Hasil Pencarian  ::  Simpan CSV :: Kembali

"Photocatalytic Degradation of Pentachlorphenol in Aqueous Solution using TIO2 Supported on Titanium Metal : Evolution of Intermediet CompoundStudy on degradation of pentachlorphenol in aqueous solution by UV black light over TiO2 supported on titanium metal have been conducted. TiO2 catalyst was made from calcination of sol-gel film from titanium (IV) bis (ethyl acetoacetato)-diisopropoxide precursor at 525 °C. Characterisation of TiO2 by XRD and SEM showed that structures of crystal were anatase, and the thichness of the film was 24,7 pm. The surface of film was homogen and porous. Amount of two catalysts sheets with size 5x5 cm2, were put in batch reactor (25 x 11x 7cm3). During Irradiation the solution of PCP was homogenized with magnetic stirrer. The effects of pH were studied by irradiation of solution for 4 hours at various pH (4,5,6 and 8) using phosphat buffer. Further experiments were conducted at pH ( pH 6), and irradiation was done for 15 min, 30 min, 1 hour up to 16 hours. The determined parameters were pH, conductivity of the solution, chloride ion by ferri thiosianat method, the absorption spectrum in the UV-VIS region, PCP residue and degradation products as organic acids by mean HPLC. The existance of degradation was indicated by decreasing of pH, increasing of conductivity, and formation of chloride ion. The degradation of pentachlorphenol solely by UV light (photolysis) was observed due to dechlorination of pentachlorphenol molecules, and aromatic intermediate were remained. The 'aromatic intermediate could be further degraded in the presence of TiO2 and UVlight (photocatalysis). The measurement of degraded products by HPLC revealed that oxalic acid was detected consistenly. The complete mineralisation of PCP was observed after irradiation for 16 hours.

---

Telah dilakukan degradasi pentaklorfenol (PCP) dalam air oleh sinar UV black light, dengan bantuan katalis TiO2 yang diimobilisasikan pada logam titanium. Katalis TiO2 dibuat dari kalsinasi lapisan sol-gel dan prekursor titanium (IV) diisopropoksi bis asetil-asetonat pada suhu 525 °C. Karakterisasi TiO2 dengan XRD dan SEM menunjukkan, bahwa kristal TiO2 mempunyai struktur anatase, dengan ketebalan lapisan 24,7 p.m. Permukaan lapisan relatif rata, seragam dan berpori. Sebanyak 2 (dua) buah lempengan katalis TiO2 berukuran 5 x 5 cm2 diletakkan di dalam reaktor curah berukuran 25 x 11 x 7 cm3 . Selama iradiasi larutan PCP diaduk dengan batang pengaduk magnet. Untuk mempelajari pengaruh pH, maka larutan PCP diiradiasi selama 4 jam dengan variasi pH, yaitu pada pH 4, 5, 6, dan 8 menggunakan bufer fosfat. Iradiasi selanjutnya dilakukan pada pH optimum, yaitu pH 6 selama 15 menit, 30 menit, 1 jam, 2, 4, 6, 8, 10, 13, dan 16 jam. Parameter yang diukur adalah pH, daya hantar listrik, konsentrasi ion klor dengan metode feri tiosianat, serapan denganspektrofotometer UV-VIS, sisa PCP dengan HPLC, dan produk-produk asam organik dengan cara HPLC. Adanya Degradasi ditunjukkan dengan terjadinya penurunan pH, kenaikan nilai daya hantar listrik dan terbentuknya klor dalam larutan. Pada larutan PCP yang diiradiasi dengan UV, degradasi terjadi karena deklorinasi dan terbentuk intermediet berupa senyawa aromatis dengan substitusi klor yang lebih rendah. Pada larutan PCP yang diiradiasi dengan UV/ TiO2, degradasi juga terjadi karena deklorinasi, namun senyawa intermediet aromatis yang terbentuk dapat didegradasi lebih lanjut menjadi asam oksalat. Mineralisasi pentaklorfenol secara sempurna terjadi setelah 16 jam iradiasi."

"Penelitian degradasi fotokatalitik gas asetaldehida dengan katalis semikonduktor TiO2 bentuk serbuk dan film telah dilakukan. Fotokatalis serbuk TiO2 dengan fasa anatase, rutile dan campuran keduanya telah dapat dipreparasi dengan menghidrolisis larutan T1C1 pada berbagai kondisi preparasi."

