Abstrak :
Kemampuan inhibitor Imidazoline dalam menginhibisi baja karbon API 5L Grade B dalam lingkungan NaCl 3.5 % diinvestigasi dengan menggunakan metode Polarisasi Tahanan Linier atau Linier Polarization Resistance (LPR) dalam berbagai variasi konsentrasi. Konsentrasi yang digunakan pada penelitian kali ini adalah 0 ppm, 50 ppm, 10 ppm, 150 ppm, 200 ppm, dan 250 ppm. Hasil pengujian menunjukkan bahwa konsentrasi optimum dalam menurunkan laju korosi terdapat pada 200 ppm dengan laju korosi sebesar 0,0005 mm/year, sedangkan nilai Rp terus meningkat dan optimum pada konsentrasi 250 ppm dengan nilai sebesar 579,042 Ohm. Kurva laju korosi vs konsentrasi inhibitor menunjukkan bahwa konsentrasi optimum inhibitor imidazoline dalam menurunkan laju korosi terdapat pada konsentrasi 200 ppm. ......The performance of Imidazoline based commercial corrosion inhibitor on carbon stel API 5L Grade B on NaCl 3.5 % solution was investigated using Linear Polarization Resistance Method or LPR. The Inhibitor concentration that used in this experiment were 0 ppm, 50 ppm, 100 ppm, 150 ppm, 200 ppm, and 250 ppm. Experimental results showed that the optimum concentration to decrease the corrosion rate is 200 ppm with the corrosion rate is 0,0005 mm/year , while the optimum polarization resistance is 579,042 Ohm at 250 ppm. The plot of corrosion rate vs inhibitor concentration show the optimum imidazoline inhibitor concentration for decreasing corrosion rate is 200 ppm.

Abstrak :
Imidazolin adalah senyawa heterosiklik yang mengandung nitrogen. Imidazolin dikenal di dunia industri, terutama di industri perminyakan sebagai inhibitor korosi pada kilang minyak baja dalam perairan laut. Dalam penelitian ini, telah berhasil disintesis empat senyawa turunan imidazolin, yaitu N1- 2- 2-undesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AL , N1- 2- 2-tridesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AM , N1- 2- 2-pentadesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AP , dan N1- 2- 2-heptadesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AS dengan mereaksikan TETA trietilentetramina dan variasi asam lemak jenuh berturut-turut asam laurat AL , miristat AM , palmitat AP , dan stearat AS tanpa pelarut dengan variasi waktu reaksi menggunakan metode MAOS Microwave Assisted Organic Synthesis . Yield optimum senyawa turunan imidazolin TETA-AL diperoleh pada waktu sintesis 7 menit 72,64 , TETA-AM 9 menit 81,13 , TETA-AP 11 menit 84,62 , dan TETA-AS 11 menit 87,49 . Metode refluks dan Dean Stark dengan pelarut xylena digunakan sebagai pembanding untuk memperoleh metode yang paling efektif dan efisien dalam sintesis senyawa imidazolin TETA-AP, dimana diperoleh yield tertinggi didapatkan pada metode Dean Stark 13 jam 95,89 , diikuti dengan metode refluks 13 jam 88,53 , dan MAOS 11 menit 84,62 . Seluruh senyawa hasil sintesis sudah dikonfirmasi strukturnya menggunakan instrumen spektrofotometer UV-Vis, spektrometer FTIR, spektroskopi 1H-NMR, dan spektrometer massa MS dengan terlebih dulu diidentifikasi dengan menggunakan kromatografi lapis tipis KLT dan uji penentuan titik leleh. Uji aktivitas sebagai inhibitor korosi terhadap baja karbon dalam larutan NaCl 1 dilakukan pada seluruh senyawa hasil sintesis dengan variasi konsentrasi imidazolin 100, 200, 300, 400, 500 ppm dengan mengukur arus korosi icorr menggunakan potensiostat eDAQ 450 dan Versasatat II . Hasil pengukuran arus menggunakan metode voltametri siklik ini kemudian diolah menggunakan metode Polarisasi Tafel untuk menentukan persen efisiensi inhibisi EI . Diperoleh EI tertinggi pada penambahan konsentrasi 500 ppm senyawa TETA-AL, TETA-AM, TETA-AP, dan TETA-AS berturut-turut adalah 74,44 ; 72,97 ; 78,55 ; dan 87,17 . Berdasarkan data tersebut, dapat disimpulkan bahwa keempat senyawa imidazolin TETA-AL, TETA-AM, TETA-AP, dan TETA-AS berpotensi sebagai inhibitor korosi pada baja karbon. ......Imidazoline is a heterocyclic compound containing nitrogen atom. Imidazoline is well known in industry, especially in petroleum field as a corrosion inhibitor of oil refineries in sea environment. In this study, four imidazoline derivatives, i.e. N1 2 2 undecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA LA , N1 2 2 tridecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA MA , N1 2 2 pentadecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA PA , and N1 2 2 heptadecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA SA had been successfully synthesized by reacting TETA triethylenetetramine and various saturated fatty acid, such as lauric LA , miristic MA , palmitic PA , and stearic acid SA , respectively, with solvent free and variation of reaction time by using MAOS Microwave Assisted Organic Synthesis method. The optimum yield of imidazoline derivative compounds were obtained from TETA AL at 7 rsquo 72,64 , TETA AM at 9 rsquo 81,13 , TETA AP at 11 rsquo 84,62 , and TETA AS at 11 rsquo 87,49 . Reflux and Dean Stark methods in xylene were also conducted as a comparison to obtained the most effective and efficient methods in imidazoline TETA AP synthesis, which the highest yield was obtained from Dean Stark method at 13 h 95,89 , followed by reflux method at 13 h 88,53 , and MAOS method at 11 rsquo 84,62 . All of the synthesized compounds were identified by using thin layer chromatography TLC and examined their melting point. The structure of all synthesized compounds had been confirmed by using UV Vis spectrophotometer, FT IR spectrometer, 1H NMR spectroscopy, and mass spectrometer MS . Inhibition corrosion test of carbon steel in 1 NaCl solution was performed on all synthesized imidazoline derivatives compounds with variation of imidazoline concentration 100, 200, 300, 400, 500 ppm by measuring the corrosion current icorr using potensiostat eDAQ 450 and Versasatat II . Using cyclic voltammetry method, the measurement result were processed through Tafel Polarization to obtain the percentage of inhibition efficiency EI . The highest EI was obtained at 500 ppm of TETA AL, TETA AM, TETA AP, and TETA AS with 74,44 , 72,97 , 78,55 , and 87,17 , respectively. It can be concluded that all of the imidazoline compounds i.e. TETA AL, TETA AM, TETA AP, and TETA AS are potential organic compound as a corrosion inhibitor towards carbon steel.

Abstrak :
Baja karbon rendah merupakan salah satu bahan yang banyak digunakan di industri oil dan gas, industri kimia, industri makanan dan lain-lain. Baja karbon rendah memiliki keuntungan, yaitu murah dan memiliki sifat mekanikal yang bagus, namun, memiliki kekurangan, yaitu mudah terkorosi jika tidak dipersiapkan dengan benar. Salah satu upaya untuk mencegah timbulnya korosi adalah menggunakan cat dan inhibitor korosi. Imidazolin merupakan salah satu inhibitor korosi organik yang efektif mencegah korosi. Imidazolin dapat disintesis dengan menggunakan asam lemak dan amina. Penelitian ini bertujuan untuk mensintesis turunan imidazolin dari soybean oil fatty acid (SOFA) dan dietilentriamin (DETA) serta aplikasinya sebagai inhibitor korosi pada cat yang berbasis alkid. Cat yang beredar saat ini masih menggunakan inhibitor anorganik yaitu seng fosfat yang memiliki kelemahan menurunkan tingkat kilap serta menurunkan transparansi cat. Pada penelitian ini berhasil mensintesis turunan imidazolin dari soybean oil fatty acid yang ditunjukkan dari hasil FT-IR dan H-NMR. Analisa sifat korosi SOFA/DETA Imidazolin merupakan inhibitor katodik. SOFA/DETA imidazolin 0,09 g pada larutan uji 5% NaCl, mampu menghasilkan efisiensi inhibisi sebesar 72,42% dan laju korosi 1,67 mpy pada baja karbon rendah. Campuran antara cat alkid dan SOFA/DETA Imidazolin 1% mampu menghasilkan efisiensi inhibisi 99,25% dan laju korosi 0,04 mpy. ......Mild steel is one of raw material that use in oil and gas industries, chemical, food industries, etc. Mild steel has advantages cheap and good mechanical properties, while a weakness is easy to corroded if wrong treatment. The way to prevent corrosion is use coating and corrosion inhibitor. Imidazoline is one of effective organic corrosion inhibitor. Synthesis imidazoline can use fatty acid and amine. In this research will syhthesis imidazoline from soybean oil fatty acid and applied it to alkyd coating. General coating still use zinc phospate as anorganic inhibitor that has a weakness decrease of gloss and decrease transparency. In this research, synthesis imidazoline from soybean oil fatty acid that showed from FT-IR and H-NMR was succesfull. Corrosion analyzation of SOFA/ DETA Imidazoline showed that it catodic inbibitor. 0.09 gram SOFA/DETA Imidazoline on 5% NaCl give result inhibition efficiency 72.42% and corrosion rate 1.67 mpy on mild steel. Alkyd coating with 1% SOFA/DETA Imidazoline give result inhibition efficiency 99.25% and corrosion rate 0.04 mpy

