Hasil Pencarian  ::  Simpan CSV :: Kembali

"ABSTRAKPerunggu Aluminium merupakan paduan tembaga yang banyak digunakan dalam bidang industri, karena mempunyai sifat mekanik yang baik. Perunggu Aluminium merupakan paduan tembaga, dengan paduan utama Cu dan Al dengan penambahan unsur lain yaitu besi (Fe). Penambahan unsur Fe dimaksudkan untuk meningkatkan sifat mekanik yang dibutuhkan. Selain itu sifat mekanik dapat ditingkatkan dengan perlakuan panas. Paduan perunggu Aluminium pada penelitian mempunyai komposisi 85% Cu, 9% Al dan 2% Ni dengan penambahan Fe sebesar 2%, 4% dan 6%. Paduan mendapat perlakuan panas kondisi celup ( oli dan air ) dan proses tempering pada temperatur 200 C, 400 C dan 600 C. Kemudian dilakukan pengujian sifat mekanik dan pengamatan struktur mikro paduan hasil tuang. Dari hasil pengujian yang dilakukan diketahui bahwa pada kondisi ascast menunjukan nilai kekuatan tarik dan kekerasan tertinggi dibandingkan pada kondisi lainnya seperti proses celup temper, sedangkan nilai regangan dan kekuatan impak rendah. Beberapa hal yang dapat disimpulkan dari penelitian ini antara lain pada daerah plastis, peningkatan dan penurunan nilai dari tegangan tarik dan regangan tidak sama pada kondisi perlakuan panas yang sama, semakin tinggi temperatur temper akan terjadi peningkatan kekuatan tarik dan peningkatan keuletan (regangan), sedangkan ketangguhan (kekuatan impak) mengalami penurunan."

"Perunggu Aluminium merupakan paduan tembaga yang banyak digunakan dalam bidang industri, kerena mempunyai sifat mekanik yang baik. Perunggu aluminium merupakan paduan dengan unsur utama Cu dan Al dan penambahan unsur lain yaitu besi (Fe). Penambahan unsur ini dimaksudkan untuk meningkatkan sifat mekanik yang dibutuhkgn. Selain itu sifat mekanik dapat ditingkatkan dengan perlakuan panas. Paduan perunggu aluminium pada penelitian ini mempunyai komposisi 85% Cu, 9% Al dan 2% Ni dengan penambahan Fe sebesar 2%, 4% dan 6%. Paduan tersebut mendapat perlakuan panas kondisi celup (oli dan air) dan proses tempering pada temperatur 200 C. 400 C dan 600 C. Kemudian dilakukan pengujian sifat mekanik dan pengamatan struktur mikro paduan hasil tuang. Dari hasil pengujian yang dilakukan diketahui bahwa pada kondisi as cast menunjukan nilai kekuatan tarik dan kekerasan tertinggi dibandingkan pada kondisi lainnya seperti proses celup temper, sedangkan nilai regangan dan kekuatan impak rendah. Beberapa hal yang dapat disimpulkan dari penelitian ini antara lain pada daerah plastis, peningkatan dan penurunan nilai dari tegangan tarik dan regangan tidak sama pada kondisi perlakuan panas yang sama. Semakin tinggi temperatur temper akan terjadi peningkatan kekuatan tarik dan peningkatan keuletan (regangan), sedangkan ketangguhan (kekuatan impak) mengalami penurunan.

---

Alumunium bronce is an alloy of copper with wide industrial application, due to good mechanical properties. Bronce aluminium is an alloy made of Cu, Al and other element such as iron. Addition of element such as Fe is aimed to improve its mechanical properties, although mechanical properties can be improved by heat treatment. Alumunium bronce in this investigation have a composition of 85% Cu, 9% Al and 2% Ni by weight with additional of iron in the range of 2%, 4% and 6% by weight respectively. This material was subsequently heat-treated and quenches in water and oil following by tempering at 200 C, 400 C and 600 C" respectively. Thereafter were tested mechanically, and its microstructures were studied. The cast material shows high hardness and high tensile strength than that of the treated material. Nonetheless its impact strength and strain is the lowest. It is observed an in this investigation that the higher the tempering temperature the higher the tensile strength as well as it toughness, however its impact strength is decreasing."

"Proyek bangunan industri atau konstruksi bangunan industri memiliki ciri sebagai suatu kegiatan yang kompleks dan melibatkan banyak disiplin ilmu. Pada setiap tahapan proyek, pemilik proyek atau owner banyak berperan, antara lain dalam bentuk keterlibatan suatu tim ahli yang dapat menjadi counterpart bagi institusi konsultan perencana proyek tersebut. Pengetahuan dan pengalaman operasional bangunan industri yang dimiliki oleh tim ahli owner menjadi salah satu sumber masukan bagi terciptanya desain bangunan industri yang bermutu.Penelitian ini mencoba untuk mendapatkan gambaran nyata tentang peran tim ahli owner pada tahap desain dan melihat adanya hubungan antara peran tersebut dengan peningkatan kinerja mutu desain pada proyek bangunan industri.Data yang digunakan pada penelitian ini merupakan data primer, dengan menggunakan metoda questionnaire (angket). Pemilihan metoda berdasarkan pengamatan bahwa banyak penelitian yang berkaitan dengan peran dan kinerja menggunakan metoda ini, selain itu juga karena kepraktisan metoda dan pertimbangan waktu. Penelitian menggunakan 36 sampel, analisis data menggunakan statistik dilakukan terhadap 30 sampel. Cakupan sampel adalah proyek bangunan industri yang desainnya dilakukan di Jakarta dan Jawa Barat.Dan hasil analisis data, terbentuk persamaan model, yang merupakan model regesi persamaan linier. Model tersebut menggambarkan peran tim ahli owner pada tahap desain terhadap peningkatan kinerja mutu desain proyek bangunan industri. Peran tim ahli owner, yang menjadi variabel penentu dan tergambar pada model dengan urutan yaitu: pertemuan/koordinasi berkala tim ahli owner sebanyak 63,7 %, penyusunan spesifikasi teknis sebanyak 11,4 %, evaluasi atas tahapan pembuatan gambar rancangan sebanyak 10,2 % dan pengalaman profesional ketua tim ahli owner sebanyak 3,1 %."