Hasil Pencarian  ::  Simpan CSV :: Kembali

"Paduan zirkonium dikembangkan untuk aplikasi biomaterial karena sifat biokompatibilitasnya yang baik dengan magnetic susceptibility lebih rendah dibandingkan biomaterial logam lain. Pengembangan pembuatan paduan Zr-12Mo dengan metode metalurgi serbuk dapat dijadikan solusi alternatif terhadap proses cor yang memerlukan peleburan zirkonium dan molibdenum yang memiliki titik lebur tinggi. Proses sinter merupakan tahapan penting yang menentukan sifat akhir produk metalurgi serbuk. Penelitian ini bertujuan untuk meneliti pengaruh temperatur dan waktu sinter terhadap densitas, porositas, struktur mikro serta sifat mekanis paduan Zr-12Mo yang diproduksi dengan berbagai parameter sinter. Penelitian menggunakan temperatur sinter 1000°C, 1100°C dan 1200°C dengan variasi waktu tahan 2 dan 4 jam di masing-masing temperatur. Sampel dilakukan pengujian densitas, XRD dan kekerasan, pengamatan dengan OM dan SEM, serta pengujian terhadap sifat bioaktif dengan menguji terbentuknya lapisan hidroksiapatit setelah perendaman dalam SBF selama seminggu. Hasil penelitian menunjukkan bahwa temperatur sinter lebih dominan dalam mempengaruhi hasil proses sinter dibandingkan waktu tahan karena peningkatan temperatur sangat meningkatkan difusi. Porositas minimum, densitas dan kekerasan maksimum serta difusivitas Mo dalam Zr optimal dicapai pada temperatur sinter 1200°C dengan waktu tahan 4 jam.

---

Zirconium alloys have been developed for biomaterial applications because it has good biocompatibility with magnetic susceptibility that is lower than other metallic biomaterials. Developing of Zr-12Mo alloys by powder metallurgy method can be used as alternative solution for casting process that need melting of zirconium and molybdenum which have high melting point. Sintering process is the important stage which determining final properties of powder metallurgy’s products. This research is aimed to study the effects of sintering time and temperature on density, porosity, microstructure, and mechanical properties of Zr-12Mo alloys produced by various sintering parameters. This research uses sintering temperatures of 1000°C, 1100°C and 1200°C with holding times for 2 and 4 hours for each temperature. Samples are examined by density, XRD and hardness testing, observation with OM and SEM, and also bioactive testing by proving the forming of hidroxyapatite layers after soaking in SBF for a week. The results show that sintering temperature more dominant in affecting sintering products than holding time because the increase of sintering temperature increase the diffusion greatly. Minimum porosity, maximum density and hardness with optimal diffusivity is achieved by using sintering temperature of 1200°C with holding time for 4 hours."

"This book highlights the various types of polymer and nanocomposites that can be derived from biorenewable resources. It covers various aspects of biobased polymers and nanocomposites, including preparation, processing, properties, and performance, and the latest advances in these materials."

"Pada umumnya, magnesium adalah pilihan material untuk dikembangkan pada aplikasi implan mampu luruh. Pada penelitian ini dikembangkan paduan Mg-1.6Gd dengan perlakuan pencanaian hangat searah dan menyilang dengan reduksi ketebalan masing-masing 95% dan dilihat pengaruhnya terhadap karakteristik dan mekanisme degradasi. Pencanaian material Mg-1.6Gd dilakukan pada temperatur rekristalisasi yaitu sekitar 400-560°C dengan reduksi 95% serta kecepatan 10mm/menit. Pencanaian dilakukan dengan 2 metode yaitu searah dan silang dengan masing-masing arah memiliki 2 sampel dengan variabel temperatur yang berbeda. Proses karakterisasi yang dilakukan berupa OM, SEM dan EDS. Mekanisme dan karakterisasi degradasi dianalisa dengan menggunakan metode EIS, polarisasi dan imersi dalam larutan kokubo SBF. Sampel pencanaian searah dan silang menghasilkan lapisan pasif yang memproteksi berdasarkan metode fitting sirkuit EIS dengan nilai Rct terbesar untuk sampel canai searah yaitu sebesar 1590 Ω. Serta pada hasil metode polarisasi didapatkan pencanaian searah memiliki laju degradasi lebih rendah daripada canai silang yaitu sebesar 0.126 mm/yr. Dan dengan metode imersi menunjukan bahwa sampel searah memiliki laju degradasi yang lebih rendah yaitu 14.0 mm/yr. Hal ini terjadi karena butir pada mikrostruktur di sampel canai searah lebih halus yang dapat menurunkan laju degradasi.

