Plasma electrolytic oxidation (PEO) merupakan metode konversi permukaan logam menjadi lapisan oksida dengan bantuan plasma yang bertujuan untuk meningkatkan sifat mekanik permukaan dan ketahanan korosi logam. Retakan dan pori menurunkan ketahanan korosi dan sifat mekanik lapisan. Dalam penelitian ini digunakan zat aditif SiO₂ dan metode post-alkali treatment pada lapisan PEO yang ditumbuhkan pada paduan magnesium AZ31 dan commercially pure titanium (CP-Ti). PEO dilakukan di dalam larutan 95 g/l Na₃PO₄ + 2 g/l KOH menggunakan rapat arus DC  sebesar 300 A.m^-2 selama 10 menit. NP-SiO₂ sebanyak 2 g/l ditambahkan di dalam larutan PEO. Setelah logam terlapisi, post-alkali treatment dilakukan di dalam larutan 0,5 M NaOH pada suhu 80 ºC selama 30 menit. Morfologi permukaan dan kandungan unsur lapisan dianalisis menggunakan SEM-EDS dan XPS. Komposisi fasa kristal diteliti menggunakan X-ray Difraction (XRD). Sifat mekanik lapisan PEO diuji dengan metode vickers microhardness dan ketahanan aus dievaluasi menggunakan metode Ogoshi. Sifat korosi dianalisis dengan uji polarisasi, EIS, dan uji rendam. Sifat bioaktivitas diteliti dengan cara perendaman sampel dalam larutan SBF. Hasil penelitian menunjukkan penambahan aditif SiO₂ dan post-alkali treatment dapat meningkatkan ketahanan korosi dan sifat mekanik lapisan PEO pada logam Mg dan Ti. Pada PEO-Mg, lapisan PEO/SiO₂+AT memiliki nilai rapat arus korosi paling rendah dan nilai kekerasan paling tinggi dibandingkan dengan sampel lainnya yaitu berturut-turut 7,34x10^-7 A.cm^-2 dan 359 HV. Tren yang sama juga dihasilkan pada PEO-Ti, lapisan PEO/SiO₂+AT memiliki nilai rapat arus korosi relatif rendah dan nilai kekerasan paling tinggi dibandingkan dengan sampel lainnya yaitu berturut-turut 3,4x10^-9 A.cm^-2 dan 305 HV.

---

Plasma electrolytic oxidation (PEO) is a method of converting metal surfaces into an oxide layer with the help of plasma which aims to improve the surface mechanical properties and corrosion resistance of metals. Cracks and pores reduce the corrosion resistance and mechanical properties of the coating. In this research, SiO₂ additives and post-alkali treatment methods were used on PEO layers grown on AZ31 magnesium alloy and commercially pure titanium (CP-Ti). PEO was carried out in a solution of 95 g/l Na₃PO₄ + 2 g/l KOH using a DC current density of 300 A.m^-2 for 10 minutes. SiO₂ additive with a concentration of 2 g/l was added to the PEO solution. After the metal is coated, post-alkali treatment is carried out in a 0.5 M NaOH solution at a temperature of 80 ºC for 30 minutes. The surface morphology and element content of the layers were analyzed using SEM-EDS and XPS. The composition of the crystal phase was investigated using XRD. The mechanical properties of the PEO coating were tested using the vickers microhardness and the wear resistance was evaluated using the Ogoshi method. Corrosion properties were analyzed by polarization test, EIS, and immersion test. The bioactivity properties were studied by immersing the samples in SBF. The research results show that the addition of SiO₂ and post-alkali treatment can improve the corrosion resistance and mechanical properties of PEO layers on Mg and Ti metals. In PEO-Mg, the PEO/SiO²+AT layer has the lowest corrosion current density value and the highest hardness value compared to other samples, namely 7.34x10^-7 A.cm^-2 and 359 HV respectively. The same trend was also produced on PEO-Ti, the PEO/SiO²+AT layer had a relatively low corrosion current density value and the highest hardness value compared to other samples, namely 3.4x10^-9 A.cm^-2 and 305 HV respectively.

