndash; 425 oC selama 2 jam.
Aluminium alloys are developed as airplane body due to its lighter weight compared to steel and good formability. Aluminium 7XXX series with Zn and Mg alloying elements are commonly used because of its mechanical properties can be improved through deformation process. Deformation such as cold rolling may increase the hardness of an alloy through strain hardening. Annealing process after deformation process will recover ductility through stress relieve, recrystallization and grain growth mechanisms. This research aimed to find out the effect of cold rolling and annealing temperatur on the recrystallization and mechanical properties of Al 4.7Zn 1.8Mg wt. alloy.
The alloy was produced by squeeze casting process. Homogenization was conducted at 400 oC for 4 hours followed by cold rolling with degree of deformation of 5, 10 and 20 . The samples with 20 of deformation were then annealed at 300, 400 and 500 oC for 2 h. Vickers hardness test was performed on the cold rolled and annealed samples to reveal strain hardening effect and subsequent recrystallization process. Microstructure was observed by using optical microscope and Scanning Electron Microscope SEM with Energy Dispersive Spectroscopy EDS.
The results showed that the higher the deformation, the more elongated the grains. Deformation of 5, 10 and 20 led to grain shape ratios of 2.19, 3.19 and 4.59, respectively and increase in the hardness of the alloy from 69.5 HV to 95.3, 100.1 and 105.4 HV, respectively. Annealing at 300 oC resulted in recovery, while at 400 oC, recrystallization occured dgrain 290 m. Grain growth was observed after annealing at 500 oC for 2 h dgrain 434 m. The annealing temperature of 300, 400 and 500 oC decrease the hardness of the alloy from 105.4 HV to 71.5, 96.8 and 95.3 HV, respectively. Full recrystallization was predicted to happen at 375 ndash 425 oC for 2 hours."
Depok: Fakultas Teknik Universitas Indonesia, 2017
S67978
UI - Skripsi Membership  Universitas Indonesia Library
cover
Irene Angela
Pengaruh canai dingin dan temperatur anil terhadap karakteristik fasa α dan βpaduan Cu-29.5Zn-2.5al hasil pengecoran gravitasi = Effect of cold rolling and annealing temperature to the characteristics of α+β phases in Cu29.5Zn-2.5al alloy produced by gravity casting
"Optimalisasi paduan cartridge brass sebelumnya telah dilakukan lewat penambahan paduan Al, menghasilkan paduan Al-brass dengan fasa α dan β biner yang memiliki kekuatan mekanis lebih tinggi dari paduan konvensional tanpa mengalami reduksi elongasi yang signifikan. Dalam penelitian ini, dipelajari mengenai pengaruh proses manufaktur canai dingin dan perlakuan anil terhadap karakteristik fasa dan yang terdapat dalam paduan Cu-29.5Zn-2.5Al wt. hasil pengecoran gravitasi. Pelat as-cast dihomogenisasi pada temperatur 800 °C selama 2 jam, dideformasi menggunakan canai dingin dengan derajat deformasi sebesar 20, 40, dan 50, dan diberikan perlakuan anil pada temperatur 150, 300, 400, dan 600 °C selama 30 menit. Karakterisasi dilakukan melalui observasi mikrostruktur dengan mikroskop optik, pengambilan gambar dengan SEM, uji komposisi OES dan SEM-EDS, karakterisasi fasa dengan XRD, dan pengujian kekerasan mikro dengan metode Vickers. Paduan as-homogenized memiliki struktur mikro martensitik dua fasa α dan βdan dengan diamond-shape configuration. Setelah canai dingin terlihat adanya mekanisme deformasi slip, cross-slip, twinning, dan pembentukan shear band hanya pada fasa ?, sementara peningkatan kekerasan mikro terjadi pada kedua fasa dan. Selanjutnya, perlakuan anil temperatur rendah pada 150 °C menghasilkan peningkatan kekerasan mikro paduan akibat pembentukan atmosfir Cottrel, sementara perlakuan anil di temperatur 300, 400, dan 600 °C menghasilkan penurunan nilai kekerasan mikro akibat mekanisme penguraian dislokasi dan relaksasi tegangan. Rekristalisasi butir equiaxed hanya terjadi di fasa α dan β pada hasil anil temperatur 600 °C.