---

Generally, Magnesium is a choice of materials that has been developed for biodegradable implants. In this study, Mg-1.6Gd alloy was warm rolled by single-pass rolling and cross rolling with 95% reduction in thickness to observe the degradation characteristics and mechanisms. Mg-1.6Gd alloy was performed at a temperature range of crystallization which is 400-560°C with 95% reduction and a speed of 10mm/min. The rolling process was employed by two methods: single-pass rolling and cross rolling with 2 samples for each methods on a different temperature.

Degradation characteristics and mechanisms was analyzed with EIS, polarization and immersion methods on a SBF kokubo solution. Single-pass and cross rolled creates a protective passive layer based on EIS circuit fitting method and the highest Rct value is the single-pass rolled which is 1590 Ω. In addition, polarization method results determined that the single-pass rolled showed the lowest degradation rate than the cross-rolled which is 0.126 mm/yr. And with the immersion method shows that the single-pass rolled has the lowest degradation rate which is 14.0 mm/yr. This happened because the grain on the microstructure of single-pass is more refined so that I could reduce the degradation rate."

"Hidroksiapatit (HA) berperan penting dalam dunia medis karena komposisi kimia dan strukturnya yang mirip dengan jaringan keras manusia. Material ini disintesis melalui proses pengendapan kimia basah dengan prekursor Ca(OH)2 dan H3PO4 yang ekonomis dan ramah lingkungan karena hasil sampingannya hanya air. Variasi temperatur sinter pada 500, 700, dan 900°C selama 4, 6, dan 8 jam untuk masing-masing temperatur digunakan pada sintesis di dalam penelitian ini. Endapan yang diperoleh diuji dengan XRD, FTIR, TGA, dan SEM. Tingkat kristalinitas dan besar kristalit meningkat seiring temperatur sinter. Diperoleh kondisi terbaik untuk tingkat kristalinitas pada 900°C selama 6 jam dengan ukuran kristalit 37.84 nm. Morfologi partikel hasil uji SEM berbentuk bulat teraglomerasi dan uji EDX menunjukkan rasio Ca/P yang rendah sebesar 0.875. Uji XRD dan FTIR menunjukkan adanya fasa trikalsium fosfat (α-TCP) dan karbonat-hidroksiapatit (CHA) di dalam endapan HA yang menurunkan rasio Ca/P.

---

Hydroxyapatite (HA) posseses significant role in medical application due to its similarity in chemical and structure to human hard tissue. This material was synthesized through wet chemical precipitation process using Ca(OH)2 dan H3PO4 which is less expensive and environmentally friendly due to its only by-product is water. Sintering temperature varied on 500, 700, and 900°C with holding time of 4, 6, and 8 hours for each temperature respectively. The best result for crystallinity obtained at 900°C at holding time 6 hours with crystallite size of 37.84 nm. Morphology observed by SEM is agglomerated round-shape particles with Ca/P ratio of 0.875 measured by EDX. Carbonatedhydroxyapatite (CHA) and α-tricalcium phosphate (α-TCP) presence is observed by XRD and FTIR on the precipitated HA obtained by this process that reduce the Ca/P ratio of HA."

"Skripsi ini membahas pengaruh teknik inkremental dan aplikasi re-etch re-bond terhadap pencegahan perubahan warna tepi restorasi resin komposit nanohybrid setelah perendaman dalam larutan kopi, dengan cara membagi 24 gigi molar 3 menjadi 4 kelompok. Sample dibuat kavitas berbentuk lingkaran dengan diameter 2 mm kemudian ditumpat resin komposit nanohybrid dengan teknik inkremental (kelompok I-II) dan bulk (kelompok III-IV),pada kelompok I juga diaplikasikan re- etch re-bond setelah finishing lalu direndam dalam larutan kopi. Hasilnya, kelompok I menunjukkan nilai pewarnaan tepi tumpatan yang terendah dan pewarnaan tepi bermakna secara statistik (p<0,05) terjadi pada penghitungan hari ke-6 dan ke-12. Kesimpulannya, teknik penumpatan inkremental dan pengaplikasian re-etch re-bond dapat meminimalkan perubahan warna tepi tumpatan.

---

This study discusses the influence of incremental technique and re-etch re-bond applications to the prevention of marginal discoloration nanohybrid composite resin after immersed in a solution of coffee, by dividing the 24 third molars into 4 groups. Sample made a circular cavity with a diameter of 2 mm then restored by nanohybrid composite resin with incremental technique (group I-II) and bulk (group III-IV), in group I also applied re-etch re-bond after finishing and then immersed in a solution of coffee . As a result, group I showed the lowest value of marginal discoloration and the marginal discoloration statistically significant (p <0.05) occurred in the counting day 6 and 12. In conclusion, incremental techniques and application of re-etch re- bond can minimize marginal discoloration of composite resin"