Abstrak :
Rhodium yang disanggah α-A1203 telah diteliti melalui proses reformasi CH4/CO2 pada temperatur tinggi (1250-1325 °K) dan di atas tekanan atmosfer (3-7 atm). Secara termodinamika pada temperatur 1285 K, pembentukan karbon terjadi pada CO2/CH4 <60/40. Aktifitas katalis (0.3%berat) Rhla-A1203 didaparkan sangat baik dan katalis menunjukkan kestabilan selama eksperimen (18 hari) serta tidak menunjukkan adanya tanda-tanda deaktivasi. Umumnya konversi metana dan CO2 meningkat dengan kenaikan temperatur, tekanan dan W/FCH4O. Peningkatan kandungan CO2 sampai CO2/CH4=80/20 ternyata juga dapat menaikkan konversi metana. Penambahan sedikit air (H2O/CH4=5%) dapat menaikkan konversi metana dan CO2. Namun penambahan air selanjutnya menurunkan konversi CO2. Perbandingan reaktan CO2/CH4=70/30 menghasilkan perbandingan gas sintesis H2/CO sekitar 0.80. Perbandingan Hz/CO dapat dinaikkan dengan penambahan H2O. Persamaan laju reaksi diperoleh berdasarkan skema mekanisme Langmuir-Hinshelwood dengan menganggap reaksi permukaan fase teradsorp CH4* dan CO2* sebagai rate limiting step. Pengujian terhadap persamaan laju hanya didasarkan atas data eksperimen variasi tekanan parsial CO2 pada tekanan parsial CH4 konstan pada 1285 K dan 4 atm. Plot antara laju reaksi eksperimen dan laju reaksi perhitungan terhadap tekanan parsial CO2 menunjukkan kurva yang sangat dekat.

Abstrak :
ABSTRAK
Pada mulanya, pembuatan katalis dengan metode amoniak oleh IRC dirancang untuk Ni/SiO2. Dengan metode yang sama dalam penelitian ini dilakukan preparasi katalis Co, Ni, Ni-Cu, Co-Cu dan Ni-Co serta Ni-Co-Cu/Al2O3 yang akan diuji pada proses oksidasi parsial metana menjadi gas sintesis CO, H2.

Kobalt, nikel, Ni-Co dan Ni-Cu dikarakterisasi dengan metode-metode Ekstraksi Magnetik dan TEM yang dilengkapi dengan pengukuran sinar-X serta infra-merah. Dan pengukuran sifat-sifat magnetik, diperoleh morfologi katalis (ukuran partikel, tingkat reduksi). Kinerja adsorpsi CO-katalis yang diamati dengan alas infra-merah, memberikan informasi adanya spesies atau gugus karbonil dan karbonat sekaligus memberikan data mengenai fenomena reduksi dan perihal paduan logam prekursor katalis bimetalik.

Pengaruh waktu kontak antara alumina dengan larutan logam kobalt-heksamin dan frekuensi pencucian prekursor dijadikan bahan pengamatan. Pada waktu kontak 10 merit dan prekursor tidak dicuci diperoleh remanensi magnetik berharga nol (2Mr/Ms = 0) yang memberikan indikasi bahwa dispersi partikel kobalt sangat baik. Akan tetapi jika prekursor dicuci, kandungan partikel Co yang tertanam pada alumina naik, namun demikian selaras dengan peristiwa tersebut diameter rata-rata permukaan partikel katalis juga naik, suatu hal yang tidak dikehendaki. Dengan metode amoniak sukar menaikkan kandungan logam Co pada penyangga, meskipun telah dilakukan teknik pengenceran dan perlakuan khusus terhadap Al2O3 namun dengan teknik tersebut berhasil diperoleh 4-6,6 % berat Co/Al2O3.

Lain halnya dengan preparasi katalis Ni/Al2O3, untuk waktu kontak antara larutan nikel heksamin dengan penyangga Al2O3 selama 96 jam; diperoleh - kandungan Ni sebesar 21,94 % pada penyangga. Dengan metode amoniak ini terlihat bahwa logam Ni lebih mudah diperkaya kandungannya dari pada Co. Jika Co dipadu dengan Ni untuk perbandingan 1/1, diperoleh komposisi akhir katalis sebesar 14,2215,74 % atau 2,48:1

Co-Ni/Al2O3, hasil ini memberikan indikasi bahwa jika Co berkompetisi dengan Ni, maka hasilnya adalah Co lebih mudah tertanam pada alumina.