Previous research displayed a successful attempt in optimizing mechanical properties of cartridge brass by utilizing Al alloying element, producing binary Al brass alloy with higher strength and hardness without a significant diminution in its elongation compared to conventional cartridge brass alloys. Hereinafter, the effect of cold rolling and annealing treatment on the characteristics of α and β phases in gravity casted Cu 29.5Zn 2.5Al wt. alloy was studied. Produced as cast samples were homogenized at 800 °C for 2 h, subjected to cold rolling with 20, 40, and 50 reduction in thickness, and annealed at 150, 300, 400, and 600 °C for 30 min. Phase characterizations were done through optical microscopy, SEM imaging, OES and SEM EDS composition analysis, XRD, and micro Vickers hardness measurement. A binary martensitic morphology with diamond shape configuration compromising of α and β phases were found in as homogenized sample. Cold rolling resulted in slip, cross slip, twinning, and formation of shear band, solely in the phase. However, increase in microhardness was detected in both α and β phases. Furthermore, it was found that low temperature annealing at 150 °C resulted in an increase of micro hardness of both phases due to the formation of Cottrel atmosphere, while usual decrease in hardness value was discovered after annealing at 300, 400, and 600 °C through disl°Cation entanglement and stress recovery mechanisms. Recrystallized phase β grains in equiaxed shape were visible in sample annealed at 600 °C."
Depok: Fakultas Teknik Universitas Indonesia, 2018
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Aryya Satwiko Mahardhika
Pengaruh canai dingin dan temperatur anil terhadap karakteristik paduan Cu-28Zn-5.5Al hasil pengecoran gravitasi untuk aplikasi selongsong peluru = The effect of cold rolling and annealing temperature on the characteristics of Cu-28Zn-5.Al alloy produced by gravity casting for bullet cartridge application
"Selongsong peluru terbuat dari cartridge brass Cu-Zn , yang mengandung 28 32 wt. Zn. Material ini di fabrikasi melalui berbagai tahap, dimulai dari canai dingin, penekanan dalam, dana nil. Deformasi yang terjadi pada saat fabrikasi selongsong peluru mencapai lebih dari 90 , dan proses rekristalisasi selesai pada temperatur 450 500 oC selama 30 menit. Pada penelitian sebelumnya, penambahan Bi kedalam paduan cartridge brass menyebabkan penggetasan karena adanya segregasi Bi ke batas butir. Sedangkan pada penambahan Mn, peningkatan sifat mekanik paduan hanya terjadi hingga penambahan 3.52 wt. Mn. Maka dari itu, pada penelitian ini dilakukan penambahan Al untuk meneliti pengaruhnya terhadap sifat mekanik dan perilaku anil nya. Pada penelitian ini, pembuatan paduan Cu-28Zn-5.5Al dilakukan dengan pengecoran gravitasi, dihomogenisasi pada temperatur 800 oC selama 2 jam, kemudian dicanai dingin dengan variasi deformasi 5, 10, dan 20 . Untuk derajat deformasi canai dingin 20 , dilakukan proses anil pada temperatur 300, 400, dan 600 oC selama 30 menit. Lalu, sampel dilakukan karakterisasi nilai kekerasan dan struktur mikronya. Peningkatan derajat deformasi akan menghasilkan peningkatan kekerasan. Al meningkatkan kekerasan cartridge brass dengan mekanisme penguatan solid solution dan grain boundary strengthening, yang menghalangi pergerakan dislokasi. Nukleasi parsial terjadi pada daerah dekat permukaan pada temperatur 300 oC, begitu juga dengan temperatur 400 oC. Proses anil pada temperatur 400 oC menyebabkan munculnya presipitasi fasa gamma yang terjadi melalui mekanisme dekomposisi fasa beta. Rekristalisasi terjadi homogen terjadi pada temperatur 600 oC pada batas butir. Pengaruh Al secara umum adalah menyebabkan terjadinya penurunan temperatur rekristalisasi paduan.
