"Research on purifying silica form Balikpapan silica sand via hydrothermal method using NaOH, and precipitation using H2SO4 as well as synthesizing silicon from the silica via metallothermic reduction (magnesiothermic reduction and aluminothermic reduction) and leaching using HCl has been done. The main goals are to extract silica using hydrothermal and precipitation techniques, optimize reduction conditions, and assess the suitability of synthesized silicon for semiconductor applications. Hydrothermal is carried out using NaOH as the solvent at a temperature of 250ᵒC for 4 hours with reaction of SiO2 + 2NaOH à Na2SiO3 + H2O to form sodium silicate solution. Precipitation is carried out using 2M H2SO4 and gradually titrate the sodium silicate solution to form a silica precipitate/gel. Metallothermical reduction is carried out using Mg and Al as the reducing agents with mass ratio of SiO2 : Mg is 5:8 gr with reaction of SiO2 + 2Mg à Si +2MgO as well as SiO2 : Al is 5:6 gr with reaction of 3SiO2 + 4Al à 3Si + 2Al2O3 and variation of temperature at 500ᵒC, 700ᵒC, and 900ᵒC to see the effect of silicon formed. Acid leaching using 2M HCl is carried out with solid/liquid ratio of 1:25 at room temperature for 2 hours to remove the impurities inside the silicon samples. Lastly, characterized the samples using XRF (X-Ray Fluorescence), XRD (X-Ray Diffraction), SEM (Scanning Electron Microscopy), and Gravimetric analysis. The yield of silica is 45.23% whereas the yield of silicon is 26.41% obtained from magnesiothermic reduction at 900ᵒC..

---

Penelitian tentang pemurnian silika dari pasir silika Balikpapan melalui metode hidrotermal menggunakan NaOH, dan presipitasi menggunakan H2SO4 serta sintesis silikon dari silika melalui reduksi metalotermal (reduksi magnesiotermal dan reduksi aluminotermal) dan pelindian menggunakan HCl telah dilakukan. Tujuan utama penelitian ini adalah mengekstraksi silika menggunakan teknik hidrotermal dan presipitasi, mengoptimalkan kondisi reduksi, dan menilai kesesuaian silikon hasil sintesis untuk aplikasi semikonduktor. Hidrotermal dilakukan dengan menggunakan NaOH sebagai pelarut pada suhu 250ᵒC selama 4 jam dengan reaksi SiO2 + 2NaOH --> Na2SiO3 + H2O membentuk larutan natrium silikat. Presipitasi dilakukan dengan menggunakan H2SO4 2M dan larutan natrium silikat dititrasi secara bertahap untuk membentuk endapan/gel silika. Reduksi metalotermik dilakukan dengan menggunakan Mg dan Al sebagai reduktor dengan perbandingan massa SiO2 : Mg sebesar 5:8 gr dengan reaksi SiO2 + 2Mg --> Si +2MgO serta SiO2 : Al sebesar 5:6 gr dengan reaksi 3SiO2 + 4Al --> 3Si + 2Al2O3 dan variasi suhu pada 500ᵒC, 700ᵒC, dan 900ᵒC untuk melihat pengaruh silikon yang terbentuk. Pelindian asam menggunakan HCl 2M dilakukan dengan perbandingan padatan/cair 1:25 pada suhu kamar selama 2 jam untuk menghilangkan pengotor di dalam sampel silikon. Terakhir, karakterisasi sampel menggunakan XRF (X-Ray Fluorescence), XRD (X-Ray Diffraction), SEM (Scanning Electron Microscopy), dan analisis Gravimetri. Hasil silika sebesar 45,23% sedangkan hasil silikon sebesar 26,41% diperoleh dari reduksi magnesiotermik pada suhu 900ᵒC."

