"Recycled fibres are important sources for paperboard industry. There are various approaches to enhance the strength of recycled fibres. These approaches include mechanical treatment, chemical addition, and physical fractionation as well as blending with virgin fibres. In this study, two types of deinked old newsprint (ONP) pulp were subjected to blending with virgin fibres of rice straw. The ONP pulp was blended with rice straw pulp at 4 intervals ranging from 0 to 100% addition. It was observed that blending ONP with rice straw pulp had enhanced the strength of the virgin fibre and vise versa. The modification of rice straw fibres was visually evaluated by scanning electron microscopy (SEM). It was observed that the addition of the flexible ONP pulp type2 seemed to fill up the voids in the paper sheet and created more bonding with rice straw fibres. Shrimps exoskeletons poweder, borax and cactus peel extract were added to paper board made from 50% rice straw+50% ONP type2 pulp at percent of 2% based on oven dry weight pulp. The antimicrobial activity of each of these three additives was studied."

"Industri gerabah plered sedang mengalami penurunan. Program Action Research merupakan bentuk pengabdian UI kepada masyarakat. Dalam penelitian ini tempurung kelapa dengan campuran sekam padi yang banyak ditemukan di Plered akan digunakan sebagai bahan bakar pada proses gasifikasi dengan menggunakan Downdraft Gasifier. Bahan bakar tersebut kemudian dikonversi menjadi gas mampu bakar melalui proses pembakaran. Variabel yang dibandingkan adalah nilai Air Fuel Ratio (AFR) sehingga diperoleh pola flame yang kemudian akan digunakan sebagai sumber energi untuk pengeringan dan pembakaran di Industri gerabah.

---

Plered Pottery Industry has been decreased. Action Research UI devotion to community. The focus of this study is mixture Sof Coconut Shell and Rice Husk are found in Plered, will be used as fuel in the Gasification process using Downdraft Gasifier. That Fuel is converted into flammable gas through combusting process. The compared variables is Air Fuel Ratio (AFR) in order to obtain the flame pattern. It will be used for drying and combustion in Pottery Industry."

"Dengan sektor konstruksi mengalami kebangkitan pertumbuhan, pasti memiliki dampak lingkungan yang merugikan. Permintaan energi selama umur bangunan sangat penting, karena dampaknya berlangsung sepanjang umur bangunan. Ada dua jenis dampak yang perlu diperhatikan selama tahap penggunaan; diwujudkan dan dampak operasional. Cladding memainkan peran penting dalam mengurangi dampak lingkungan bangunan. Jadi, memilih bahan kelongsong dengan dampak lingkungan yang rendah sangat penting. Di Indonesia, material komposit daur ulang kayu-plastik mulai tumbuh menanggapi permintaan material yang berdampak rendah dan masalah limbah. Studi ini menyelidiki dampak lingkungan dari kelongsong komposit plastik daur ulang kayu selama tahap penggunaan, dari perspektif daya tahan material dan konduktivitas termal dalam konteks tropis. Tinjauan daya tahan dan kinerja termal pertama kali dilakukan untuk memahami sifat material. Kemudian dilanjutkan dengan menganalisis dampak lingkungan dari komposit daur ulang kayu-plastik selama tahap penggunaan dengan menggunakan teori-teori sebelumnya pada bab dua dan hasil review durabilitas dan konduktivitas termal pada bab 3 sebagai acuan. Hasilnya menunjukkan bahwa komposit daur ulang kayu-plastik memiliki dampak lingkungan yang rendah. Hal ini disebabkan daya tahan material yang tinggi terhadap faktor degradasi tropis dan konduktivitas termal yang rendah. Ketahanan yang tinggi dan konduktivitas termal yang rendah berkontribusi pada perawatan & penggantian material yang minimal dan mendorong pengurangan beban pendinginan, sehingga menurunkan kebutuhan energi yang menghasilkan emisi dan limbah.