Abstrak :
Imidazolin merupakan senyawa organik yang sering digunakan sebagai inhibitor korosi. Berdasarkan strukturnya, imidazolin termasuk senyawa heterosiklik yang memiliki gugus pendant dan rantai hidrokarbon yang penting dalam menginhibisi korosi. Pada penelitian ini telah dilakukan sintesis senyawa ester-imidazolin dari aminoetiletanolamina (AEEA) dan asam oleat (AO) dengan perbandingan 1:2 menggunakan pelarut xilena dan variasi waktu reaksi (7, 9, 11, dan 13 menit) menggunakan metode MAOS (Microwave Assisted Organic Synthesis). Hasil reaksi menunjukkan % yield optimum diperoleh pada waktu reaksi 9 menit dengan nilai % yield sebesar 87,53%. Ester-imidazolin AEEA-AO kemudian dimodifikasi strukturnya menjadi garam menggunakan dimetil sulfat (DMS) dengan menggunakan metode yang sama selama 2 menit. Berdasarkan hasil karakterisasi, senyawa garam belum berhasil disintesis dan terjadi reaksi transesterifikasi menjadi metil oleat. Kedua senyawa hasil sintesis telah dianalisis menggunakan kromatografi lapis tipis (KLT) dan strukturnya telah dielusidasi menggunakan spektrum FTIR, UV-Vis, dan 1H-NMR. Pengujian aktivitas sebagai inhibitor korosi dilakukan terhadap kedua senyawa hasil sintesis serta sampel komersil pada baja karbon dalam larutan 1% NaCl dengan variasi konsentrasi (20, 40, 60, 80, dan 100 ppm) menggunakan metode polarisasi Tafel untuk mencari nilai persen efisiensi inhibisi (%EI). %EI tertinggi ditunjukkan oleh senyawa ester- imidazolin AEEA-AO pada konsentrasi 100 ppm sebesar 51,26%. Nilai %EI ini kemudian digunakan dalam analisis isoterm adsorpsi dan diperoleh bahwa senyawa ester-imidazolin AEEA-AO mengikuti teori Temkin dalam menginhibisi baja karbon dengan nilai energi bebas Gibss sebesar -38,716 kJ/mol. Berdasarkan hasil isoterm adsorpsi, dapat disimpulkan bahwa mekanisme inhibisi senyawa ester-imidazolin AEEA-AO adalah intermediet dari adsorpsi fisik dan kimia. Senyawa ini dapat direkomendasikan sebagai agen anti korosi yang baik karena senyawa ini memiliki nilai %EI yang lebih baik daripada sampel komersil. ......Imidazoline is an organic compound that widely used as a corrosion inhibitor. Based on its structure, imidazoline is a heterocyclic compound having pendant group and hydrocarbon chain which important for its activity as corrosion inhibitor. In this research, ester-imidazoline from aminoethylethanolamine (AEEA) and oleic acid (OA) was successfully synthesized with a ratio of 1:2 in xylene solvent with various reaction time (7, 9, 11, and 13 minutes) using MAOS (Microwave Assisted Organic Synthesis) method. The optimum % yield was obtained at 9 minutes reaction time with 87.53%. Ester-imidazoline AEEA-OA then was modified to its salt using MAOS method for 2 minutes. According to characterization data, salt of ester-imidazoline AEEA-OA was not successfully synthesized and produced methyl oleate, a transesterification product. All of synthesized compounds then were analyzed using thin layer chromatography (TLC) and its structures were elucidated using FTIR, UV-Vis, and 1H-NMR spectral data. The activity as corrosion inhibitor from all of synthesized compounds compared with commercial sample were measured towards carbon steel in 1% NaCl with various concentration (20, 40, 60, 80, and 100 ppm) using Tafel polarization method to afford inhibition efficiency (%IE). The highest %IE was yielded from ester-imidazoline AEEA-OA in 100 ppm with 51.26%. This %IE then was used in adsorption isotherm analysis resulting ester-imidazoline AEEA-OA followed Temkin in corrosion inhibition towards carbon steel with Gibbs free energy of -38.716 kJ/mol. It can be concluded that inhibition mechanism of ester-imidazoline AEEA-OA was intermediate between physicsorption and chemisorption. Ester-imidazoline AEEA-OA can be recommended as a good anticorrosion agent since it showed higher %IE compared with commercial sample.