"ABSTRACTCurrent electronics technology still relies on semiconductors for several purposes. The special property that distinguishes a semiconductor from another material is band gap energy inside of which the Fermi energy is located. Most conventional semiconductors such as Ge, Si, or GaAs may be classified into none or weakly correlated systems in which electron electron e e interactions do not play any significant role, where the band gaps insensitive to temperature change. Meanwhile, in semiconductors containing transition metal elements having d orbitals in their valence and or conduction band s , which we consider as strongly correlated semiconductors, e e interactions may play a more significant role. We hypothesize that such kind of semiconductors would have band structures, including their band gaps, being rather sensitive to temperature change due to e e interactions. We propose to explore this hypothesis theoretically by modeling the semiconductor band structure through Tight Binding Approximation with the GW method numerically in the Matsubara frequency domain. At the end, we use Pad approximant to obtain the self energy defined in the real frequency domain. Using this self energy we can calculate and analyze the Density Of States DOS at various temperatures, by giving the certain range of bare interaction line V. Our research results the correlation effects become stronger as we decrease the temperature. In short ranged interaction confirms that the semiconductor band gap increases and chemical potential shifts to a higher energy. Whereas with long ranged interaction shows that the range of two bands semiconductor becomes farther apart as compared to the bare DOS.

---

ABSTRACTTeknologi elektronik saat ini masih mengandalkan material semikonduktor untuk berbagai kebutuhan. Properti yang membedakan semikonduktor dari material lain adalah celah pita energi di mana energi Fermi berada di dalamnya. Umumnya semikonduktor seperti Ge, Si, atau GaAs dapat diklasifikasikan ke dalam sistem non terkorelasi / terkorelasi lemah di mana interaksi elektron-elektron e-e tidak memiliki peran penting, sehingga pita energi nya mungkin tidak sensitif terhadap perubahan suhu. Sedangkan semikonduktor yang mengandung unsur logam transisi dan orbital d dalam pita valensi dan / atau pita konduksi dianggap sebagai semikonduktor terkorelasi kuat, dimana interaksi e-e memainkan peran lebih signifikan. Kami berhipotesis bahwa jenis semikonduktor ini akan memiliki lebar celah pita yang agak sensitif terhadap perubahan suhu. Kami mengeksplorasi hipotesis ini secara teoritis dengan pemodelan struktur pita semikonduktor melalui pendekatan Tight-Binding, kemudian menerapkan interaksi e-e dalam metode GW secara numerik dalam domain frekuensi Matsubara. Setelah itu kami menggunakan Pad approximant untuk memperoleh self-energy yang didefinisikan dalam domain frekuensi riil. Dengan menggunakan self-energy ini kita dapat menghitung dan menganalisis Density Of States DOS seiring dengan bertambahnya suhu, dengan memberikan variasi rentang dari bare interaction line V . Penelitian kami membuktikan bahwa efek-efek korelasi menjadi lebih kuat seiring menurunnya suhu. Untuk variasi interaksi rentang pendek, pita energi melebar dan potensial kimia semakin bergeser ke tingkat energi lebih tinggi. Sedangkan pada variasi interaksi rentang panjang, jarak antara dua pita energi semikonduktor semakin melebar jika dibandingkan dengan DOS murni."

