Abstrak :
ABSTRAK
< Penelitian  ini  ditujukan  untuk  mengetahui  ukuran  dan  konsentrasi  optimum  partikel  yang  ditambahkan  kedalam nanofluida untuk proses pendinginan cepat. Nanofluida digunakan dalam media pendingin untuk meningkatkan nilai konduktivitas termal dalam proses pendinginan cepat. Dalam penelitian ini, digunakan partikel TiO 2  berukuran 44  μm, TiO 2 berukuran 44  μm kemudian dilakukan proses penggilingan, dan TiO 2  berukuran 21 nm. Nanofluida diperoleh dengan mencampurkan 0,1, 0,2, 0,3, 0,4, dan 0,5 % TiO 2  ke dalam air. Planetary ball mill  digunakan untuk mereduksi ukuran TiO 2-44 μm. Karakterisasi komposisi TiO 2  menggunakan Energy Dispersive Spectroscopy (EDS). Dari hasil pengujian menunjukkan bahwa nilai kekerasan nilai kekerasan tertinggi pada  kadar 0,5 % serbuk TiO 2  berukuran 21 nm dengan nilai kekerasan 64 HRC. Untuk pengujian kekerasan dengan media pendingin berupa air didapatkan nilai kekerasan sebesar 55 HRC. Hasil pengujian juga menunjukkan kecenderungan semakin kecil ukuran partikel, maka kekerasan pada material akan semakin meningkat. 

---

ABSTRACT
Recently,  nanofluid  is  used  to  improve  the  thermal  conductivity  of  the  quench medium in the heat treatment industry. In this research, micro-sized TiO 2  powder, ball-milled micro-sized TiO 2   powder and  nano-sized  TiO 2 particle  were  used  and  compared  for  their  cooling  characteristic  in  a microfluid. The microfluid were produced by mixing 0.1%, 0,2%, 0.3%, 0,4%, and 0.5% volume of both micro- and nano-sized particle into 100 ml of distilled water. The planetary ball mill was used at 500 rpm  for 15 hours to  reduce the dimension of micron-sized  TiO 2. Composition characterization by Energy Dispersive Spectroscopy (EDS) showed that the powder used were free from impurities. The hardness test result showed that the sample quenched with 0.5%addition of the nano-sized particle  in  nanofluid had the highest number up to 64 HRC, more than  5 HRC increment  from  a  water-quenched  sample where  the  hardness  was  55 HRC, showing that the cooling rate in the nanofluid was  much  higher. The addition of micro-size particle in fluid generally had a lower cooling rate than the addition of nano-size particle.