Abstrak :
Dengan perkembangan industri yang cukup cepat diperlukan perlindungan untuk alat-alat proses yang merupakan suatu komponen penting dalam proses produksi. Perlindungan ini dapat berupa inhibitor korosi yang menjaga peralatan dari korosi terutama industry minyak dan gas bumi yang bersentungan langusng dengan fluida yang memiliki kecepatan dan tekanan tinggi, serta keadaan fluida yang asam sehingga dapat menyebabkan korosi pada peralatan produksi seperti sistem perpipaan. Proposal ini akan membahas mengenai produksi dari turunan imidazolin yang terbentuk dari asam oleat dan trietiltertamina yang dapat digunakan sebagai inhibitor korosi dengan melakukan simulasi proses serta pada proposal ini akan dilakukan perhitungan keekonomian untuk mengetahui seberapa mungkin perusahaan ini untuk dibangun di Indonesia. ......With the rapid development of the industry, protection is needed for process equipment, which is an important component in the production process. This protection can take the form of corrosion inhibitors that protect equipment from corrosion, especially in the oil and gas industry, where they come into direct contact with fluids that have high velocity and pressure, as well as acidic conditions that can cause corrosion in production equipment such as pipeline systems. This proposal will discuss the production of turunan imidazoline, which is formed from oleic acid and triethylamine and can be used as a corrosion inhibitor. It will simulate the process and also include an economic calculation to determine the feasibility of establishing this company in Indonesia.

Abstrak :
Imidazolin merupakan senyawa heterosiklik yang telah banyak dikenal dalam industri perminyakan sebagai inhibitor korosi pada kilang minyak baja di perairan laut. Pada penelitian ini telah dilakukan sintesis senyawa turunan imidazolin menggunakan metode MAOS (Microwave Assisted Organic Synthesis) dengan mereaksikan tetraetilenpentamina (TEPA) dan asam oleat (AO) pada perbandingan ekivalen reaksi 1:1 membentuk imidazolin TEPA-AO dan 1:2 membentuk bis-imidazolin TEPA-AO dengan variasi waktu reaksi 7, 9, 11, dan 13 menit. Persen yield optimum senyawa imidazolin TEPA-AO diperoleh pada waktu sintesis 9 menit (82,62%) dan senyawa bis-imidazolin TEPA-AO pada 11 menit (88,56%). Kedua senyawa hasil sintesis kemudian dimurnikan dengan metode ekstraksi cair-cair dan dianalisis menggunakan kromatografi lapis tipis (KLT). Struktur kedua senyawa hasil sintesis telah dikonfirmasi berdasarkan data spektrum UV-Vis, FTIR, dan 1H-NMR. Penentuan aktivitas kedua senyawa hasil sintesis sebagai inhibitor korosi dilakukan pada baja karbon dalam larutan 1% NaCl dengan variasi konsentrasi (100, 200, 300, 400, dan 500 ppm) menggunakan metode polarisasi Tafel. Persen efisiensi inhibisi (%EI) tertinggi untuk kedua senyawa diperoleh pada penambahan konsentrasi 500 ppm berturut-turut sebesar 86,37% dan 89,70% untuk senyawa imidazolin TEPA-AO dan bis-imidazolin TEPA-AO. Untuk mengetahui mode inhibisi korosi pada baja karbon, ada tidaknya perubahan struktur senyawa setelah uji inhibisi korosi dianalisis menggunakan FTIR. Berdasarkan spektrum FTIR diperoleh bahwa masih terdapat puncak-puncak khas cincin senyawa imidazolin dan juga ditemukan perubahan struktur dari kedua senyawa hasil sintesis setelah dilakukan uji inhibisi korosi, sehingga dapat dikatakan mode inhibisi korosi dari kedua senyawa tersebut terjadi secara adsorpsi fisik dengan sedikit adsorpsi kimia. Dari penelitian ini dapat disimpulkan bahwa senyawa imidazolin TEPA-AO dan bis-imidazolin TEPA-AO dapat digunakan sebagai inhibitor korosi terhadap baja karbon dalam larutan 1% NaCl.