"Kerusakan jalan umum terjadi karena beberapa faktor diantaranya oleh buruknya drainase sehingga menyebabkan terjadinya genangan air di jalan yang dapat menurunkan kualitas bitumen. Upaya meningkatkan performa bitumen dilakukan yaitu dengan menambahkan bahan polimer dan membuat permukaan jalan memiliki sifat superhidrofobik sehingga suatu permukaan memiliki sifat anti adesif dan anti basah. Salah satu material yang dapat digunakan sebagai material superhidrofobik adalah silika nanopartikel. Silika nanopartikel superhidrofobik dapat disintesis dari pasir silika. Penelitian ini dilakukan dengan gabungan metode mechanical milling dan sol–gel. Pada Mechanical milling, digunakan rasio pasir silika dan bola zirconia sebanyak 1:20 dengan variasi waktu bertujuan untuk mengecilkan ukuran partikel dan sol–gel untuk membuat silika nanopartikel dengan ukuran 100-200 nm. pH pada sistem reaksi juga merupakan faktor penting yang mempengaruhi perolehan hasil sintesis sehingga dilakukan kontrol medium reaksi menggunakan asam (HNO3) dan basa (NH3) yang juga berfungsi sebagai katalis untuk menghindari terjadinya aglomerasi. Untuk mendapatkan silika nanopartikel dengan sifat superhidrofobik, maka dilakukan modifikasi permukaan menggunakan asam stearat.Hasil penelitian ini menunjukkan bahwa ukuran partikel pada silika nanopartikel yang dihasilkan dalam metanol, etanol dan propanol memiliki ukuran berturut-turut 149,1 ± 10,7 nm, 170,3 ± 14,3 nm, dan 198,6 ± 19,5 nm. Hasil zeta potensial juga menunjukkan bahwa silika nanopartikel yang disintesis dalam pelarut etanol memiliki zeta potensial tertinggi yaitu -50,4 ± 0,3 mV, diikuti dalam metanol (-72,2 ± 1,6 mV) dan propanol (- 67,5 ± 0,2 mV). Proses modifikasi permukaan silika nanopartikel dari hidrofilik menjadi hidrofobik optimal dilakukan dengan perbandingan massa 1:5 antara silika nanopartikel dengan asam stearat. Pengujian yang dilakukan pada substrat kaca, menghasilkan sudut kontak air sebesar 137,9 ± 1,2˚, 153,7 ± 2,9˚, dan 135,7 ± 1,0˚ untuk pelarut alkohol metanol, etanol, dan propanol. Hasil pengujian sifat hidrofobik pada bitumen memberikan hasil sudut kontak air yang dilapisi dan bercampur dengan nanopartikel silika termodifikasi berturut-turut 149,2˚ dan 148,1˚, sedangkan bitumen tanpa silika nanopartikel termodifikasi memberikan nilai sudut kontak air sekitar 89,80˚. Hasil ini menunjukkan bahwa kombinasi silika nanopartikel dalam bitumen mendekati sifat superhidrofobik

---

Road damage is common due to several factors including poor drainage causing puddles on the road that can decrease the quality of bitumen. Efforts to improve the performance of bitumen are carried out by adding polymer materials and to make the road surface has superhydrophobic properties so that a surface has anti-adhesive and anti-wet properties. One of the materials that can be used as a superhydrophobic material is silica nanoparticles. Superhydrophobic nanoparticle silica can be synthesized from silica sand. This research was conducted by a combination of mechanical milling and sol-gel methods. In Mechanical milling, silica sand and zirconia balls ratio is used as much as 1:20 with a time variation aimed at shrinking the particle size and sol–gel to synthesize silica nanoparticles about 100-200 nm. pH in the reaction is also an important factor that affects the acquisition of synthesis results so that the control of reaction medium using acids (HNO3) and bases (NH3) which also serve as a catalyst, in order to avoid the occurrence of agglomeration. To obtain silica nanoparticles with superhydrophobic effect, surface modification is carried out using stearic acid.

The results of this research showed that particle sizes in silica nanoparticles produced in methanol, ethanol and propanol had consecutive sizes of 149.1 ± 10.7 nm, 170.3 ± 14.3 nm, and 198.6 ± 19.5 nm. Potential zeta results also showed that silica nanoparticles synthesized in ethanol solvents had the highest potential zeta of about -50.4 ± 0.3 mV, followed in methanol (-72.2 ± 1.6 mV) and propanol (-67.5 ± 0.2 mV). The process of modifying the surface of silica nanoparticles from hydrophilic to hydrophobic is done with a ratio of 1:5 between silica nanoparticles with stearic acid. Superhydrophobic test was conducted on the glass substrate resulted with water contact angle of 137.9 ± 1.2°, 153.7 ± 2.9°, and 135.7 ± 1.0° for methanol, ethanol and propanol alcohol solvents, respectively. The results of hydrophobic properties on bitumen resulted in water contact angles coated and mixed with modified silica nanoparticles at 149.2° and 148.1°, while bitumen without modified silica nanoparticles gave a water contact angle value of about 89.80. These results showed that the combination of modified silica nanoparticles in bitumen is close to superhydrophobic properties.