"

"Penggunaan paduan magnesium sebagai material bio-metalik memiliki potensi untuk terurai secara alami dalam cairan tubuh dan berperan penting dalam struktur tulang. Dalam aplikasinya, modifikasi permukaan paduan magnesium diperlukan untuk meningkatkan sifat mekanik dan anti-korosinya. Salah satu metode pelapisan menjanjikan adalah Plasma Electrolytic Oxidation (PEO). Pada penelitian ini, dilakukan pelapisan paduan magnesium AZ31 dengan metode PEO menggunakan pendekatan one-step dan two-step. Parameter ditetapkan sama dalam penggunaan kedua metode ini yaitu meliputi waktu, rapat arus, sumber tegangan, dan suhu. Pada metode two-step PEO, lapisan HA (hidroksiapatit) disisipkan ke dalam lapisan oksida yang terbentuk. Hasil penelitian menunjukkan bahwa metode two-step PEO menghasilkan lapisan dengan karakteristik lebih baik dibandingkan metode one-step PEO. Lapisan two-step PEO memiliki persentase pori lebih kecil, ketebalan lapisan lebih besar, dan nilai spesifik abrasi lebih rendah. Selain itu, fasa kristalin baru, yaitu Ca5(PO4)3OH atau HA, terdeteksi dalam lapisan two-step PEO. Penggunaan metode two-step PEO dengan penambahan hidroksiapatit memberikan hasil lebih baik dalam hal karakterisasi morfologi dan sifat ketahanan aus. Dalam konteks aplikasi biomedis, hal ini menunjukkan potensi penggunaan paduan magnesium dengan metode pelapisan two-step PEO sebagai material cocok untuk aplikasi tulang dan gigi manusia.

---

The use of magnesium alloy as a bio-metallic material has the potential to decompose naturally in body fluids and plays an essential role in bone structure. In its application, surface modification of magnesium alloy is required to improve its mechanical and anti-corrosion properties. One of the promising coating methods is Plasma Electrolytic Oxidation (PEO). In this study, the coating of magnesium alloy AZ31 was carried out using a one-step and two-step approach using the PEO method. The parameters used in both methods include the same time, current density, voltage source, and temperature. In the two-step PEO method, a HA (hydroxyapatite) layer is inserted into the formed oxide layer. The results showed that the two-step PEO method produced layers with better characteristics than the one-step PEO method. The PEO two-step coating has a smaller pore percentage, a larger layer thickness, and a lower abrasion-specific value. In addition, a new crystalline phase, namely Ca5(PO4)3OH or HA, was detected in the two-step PEO layer. The two-step PEO method with hydroxyapatite adds better morphology characterization and wear resistance properties. This demonstrates the potential use of magnesium alloys coated by the two-step PEO method as suitable materials for human bone and tooth applications in biomedical applications."

"Aluminium (Al) dan paduannya telah secara luas digunakan dalam berbagai industri seperti konstruksi, otomotif, manufaktur, dan kedirgantaraan karena memiliki kekuatan tinggi, kerapatan rendah, serta kemampuan pembentukan yang baik. Meskipun Al memiliki lapisan oksida alami di permukaannya, lapisan ini dapat terkelupas atau larut dalam lingkungan korosif, yang menyebabkan turunnya ketahanan korosi. Oleh karena itu, diperlukan pelapisan permukaan. Plasma Electrolytic Oxidation (PEO) menghasilkan lapisan keramik oksida tebal yang meningkatkan resistansi korosi. Diperlukan aditif sebagai penguat untuk mengoptimalkan ketahanan korosi dan mekanik lapisan. Pada penelitian ini, graphene oxide (GO) digunakan sebagai aditif selain untuk meningkatkan ketahanan korosi lapisan, juga untuk meningkatkan konduktivitas listrik lapisan. Proses PEO dilakukan pada paduan AA7075-T735 menggunakan elektrolit 30 g/l Na2SiO3, 30 g/l KOH, 20 g/l trietanolamin (TEA) dengan aditif 2 g/l dan 20 g/l GO pada rapat arus konstan sebesar 200 A/m2 dan suhu 10 °C ± 1 °C. Karakterisasi morfologi dan komposisi dilakukan SEM-EDS dan XRD. Uji korosi dilakukan dengan metode elektrokimia. Sifat mekanik lapisan diuji dengan uji aus dan keras. Penambahan GO sebesar 2 g/l berhasil meningkatkan sifat mekanik dan ketahanan korosi coating yang didukung oleh morfologi permukaan yang lebih halus dan sedikit pori. Perfoma coating menurun pada konsentrasi GO sebesar 20 g/l, hal ini disebabkan penurunan laju pertumbuhan dari coating yang disebabkan GO melebihi batas dispersif sehingga GO yang terinkorporasi di dalam coating lebih sedikit karena aglomerasi GO.