"ABSTRAKSalah satu alternatif yang cukup prospektif untuk mereduksi gas CO2 adalah dengan reduksi fotokatalitik terhadap gas CO2 (atau dalam bentuk larutan karbonatnya) dengan TiO2 sebagai katalis semikonduktor dan sinar ultra violet (UV) sebagai sumber energi fotonnya. Kelebihan dari metode ini diantaranya tidak memerlukan reduktan Hg, energi panas yang tinggi, dan tekanan tinggi.Pada penelitian ini ingin didapatkan kondisi operasi yang optimal untuk menghasilkan laju pembentukan produk yang tinggi. Kondisi opreasi yang divariasikan adalah konsentrasi reaktan, berat katalis, pH dan penambahan EDTA dengan konsentrasi yang berbeda. Katalis yang digunakan adalah katalis TiO2 dalam bentuk serbuk yang dipreparasi dengan bahan awal TiCl4. Reaktor yang digunakan adalah reaktor fotokatalitik dengan sistem batch dengan aliran gas nitrogen dan CO2. Produk diambil setelah 5 jam dan dianaiisa dengan Gas Chromatography dengan detektor FID (Shimadzu Model GC-SA) yang dilengkapi dengan kolom propak-Q, dengan nitrogen sebagai gas carrier.Produk yang didapatkan setelah analisa adalah metanol, etanol dan aseton, dengan produk terbanyak adalah metanol. Kondisi optimum yang diperoleh adalah pada konsentrasi KHCO3 1 M dengan berat katalis 0,5 gr - 1 gr. pH optimum yang diperoleh adalah dalam keadaan asam yaitu pada pH 4, sedangkan untuk penarnbahan EDTA belum didapatkan hasil yang optimum.

---

"

"Degradasi fotokatalitik menggunakan katalis TiO2 dan sinar UV merupakan metode degradasi zat organik terlarut. Penelitian ini adalah degradasi fotokatalitik senyawaan kompleks asam humat dengan ion logam Fe3+, Pb2+ dan Cu2+ dibandingkan dengan asam humat bebas, dengan menggunakan suspensi TiO2. Prinsip fotokatalitik dengan katalis TiO2 dan sinar UV adalah pembentukan radikal hidroksil dan radikal yang mengandung oksigen lain, yang berfungsi sebagai oksidator pemecah molekul asam humat menjadi molekul karbon yang lebih sederhana CO2 dan H2O.Sampel yang digunakan dalam penelitian ini adalah campuran larutan Asam humat dengan larutan ion logam Fe3+, Pb2+ dan Cu2+ dengan perbandingan 1:1 sebanyak 500 mL dengan kondisi optimum 10 ppm dan pH 6. Konsentrasi katalis TiO2 yang digunakan adalah 1 mg/mL. Suspensi ini diiluminasi selama 8 jam. Penurunan Konsentrasi Asam Humat diukur dengan menggunakan Spektrofotometer UV-Vis dan Fluoresensi. Sedangkan kandungan zat organik terlarutnya diukur dengan bilangan Permanganat. Proses degradasi dilakukan dengan tiga variasi perlakuan yaitu iluminasi TiO2/UV, TiO2 saja dan UV saja.Karakterisasi hasil dilakukan dengan Spektrofotometer UV-Vis dan Fluoresensi pada setiap jam degradasi. Dari data yang diperoleh, terjadi penurunan konsentrasi Asam Humat dengan urutan TiO2/UV > TiO2 > UV. Sedangkan pengaruh ion logam pada proses degradasi fotokatalitik dengan urutan Fe3+ > Cu2+ > Pb2+. Dari data pengukuran bilangan permanganat, terjadi penurunan bilangan permanganat, tetapi tidak memberikan penurunan yang cukup berarti. Sehingga dapat disimpulkan proses degradasi fotokatalitik ini tidak dapat mengurangi Kandungan zat Organik secara optimal. Urutan penurunan bilangan permanganat berdasarkan penurunan konsentrasi asam humat yaitu pada degradasi TiO2/UV > TiO2 > UV. Proses degradasi fotokatalitik dapat mengurangi konsentrasi asam humat tetapi tidak dapat mengurangi kandungan zat organiknya sehingga dapat disimpulkan terjadi zat antara ( intermediate) dimana modelnya mendekati pembentukan intermediate fenol."

"Nanopartikel ZnO didop Cr disintesis menggunakan metode kopresipitasi untuk empat variasi konsentrasi Cr. Karakteristik nanopartikel dipelajari menggunakan Energy Dispersive X-Ray (EDX), X-Ray Difraction (XRD), Electron Spin Resonance (ESR), Field Emision - Scanning Electron Microscope (FESEM), Fourier Transform-Infrared (FTIR), and spektroskopi Ultra Violet- Visible (UV- Vis). Uji aktivitas nanopartikel diukur melalui degradasi Methyl Orange (MO) dan Methylene Blue (MB) pada daerah sinar Ultraviolet (UV). Hasil menunjukkan keberadaan Cr dan cetyltrimethylammonium bromide (CTAB) dalam sistem ZnO nanopartikel. Nanopartikel yang dihasilkan berfase tunggal dengan struktur heksagonal wurtzite dan mempunyai bentuk spherical-like. Peningkatan konsentrasi dopan Cr dan kehadiran surfaktan kationik CTAB menyebabkan berkurangnya celah energi dan lebih lanjut lagi meningkatkan aktivitas fotokatalitik. Kehadiran surfaktan kationik CTAB menyebabkan nanopartikel ZnO didop Cr lebih efektif dalam mendegradasi zat pewarna anionik MO dibanding kationik MB.