"

"Olefin ringan merupakan salah satu bahan baku petrokimia yang yang sebagian besar dihasilkan menggunakan sumber daya alam yang tidak dapat diperbarui. Limbah jerami padi merupakan sumber biomassa lignoselulosa yang potensial karena memiliki kandungan selulosa yang besar dan jumlah yang melimpah di Indonesia. Pada penelitian ini, proses yang terjadi adalah proses katalitik pirolisis dengan suhu operasi sekitar 500oC dan laju alir N2 sekitar 150 ml/menit. Jenis katalis logam tersangga yang digunakan yaitu La2O3/ZSM-5, ZnO/ZSM-5, La2O3/Al2O3 dan ZnO/Al2O3 yang dibuat dengan metode impregnasi. Proses katalitik pirolisis dilakukan menggunakan reaktor unggun tetap dengan tungku listrik sebagai sumber panas. Untuk memahami hasil katalitik pirolisis, percobaan juga dilakukan dalam kondisi pirolisis limbah jerami padi tanpa katalis. Hasil pirolisis dikondensasikan dengan menggunakan perangkap serapan dingin dengan n-heksana. FT-IR Fourier Transform - Infrared dan GC-TCD Gas Chromatography-Thermal Conductivity Detector digunakan sebagai instrumen analitik untuk mengidentifikasi keberadaan dan kuantitas olefin ringan dalam bio-oil dan bio-gas. Dalam metode ini, ada beberapa variasi yang ditentukan, yaitu jenis katalis logam tersangga dan komposisi logam pada katalis 1, 5, dan 10. Keberadaan olefin ringan terdeteksi dengan adanya peak pada FT-IR dengan nomor gelombang 3010-3095 cm-1, 1610-1680 cm-1, dan 675-995 cm-1. Perbedaan susut massa yang sedikit, yaitu diantara 66,5 hingga 78,5 selama 25 menit pada setiap sampel, dengan massa awal sebesar 2 gram menunjukkan katalis tidak mempengaruhi mekanisme reaksi. Produk olefin ringan yang paling besar kandungannya terdapat pada sampel dengan katalis ZnO/ZSM-5 dengan komposisi logam 5, yaitu sebesar 29,1, sedangkan produk olefin ringan tanpa katalis yang terbentuk sebesar 11.

---

Light olefins are one of the most common petrochemical raw materials produced using non renewable natural resources. Rice straw waste is a potential source of lignocellulosic biomass because it has a large cellulose content and an abudant amount in Indonesia. In this research, the process is developed by catalytic pyrolysis processes with operating temperature around 500oC and N2 flow rate around 150 ml min. The type of supported metal catalyst used are La2O3 ZSM 5, ZnO ZSM 5, La2O3 Al2O3 and ZnO Al2O3, which made with the impregnation method. The catalytic pyrolysis process was carried out in a fixed bed turbular reactor with electric furnace as the heat source. To comprehend the catalytic pyrolysis processes, the experiment was also performed in condition pyrolysis rice straw waste without catalyst.

The output of pyrolysis is condensed by using cold absorption trap with n hexane. FT IR Fourier Transform Infrared and GC TCD Gas Chromatography Thermal Conductivity Detector serve as analytical instrument in order to identify the presence and the quantity of light olefins group in bio oil and bio gas. In this method, there are several variations to be determine, there are type of supported metal catalyst and metal composition on catalysts 1, 5, and 10. Light olefins were detected with peaks in FT IR with a wavenumber of 3010 3095 cm 1, 1610 1680 cm 1, and 675 995 cm 1. A slight difference in mass shrinkage, which is between 66.5 to 78.5 for 25 minutes in each sample, with an initial mass of 2 grams indicates that the catalysts does not affect the reaction. The largest light olefins yields were found in samples with ZnO ZSM 5 catalyst with 5 metal oxide, which amounted to 29.1, while light olefin products without catalyst were formed at 11."