---

Aluminium (Al) and its alloys are widely used in various industries such as construction, automotive, manufacturing, and aerospace due to their high strength, low density, and good formability. Despite the natural oxide layer on its surface, which can peel or dissolve in corrosive environments, leading to a decrease in corrosion resistance, surface coating is necessary. Plasma Electrolytic Oxidation (PEO) produces thick ceramic oxide layers that enhance corrosion resistance. Additives are required to strengthen and optimize the corrosion resistance and mechanical properties of the coating. In this study, graphene oxide (GO) is used as an additive not only to improve corrosion resistance but also to enhance the electrical conductivity of the coating. The PEO process is conducted on AA7075-T735 alloy using an electrolyte of 30 g/l Na2SiO3, 30 g/l KOH, 20 g/l triethanolamine (TEA) with 2 g/l additive and 20 g/l GO at a constant current density of 200 A/m2 and a temperature of 10 °C ± 1 °C. Morphological and compositional characterization is performed using SEM-EDS and XRD. Corrosion testing is conducted using electrochemical methods, while the mechanical properties of the coating are assessed through wear and hardness tests. The addition of 2 g/l of GO successfully improves the mechanical properties and corrosion resistance of the coating, supported by a smoother surface morphology with fewer pores. However, coating performance decreases at a GO concentration of 20 g/l, attributed to a reduction in coating growth rate caused by GO exceeding the dispersal limit, resulting in less incorporated GO due to agglomeration."

"

Meningkatnya permintaan akan electronic vehicle (EV) menyebabkan meningkatnya penggunaan Magnesium yang memiliki sifat lebih ringan sehingga mampu mengunggulkan efisiensi bahan bakar. Salah satu paduan Maagnesium yang sering digunakan adalah AZ31B. Namun, sheet metal forming dan perlakuan panas pada manufaktur dapat memengaruhi sifat mekanisnya. Penelitian ini dilakukan pada plat paduan Magnesium AZ31B yang dilakukan cold rolling hingga terjadi deformasi sebesar 22% dan perlakuan panas annealing pada 349℃ pada waktu tahan 0, 10, 30, 60, dan 120 menit. Penelitian ini didukung dengan pengujian metalografi dan kekerasan microvickers. Didapatkan bahwa rolling menghasilkan butir dengan ukuran diameter terkecil, sedangkan annealing pada waktu tahan yang lebih lama menghasilkan butir dengan ukuran diameter yang lebih besar pula. Tak hanya itu, sampel yang memiliki ukuran butir yang kecil memiliki nilai kekerasan yang tinggi. Hal ini terlihat dari sampel yang dilakukan rolling memiliki nilai kekerasan tertinggi, sedangkan sampel yang ditahan pada annealing selama 120 menit memiliki nilai kekerasan terendah. Berdasarkan pertumbuhan butir, didapatkan persamaan empiris yang mampu menunjukkan kinetika pertumbuhan butir sebagai berikut: D^(0,18)=D0^(0,18)+2244,35.exp(-70.000/8,314.T).t^(0,48)