---

With the construction sector experiencing a resurgence in growth, it is bound to have a detrimental environmental impact. The energy demand during the building service life is crucial, as the impact lasts throughout the building’s life. There are two types of impact that needs to considered during the use stage; the embodied and the operational impact. Cladding plays an important role in reducing the environmental impact of buildings. Thus, choosing a cladding material with a low environmental impact is essential. In Indonesia, Wood-plastic recycled composite material is starting to grow responding to the low-impact material demand and waste problem. This study investigates the environmental impact of wood-recycled plastic composite cladding during the use stage, from the perspective of material durability and thermal conductivity within a tropical context. A review of the durability and thermal performance is first conducted to understand the material's properties. Then, it is followed by analyzing the environmental impact of the wood-plastic recycled composite during the use stage using the former theories in chapter two and the result of the durability and thermal conductivity review in chapter 3 as a reference. The result shows that wood-plastic recycled composite has a low environmental impact generation. This is due to the material's high durability to tropical degradation factors and low thermal conductivity. High durability and low thermal conductivity contribute to minimal maintenance & replacement of the material and encourages the reduction of cooling load, thus lowering the energy demand that results in emission and waste."

"ABSTRAKPada sektor industri, kemasan telah menjadi barang penting setiap hari, dan penggunaannya semakin meningkat sejalan dengan ekonomi global. Jenis kemasan dengan penggunaan paling banyak adalah menggunakan paper and paperboard. Material kertas juga memiliki beberapa kelemahan, diantaranya proses penguraian oleh alam yang memerlukan waktu 2 ndash; 5 bulan. Jenis material kertas yang paling banyak diproduksi didunia adalah Corrugated. Setelah End-of-life EOL produk kemasan kertas menumpuk dan menjadi sampah. Studi penelitian ini dilakukan untuk meningkat nilai material dari segi value, fungsi dan performa dengan mengimplementasikan dari beberapa pendekatan, prinsip desain, proses atau perlakuan dari material dan usaha lainnya yang disebut material value upgrading. Salah satu pemanfaatan kemasan kertas karton bergelombang untuk meningkatkan nilai material setelah masa End-of-life EOL telah selesai, yaitu menggunakan prinsip Design For Other Usage untuk pembuatan papan serat.

---

ABSTRACTIn the industrial sector, packaging has become an important item every day, and its use is increasing in line with the global economy. Type of packaging with the most use is to use paper and paperboard. Paper materials also have some weaknesses, betwixt the process of decomposition by nature that takes 2 5 months. The most widely produced paper material in the world is Corrugated Paperboard. After End of life EOL paper packaging products pile up and become waste. The study was conducted to minimize the reduction of value degradation and maximize residual value and also improve the life cycle and total value of the goods by implementing from several approaches, design principles, processes or treatment of materials and other business called material value upgrading. One the use of Corrugated Paperboard to increase the value of material after the End of life EOL period that has been completed, using the Design For Other Usage principle for the manufacture of fiber board and coatings of the fiberboard "

"ABSTRACTFurnitur pada ruang komersil umumnya menggunakan material kayu, plastik, atau metal sebagai bahan bakunya karena material tersebut versatile dalam desain furnitur. Seluruh material tersebut dengan karakteristiknya masing-masing telah terbukti kekuatannya, dapat dimodifikasi dengan mudah dan tahan untuk pemakaian indoor maupun outdoor pada ruang komersil untuk berbagai jenis aktivitas dan intensitas pemakaian yang tinggi. Di sisi lain, material corrugated cardboard merupakan material yang biasanya hanya digunakan untuk pengemasan produk. Material tersebut memiliki struktur yang membuatnya memiliki kemampuan bantalan untuk menahan beban, yakni lapisan medium bergelombang atau flute yang didukung dengan lapisan liner pada masing-masing sisinya. Corrugated cardboard merupakan jenis kertas, dan terdapat familiaritas bahwa material ini adalah material yang murah dan lemah, terutama karena sifatnya yang tidak tahan air, ringan, dan mudah mengalami deformasi. Dengan struktur material dan karakteristiknya tersebut, maka perlakuan material, performa dan durabilitas corrugated cardboard sebagai furnitur akan berbeda dibandingkan material lain yang umum digunakan pada furnitur di ruang komersil. Perlakuan material corrugated cardboard yang digunakan sebagai struktur dan tektonik furnitur, akan menciptakan fungsi dan estetika visual pada desain furnitur.