"

Perusahaan asuransi perlu memastikan bahwa mereka memiliki dana yang cukup untuk membayar segala biaya dan kewajibannya, agar terhindar dari gagal bayar. Teori ruin dapat membantu dalam memahami kerentanan perusahaan mengalami peristiwa gagal bayar tersebut. Dalam compound Poisson ruin model digunakan asumsi bahwa premi diterima dalam jumlah konstan, dan besar klaim dengan jarak antarklaim saling bebas. Skripsi ini mengembangkan model ruin tersebut dengan menggunakan asumsi yang lebih sesuai dengan keadaan di dunia nyata, yaitu premi yang diterima mengikuti proses compound Poisson dan terdapat dependensi antara besar klaim dan jarak antarklaim. Kemudian, ditelaah pula fungsi discounted penalty dari model ruin yang baru tersebut. Fungsi discounted penalty merupakan fungsi yang cukup penting dalam teori ruin karena dapat menjadi ekspresi dari kuantitas penting dalam teori ruin, termasuk probabilitas ruin. Setelah itu, dilakukan contoh perhitungan probabilitas ruin melalui fungsi discounted penalty yang telah ditelaah dan dilakukan juga analisis pengaruh rate distribusi waktu antarklaim 𝜆1 dan 𝜆2 terhadap probabilitas ruin. Diperoleh bahwa semakin kecil rate 𝜆1 dan 𝜆2, waktu antarklaim semakin besar sehingga probabilitas ruin semakin kecil. Sedangkan untuk rate 𝜆1 dan 𝜆2 yang semakin besar, waktu antarklaim semakin kecil sehingga probabilitas ruin semakin besar.

---

"

"Provinsi Kepulauan Bangka Belitung memiliki 78,6 juta ton cadangan terukur pasir silika. Pengolahan pasir silika sebagai produk samping dari penambangan timah berpotensi menciptakan peluang ekonomi daerah. Saat ini, pengolahan pasir silika di Kabupaten Bangka menghasilkan 90-95% SiO2. Sementara itu, permintaan global untuk pasir silika dalam industri kaca diproyeksikan meningkat hingga 2025, dengan persyaratan kemurnian 99,500-99,999% SiO2. Oleh karena itu, diperlukan peningkatan kadar pasir silika untuk memenuhi syarat ekspor sebagai low-iron silica sand, yang juga diatur dalam Permendag RI Nomor 12 Tahun 2022 (>99,500% SiO2 dan 0,012% Fe2O3). Peningkatan kadar pasir silika dapat dilakukan dengan penggunaan ultrasonik untuk membebaskan pengotor yang inheren. Material pasir silika yang digunakan dari Bangka dan berukuran -30+100 mesh, dengan kemurnian 74,720% SiO2 dan 97,840% SiO2 (ICP-OES). Pengolahan pasir silika dapat dilakukan dengan rangkaian metode washing, classifying, intensive scrubbing (ultrasonic), gravity concentrating, magnetic separation, dan natural drying. Pasir silika masukan dengan 97,840% SiO2 dan 0,050% Fe2O3 berhasil diolah menjadi produk low-iron silica sand, yakni 99,600% SiO2 dan 0,011% Fe2O3. Dengan demikian, pasir silika di Kabupaten Bangka berpotensi diolah dan diekspor sehingga mampu menjadi sumber pendapatan negara.