---

The increasing demand for electric vehicles (EVs) has led to a rise in the use of magnesium, which is lighter and thus enhances fuel efficiency. One commonly used magnesium alloy is AZ31B. However, sheet metal forming and heat treatment during manufacturing can affect its mechanical properties. This study focuses on AZ31B magnesium alloy plates subjected to cold rolling, achieving a deformation of 22%, and annealing heat treatment at 349°C for various holding times: 0, 10, 30, 60, and 120 minutes. The research includes metallographic analysis and microvickers hardness testing. It was found that rolling produces the smallest grain diameters, while longer annealing times result in larger grain diameters. Additionally, samples with smaller grain sizes exhibited higher hardness values. Specifically, the rolled samples had the highest hardness, while samples annealed for 120 minutes had the lowest hardness. From the grain growth observations, an empirical equation was derived to describe the kinetics of grain growth as follows: D^(0.18)=D0^(0.18)+2244.35.exp(-70,000/8.314.T).t^(0.48)

"

"Magnesium merupakan merupakan logam struktural yang paling ringan di dunia yang biasa digunakan di bidang otomotif. Dalam aplikasinya, sifat mampu bentuk magnesium sangat penting untuk diketahui agar dapat meningkatkan efektivitas proses produksi. Sifat mampu bentuk ini dapat dipengaruhi oleh banyak faktor, salah satunya adalah ketebalan material. Batas limit magnesium saat dibentuk digambarkan pada diagram batas pembentukan (FLD). Pada penelitian ini, material yang digunakan adalah lembaran paduan magnesium AZ31B dengan ketebalan 0,5, 0,8, dan 1 mm. Pengujian tarik dilakukan untuk mengetahui sifat mekaniknya sekaligus mendapatkan koefisien pengerasan regang yang juga mempengaruhi mampu bentuk material. Pengujian stretching dilakukan menurut metode Nakazima dengan berbagai variasi geometri sampel yang sudah dibuat kisi lingkaran berdiameter 2 mm pada area permukaannya, menggunakan punch setengah lingkaran, dan dalam kondisi pelumasan minyak. Metode pengukuran regangan menggunakan Dino-Lite portable digital microscope untuk mendapatkan forming limit strain. Hasil dari penelitian ini menunjukkan bahwa lembaran paduan magnesium AZ31B memiliki sifat mampu bentuk yang buruk pada temperatur ruang. Koefisien pengerasan regang (nilai n) yang didapat untuk masing-masing tebal, yaitu berturut-turut sebesar 0.32, 0.33, dan 0.3. Terlihat bahwa FLD yang diperoleh tidak dipengaruhi oleh ketebalan tetapi akan semakin tinggi dengan semakin besarnya nilai n.

---

Magnesium is the lightest structural metal in the world which is commonly used in the automotive field. In its application, it is known that the formability of magnesium is very important to increase the effectiveness of the production process. This formability can be influenced by many factors, one of which is the thickness of the material. The limits of magnesium when formed are depicted on the formation limit diagram (FLD). In this research, the material used was AZ31B magnesium alloy sheet with a thickness of 0.5, 0.8, and 1 mm. Tensile testing is carried out to determine the mechanical properties as well as obtain the strain hardening coefficient which also affects the formability of the material. Stretching tests were carried out according to the Nakazima method with various variations of sample geometry which had been made into a circular grid with a diameter of 2 mm on the surface area, using a hemispherical punch, and under lubrication oil conditions. The strain measurement method uses a Dino-Lite portable digital microscope to obtain the forming limit strain. The results of this research indicate that AZ31B magnesium alloy sheet has poor formability at room temperature. The strain hardening coefficient (n value) obtained for each thickness is 0.32, 0.33, and 0.3 respectively. It can be seen that the FLD obtained is not influenced by thickness but will be higher with the increasing n value."