---

Imidazoline is a heterocyclic compound which has been widely known in the oilfields industry as corrosion inhibitor for oil refineries in sea environment. In this research, imidazoline derivatives was successfully synthesized by reacting tetraethylenepentamine (TEPA) and oleic acid (OA) using MAOS (Microwave Assisted Organic Synthesis) method at equivalent ratio of 1:1 to yield TEPA-OA imidazoline and 1:2 to yield TEPA-OA bis-imidazoline in various reaction times (7, 9, 11, and 13 minuntes). The optimum yield of TEPA-OA imidazoline was obtained at 9 minutes reaction time (82.62%) and TEPA-OA bis-imidazoline at 11 minutes (88.56%). Both of synthesized compounds then was purified by liquid-liquid extraction method and analyzed by thin layer chromatography (TLC). The structure of all synthesized compounds was confirmed based on UV-Vis, FTIR, and 1H-NMR spectral data. Corrosion inhibition activity of all synthesized compounds was determined towards carbon steel in 1% NaCl solution with variation of imidazoline concentration (100, 200, 300, 400, and 500 ppm) using Tafel polarization method. The highest percentage of inhibition efficiency (%IE) was obtained at 500 ppm with 86.37% dan 89.70% for TEPA-OA imidazoline and TEPA-AO bis-imidazoline, respectively. To analyze corrosion inhibition mode towards carbon steel, the structure of synthesized compound after corrosion inhibition test was analyzed using FTIR. Based on FTIR spectra, the structure of both synthesized compounds still had imidazolines ring-peaks characteristics and were slightly altered after corrosion inhibition test, therefore corrosion inhibition mode of synthesized compounds were physic- and slightly chemisorption. From this research, it can be concluded that TEPA-OA imidazoline and TEPA-OA bis-imidazoline compounds can be used as a corrosion inhibitor towards carbon steel in 1% NaCl solution.

Abstrak :
Korosi merupakan peristiwa yang kerap terjadi pada pipa di industri perminyakan yang ditandai dengan penurunan kualitas akibat reaksi kimia pada logam sehingga dapat mengakibatkan kerugian bagi industri tersebut. Oleh karena itu, untuk memperlambat laju korosi dibutuhkan suatu inhibitor korosi. Inhibitor korosi organik lebih banyak digunakan dibanding dengan inhibitor korosi anorganik karena bersifat nontoksik dan lebih efektif. Salah satu dari inhibitor korosi organik yang banyak digunakan adalah imidazolin. Imidazolin merupakan senyawa organik heterosiklik dengan 2 unsur nitrogen, rantai panjang hidrokarbon, dan rantai sisi dengan gugus fungsi aktif . Pada penelitian ini senyawa turunan imidazolin telah disintesis dari trietilentetramina (TETA) dengan variasi asam lemak, yaitu asam stearat (AS) proanalisis dan teknis, serta asam oleat (AO) pro analisis dan teknis dengan menggunakan kondisi optimum pada penelitian sebelumnya. Produk yang diperoleh kemudian dipisahkan dengan metode ekstraksi pelarut dan diidentifikasi menggunakan kromatografi lapis tipis (KLT). Terhadap masing-masing hasil reaksi juga telah dikarakterisasi menggunakan instrumen UV-Vis, FTIR, dan LC-MS/MS. Uji aktivitas terhadap inhibisi korosi pada baja karbon dalam larutan 1% NaCl dilakukan untuk masing-masing produk untuk memperoleh nilai persen efisiensi inhibisi (%EI). Nilai persen efisiensi inhibisi untuk TETA-AO murni; TETA-AO teknis; TETA-AS murni; TETA-AS teknis; dan imidazolin komersil terbesar terdapat pada konsentrasi 500 ppm dengan %EI berturut-turut 87,95%; 83,26%; 84,43%; 75,42%; dan 84,41%. TETA-AO murni memiliki %EI terbesar sehingga dilanjutkan untuk penentuan data kinetika dan termodinamika dari reaksi sintesis senyawa imidazolin tersebut dengan menggunakan instrumen UV-Vis dan titrasi melalui penentuan angka asam. Data kinetika dan termodinamika yang diperoleh diharapkan dapat diaplikasikan dan dikembangkan untuk TETA-AO teknis pada sintesis skala besar senyawa inhibitor korosi turunan imidazolin di dunia industri karena harganya lebih ekonomis. Melalui hasil penentuan angka asam didapatkan data jika reaksi merupakan pseudo-orde 1, energi aktivasi sebesar 36.96 kJ/mol, faktor frekuensi sebesar 112,62 menit. Data termodinamika yang didapatkan meliputi energi entalpi sebesar 33,65 kJ/mol, entropi sebesar -0,2504 kJ/mol.K, dan energi gibbs untuk suhu 110, 120, 130, dan 140^o C berturut-turut sebesar 129,55 kJ/mol; 132,06 kJ/mol; 134,56 kJ/mol; dan 1237,07 kJ/mol.