---

The Bangka Belitung Islands province has a measured reserve of 78.6 million tons of silica sand. Processing silica sand as a byproduct of tin mining has the potential to create economic opportunities for the region. Currently, silica sand processing in the Bangka Regency yields 90-95% SiO2. Meanwhile, the global demand for silica sand in the glass industry is projected to increase until 2025, with purity requirements of 99.500-99.999% SiO2. Therefore, an increase in the silica sand content is needed to meet the export requirements as low-iron silica sand, which is also regulated in the Indonesian Trade Minister Regulation No. 12 of 2022 (>99.500% SiO2 and 0.012% Fe2O3). The increase in silica sand content can be achieved through the use of ultrasonic technology to remove inherent impurities. The silica sand material used from Bangka is sized -30+100 mesh, with purity levels of 74.720% SiO2 and 97.840% SiO2 (ICP-OES). Silica sand processing can be carried out through a series of methods, including washing, classifying, intensive scrubbing (ultrasonic), gravity concentrating, magnetic separation, and natural drying. Silica sand with an input of 97.840% SiO2 and 0.050% Fe2O3 has been successfully processed into low-iron silica sand products, with 99.600% SiO2 and 0.011% Fe2O3. Thus, silica sand in the Bangka Regency has the potential to be processed and exported, becoming a source of national revenue."

"Salah satu unsur logam tanah jarang adalah lantanum. Lanthanum dapat dipisahkan dengan beberapa teknik seperti ekstraksi solven, pertukaran ion, dan metode pengendapan fraksional. Salah satu sumber lantanum adalah mineral pasir silika, dan Indonesia memiliki jumlah pasir silika yang cukup berlimpah sehingga dapat dijadikan potensi produksi lantanum yang tinggi.Pada penelitian ini akan dilakukan ekstraksi lanthanum dari mineral pasir silika. Pemisahan logam lantanum dari pasir silika menggunakan ekstraksi padat cair, karena sifat fisik dari pasir silikanya sendiri.Metode ekstraksi yang digunakan adalah metode Heap Leaching menggunakan H2SO4, metode ini digunakan karena merupakan metode yang murah, praktis, tidak perlu destruksi, dan preparasi yang tidak rumit.Metode pengendapan menggunakan natrium sulfat kemudian dilakukan untuk memisahkan logam-logam maupun pengotor yang terdapat dalam larutan. Selanjutnya dilakukan pemisahan kembali darilogam pengotor menggunakan asam fitat untuk kemudian diperoleh hasil ion lantanum yang lebih murni. Didapatkan hasil lantanum yang berhasil didapat.

---

One of rare earth metal element is lanthanum. Lanthanum can be separated by several techniques such as solvent extraction, ion exchange, and fractional precipitation methods. One of many source of lanthanum is the silica sand mineral, and Indonesia has a considerable amount of silica sand that can be used as a high lanthanum production potential. In this research, the extraction of lanthanum from silica sand mineral will be done. Separation of lanthanum metal from silica sand using liquid solid extraction is done due to the physical properties of the silica sand itself.

The extraction method that is used in this research is Heap Leaching method using H2SO4. This method is used because it is a cheap, practical method, no need for destruction, and the preparation is not complicated. The precipitation method using sodium sulfate is then carried out to separate the metals and impurities present in the solution. Furthermore, the separation of the impurity metal using phytic acid is then obtained to produce purer lanthanum ions. The result of lanthanum obtained by this method ide 0.709 ppm with percent extraction is 11.3."