A bullet case is made of cartridge brass Cu Zn , which consists of 28 32 wt. Zn. This material is fabricated through various kinds of process, starting from cold rolling, deep drawing, and annealing. The deformation occurred along the fabrication of bullet case is more than 90 , and the recrystallization process is completed at 450 500 oC for 30 minutes. In the previous research, addition of Bi into cartridge brass causes mechanical properties degradation due to segregation of Bi. Mn improves mechanical properties only up to 3.52 wt. of addition. Therefore, this research studied the effects of Al addition on mechanical properties and annealing behavior of Cu 28Zn. In this research, fabrication of Cu 28Zn 5.5Al was fabricated by gravity casting, followed by homogenization at 800 oC for 2 hours, then cold rolled with deformation degree varied from 5, 10, to 20 . Annealing was conducted at 300, 400, and 600 oC for 30 minutes. Then, the hardness values and microstructures were characterized. Al improved hardness of Cu 28Zn alloy through solid solution and grain boundary strengthening. Partial nucleation started at 300 oC around the edge of the sampel. Annealing at 400 oC led to the formation of gamma phase due to the beta phase decomposition. Full recrystallization occurred at 600 oC. Al addition into Cu 28Zn alloy decrease the recrystallization temperature."
Depok: Fakultas Teknik Universitas Indonesia, 2017
S66157
UI - Skripsi Membership  Universitas Indonesia Library
cover
Nuzulian Akbar Arandana
Studi pengaruh temperatur laku pelarutan terhadap struktur mikro dan sifat mekanis paduan al-4.7zn-1.7mg-0.37cr berat hasil squeeze casting = Effect of solution treatment temperature on microstructure and mechanical properties of al al-4.7zn-1.7mg-0.37cr wt alloy produced by squeeze casting
"Aluminium merupakan logam yang mudah untuk dipadukan dengan logam lain. Salah satu paduan aluminium yang sedang banyak dikembangkan adalah seri 7xxx Al-Zn-Mg karena memiliki densitas yang rendah dan sifat mekanis yang baik. Peningkatan sifat mekanis paduan tersebut dapat dilakukan dengan penambahan sejumlah unsur paduan seperti Cr yang dapat memperhalus butir. Selain itu, paduan juga dapat dikeraskan melalui proses pengerasan pengendapan dengan tahapan laku pelarutan, pencelupan cepat, dan penuaan.
Untuk memeroleh pengerasan pengendapan yang diinginkan maka tahapan laku pelarutan harus diperhatikan karena akan memengaruhi sejumlah unsur paduan yang dapat larut dan jumlah kekosongan yang terbentuk. Sementara itu, masih sedikit penelitian mengenai pengaruh kombinasi penambahan Cr dan temperatur laku pelarutan pada paduan. Oleh karena itu, penelitian ini bertujuan untuk mengetahui pengaruh penambahan Cr terhadap variasi temperatur laku pelarutan pada paduan Al-4.7Zn-1.7Mg-0.37Cr berat.
Paduan dibuat dengan metode squeeze casting. Kemudian dilakukan proses homogenisasi pada temperatur 400 C selama 4 jam. Pada paduan selanjutnya dilakukan proses laku pelarutan pada temperatur 220, 420, dan 490°C yang dilanjutkan dengan pencelupan dalam air. Setelah itu, paduan dilakukan pengerasan penuaan pada temperatur 130°C selama 48 jam. Karakterisasi yang dilakukan berupa pengamatan struktur mikro menggunakan OM Optical Microscope dan SEM-EDS Scanning Electron Microscope - Energy Dispersive Spectroscopy, pengujian kekerasan HRB dan HB, pengujian XRD X-Ray Diffraction, dan STA Simultaneous Thermal Analysis.
Hasil penelitian menunjukkan bahwa semakin tinggi temperatur laku pelarutan menyebabkan semakin banyaknya fasa interdendritik yang dapat larut dalam matriks Al. Hal ini dibuktikan dengan fraksi volume fasa interdendritik setelah laku pelarutan 220, 420, dan 490°C yang menurun menjadi 6.67, 4.55, dan 4.14 dari 6.9 setelah homogenisasi. Hasil tersebut menunjukkan bahwa penambahan 0.37 berat Cr tidak berpengaruh terhadap proses pelarutan fasa interdendritik selama laku pelarutan. Sebaliknya, intermetalik Cr seperti Al18Cr2Mg3 dan Cr,Fe Al7 yang terbentuk dapat meningkatkan kekerasan paduan. Kekerasan paduan setelah penuaan pada temperatur 130 C selama 48 jam meningkat menjadi 49.64, 52.54, dan 70.52 HRB pada variasi laku pelarutan 220, 420, 490°C.