Corrosion is an event that often occurs in the pipeline in the oil industry which is characterized by a decrease in quality due to chemical reactions on the metal so that it can cause harm to the industry. Therefore, to slow down the corrosion rate a corrosion inhibitor is needed. Organic corrosion inhibitors are more widely used than inorganic corrosion inhibitors because they are non-toxic and more effective. One of the most widely used organic corrosion inhibitors is imidazoline. Imidazoline is a heterocyclic organic compound with 2 nitrogen elements, a long chain of hydrocarbons, and a side chain with an active function group (pendant). In this study, imidazoline derivatives had been synthesized from triethylenetetramine (TETA) ) with a variety of fatty acids, namely stearic acid (SA) and oleic acid (OA) both in pro analysis and in technical grade using Microwave Assisted Organic Synthesis (MAOS) with optimum condition followed the previous study. The obtained products then were separated by a solvent extraction method and identified using thin-layer chromatography (TLC). Moreover, the products had also been characterized using FTIR, UV-Vis spectral data, and LC-MS/MS. The activity of corrosion inhibition on carbon steel in a solution of 1% NaCl was carried out for all products to obtain inhibition efficiency (% IE). %IE for TETA-OA pro analysis; TETA-OA technical; TETA-SA pro analysis; TETA-SA technical; and the commercial imidazoline at a concentration of 500 ppm were 87.95%; 83.26%; 84.43%; 75.42%; and 84.41%, respectively. It can be concluded that triethylenetetramine-derived imidazoline can be used as a corrosion inhibitor towards carbon steel. TETA-OA pro analysis has the largest %IE so that it will be continued for the determination of kinetic and thermodynamic data from the synthesis reaction of the imidazoline compound by using the UV-Vis instrument and titration through the determination of acid numbers. The kinetic and thermodynamic data obtained are expected to be applied to the synthesis of large scale imidazoline derivative corrosion inhibitor compounds in the industrial world. Through the results of the determination of acid numbers obtained data if the reaction is pseudo-order 1, the activation energy is 36.96 kJ/mol, and pre-exponential factors are 112.62  min^-1. For thermodynamic data obtained enthalpy energy of 33.65 kJ/mol; entropy equal to -0,2504 kJ/mol.K, and Gibbs energy for 110, 120, 130, dan 140^o C are 129.55 kJ/mol; 132.06 kJ/mol; 134.56 kJ/mol;  137.07 kJ/mol, respectively.

Abstrak :
Baja karbon adalah bahan utama yang digunakan dalam struktur jaringan pipa untuk jalur produksi gas dan minyak. Namun, baja karbon rentan mengalami korosi akibat media korosif di sekitarnya. Hal inilah yang menjadi alasan utama kerusakan pipa yang menyebabkan kerugian ekonomi. Meskipun demikian, korosi dapat dikendalikan untuk memperlambat proses perusakannya menggunakan senyawa turunan imidazolin sebagai inhibitor korosi organik. Pada penelitian ini telah berhasil disintesis senyawa imidazolin-oleat dari trietilentetramina (TETA) dan asam oleat (AO) pada suhu 140°C dengan variasi kecepatan pengadukan 500, 750, dan 1000 rpm. Senyawa hasil sintesis tersebut kemudian dimurnikan dengan metode ekstraksi pelarut, diidentifikasi (KLT), dan dikarakterisasi menggunakan instrumen UV-Vis, FTIR, dan ¹H-NMR. Berdasarkan hasil karakterisasi, senyawa imidazolin-oleat telah berhasil disintesis dengan menunjukkan adanya puncak serapan maksimum pada panjang gelombang 204 nm (UV-Vis), serapan pada bilangan gelombang 1600 dan 1500 cm^-1 yang berasal dari C=N dan C-N-C (FTIR), serta sinyal pada geseran kimia 2,17 ppm yang menunjukkan H-C-C=N (¹H-NMR). Analisis penentuan data kinetika dan termodinamika serta penentuan persen konversi dari reaksi sintesis senyawa imidazolin-oleat dengan variasi waktu, suhu, dan kecepatan pengadukan ditentukan dengan metode titrasi asam