---

ABSTRACTCommercial furnitures generally use wood, plastic, or metal materials as their materials because they are versatile for furniture design. All these materials with their respective characteristics have proven their strength, can be easily modified and resistant for indoor or outdoor use in commercial space for various types of activity and high intensity of use. On the other hand, corrugated cardboard is a material that usually used only for packaging of products. The material has a structure that has the cushioning ability to withstand loads, which is a layer of corrugated medium or flute supported by a layer of liner on each side. Corrugated cardboard is a type of paper, and there is the familiarity that this material is a cheap and weak material, mainly because it is not waterproof, lightweight, and easy to deform. With the material structure and its characteristics, then the material treatment, performance and durability of corrugated cardboard as furniture will be different than other materials commonly used for furniture in commercial space. The corrugated cardboard material treatment used as the structure and tectonic of furniture, will create the function and visual aesthetics of the furniture design."

"Studi pemanfaatan limbah untuk adsorpsi logam berat banyak menarik perhatian. Pada penelitian ini, selulosa yang berasal dari serat kardus bekas (WCF) dimodifikasi dengan nanokitosan (WCF/NCH) untuk meningkatkan kemampuan adsorpsi ion logam berat. WCF disiapkan dengan penambahan NaOH untuk memisahkan serat dengan material non selulosa. Hasil karakterisasi spektrofotometer FTIR menunjukkan modifikasi WCF dengan nanokitosan berhasil dilakukan dengan kondisi optimum pada 1 kali pencelupan nanokitosan. Hasil modifikasi WCF/NCH mampu mengadsorpsi larutan ion logam Pb(II) dan Cd(II). Kondisi optimum adsorpsi ion logam Pb(II) didapatkan pada pH awal 6,5, dosis adsorben 0,025 g, waktu kontak selama 10 menit, temperatur reaksi 30 ºC serta kapasitas adsorpsi maksimum sebesar 167,19 mg/g. Hasil optimasi ion logam Cd(II) menunjukkan proses adsorpsi berlangsung optimum pada pH awal 7,0, dosis adsorben 0,025 g, waktu kontak 15 menit, temperatur reaksi 30 ºC serta kapasitas adsorpsi maksimum sebesar 15,86 mg/g. Proses adsorpsi pada WCF/NCH untuk ion logam Pb(II) dan Cd(II) mengikuti model isoterm adsorpsi Langmuir. Studi termodinamika pada adsorpsi ion logam Pb(II) menunjukkan nilai energi bebas Gibbs (ΔGo) negatif pada semua temperatur yang diamati mengindikasikan proses adsorpsi berlangsung secara spontan, sedangkan pada adsorpsi ion logam Cd(II) menunjukkan nilai positif yang mengindikasikan proses adsorpsi berlangsung tidak spontan.

---

Recent Study of the utilization of wastes as low-cost adsorbent have become attention. In this work, cellulose from waste corrugated board fiber (WCF) was modified with nanochitosan (WCF/NCH) to enhance its ability to adsorb heavy metal ion. WCF was prepared by the addition of NaOH to separate the cellulose fiber with non-cellulose material. Modification of WCF/NCH was characterized by FTIR. Optimum modification process was obtained at 1 layer of nanochitosan. WCF / NCH can be used for adsorption Pb (II) and Cd (II) ion. Optimum condition for adsorption of Pb(II) ion takes place at the initial pH 6.5, 0.025 g adsorbent dose, 10 minutes of contact time, temperature 30 ºC, and the maximum adsorption capacity was 167.19 mg/g. Optimum condition for adsorption of Cd(II) ion occur at initial pH 7, 0.025 g of adsorbent dose, 15 minutes of contact time, temperature 30 oC, and the maximum adsorption capacity was 15.86 mg/g. The process of adsorption for Pb(II) and Cd(II) ion on WCF/NCH follow Langmuir adsorption isotherm model. Thermodynamics studies for adsorption of Pb(II) shows that the adsorption have negative value at any temperatures indicating adsorption process takes place spontaneously, whereas adsorption of Cd(II) ion have positive value indicating adsorption process takes place non-spontaneously."