Aluminium is a metal that can be easily alloyed with other metals. One of them is the 7xxx Al Zn Mg series which are the most developed series due to their low density and good mechanical properties. Their mechanical properties can also be strengthened by adding some microalloying element such as Cr which can refine the grain of the alloy. Aside from that, heat treatment such as precipitation hardening through solution treatment, quenching, and ageing can also be done to strengthen its properties. Solution treatment temperature may affect the amount of dissolved interdendritic phase and the number of vacancy, thus it has to be considered in case of getting the desired properties after the precipitation hardening.
Meanwhile, there are very few research on the combined effects of addition of Cr and solution treatment temperature on the properties of this alloy. Therefore, this research is aimed to investigate the effect of Cr and variation of solution treatment temperature on the properties of Al 4.7Zn 1.7Mg 0.37Cr wt. alloy.
The alloy was fabricated by squeeze casting process. Then it was homogenized at 400 C for 4 hours. Three samples were then solutionized at 220, 420, and 490 C for 1 hour and followed by rapid quenching in water. Ageing was then conducted at 130 C for 48 hours. Characterization included microstructure observation by using OM Optical Microscope and SEM EDS Scanning Electron Microscope Energy Dispersive Spectroscopy , hardness testing HRB and HB, XRD X Ray Diffraction, and STA Simultaneous Thermal Analysis.
The results showed that the higher solution treatment temperature increased the dissolution of interdendritic phase to the Al matrix. It was shown by the decreasing of interdendritic volume after solution treatment at 220, 420, and 490°C which became 6.67, 4.55, and 4.14 after 6.9 in the homogenized alloy. The results showed that the 0.37 wt. Cr addition had no effect on the dissolution process of the interdendritic phase. However, the formation of Cr intermetallic such as Al18Cr2Mg3 and Cr,Fe Al7 increased the hardness of the alloy. The hardness of the alloy after ageing at 130°C for 48 hours was increased to 49.64, 52.54, and 70.52 HRB in 220, 420, 490°C solutionized alloy respectively."
Depok: Fakultas Teknik Universitas Indonesia, 2018
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Dimas Pratamawansyah Putra
Studi pengaruh temperatur laku pelarutan terhadap struktur mikro dan sifaf mekanis paduan al-5.1zn-1.9mg hasil squeeze casting = Effect of solution treatment temperature on microstructure and mechanical properties of al 5 1zn 1 9mg alloy produced by squeeze casting
"Penggunaan paduan aluminium terus berkembang khususnya dalam industri penerbangan yaitu untuk badan dan sayap pesawat. Densitasnya yang rendah dan sifat mekanisnya yang bisa ditingkatkan melalui pemaduan unsur lain serta perlakuan panas menjadi alasan aluminium digunakan di industri penerbangan. Paduan aluminium 7xxx dengan kandungan Zn dan Mg dapat ditingkatkan kekerasannya melalui pengerasan pengendapan dengan tahapan laku pelarutan, pencelupan, dan penuaan. Salah satu kunci peningkatan kekuatan saat penuaan adalah seberapa banyak atom paduan dapat larut dan kekosongan yang terbentuk saat laku pelarutan. Oleh karena itu, pada penelitian ini diamati pengaruh temperatur laku pelarutan terhadap kekerasan dan struktur mikro paduan Al-5.1Zn-1.9Mg berat hasil squeeze casting 76 MPa selama 10 menit.