Untuk sari karakterisasi dan uji aktifitas katalis nikel digunakan 2 jenis alumina, yakni: γ-Al2O3dan Degussa (100 m²/g) dan γ-alumina produksi Rhone-Poulenc (312 m²/g). Dan hasil uji aktivitas, katalis nikel memperlihatkan kinerja sangat baik, dihasilkan perolehan (yield) CO dan H2 mendekati 100 %.

Katalis Ni-Co-Cu/Al2O3 juga dibuat dengan metode amoniak, perbandingan berat antara nikel-nitrat/kobalt-nitrat/tembaga-nitrat/alumina = 1/1/1/0,67. Dengan waktu kontak antara larutan campuran ketiga logam tersebut dengan Al203 selama 15 menit, maka diperoleh berat prekursor katalis sebesar 13,3 gram. Katalis ini belum pernah diuji termasuk sari katalis Ni-Co, Co-Cu dan Ni-Cu/Al2O3.

Pembuatan sari katalis Co, Ni dan paduannya dengan metode amoniak telah diperoleh hasil yang baik, partikel logam tertanam dengan sempurna pada penyangga; dispersi partikel dan uji aktifitas pada suhu tinggi untuk proses oksidasi parsial atau reformasi CO2 metana menjadi gas sintesis memberikan hasil yang memuaskan.

Abstrak :
Reaksi reformasi metana dengan karbondioksida (CO2 reforming) untuk menghasilkan gas sintesis (campuran gas CO dan H2) belum dimanfaatkan pada skala industri. Pada beberapa aplikasi, reaksi ini lebih unggul dibandingkan reaksi reformasi dengan kukus (steam reforming) untuk menghasilkan gas sintesis. Riset dan pengembangan pada saat ini terutama dititikberatkan pada pengembangan katalis dan reaktor untuk reaksi reformasi CO2 yang diaplikasikan sebagai reaksi termokimia untuk konversi dan transmisi energi matahari menjadi energi panas, pembuatan gas sintesis untuk sintesa metanol dan pemanfantan gas alam yang mengandung CO2. Pada penelitian ini, dilakukan pengujian katalis bermuatan logam M dari golongan VIIB dengan penyangga γ-Al2O3. Katalis dipersiapkan dengan metoda impregnation to incipient wetness, dengan muatan 1, 2 dan 3 % mol M/Al, dan dengan metoda impregnasi pelet. Sebagai pembanding, diuji katalis bermuatan 0,5 % mol Rh/Al. Pengujian katalis dilakukan menggunakan reaktor unggun tetap pada suhu 600 - 850 °C dan tekanan 1 atm. Katalis berbentuk butiran berukuran 150 - 250 μm. Sebagai umpan digunakan campuran gas CH4 dan CO2 dengan perbandingan 1 : 1,1 pada laju alir 200 ml/min STP. Hasil terbaik diberikan katalis 2 % mol M/γ-Al2O3 dimana konversi, selektivitas, yield, perbandingan CO/H2 dan parameter kinetika reaksinya lebih baik dari katalis bermuatan M lainnya. Energi aktivasi rata-rata katalis bermuatan logam M yang diuji adalah 131 kJ/mol. Ada kemungkinan pembentukan deposit karbon pada suhu rendah.