basa untuk melihat jumlah AO yang tersisa. Hasil penentuan angka asam menunjukkan bahwa reaksi mengikuti kinetika pseudo-orde 1 pada suhu maksimum 140°C. Nilai konstanta laju reaksi pada suhu 140°C dengan variasi pengadukan 500, 750, dan 1000 rpm berturut-turut sebesar 2,081 x 10^-3; 2,177 x 10^-3; dan 2,212 x 10^-3 menit^-1. Persen konversi tertinggi didapatkan sebesar 86,143±1,089% (140°C, 1000 rpm). Pada suhu yang lebih tinggi, 150°C dan 160°C, menunjukkan adanya perubahan orde reaksi menjadi orde 2 sehingga data tersebut kurang relevan digunakan dalam penentuan termodinamika reaksi. Uji aktivitas sebagai inhibitor korosi pada baja karbon dilakukan pada senyawa hasil sintesis dengan persen konversi tertinggi dan sampel komersil menggunakan metode gravimetri dalam larutan 1% (w/v) NaCl. Nilai persen efisiensi inhibisi (%EI) tertinggi dari senyawa imidazolin-oleat dan sampel komersil pada konsentrasi 500 ppm berturut-turut sebesar 86,67% dan 80,00%. Nilai %EI senyawa imidazolin-oleat yang didapat dari metode gravimetri ini tidak berbeda signifikan dengan metode elektrokimia (87,95%, 500 ppm). Hal ini menunjukkan bahwa laju korosi menurun secara signifikan dengan adanya senyawa imidazolin-oleat. Senyawa imidazolin-oleat dari penelitian ini diharapkan dapat diaplikasikan dan dikembangkan dalam skala besar di industri.

---

Carbon steel is the principal material used in gas and oil pipelines for production lines. However, carbon steel is vulnerable to corrosion due to its corrosive media. Therefore, this is the main reason for pipelines damage which is causing economic losses. However, corrosion rate can be slow down by using imidazoline, one of the organic corrosion inhibitors. In this study, oleic-imidazolin was successfully synthesized from triethylentetramine (TETA) and oleic acid (OA) at 140°C with various stirring speeds of 500, 750, and 1000 rpm. The reaction mixture then was separated using solvent extraction method, identified using TLC, and characterized using UV-Vis, FTIR, and ¹H-NMR instruments. According to characterization data, oleic-imidazolin was successfully produced by showing a maximum absorption peak at wavelength of 204 nm (UV-Vis), absorption at wavenumber of 1600 and 1500 cm^-1 from C=N and C-N-C, respectively, (FTIR), and a peak at chemical shift of 2.17 ppm to indicate H-C-C=N (¹H-NMR). Determination of kinetic and thermodynamic data as well as the conversion percentage of synthesis reaction with various reaction time, temperature, and stirring speed were analyzed by using acid-base titration to analyze the remaining amount of OA. The results of acid number indicated that the reaction follows the pseudo first order at a maximum temperature of 140°C with the reaction rate constant at 140°C with various stirring speeds of 500, 750, and 1000 rpm were 2.081 x 10^-3; 2.177 x 10^-3; and 2.212 x10^-3 minutes^-1, respectively. The maximum conversion percentage was obtained at 86,143±1,089% (140°C, 1000 rpm). At higher temperatures, 150°C and 160°C, the reaction showed different reaction order (second order), therefore these data were less relevant for determination of reaction thermodynamic study. The ability as corrosion inhibitor of oleic-imidazoline towards carbon steel was conducted on the highest conversion percentage product together with the commercial sample using gravimetric method in 1% (w/v) NaCl solution. The highest inhibition efficiency percentage (%IE) from oleic-imidazoline and commercial sample at concentration of 500 ppm were 86.67% and 80.00%, respectively. The %IE value of oleic-imidazoline obtained from gravimetric method was not significantly different from the electrochemical method (87.95%, 500 ppm). The %IE values from both gravimetric and electrochemical methods indicated a significant corrosion inhibitor. Therefore, oleic-imidazoline from this study are expected to be applied and developed on a large scale in the industry.