Paduan hasil pengecoran dilakukan homogenisasi pada temperature 400 oC selama 4 jam. Selanjutnya dilakukan pelarutan pada temperatur 220, 420, dan 490 oC selama 60 menit dan dilanjutkan dengan pencelupan cepat. Paduan disimpan pada temperatur -10 oC untuk menghindari penuaan alami dan kemudian dilakukan karakterisasi berupa pengujian kekerasan, pengamatan struktur mikro menggunakan mikroskop optik dan SEM-EDS Scanning Electron Microscope-Energy Dispersive Spectroscopy , pengujian XRD X-Ray Diffraction, dan STA Simultaneous Thermal Analysis. Setelah itu, paduan dilakukan penuaan pada temperatur 130 oC selama 48 jam untuk kemudian dilakukan pengujian kekerasan dan pengamatan struktur mikro.
Hasil penelitian menunjukkan bahwa kenaikan temperatur laku pelarutan meningkatkan pelarutan fasa kedua ke dalam matriks dan jumlah kekosongan yang terperangkap. Namun, pelarutan fasa kedua hampir tidak terjadi pada laku pelarutan temperatur 220 oC. Hal ini ditunjukkan oleh fraksi volume dari fasa kedua setelah homogenisasi yaitu sebesar 7.13 dan turun menjadi 7.06, 4.80, dan 4.19 setelah laku pelarutan pada temperatur 220, 420, dan 490 oC berturut-turut. Penurunan fasa kedua menyebabkan kenaikan nilai kekerasan setelah penuaan pada temperatur 130 oC selama 48 jam yaitu sebesar 11.54, 42,1, dan 66.7 HRB secara berurutan untuk laku pelarutan temperatur 220, 420, dan 490 oC.
Aluminum alloys are widely used in aviation industries, especially for the body and wings of aircraft. This is due to their low density and mechanical properties which can be enhanced by microalloying and heat treatment. The heat treatment for 7xxx series aluminum alloys is precipitation hardening which consists of solution treatment, quenching, and ageing. One key for successful ageing process is the amount of solute elements and vacancies dissolve in the matrix during solution treatment. Therefore, this research is aimed to study the effects of solution treatment temperature on the hardness and microstructure of Al 5.1Zn 1.9Mg wt. alloy which produced by squeeze casting.
The alloys was squeeze cast at 76 MPa for 10 minutes and then homogenized at 400 oC for 4 h. Solution treatment temperatures were varied to 220, 420, and 490 oC for 60 minutes, followed by quenching. The samples were then stored at 10 oC to prevent natural ageing. Characterization included hardness testing and microstructural observation by using OM Optical Microscope and SEM EDS Scanning Electron Microscope Energy Dispersive Spectroscopy , XRD X Ray Diffraction , and STA Simultaneous Thermal Analysis . Ageing was conducted at 130 oC for 48 h followed by hardness testing and microstructural observation.
The results showed that increasing solution treatment temperature induced enhancement of second phase dissolution and the amount of trapped vacancies in the matrix. However dissolution of second phase was hardly detected at solution treatment temperature of 220 C. It was shown by the volume fraction of the second phase found after homogenizing was 7.13 and decreased to 7.06, 4.80, and 4.19 after solution treatment at temperatures 220, 420, and 490 oC respectively. Therefore the increase in hardness after ageing at 130 oC for 48 hours was 11.54, 42,1, and 66.7 HRB for solution treatment temperatures of 220, 420, and 490 oC respectively."
Depok: Fakultas Teknik Universitas Indonesia, 2016
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Alfahari Mardi
Efek Anil terhadap pertumbuhan butir Zr-4 terekristalisasi sempurna
"ABSTRAK
Tujuan utama penelitian ini adalah mempelajari efek anil terhadap pertumbuhan butir Zr-4 terekristalisasi sempurna. Kegiatan penelitian meliputi penganilan cuplikan dalam vakum, metallografi, penentuan ukuran butir, serta pengukuran kekerasan cuplikan secara mikro.
Penganilan cuplikan dilakukan pada suhu 600°C, 650°C, 700°C dan 750°C dengan waktu anil masing-masing 1 jam, 3 jam,dan 10 jam. Penentuan ukuran butir Zr-4 diperoleh dari perhitungan butir dengan menggunakan metode Heyn atau metode pintasan linier.
Pada keadaan isotermal maupun pada kenaikan suhu, dengan waktu anil tetap, terjadi adanya kenaikan diameter butir. Pada suhu anil 750°C dan waktu anil 3 jam dan 10 jam terjadi pertumbuhan butir abnormal.