"Magnesium menjadi salah satu material berpotensi untuk memberikan solusi energi hijau berkelanjutan. Dalam bidang teknik, paduan magnesium dikenal sebagai logam paling ringan. Sudah banyak aplikasi paduan magnesium di berbagai bidang. Namun, secara komersial penggunaan magnesium belum seluas alumunium. Salah satu penyebabnya, dikarenakan mampu bentuk magnesium lebih rendah dari aluminium, terutama di temperatur ruang. Hal tersebut berkaitan dengan struktur HCP magnesium yang memiliki rasio c/a tinggi membuat bidang basal menjadi sistem slip utama yang terjadi ketika paduan magnesium terdeformasi. Oleh karena itu, energi panas dapat digunakan untuk mengaktifkan sistem slip lain agar dapat memenuhi kriteria von misses. Pemrosesan dan perlakuan panas yang diterapkan pada material mempengaruhi sifat material dan dalam skala mikroskopis akan terjadi berbagai fenomena. Penelitian ini akan menginvestigasi terkait fenomena apa yang terjadi selama deformasi plastis menggunakan metode pencanaian dan perlakuan panas yang dilakukan pada temperatur 350^oC. Pada penelitian ini pencanaian dilakukan pada suhu ruang dan perlakuan panas diberikan setelah proses deformasi menggunakan tungku muffle. Shear band, twinning, rekristalisasi butir, dan pertumbuhan butir merupakan fenomena-fenomena yang ditemukan pada penelitian ini.  Fenomena- fenomena tersebut hadir dalam paduan magnesium dipengaruhi oleh struktur kristal yang dimilikinya.

---

Magnesium is one of the potential materials to provide sustainable green energy. In engineering, magnesium alloys are known as the lightest metals. There have been many applications of magnesium alloys in various industries. However, the commercial use of magnesium has not been as common as aluminum. One of the reasons is because the formability of magnesium is lower than aluminum, especially at room temperature. This is related to the HCP structure of magnesium which has high c/a ratio making the basal plane become the main slip system when the magnesium alloy is deformed at room temperature. Therefore, thermal expected to activate other slip systems in order to fulfill the von misses criterion. Deformation and heat treatment applied to materials can affect material properties and at the microscopic scale various phenomena will occur. This study will investigate phenomena during plastic deformation using rolling method and heat treatment conducted at 350^oC. In this study, rolling was carried out at room temperature using pilot rolling machine and heat treatment was conducted after the deformation using muffle furnace. Shear bands, twinning, grain recrystallization, and grain growth were found in this study. Those phenomena are present in magnesium alloys influenced by its crystal structure."

"Disertasi ini membahas mengenai pengembangan paduan titanium berbasis Ti-Mo-Nb untuk mendukung kebutuhan akan material implan medis. Perekonomian yang meningkat dan meningkatnya populasi merupakan kombinasi yang menarik di mana terdapat potensi kebutuhan material implan medis. Peningkatan populasi ini berdampak pada peningkatan penduduk usia lanjut dan penyakit degeneratif seperti osteoporosis. Saat ini penggunaan paduan Ti6Al4V telah banyak digunakan sebagai material implan medis, namun permasalahannya adalah kandungan logam Al dan V yang berpotensi berbahaya bagi tubuh manusia serta nilai modulus elastisitas yang jauh lebih tinggi dibandingkan dengan tulang sehingga mendorong peneliti untuk mengembangkan paduan titanium baru untuk menggantikan Ti6Al4V. Paduan titanium β (beta) berbasis Ti-Mo-Nb dengan penambahan Sn dan Mn ini merupakan paduan yang aman digunakan dan memiliki modulus elastisitas yang lebih rendah dibandingkan Ti6Al4V.Paduan Ti-Mo-Nb-Sn-Mn dibuat melalui peleburan menggunakan electric arc vaccuum furnace pada lingkungan inert gas argon. Ingot hasil peleburan dihomogenisasi pada temperatur 1100 oC kondisi inert selama 7 jam dilanjutkan dengan pendinginan air. Selanjutnya dilakukan karakterisasi struktur mikro, sifat mekanis, sifat korosi dan in-vitro untuk mengetahui sifat–sifat yang dihasilkan sesuai aplikasi. Desain paduan Ti-6Mo-6Nb-8Sn-4Mn merupakan komposisi optimum yang dicapai. Paduan ini memiliki modulus elastisitas 92,4 GPa, laju korosi 0,00160 mmpy dan visibilitas sel mencapai 100%. Jadi dapat disimpulkan bahwa sifat mekanik, perilaku korosi dan hasil uji sel in-vitro menunjukkan bahwa paduan ini lebih baik daripada paduan komersial Ti6Al4V dan merupakan kandidat yang menarik untuk aplikasi material implant medis.