---

Cr doped ZnO nanoparticles were synthesized by coprecipitation methods with four variation Cr concentrations. The nanoparticles were characterized by using Energy Dispersive X-Ray (EDX), X-Ray Difraction (XRD), Electron Spin Resonance (ESR), Field Emision - Scanning Electron Microscope (FESEM), Fourier Transform-Infrared (FTIR), and UltraViolet-Visible (UV-Vis) Spectroscopy. The photocatalytic activity of nanoparticles were evaluated by measuring degradation of Methyl Orange (MO) and Methylene Blue (MB) in Ultraviolet (UV) region. The results confirmed the presence of Cr dopant and cationic surfactant cetyltrimethylammonium bromide (CTAB) in the ZnO nanoparticles system. The resulting nanoparticles have single-phases with hexagonal wurzite structures and spherical-like shapes. Increasing the Cr dopant concentrations and the presence of cationic surfactant CTAB cause a reduction in energy gap and more futher improve the photocatalytic activity. The presence of cationic surfactant CTAB causes the Cr doped ZnO nanoparticles were more effective in degrading MO anionic dyes than MB cationic dyes."

"Material fotokatalis MgxZn(1-x)O-Zeolite telah berhasil dilakukan dengan metode kimiawi basah melalui teknik presipitasi dengan variasi konsentrasi Mg (2%, 3%, 6%, dan 7.5%). Seng oksida didapat dari serbuk ZnSO4.7H2O, ion Mg2+ dari MgSO4.7H2O, dan zeolit alam dari clinoptilolite. serangkaian pengujian dilakukan untuk mengkarakterisasi sampel. Uji yang dilakukan adalah uji difraksi sinar-X (XRD), Energy Dispersive X-Ray (EDX), dan spektroskopi UV-Vis. Pengujian aktivitas fotokatalisis sampel dilakukan dengan media degradasi metil jingga. Hasil karakterisasi menunjukkan struktur kristal ZnO tetap berbentuk wurtzite hexagonal. Penambahan doping Mg berpengaruh terhadap penurunan ukuran kristalit sekaligus penurunan kisi yang berdampak pada peningkatan energi celah pita dengan rentang 3.31 ? 3.44 eV pada fotokatalis dengan kadar 2% hingga 7.5%. Peningkatan energi celah pita disebabkan pembentukan Fermi level didalam pita konduksi sehingga pita konduksi terangkat dan jarak untuk eksitasi elektron semakin lebar. Fotokatalis ZnO dengan kadar Mg 2% memiliki efisiensi aktivitas fotokatalisis yang paling baik dari semua sampel, begitu pun dengan laju degradasinya.

---

Photocatalyst material MgxZn(1-x)O-Zeolite has been successfully synthesized through the precipitation method with variation of dopant Mg content (2%, 3%, 6%, and 7.5%). Zinc oxide was obtained from ZnSO4.7H2O powder, while Mg2+ ion was obtained from MgSO4.7H2O, and natural zeolite from clinoptilolite. The samples were characterized by X-Ray Diffraction (XRD), Energy Dispersive X-Ray (EDX), and UV-Vis Spectroscopy. The photocatalytic activity was tested for methyl orange degradation under UV irradiation. X-ray diffraction showed the prepared ZnO particles were in wurtzite structure. The addition of Mg doping had an effect on crystallite size reduction as well as reduction of lattice parameter. The band gap energy of MgxZn(1-x)O-Zeolite changed within a range of 3.31 ? 3.44 eV with increasing of Mg content from 2% to 7.5%. This enhancement of band gap energy due to the formation of Fermi level inside the conduction band so that the conduction band was lifted and broaden the distance for photoinduced electron to do the excitation. ZnO photocatalyst with 2% Mg content showed the highest efficiency in photocatalytic activity and also the greatest degradation rate of all samples."