"Katalis heterogen dengan support silika berpori yang disintesis dengan teknik co-Micelle/Emulsion Templating (co-MET) memiliki porositas yang seragam. Penggunaan polimer kationik, 2–(Acryloyloxy)–N,N,N–Trimethylethanaminium Chloride dalam teknik co-MET berfungsi untuk menstabilkan emulsi dan membentuk struktur mesopori. Dalam penelitian ini FeCl3 dan HSO3CF3 diimpregnasikan pada silika makro/mesopori yang dihasilkan kemudian dikarakterisasi menggunakan SEM, EDS, FTIR, dan XRD. Data SEM menunjukkan bahwa pori yang dihasilkan pada silika semakin meningkat seiring bertambahnya konsentrasi polimer kationik. Pada FTIR, impregnasi FeCl3 dan HSO3CF3 berhasil dengan adanya peak pada 1036 cm-1 (ikatan Si-O-Fe), 462 cm-1 (vibrasi Fe-Cl) dan 615 cm-1 (ikatan C-S). Uji katalitik reaksi antara benzaldehid dan etanol menunjukkan bahwa katalis HSO3CF3-silika makro/mesopori dengan konsentrasi 5% polimer kationik memiliki hasil yang lebih baik dibandingkan katalis dengan konsentrasi polimer kationik 0,5%, 1%, 2,5% dan 10%.

---

Heterogeneous catalysts with porous silica support whichwere synthesized by co-Micelle/Emulsion Templating (co-MET) techniques have uniform porosity. The use of cationic polymers, 2-(Acryloyloxy)-N,N,N-trimethylethanaminium chloride in co-MET technique serves to stabilize the emulsion and form mesoporous structure.

In this study, FeCl3 and HSO3CF3 were impregnated into macro/mesoporous silica and then were characterizated using SEM, EDS, FTIR, and XRD. SEM data show that the silica pores generated in increases with increasing concentrations of cationic polymer. On FTIR spectrum, impregnation of FeCl3 and HSO3CF3 proven by the peak at 1036 cm-1 (Si-O-Fe bond), 462 cm-1 (vibrations of Fe-Cl) and 615 cm-1(C-S bond).

Catalytic reaction between benzaldehid and ethanol shows that HSO3CF3-Silica macro/mesoporous catalyst with a 5% concentration of cationic polymer has the best result than those with cationic polymer concentration of 0,5%, 1%, 2,5% and 10%."

"Berdasarkan data ESDM produksi olahan nikel Indonesia mencapai 2,47 ton pada 2021 yang naik 2,17% dari tahun sebelumnya. Tren produksi olahan nikel ini terus mengalami pertumbuhan setiap tahunnya. Akan tetapi dengan naiknya produksi nikel menyebabkan permasalahan yang tidak dapat diselesaikan oleh pelaku industri smelter di Indonesia. Terhitung pada tahun 2019 Industri nikel menghasilkan 19 juta ton terak yang diperkirakan akan terus bertambah. Penelitian ini menjelaskan proses ekstraksi silika dari terak feronikel secara sederhana dan ekonomis sehingga menghasilkan karakteristik produk yang baik untuk diguakan sebagai absorbent untuk penyerapan logam berat. Metode ekstraksi yang diguankan yaitu hidrotermal dengan penambahan aditif berupa NaOH, pelindian menggunakan air (aquaades), pengendapan menggunakan proses titrasi dengan HCL sebagai agen titrasi, pencucian menggunakan air (aquades), dan kalsinasi untuk menghilangkan klorin. Dalam Penelitian ini, produk silika yang didapatkan memiliki nilai recovery 91% dan tingkat efisiensi 98% sebagai absorbent untuk logam berat.

---

Based on ESDM data, Indonesia's nickel processed production will reach 2.47 tons in 2021, an increase of 2.17% from the previous year. This trend of nickel-processed production continues to grow every year. However, the increase in nickel production causes problems that cannot be solved by the smelter industry players in Indonesia. As of 2019 the nickel industry produced 19 million tons of slag which is expected to continue to grow. This study describes the process of extracting silica from ferronickel slag in a simple and economical way so as to produce good product characteristics to be used as an absorbent for heavy metal absorption. The extraction method used is hydrothermal with the addition of additives in the form of NaOH, leaching using water (aquades), precipitation using a titration process with HCL as a titration agent, washing using water (aquades), and calcination to remove chlorine. In this study, the silica product obtained had a recovery value of 91% and an efficiency rate of 98% as an absorbent for heavy metals."