---

This dissertation discusses the development of Ti-Mo-Nb-based titanium alloys to support the need for medical implant materials. An increasing economy and a growing population is an attractive combination where there is a potential demand for medical implant materials. This population increase has an impact on the increase in the elderly population and degenerative diseases such as osteoporosis. Currently, the use of Ti6Al4V alloys has been widely used as medical implant materials. However, the problem is the content of Al and V metals which are potentially harmful to the human body, and the value of the modulus of elasticity is much higher than that of human bone, thus encouraging researchers to develop new titanium implant alloys to replace Ti6Al4V. Ti-Mo-Nb alloy with the addition of Sn and Mn is an element that is safe to use and has a lower modulus of elasticity than Ti6Al4V.

Ti-Mo-Nb-Sn-Mn alloys are made by electric arc vaccuum furnace in an inert argon gas atmosphere. The ingot resulting was homogenized at a temperature of 1100 °C for 7 hours in an inert atmosphere of argon gas, followed by water quenching. Microstructure characterization, mechanical and corrosion properties, and in-vitro were carried out to determine the suitability of the resulting properties for biomedical applications. Alloy Ti-6Mo-6Nb-8Sn-4Mn is the optimum composition achieved. This alloy has an elastic modulus of 92.4 GPa, a corrosion rate of 0.00160 mmpy and a visibility cell of 100%. So it can be concluded that the mechanical properties, corrosion behavior, and in vitro cell test results indicate that this alloy is better than the commercial alloy Ti6Al4V and is an attractive candidate for medical implant material applications.

"

"Plasma electrolytic oxidation (PEO) merupakan metode rekayasa permukaan logam untuk menghasilkan lapisan oksida yang keras dan tahan korosi. Sifat lapisan oksida yang dihasilkan bergantung pada jenis substrat dan komposisi larutan yang digunakan. Dalam penelitian ini, PEO dilakukan pada substrat AZ31B pada kondisi rapat arus tetap 800 A/m2 dan suhu 30°C. Larutan terdiri atas campuran garam basa dan etanol. Larutan A terdiri atas campuran 0,5 M Na3PO4 dan etanol dengan komposisi 9:1, larutan B campuran Na3PO4, NaOH dan Na2CO3 dengan komposisi 8:1:1, larutan C, D, dan E campuran Na3PO4, NaOH, Na2CO3, dan etanol dengan komposisi 7:1:1:1, 6:1:2:1, dan 6:2:1:1. Morfologi dan komposisi lapisan oksida diamati dengan scanning electron microscope dan energy dispersive spectroscopy (SEM – EDS). Komposisi kristal dianalisis dengan x-ray diffraction (XRD). Nilai kekerasan mekanik diuji dengan mesin microVickers Hardness. Perilaku korosi sampel diuji dengan metode electrochemical impedance spectroscopy (EIS) dan potentiodynamic polarization (PDP). Etanol di dalam larutan tidak mempengaruhi morfologi dan komposisi coating. Semua coating memiliki kandungan fasa kristal Mg3(PO4)2 pada puncak 29° hingga 35°. Nilai kekerasan coating yang terbentuk di larutan A, B, C, D, dan E adalah 451,8; 388; 237; 156,8; 158,4 HV. Nilai kekerasan yang rendah pada coating C, D, dan E disebabkan oleh rendahnya konsentrasi Na3PO4 yang menurunkan populasi plasma selama proses coating. Selain itu, kehadiran ion karbonat di dalam larutan mentriger peningkatan pori di dalam coating. Hasil uji polarisasi menunjukkan peningkatan ketahanan korosi dua orde dibanding substrat. Penambahan etanol ke dalam larutan cenderung menurunkan sedikit ketahanan korosi coating.