Abstrak :
Latar Belakang: Reaksi transfusi adalah reaksi yang disebabkan oleh banyak hal. Reaksi yang paling sering ditemukan adalah reaksi yang berbentuk alergi pada pasien karena ada perbedaan jenis antigen dan antibodi yang ditransfusikan kepada pasien tersebut. Hal ini dapat terjadi karena alasan seperti: kontaminasi virus, bakteri dan juga kesalahan dalam menjaga produk sampai ke tangan pasien. Selain itu faktor yang dapat membuat hal ini terjadi dapat ditemukan dari perbedaan produk pemakaian dan juga kondisi pasien yang sudah ada sebelum pasien di transfusi. Penelitian ini dilakukan untuk melihat apakah perbedaan jenis dan juga penggunaan produk platelet dapat menimbulkan reaksi transfusi. Metode: Penelitian ini menggunakan metode penelitian analitik. Hal ini dilakukan dengan pemberian questionnaire kepada 82 pasien di ruang transfusi dan ruang perinatologi RSCM . Penelitian ini adalah penelitian analitik untuk melihat apa yang menimbulkan reaksi transfusi pada pasien jika ada. Hasil: Reaksi akut adalah reaksi yang paling sering terjadi pada pasien di dalam ruang transfusi dan ruang perinatologi RSCM, dengan gejala yang paling sering terjadi adalah reaksi alergi. Insiden terbanyak adalah terkait dari pemakaian produk TC Kesimpulan: Reaksi transfusi adalah sebuah reaksi yang mungkin terjadi pada setiap episode transfusi. Reaksi dapat terjadi karena adanya reaksi antara antigen dan antibodi pasien yang mungkin saja tidak sesuai dengan produk itu sendiri. Hal seperti kontaminasi dan kelalaian saat memberikan produk juga adalah salah satu faktor resiko adanya kejadian reaksi transfusi ini. Pada 82 pasien yang menggunakan produk platelet ditemukan reaksi akut yang terjadi kepada 59,8% dari keseluruhan pasien transfusi. Pemakaian yang paling sering menimbulkan reaksi adalah produk TC dari seluruh derivatives platelet. ......Background: Transfusion reaction is one of the problems that are most commonly found in hospital setting after the process of transfusion. The occurrences are still present after several preventive measures, transfusion reaction is usually elicited because the product is contaminated by virus, bacteria and also the mismanagement of the product. Other factors that could elicit such reaction varies from the kind of blood product that the patient acquired, how many times the patient have undergone the procedure and also their own diagnosis. Method: Use of questionnaires that are given to 82 pediatric patients in the transfusion ward and perinatologi ward. This is an analytical research that dwells into finding out the causes and also the risk factor of transfusion reaction. Result: Acute reaction is the most common type of reaction happening after the use of platelet product, with the symptoms similar to those of allergic reaction (urticaria, pruritus and rashes). The most common type of product used in RSCM is Thrombocyte Concentrate. Conclusion: Transfusion reaction is a reaction that may occur in every transfusion episode. The reaction could occur due to a reaction between the patient's antigen and antibodies which may not be compatible with the product. Matters such as contamination and negligence when providing products are also one of the risk factors for the occurrence of this transfusion reaction. In 82 patients using platelet products, it is found that acute reaction was the most common reaction in patients from the RSCM transfusion ward with a prevalence of 59.8% of all transfusion patients. The most common product that caused reaction was TC with prevalence causing transfusion reaction as much as 64.2% of all TC product usage. In RSCM, platelet and plasma products used are at TC = 64.6%, Pooled TC = 26.8% and Apheresis Platelet along with other products at 8.5%. In short using platelet product can be deemed as safe since the risk outweighs its benefit.

Abstrak :
Die soldering merupakan salah satu cacat proses pengecoran logam dimana cairan logam melekat pada permukaan baja cetakan. Proses ini merupakan hasil reaksi antar muka antara aluminium cair dengan permukaan cetakan. Aluminium dengan kandungan silikon 7 dan 11% serta baja cetakan SDK 61 merupakan hal yang umum digunakan sebagai cairan logam dan material cetakan pada proses pengecoran tekan (die casting) paduan aluminium. Penelitian ini dilakukan untuk mempelajari morfologi dan karakteristik lapisan intermetalik AlxFeySiz yang terbentuk selama proses reaksi antar muka pada saat pencelupan. Sampel uji yang digunakan yaitu baja perkakas jenis SKD 61 hasil annealing, yang dicelup pada Al-7%Si dengan temperatur tahan 680oC dan dicelup pada Al-11%Si dengan temperatur tahan 710oC pada waktu kontak yang berbeda-beda, yaitu 10 menit; 30 menit dan 50 menit. Hasil penelitian menunjukkan dua lapisan intermetalik terbentuk pada permukaan baja perkakas SKD 61 yakni compact intermetallic layer dengan fasa intermetalik AlxFey dan broken intermetallic layer dengan fasa intermetalik AlxFeySiz. Peningkatan waktu kontak pada proses pencelupan baja perkakas SKD 61 baik pada paduan Al-7%Si maupun Al-11%Si akan meningkatkan ketebalan lapisan intermetalik yang terbentuk sampai titik optimum kemudian menurun kembali. Sedangkan nilai kekerasan mikro dalam setiap lapisan intermetalik AlxFeySiz tergantung dari kadar Fe di dalamnya. Semakin meningkat kadar Fe maka kekerasan intermetallik akan semakin meningkat. Hal ini terjadi karena peningkatan kadar Fe akan berakibat pembentukan partikel fasa intermetalik AlxFeySiz mejadi lebih cepat.