"ABSTRAKSalah satu aplikasi yung cukup potensial dari fenomena fotokatalisis adalah untuk mcngkonversi karbon padu senynwa anorganik seperti CO2 menjadi senyawa-senyawa organik yang lebih berguna. Selain diperolehnya produk senyawa organik yang dapat digunakan untuk keperluan tertentu, transformasi CO2 tersebut dalam kurun waktu tertentu dapat mengurangi laju emisi CO2 di atmosfer, yang akhir-akhir ini menjadi isu lingkungan global karena dipercaya dapat memberikan kontribusi yung signifikan terhadap timbulnya efek rumah kaca (green house effect). Efisiensi reduksi CO2 sangat tergantung pada fotokatalis yang digunakan. Beberapa peneliti telah membuktikan bahwa CO2 dapat direduksi secara fotokatalitik dalam uap air atau larutan dengan TiO2, akan tetapi efisiensinya masih sangal rendah. Studi ini difokuskan pada pengembangan fotokatalis yang efektif untuk proses reduksi CO3 menjadi metanol.Fotokatalis TiO2 serbuk dengan berbagai komposlsi kristal anatase dan rutile dibuat dengan cara menghidrolisis TiCl2, yang dilanjutkan dengan kalsinasi pana berbagai temperatur. Modifikasi kalalis TiO2 film dilakukan dengan menambahkan polyethilene glycol atau sillika, menggunakan metodesol-gel dan dip-coating.Fotokatalis tembaga-titania dibuat dengan metode impregnasi-termodifikasi menggunakan TiO2 Degussa P25 dan larutan tembaga nitrat, serta metode pencampuran fisik menggunakun serbuk TiO2 Degussa P25, CuO, Cu2O, dan Cu. Katalis-katalis yang telah dibuat kemudian dikarakterisasi dengan XRD, DRS, SEM/EDX/Mapping, ASS, dan BET. Uji kinerja katalis yang dilakukan meliputi uji aktivitas fasa cair dan gas, uji kinetika. dan uji mekanisme reaksi dengan metode in-situ FTIR.Hasil penelitian membuktikan bahwa dengan bantuan fotokatalis titania dan tembaga-titania, karbon dioksida dapat direduksi oleh air baik dalam sislem cair-padat maupun gas-padat, menghasilkan produk utama metanol. Metana, etanol, propanol dan aseton adalah senyawa-senyawa lain yang juga terbentuk, meskipun dalam jumlah yang relaif lebih sedikit. Aktivitas reduksi fotokatalisis CO2 pada larutan l M KHCO3 paling optimal diamati terjadi ketika keasaman larutan diatur pada pH 4. Katalis TiO2 serbuk dengan komposisi kristal anatase yg tinggi, ukuran kristal kecil, dan luas permukaan besar, mempunyai efisiensi fotoreduksi CO2 yang tinggi. Penambahan dopan PEG atau SiO2 sampai pada tingkat loading tertentu dapat meningkatkan porositas fotokatalis TiO2 film, sehingga kinerjanya menjadi lébih baik. Katalis tembaga TiO3 dcngan loading tertentu menunjukkan kinerja fotokatalisis yang sangat efisien untuk reduksi CO3, balk pada sistem cair-padat maupun gas-padat.Hasil investigasi menunjukkan bahwa Cu"O adalah spesi dopan yang paling signifikan dalam meningkatkan kinerjia TiO3 pada reduksi CO2 menjadi metanol. Loading optimal yang diperoleh pada katalis CuO/TiO3 hasil impregnasi adalah 3% berat Cu, sedangkan pada katalis yang dibuat dengan pencampuran fisik adalah 5% berat untuk dopan Cu2O dan l% berat untuk dopan CuO.Peningkatan efisiensi reduksi CO2 menjadi metanol yang signifikan oleh dopan tembaga (terutama dalam bentuk metal oksida) pada fotokatalis TiO2 diduga karena adanya peran ganda yang sinergis dari dopan tembaga tersebut, yaitu sebagai electron trapper pada proses fotokatalisis dan sebagai intl aktif pada proses katalisis. Sebagai electron trapper, dopan tembaga secara efeklif dapat menghambat laju rekombinasi pasan gan elektron-hole sehingga secara signifikan dapat meningkatkan efisiensi reduksi CO2. Sebagai inti aktif pada proses katalisis, dopan tembaga diperkirakan dapat meningkatkan selektivitas produk metanol, dengan mekamisme melalui pembentukam intermediate format dan metoksida.Uji kinetika yang dilakukan pada rentang temperatur 43 - 100 derajat C menunjukkam bahwa dopan CuO dapat meningkatkan laju reaksi, sehingga secara signifikan dapat meningkatkan photoefficiency dari katlalis TiO2. Nilai energi aktivasi teramati (Ea) yang diperoleh untuk katalis 3%CuO/TiO2 adalah sebesar +12 kJ/mol, yang mengindikasikan bahwa desorpsi produk adalah merupakan tahap penentu laju reaksi pada pembentukan metanol dari CO2 dan H2O dengan katalis 3%CuO/TiO2"