Abstrak :
Pada penelitian ini, telah dilakukan sintesis scale-up senyawa imidazolin berbasis asam palmitat dan trietilen tetraamina pada suhu 130, 140 dan 150℃ dengan kecepatan pengadukan 800, 1000 dan 1200 rpm. Senyawa hasil sintesis kemudian diekstraksi dan diidentifikasi menggunakan KLT. Kemudian senyawa dikarakterisasi dengan instrumen FTIR, UV-Vis, NMR (1H dan 13C) dan LC-MS. Senyawa imidazolin-palmitat telah berhasil disintesis dengan menunjukkan adanya puncak absorbansi pada panjang gelombang 212 nm pada UV-Vis, serapan pada bilangan gelombang di sekitar 1600-1400 cm-1 yang menandakan terbentuknya gugus C=N dan C-N-C pada FTIR serta adanya chemical shift 0,86-3,52 dan 4,40 ppm yang menandakan karakteristik proton pada cincin imidazolin, grup pendan, rantai hidrokarbon dan gugus –NH2 pada 1H-NMR didukung dengan hasil analisis 13C NMR yang menunjukkan adanya chemical shift di 22,69-77,32 dan 14,12 ppm. Selanjutnya dilakukan pengujian dengan LC-MS dimana kromatogram memberikan puncak pada waktu retensi 9,72 menit dengan nilai m/z = 367,378. Dilakukan pula penentuan angka asam dengan metode titrasi asam basa untuk studi data kinetika dan persen konversi. Didapatkan bahwa reaksi mengikuti kinetika orde 2 pada suhu 150℃ pada variasi kecepatan pengadukan 800, 1000 dan 1200 dengan nilai konstanta laju reaksi berturut-turut sebesar 1,0 x 10^-4; 2,0 x 10-4 dan 0,9 x 10-4 M-1 menit-1. Persen konversi tertinggi dicapai dengan nilai 94,68% pada sintesis dengan variasi suhu dan kecepatan pengadukan berturut-turut 130℃ dan 800 rpm. Uji inhibisi korosi pada baja karbon dilakukan terhadap imidazolin-palmitat dengan konversi tertinggi antara sampel dengan dan tanpa pemurnian dengan menggunakan metode elektrokimia dan gravimetri dalam larutan NaCl 1,5% yang dijenuhkan dengan CO2. Didapatkan nilai %EI tertinggi sebesar 72,20% dan 80,49% pada metode gravimetri dan elektrokimia secara berurutan dengan konsentrasi senyawa imidazolin-palmitat sebesar 500 ppm. Kemudian dilakukan pencitraan terhadap baja dengan instrumen SEM-EDX. Didapatkan baja dengan penambahan inhibitor memiliki struktur yang lebih bersih dengan pengurangan kadar Fe sebesar 5% dibandingkan dengan baja tanpa penambahan inhibitor dengan pengurangan kadar Fe sebesar 23,9%. Senyawa imidazolin-palmitat dari penelitian ini diharapkan dapat dikembangkan dalam skala yang lebih besar di bidang industri. ......In this research, scale-up synthesis of imidazoline compounds based on palmitic acid and triethylene tetramine has been carried out at 130, 140 and 150℃ with steering speed of 800, 1000 and 1200 rpm. The synthesized compounds were then extracted and identified using TLC. Then the compounds were characterized by FTIR, UV-Vis, NMR (1H and 13C) and LC-MS instruments. The palmitic-imidazoline compound has been successfully synthesized by showing an absorbance peak at a wavelength of 212 nm in UV-Vis, absorption at wave numbers around 1600-1400 cm-1 which indicates the formation of C=N and C-N-C groups on FTIR and the presence of a chemical shift of 0,86-3,52 and 4,40 ppm which indicate the characteristics of the proton in the imidazoline ring, pendant group, hydrocarbon chain and –NH2 group on 1H-NMR supported by the results of 13C NMR analysis which showed a chemical shift at 22,69-77,32 and 14,12 ppm. Furthermore, testing was carried out with LC-MS where the chromatogram gave a peak at a retention time of 9.72 minutes with a value of m/z = 367,378. The acid number was also determined using the acid-base titration method to study kinetic data and conversion percentages. It was found that the reaction followed second-order kinetics at 150℃ at variations of stirring speed of 800, 1000 and 1200 with a reaction rate constant value of 1,0 x 10-4; 2,0 x 10-4 dan 0,9 x 10-4 M-1 min-1respectively. The highest conversion percentage was achieved with a value of 94.68% in the synthesis with variations in temperature and stirring speed of 130℃ and 800 rpm. Corrosion inhibition test on carbon steel was carried out on palmitic-imidazoline with the highest conversion between samples with and without purification using electrochemical and gravimetric methods in 1,5% NaCl solution saturated with CO2. The highest %IE values were obtained at 72.20% and 80.49% in the gravimetric and electrochemical methods respectively with a concentration of imidazoline-palmitate of 500 ppm. Then imaging of the steel was carried out with the SEM-EDX instrument. It was found that steel with the addition of inhibitors had a cleaner structure with a reduction in Fe content of 5% compared to steel without the addition of inhibitors with a reduction in Fe content of 23,9%. The palmitic-imidazoline compound from this research is expected to be developed on a larger scale in the industrial field.