---

Effect of Contact Time on Interface Reaction between Aluminum Silicon (7% and 11%) Alloy and Steel Dies SKD 61. Die soldering (die sticking) is a defect of metal casting in which molten metal ?welds? to the metallic die mold surface during casting process. Die soldering is the result of an interface reaction between the molten aluminum and the die material. Aluminum alloy with 7 and 11% silicon and SKD 61 die steel are the most common melt and die material used in aluminum die casting. This research is done to study the morphology and the characteristics of the formed AlxFeySiz intermetallic layer during interface reaction at dipping test. The samples of as-anneal SKD 61 tool steel was dipped into the molten of Al-7%Si held at temperature 680oC and into molten Al-11%Si held at temperature 710oC with the different contact time of 10 minutes; 30 minutes; and 50 minutes. The research results showed that the interface reaction can form a compact intermetallic layer with AlxFey phase and a broken intermetallic layer with AlxFeySiz phase on the surface of SKD 61 tool steel. The increasing of the contact time by the immersion of material SKD 61 tool steel in both of molten Al-7%Si and Al-11%Si will increase the thickness of the AlxFeySiz intermetallic layer until an optimum point and then decreasing. The micro hardness of the AlxFeySiz intermetallic layer depends on the content of the iron. Increasing of the iron content in intermetallic layer will increase the micro hardness of the AlxFeySiz. This condition happened because the increasing of Fe content will cause forming of intermetallic AlxFeySiz phase becomes quicker.

Abstrak :
Ruang lingkup dan Cara Penelitian : Methisillin Resistant Staphylococcus aureus (MRSA) adalah strain Staphylococcus aureus yang telah mengalami resisten terhadap antibiotika metisilin dan lainnya dalam 1 golongan. Mekanisme resistensi MRSA terjadi karena Staphylococcus aureus menghasilkan Penicillin Binding Protein (PBP2a atau PBP2') yang dikode oleh gen mecA yang memiliki afinitas rendah terhadap metisilin. Saat ini MRSA diuji dengan cara uji resistensi dengan cara Cakram Cxacillin 1 ug. Cara ini memerlukan isolat murni dan kultur bakteri sehingga hasilnya baru bisa diketahui paling cepat 5 hari. Dalam upaya untuk mencari teknik diagnostik yang cepat dan tepat untuk mendeteksi MRSA, deteksi gen mecA dengan teknik PCR merupakan salah satu diagnostik alternatif Tujuan penelitian ini adalah mencari alternatif teknik diagnostik yang cepat dan tepat untuk pemeriksaan MRSA, dalam hal ini PCR. Pengujian dibagi dalam 2 tahap, yaitu : (1). Isolasi dan Identifikasi MRSA secara fenotipik, (2). Deteksi gen mecA pada isolat MRSA dengan teknik PCR yang terdiri dari: optimasi uji PCR untuk deteksi gen mecA, spesifisitas uji PCR, sensitifitas dan spesifisitas deteksi gen mecA sebagai uji diagnostik alternatifMRSA. Basil dan Kesimpulan : Hasil isolasi dan identifikasi secara fenotipik dari 114 isolat diperoleh MRSA sebanyak 76 isolat, dan MSSA sebesar 38 isolat. Berdasarkan hasil penelitian deteksi gen mecA pada isolat MRSA dengan teknik PCR diperoleh 75 isolat menunjukkan hasil positif terhadap gen mecA, sedangkan 1 isolat menunjukkan hasil negatif terhadap gen mecA, isolat tersebut adalah 12951MUI yang diperoleh dari Laboratorium Mikrobiologi Klinik (LMK) FKUI. Dan hasil penelitian ini diperoleh hasil uji PCR gen mecA terhadap beberapa bakteri lain yaitu Staphylococcus epidermidis, S citreus, B. subtilis, Streptococcus beta haemolysicus, E. coli, K. pneumoniae dan P. aeruginosa, ternyata S. epidermidis dan S ciireus menunjukkan hasil PCR positif terhadap gen mecA, sedangkan bakteri lain menunjuldcan hasil negatif terhadap gen mecA. Basil uji PCR gen mecA dibandingkan dengan baku emas pemeriksaan sensitivitas dan spesifisitas secara fenotipik terhadap isolat MRSA dan MSSA adalah 98,7% dan 100%, dan nilai Posistive Predictive Value (PPV)& Negative Predictive Value (NPV) adalah 100% & 97,4%.