Hasil Pencarian  ::  Simpan CSV :: Kembali

"Polyclonal antibodies of aflatoxin B1 were successfully produced from New Zealand White female rabbits afterimmunization by the hapten of aflatoxin B1-carboxymethyl hydroxylamine hemihydrochloride (AFB1-CMO)conjugated with bovine serum albumin (BSA) as the antigen. The hapten was synthesized using the carbodiimidemethod with CMO as a linker. Absorption peaks at 362, 264, and 218 nm were observed as a result of characterizationwith UV-Vis spectroscopy, while IR spectroscopy showed peaks at 3448 cm-1 and 1642 cm-1 attributable to thehydroxyl and nitrile groups, respectively. Furthermore, mass spectrometry showed fragmentation at the m/z of 386,368.2, and 310, which confirms that the hapten of AFB1-CMO was successfully synthesized. The hapten was thenconjugated with BSA to serve as an antigen of AFB1 when it was injected into the rabbits. The specificity of the antigentowards its antibody and the confirmation of hapten-BSA conjugation were characterized using the dot blotimmunoassay, which showed a BSA concentration of 1.74 mg/mL. Two weeks after the primary immunization by itsantigen, agar gel precipitation testing showed that the rabbit blood serum had positive results for polyclonal antibodiestagainst AFB1 with the highest concentration of antibodiest of 2.19 mg/mL.Sintesa of Poliklonal Antibodi Aflatoxin B1. Antibodi poliklonal aflatoksin B1 telah berhasil diproduksi pada hewanuji kelinci betina New Zealand White setelah diimunisasi dengan hapten aflatoksin B1-carboxymethyl hydroxylaminehemihydrochloride (AFB1-CMO) yang dikonjugasikan dengan bovin serum albumin (BSA) sebagai antigen. HaptenAFB1 disintesis menggunakan metode karbodiimida dengan CMO sebagai linker. Puncak absorbansi pada 362, 264,218 nm teramati sebagai hasil karakterisasi menggunakan spektrofotometer UV-Visibel, sementara dengan spektrum IRdiperoleh puncak pada 3448.126 cm-1 dan 1642.451 cm-1 yang masing-masing mengindikasikan adanya gugus hidroksildan nitril. Hasil spektrometri massa menunjukkan fragmentasi pada m/z 386, 368.2, dan 310 yang membuktikan haptenAFB1-CMO telah berhasil disintesis. Hapten ini kemudian dikonjugasikan dengan BSA agar dapat berperan sebagaiantigen AFB1 ketika diinjeksikan pada kelinci. Kekhususan antigen aflatoksin B1 terhadap antibodinya dan konfirmasikonjugat hapten-BSA menunjukkan hasil positif pada uji dot blot immunoassay dengan konsentrasi BSA sebesar 1.74mg/mL. Dua pekan setelah imunisasi primer, agar gel precipitation test menunjukkan hasil positif terhadap antibodipoliklonal AFB1 dengan konsentrasi tertinggi sebesar 2.19 mg/mL."

"An efficient and rapid method for preparation of Au nanoparticles (Au-NP) has been developed by direct microwaveirradiation of metal precursor and alginate mixed solution in a single step. Here, alginate molecules act as both thereducing and stabilizing agents of Au-NP. The obtained nanoparticles were characterized by ultraviolet-visible (UVVis)spectroscopy, particle size analyzer, fourier transform infrared spectroscopy, and transmission electronmicroscopy. The nanoparticles have a spherical form and perfectly capped with alginate when using alginate and chloroauric acid (HAuCl4) precursor in the concentration range of 0.50 to 0.75% (w/v) and 0.40 mM, respectively. The use ofa lower concentration of alginate and/or higher concentration of HAuCl4 caused agglomeration to occur, therebyresulting in a bigger size of Au-NP and red shifting of surface plasmon resonance (SPR) peak to a higher wavelength.Sintesis Nanopartikel Au yang Distabilkan Alginat dengan Bantuan Gelombang Mikro. Sintesis nanopartikel Au(Au-NP) dengan metode yang cepat dan efisien dalam hitungan menit telah berhasil dilakukan dengan teknik iradiasimenggunakan gelombang mikro terhadap campuran garam prekursor dan alginat dalam satu langkah. Molekul alginatberperan sebagai pereduksi maupun penstabil Au-NP. Nanopartikel yang diperoleh dikarakterisasi dengan spektroskopiultraviolet-visible (UV?Vis), particle size analyzer, fourier transform infrared spectroscopy dan transmission electronmicroscopy. Nanopartikel yang diperoleh berbentuk bulat dan terlapisi sempurna oleh alginat pada rentang konsentrasialginat dalam rentang 0,50?0,75% (w/v) dan prekursor HAuCl4 0,20 mM. Pada konsentrasi alginat yang lebih rendahdan/atau konsentrasi HAuCl4 yang lebih tinggi, aglomerasi cenderung terjadi dan menghasilkan ukuran partikel Au-NPyang lebih besar serta pergeseran panjang gelombang surface plasmon resonance (SPR) ke nilai yang lebih besar."