---

Plasma Electrolytic Oxidation (PEO) is a method of engineering metal surface treatment to produce a hard and corrosion-resistant oxide layer. The result properties of oxide layer depend on type of substrate and composition solution was used. PEO process is carried out a constant current 800 A/m2 at temperature 30℃. The solution composed of mixture alkaline salts and ethanol. Solution A mixture of 0,5 M Na3PO4 and ethanol with composition of 9:1, solution B a mixture Na3PO4, NaOH and Na2CO3 with composition of 8:1:1, solution C, D, and E a mixture of Na3PO4, NaOH and Na2CO3 with ethanol with composition of 7:1:1:1; 6:1:2:1; and 6:2:1:1. Morphology and composition of the oxide layer were observed by scanning electron microscope and energy dispersive spectroscopy (SEM – EDS). The crystal composition was analyzed by x-ray diffraction (XRD). The value of mechanical hardness was tested with a microVickers Hardness machine. The corrosion behavior of the samples was tested by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP) methods. The presence of ethanol in the solution didn’t affect morphology and composition of coating. All coatings contain Mg3(PO4)2 crystal phase at peak 29° to 35°. The hardness value of coating formed in solution A, B, C, D and E is 451.8; 388; 237; 156.8; 158.4 HV. The low hardness values in coatings C, D, and E were caused by the low concentration of Na3PO4 which reduced plasma population during the coating process. In addition, the presence of carbonate ions in the solution triggers an increase in the pores in the coating. The results of the polarization test showed can increase corrosion resistance of two orders compared to substrate. Addition of ethanol to solution tends to slightly lower the corrosion resistance of coating."

"Permintaan akan produk berskala mikro meningkat secara cepat di berbagai bidang perusahaan seperti elektronik, bio-medis, dan sebagainya. Penelitian ini bertujuan untuk menginvestigasi pengaruh parameter pemesinan yang paling signifikan untuk menghasilkan produk mikro dengan tingkat kekasaran permukaan yg rendah pada material Titanium Ti-6Al-4V dengan menggunakan mesin micromilling Hadia 5X Micromill. Dilakukan eksperimen dengan melakukan proses micromilling dengan variasi parameter pemesinan spindle speed dan feed rate dengan depth of cut konstan 10 μm menggunakan pahat potong material karbida dengan diameter 1 mm. Parameter dibagi menjadi 2 yaitu parameter pemesinan low speed cutting dan high speed cutting. Hasil pemesinan berupa slot sepanjang 4 mm dengan kedalaman 10 μm yang kemudian diukur kekasaran permukaannya menggunakan alat ukur kekasaran permukaan.Dari hasil kekasaran permukaan yang didapat dari eksperimen pemesinan slot Ti-6Al-4V, diperoleh bahwa pada parameter pemesinan yang tepat, hasil kekasaran permukaan proses slot cutting Ti-6Al-4V low speed cutting dan high speed cutting tidak memiliki perbedaan yang signifikan. Dari segi produktivitas, high speed cutting memiliki keunggulan dalam menghasilkan produk dengan waktu pemesinan yang cepat dengan kekasaran permukaan yang rendah. Low cutting speed tetap dapat digunakan pada kondisi machine tool yang tidak mempunyai kapabilitas high speed machining dengan mendapatkan kekasaran permukaan yang rendah.

---

The demand for micro-scale products is increasing rapidly in various fields of industries such as electronics, bio-medical, optical industry, and so on. This study aims to investigate the influence of the most significant machining parameters to produce micro-products with a low level of surface roughness in Titanium Ti-6Al-4V material using the Micromill Hadia 5X micromilling machine. Experiments carried out by micromilling process with variations in machining parameters of spindle speed and feed rate with a constant depth of cut of 10 μm using a cutting tool of carbide material with a diameter of 1mm. The machining parameters of the micromilling process are divided into 2, namely machining parameters, low speed cutting and high speed cutting. The machining results in the form of a 4 mm long slot with a depth of 10 μm, which then measures its surface roughness using a surface roughness measuring instrument.

From the results of surface roughness obtained from the Ti-6Al-4V slot machining experiment, it was found that with the appropriate cutting parameter, the results of the surface roughness of the Ti-6Al-4V slot cutting process with low speed cutting and high speed cutting did not have a significant difference. In terms of productivity, high speed cutting has the advantage of producing products with fast machining times with low surface roughness. On the other hand, low speed cutting still can be useful for machine tools that does not have the capability of high speed cutting and still can produce the same surface roughness as high speed cutting does."