"Lumpur sludge hasil sisa instalasi pengolahan air limbah industri pasta gigi termasuk dalam kategori limbah B3 bahan berbahaya dan beracun sumber spesifik khusus, maka perlu dilakukan pengolahan limbah B3 ini, sesuai dengan Peraturan Pemerintah No.101 tahun 2014 tentang Pengelolaan Limbah Bahan Berbahaya dan Beracun. Salah satu teknik pengolahan limbah B3 adalah dengan menggunakan metode solidifikasi-stabiliasi, agar limbah B3 terikat dengan suatu bahan sehingga tidak terlepas ke lingkungan. Limbah B3 dicampur dengan bahan penyusun beton seperti semen, pasir, kerikil, dan air. Beton ini bisa dimanfaatkan sebagai bahan bangunan. Dalam penelitian ini dilakukan uji pencampuran sludge sebagai limbah B3 sebagai pengganti pasir sebagai dalam pembuatan beton. Komposisi sludge sebagai pengganti pasir mulai dari 10 , 20 , 30 , 40 , dan 50. Pretreatment sludge dengan pengeringan dan tanpa pengeringan. Dari hasil uji tekan terhadap beton yang dihasilkan tiap campuran, didapat bahwa pada pemakaian sludge sebesar 10 pengganti pasir, menghasilkan kuat tekan yang lebih tinggi daripada beton kontrol beton tanpa campuran sludge sebesar 226,1 kg/cm2 dibanding kuat tekan beton tanpa campuran sebesar 224,3 kg/cm2. Beton hasil campuran ini dapat dimanfaatkan sebagai paving block pada mutu B sesuai SNI 03-0691-1996. Beton hasil solidifikasi-stabilisasi diuji dengan TCLP ndash; toxicology characteristic leaching procedure dengan hasil uji semua parameter anorganik di bawah baku mutu TCLP-A dan TCLP-B sesuai dengan Peraturan Pemerintah RI no.101 tahun 2014. Dilakukan juga uji karakteristik limbah B3, dengan memberikan hasil beton: tidak mudah meledak, tidak mudah terbakar, tidak reaktif terhadap air, H2S, CN-, tidak korosif.

---

The sludge from the wastewater treatment plant in toothpaste industry is included in hazardous waste category. So, it is necessary to do process of this hazardous waste, in accordance with Government Regulation PP No.101 of 2014 on the Management of Hazardous and Toxic Waste. One of hazardous waste method treatment is solidification stabilization. The result of this is concrete materials, that bound the hazardous waste. This concrete can be utilized as a building material. In this research, sludge is mixing with concrete material, as a substitute for fine aggregate with percentage 10 , 20 , 30 , 40 , and 50. Sludge is also given pretreatment process, drying and without drying. From the result of compressive test to the concrete produced by each mixture, it was found that at 10 sludge usage of sand substitute, yielded higher compressive strength than the control concrete concrete without sludge mixture of 226,1 kg cm2 compared to concrete compressive strength without mixture of 224.3 kg cm2. This mixed concrete can be utilized as a concrete paving block of B quality according to SNI 03 0691 1996. The solidified stabilization concrete was tested by TCLP toxicology characteristic leaching procedure with the test results of all inorganic parameters under the TCLP A and TCLP B standards in accordance with the Government Regulation No. 101 of 2014. Also performed the characteristic test of B3 waste, by providing concrete results non explosive, non flammable, non reactive to water, H2S, CN , and non corrosive."