The main aim of this research is to study of the effect of annealing to the grain growth of fully re-crystallized Zr-4. The annealing of the samples under vacuum condition, metallography, grain size determination and micro hardness measurement are the scope of this activity.
The samples are annealed at 600°C, 650°C, 700°C and 750°C and annealing time 1,3, and 10 hours respectively. Grain size in Zr-4 is determined from grain quantification by using Heyn Method or Linear Intercept Method.
At the thermal condition and at the increasing temperature, with constant annealing time, the grain diameter increased. The abnormal grain growth occurred at annealing temperature 750°C and annealing time 3 and 10 hours."
Jakarta: Program Pascasarjana Universitas Indonesia, 1992
T-Pdf
UI - Tesis Membership  Universitas Indonesia Library
cover
Riza Enu Annisa Utami
Pengaruh anil terhadap sifat struktur dan sifat listrik double perovskite La2FeTiO6 dipreparasi dengan metode sol-gel = Effect of annealing on structural and electrical properties of double perovskite La2FeTiO6 prepared by sol-gel method
"Telah dilakukan penelitian sifat struktur dan sifat listik material double perovskite La2FeTiO6 yang di preparasi dengan metode sol-gel. Hasil karakterisasi XRD sampel bubuk hasil kalsinasi 9000C selama 6 jam menunjukkan La2FeTiO6 memiliki struktur kristal orthorhombik dengan space grup Pnma, masih terdapat fase kedua berupa senyawa nitrat. Sampel disinter pada suhu 13000C untuk mendapatkan bentuk bulk yang keras dan tidak mudah pecah. Hasil karakterisasi XRD sampel bulk hasil sintering menunjukkan telah diperoleh fase tunggal dengan crystallite size 24.1nm. Sampel dianil pada suhu 11000C selama 4 jam untuk memperbaiki mikrostruktur material sehingga dapat menghasilkan sifat listrik yang lebih baik. Hasil karakterisasi XRD menunjukkan sampel bulk hasil anil memiliki fase tunggal dengan intensitas peak yang meningkat dan crystallite size menurun 21.7nm , menunjukan terbentuknya kristalisasi yang baik. Hasil karakterisasi SEM menunjukan La2FeTiO6 hasil sinter dan hasil anil memiliki bentuk butiran yang seragam dengan ukuran yang berbeda-beda. Rata-rata grainsize 247nm untuk La2FeTiO6 hasil sinter dan 137nm untuk La2FeTiO6 hasil anil. Hasil EDS menunjukan tidak terlihat adanya kemunculan elemen lain yang mengindikasikan fase sekunder pada sampel sinter dan anil. Sifat listrik material dianalisis dengan impedansi spectroskopi. Hasil yang diperoleh menunjukan La2FeTiO6 hasil anil memiliki nilai konstanta dielektrik dan konduktivitas lebih tinggi dibandingkan dengan hasil sinter.
The structure and electrical properties of double perovskite La2FeTiO6 by sol gel method have been investigated. XRD characterization of calcined sample powder at 9000C for 6 hours showed La2FeTiO6 has orthorhombic crystal structure with space group Pnma, there is still impurities of nitrate compound. Samples were sintered at 13000C to obtain samples in bulk form which were hard and not easily broken. XRD characterization of the sintered bulk sample showed a single phase with crystallite size 24.1nm. Samples were annealed at 11000C for 4 hours to improve microstructure of material so can produce a better electrical properties. XRD characterization show the annealed bulk have increased peak intensity and decreased crystallite size 21.7nm . Indicating that a good crystallization was form. SEM characterization shows, double perovskite La2FeTiO6 sinter and anneal well separated with different grain size . Grain size average of La2FeTiO6 sintered and annealed are 247 nm and 137 nm respectively. EDS results show no visible presence of other elements that indicate secondary phase in sinter and anneal samples. Electrical properties materials are analyzed by impedance spectroscopy. The result shows that La2FeTiO6 annealed has dielectric constant and conductivity value which is superior than La2FeTiO6 sintered"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
T49799
UI - Tesis Membership  Universitas Indonesia Library